• Journal of Surface Science and Engineering
• /
• v.33 no.1
• /
• pp.3-9
• /
• 2000

Arc-melted alloys of TiAl-(o.25, 0.5, 1.0at%) Si were isothermally oxidized at 800, 900 and $1000^{\circ}C$ in air for 60hr. It was found that the oxidation resistance of the prepared TiAl-Si alloys was much better than that of pure TiAl, being progressively increasing with an increase in the Si content. This was attributed to the formation of $SiO_2$in addition to ($TiO_2$+$Al_2$$O_3$) oxides which formed in TiAl alloys with and without silicon additions. However, the silica formation within the oxide layer unfortunately accelerated the oxide scale spallations. During oxidation, all the elements in the base alloy diffused outward, whereas oxygen from the atmosphere diffused inward. The oxides were primarily composed of an outer thick $TiO_2$layer, an intermediate diffuse $Al_2$$O_3$layer and an inner $TiO_2$layer. A small amount of $SiO_2$was present all over the oxide scale and some voids were found around the intermediate layer.

• Journal of Hydrogen and New Energy
• /
• v.14 no.2
• /
• pp.97-104
• /
• 2003

The structural transitions of the matrix and the second phases of $Ti_{1.0}Mn_{0.9}V_{1.1}$ and $Ti_{1.0}Cr_{1.5}V_{1.7}$ alloys upon hydrogenation have been investigated at 293K. The effect of hydrogen isotope on their crystal structures has been also discussed. The crystal structures, Phase abundance and lattice parameters of the hydrides were determined by the Rietveld method using X-ray diffraction data. At the experimental temperature, the $Ti_{1.0}Mn_{0.9}V_{1.1}$ alloy and $Ti_{1.0}Cr_{1.5}V_{1.7}$ alloy revealed different structural transition processes upon hydrogenation although the crystal structures of these two alloys are both BCC at room temperature. The second phases such as Ti-rich phase with $NiTi_2$ structure and $\alpha$-Ti with HCP structure absorbed hydrogen at relatively low hydrogen pressures and the phase abundance remained almost constant. This means that it is desirable to decrease the amount of the second phases as far as possible in order to increase the effective hydrogen storage capacities of the alloys. The crystal structures of corresponding isotope hydrides, the phase abundance and the lattice parameters did not depend on the kind of hydrogen isotope, but only on the hydrogen content.

• Journal of Korea Foundry Society
• /
• v.24 no.1
• /
• pp.45-51
• /
• 2004

Fe and Si are common impurity elements in the aluminum alloys. In this investigation, the effects of the addition of Fe and Si on the age-hardening behaviors of the Al-Cu-Mn-Ti-Zr-Cd casting alloys were examined through hardness measurements, calorimetric techniques and observation of the transmission electron microscopy. The addition of Fe depresses the formation of GPII and ${\theta}'$, and thus retards the peak aging time and reduces the peak hardness of the Al-Cu-Mn-Ti-Zr-Cd alloys. On the contrary, the addition of Si accelerates the formation of GPII and ${\theta}'$ and thus accelerates age-hardening behaviors of the Al-Cu-Mn-Ti-Zr-Cd alloys.

• Proceedings of the Korean Radioactive Waste Society Conference
• /
• 2003.11a
• /
• pp.395-400
• /
• 2003

For the long term storage safety study of the metallic spent fuel, U-Nb, U-Ti, U-Ni, U-Zr, and U-Hf simulated metallic uranium alloys, known as corrosion resistant alloys, were fabricated and oxidized in oxygen gas at $200^{\circ}C~300^{\circ}C$. Simulated metallic uranium alloys were more corrosion resistant than pure uranium metal, and corrosion resistance increases Nb, Ni, Ti in that order. The oxidation rates of uranium alloys determined and activation energy was calculated for each alloy. The matrix microstructure of the test specimens were analyzed using OM, SEM, and EPMA. It was concluded that Nb was the best acceptable alloying elements for reducing corrosion of uranium meta] considered to suitable as candidate.

• Corrosion Science and Technology
• /
• v.21 no.6
• /
• pp.454-465
• /
• 2022

The objective of this study was to determine effects of temperatures and pH of sodium chloride solution with MgCl₂ ions on corrosion resistance of duplex stainless-steel X2CrNiMoN22-5-3 (DSS) and Ti 6Al 2Nb1Ta1Mo (Ti). Effects of sodium chloride concentration on corrosion resistance were also studied. Corrosion behavior and pitting morphology of duplex stainless steel (DSS) and Ti alloys were evaluated through potentiodynamic polarization, electrochemical impedance spectroscopy (EIS), and scanning electron microscopy (SEM). It was found that a decrease in pH significantly reduced the corrosion resistance of both alloys. Changes in chloride concentration and temperature had more substantial impact on corrosion behavior of DSS than on Ti alloys. Pitting corrosion was formed on DSS samples under all conditions, whereas crevice corrosion was developed on Ti samples with the presence of magnesium chloride at 90 ℃. In conclusion, magnesium chloride ions in an exceedingly strong acidity solution appear to interact with re-passivation process at the surface of these alloys and influence the resulting surface topography.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.165-166
• /
• 2006

Nb-Ti alloys were hydrogenated to prepare fine and contamination-free powders. Cracks were introduced in the alloys when they were annealed at 1473 K and cooled in a hydrogen atmosphere. The fragments produced by hydrogen-induced cracking are brittle and the friability enhanced with the Ti content of the alloy, which is beneficial for further refinement of particle size. We also demonstrate that Nb-Ti powders with the average particle size less than 1 m can be produced by ball milling at a temperature lower than 203 K. Furthermore, hydrogen-free powders can then be obtained by annealing above the temperature corresponding to hydrogen desorption from Nb solid solution.

• Resources Recycling
• /
• v.21 no.1
• /
• pp.60-65
• /
• 2012

The Ti-6Al-4V alloys were prepared by recycling of dental Ti pure scraps using vacuum arc melting process, and their physical properties were evaluated the Ti-6Al-4V alloys with different oxygen concentrations. For the preparation of Ti-6Al-4V alloys, Ti pure scraps used for dental implant were utilized as a raw material, and their different oxygen concentrations were ranged from G1 to G4 grade in ASTM standards. It was confirmed that the weight loss of Al in the composition of Ti-6Al-4V alloy could be controlled under the Ar pressure of 875 torr during the melting of alloy. The oxygen concentrations of the Ti-6Al-4V alloys were ranged from 1170 to 3340 ppm. The vickers hardness change of the Ti-6Al-4V alloys showed a similar behavior with that of pure Ti. As a result, we confirmed a possibility of preparation of Ti-6Al-4V alloy by recycling of dental Ti scraps using vacuum arc melting process in this study.

• Journal of Surface Science and Engineering
• /
• v.51 no.3
• /
• pp.139-148
• /
• 2018

In this study, surface analysis of Ni-Cr and Co-Cr alloys with addition of Ti and Mo for dental CAD/CAM use has been researched experimentally. The surface characteristics of the alloys were examined by Vickers hardness test, bonding strength test, surface roughness test, field-emission scanning electron microscopy, energy dispersive X-ray spectroscopy, and X-ray diffraction spectroscopy. The shrinkage of the sintered Ni-Cr alloy alloy was slightly larger than that of Ni-Cr-Ti alloy, and larger than Co-Cr alloy. Also, the addition of Mo showed a tendency to decrease shrinkage somewhat. From the result of XRD analysis, NiCr, $Ni_3Cr$ and $Ni_3Ti$ were observed in the sintered Ni-13Cr-xTi and Ni-13Cr-xMo alloys. In addition, ${\sigma}-CrCo$, $Co_2Mo_3$ and $TiCo_2$ were formed in the sintered Co-Cr-xTi and Co-Cr-xMo alloys. Surface hardness of Ti and Mo added alloy was higher than those of Ni-Cr and Co-Cr alloy. The bond strength between sintered alloy and porcelain was $16.1kgf/mm^2$ for Ni-13Cr alloy, $17.8kgf/mm^2$ for Ni-13Cr-5Ti alloy, and $8.2kgf/mm^2$ for Ni-13Cr-10Ti alloy, respectively.

• Nuclear Engineering and Technology
• /
• v.51 no.1
• /
• pp.190-197
• /
• 2019

W-K-TiC alloys with different titanium carbide concentrations (0.05, 0.1, 0.25, 0.5, 1, 2) wt.% were fabricated through Mechanical Alloying and Spark Plasma Sintering. The effects of the addition of nano-scaled TiC particles on the relative density, Vickers micro-hardness, microstructure, crystal information, thermal shock resistance, and tensile strength were investigated. It is revealed that the doped TiC nano-particles located at the grain boundaries. The relative density and Vickers micro-hardness of W-K-TiC alloys was enhanced with TiC addition and the highest Vickers micro-hardness is 731.55. As the TiC addition increased from 0.05 to 2 wt%, the room-temperature tensile strength raised from 141 to 353 MPa. The grain size of the W-K-TiC alloys decreased sharply from $2.56{\mu}m$ to 330 nm with the enhanced TiC doping. The resistance to thermal shock damage of W-K-TiC alloys was improved slightly with the increased TiC addition.

• Transactions on Electrical and Electronic Materials
• /
• v.12 no.1
• /
• pp.28-31
• /
• 2011

Transformation behavior and shape memory characteristics of Ti-(45-x)Ni-5Cu-xCr (x=0.5-2.0) alloys have been investigated by means of electrical resistivity measurements, differential scanning calorimetry, X-ray diffraction and thermal cycling tests under constant load. Two-stage B2-B19-B19' transformation occurred in Ti-(45-x)Ni-5Cu-xCr alloys. The B2-B19 transformation was separated clearly from the B19-B19' transformation in Ti-44.0Ni-5Cu-1.0Cr and Ti-43.5Ni-5Cu-1.5Cr alloys. A temperature range where the B19 martensite exists was expanded with increasing Cr content because decreasing rate of Ms (85 K / % Cr) was larger than that of Ms' (17 K / % Cr). Ti-(45-x)Ni-5Cu-xCr alloys were deformed in plastic manner with a fracture strain of 68% ~ 43% depending on Cr content. Substitution of Cr for Ni improves the critical stress for slip deformation in a Ti-45Ni-5Cu alloy due to solid solution hardening.