• Korean Journal of Metals and Materials
• /
• v.46 no.5
• /
• pp.321-327
• /
• 2008

Cu based amorphous ($Cu_{54}Zr_{22}Ti_{18}Ni_6$) coating was produced by cold spraying as a new fabrication process. The microstructure and macroscopic properties of amorphous coating layer was investigated and compared with those of cold sprayed pure Cu coating. Amorphous powders were prepared by gas atomization and Al 6061 was used as the substrate plate. X-ray diffraction results showed that Cu based amorphous powder could be successfully deposited by cold spraying without any crystallization. The Cu based amorphous coating layer ($300{\sim}400{\mu}m$ thickness) contained 4.87% porosity. The hardness of Cu based amorphous coating represented $412.8H_v$, which was correspond to 68% of the hardness of injection casted bulk amorphous material. The wear resistance of Cu based amorphous coating was found to be three times higher than that of pure Cu coating. The 3-point bending test results showed that the adhesion strength of Cu based amorphous coating layer was higher than that pure Cu coating. It was also observed that hard Cu base amorphous particle could easily deform soft substrate by particle collisions and thus generated strong adhesion between coating and substrate. However, the amorphous coating layer unexpectedly represented lower corrosion resistance than pure Cu coating, which might be resulted from the higher content of porosity in the cold sprayed amorphous coating.

• Economic and Environmental Geology
• /
• v.39 no.6 s.181
• /
• pp.675-687
• /
• 2006

The purpose of this study is to determine the geochemical characteristics of the stream sediments in the Cheongpung area. So that we can understand the natural background and predict the prospects of geochemical disaster, if any. We collected the stream sediments samples by wet sieving along the primary channels and slow dried the collected samples in the laboratory and ground them to pass a 200 mesh using an alumina mortar and pestle for chemical analysis. Miner-alogical characteristics, major, trace and rare earth elements were determined by XRD, XRF, ICP-AES and NAA analysis methods. For geochemical characteristics on the geological group of stream sediments, the studied area was grouped into granitic gneiss area, metatectic gneiss area, Dado tuff area, Yuchi conglomerate area, and Neungju flow area in the Cheongpung area. Contents of major elements for the stream sediments in the Cheongpung area were $SiO_2\;47.31{\sim}72.81\;wt.%,\;A1_2O_3 \;11.26{\sim}21.88\;wt.%,\;Fe_2O_3\;2.83{\sim}8.39\;wt.%,\;CaO\;0.34{\sim}7.54\;wt.%,\;MgO\; 0.55{\sim}3.59\;wt.%,\;K_2O\;1.71{\sim}4.31\;wt.%,\;Na_2O\;0.56{\sim}2.28\;wt.%,\;TiO_2\;0.46{\sim}1.24\;wt.%,\;MnO\;0.04{\sim}0.27\;wt.%,\;P_2O_5\;0.02{\sim}0.45\;wt.%$. The con-tents of trace and rare earth elements for the stream sediments were $Ba\;700ppm{\sim}8990ppm,\;Be\;1.0{\sim}3.50ppm,\;Cu\;6.20{\sim}60ppm,\;Nb\;12{\sim}28ppm,\;Ni\;4.4{\sim}61ppm,\;Pb\;13{\sim}34ppm,\;Sr\;65{\sim}787ppm,\;V\;4{\sim}98ppm,\;Zr\;32{\sim}164ppm,\;Li\;21{\sim}827ppm,\;Co\;3.68{\sim}65ppm,\;Cr\;16.7{\sim}409ppm,\;Cs\;2.72{\sim}37.1ppm,\;Hf\;4.99{\sim}49.2ppm,\;Rb\;71.9{\sim}649ppm,\;Sb\;0.16{\sim}5.03ppm,\;Sc\;4.97{\sim}52ppm,\;Zn\;26.3{\sim}375ppm,\;Ce\;60.6{\sim}373ppm,\;Eu\;0.82{\sim}6ppm,\;Yb\;0.71{\sim}10ppm$.

• The Journal of the Petrological Society of Korea
• /
• v.7 no.2
• /
• pp.111-131
• /
• 1998

The migmatitic gneiss in the Odesan Gneiss Complex has small amount of quartzite, amphibolite and marble and the Kuryong Group which contact with migmatitic gneiss unconformitly, also contains some amphibolite. Preview studies of this area had regarded that the amphibolites contact with marble had been produced by metasomatism from the pelitic and calcareous sediments mixtures, but the amphibolite is reinterpreted as igneous origin. $SiO_2$ content of the amphibolite is 45.9~52.7 wt%, which corresponds to basaltic composition. MgO content has narrow range (4.6~6.87 wt%) and major and trace element are plotted against MgO,$TiO_2, P_2O_5$, Hf, Zr are reduced and Cr and Ni are increased their content with increasing MgO. This phenomenon indicates that the basaltic magma as the protolith of the amphibolite had frationated with the crystallization of the pyroxene and/or olivine. REE pattern has smoothly decrease from LREE to HREE. Eu/Eu(0.83~1.19) show the flat Eu anomaly, which indicate small fractional crystallization of plagioclase. HREE is enriched in the garnet-bearing amphibolites. Several discrimination diagram for the basaltic magma show that the amphibolite of the study area is originated tholeiitic basaltic magma indicating continental rift environment. Due to determine the metamorphic condition garnet-hornblende geothermometry and hornblende-plagioclase geobarometry are used. Peak metamorphic temperature range of the amphibolite $788~870^{\circ}C$ and is deduced toward the northeastern part. The calculated temperature from the amphibolite has slightly higher than the temperature of the metapelites but the trend of metamorphic grade which decrease from western to eastern part progradly is similar to each other. The metamorphic pressure calculated by garnet- hornblede-plagioclase geobarometry is 4~5kb. But ilmenite-plagioclase pair enclosed in garnet show 8 kb at $700^{\circ}C$ by garnet-ilmenite-rutile-plagioclase geobarometery. The zonal profile of garnet in sample 84 shows the bell-shape profile, which grossular content decreases whereas pyrope content increases progressively. This means that the amphibolite has undergone the clockwise P-T-t path which is shown in the migmatitic gneiss of the Odesan Gneiss Complex.

• Economic and Environmental Geology
• /
• v.38 no.4 s.173
• /
• pp.481-492
• /
• 2005

The purpose of this study is to determine geochemical characteristics for stream sediments in the Gwangju area. We collect the stream sediments samples by wet sieving along the primary channels and dry these samples slowly in the laboratory and grind to under 200mesh using an alumina mortar fur chemical analysis. Major elements, trace and rare earth elements are determined by XRF, ICP-AES and NAA analysis methods. For geochemical characteristics on geological groups of stream sediments, we separate geologic groups which are derived from Precambrian granite gneiss area, Jurassic granite area and Cretaceous Hwasun andesite area. Contents range of major elements for stream sediments in the Gwangju area are $SiO_2\;51.89\~70.63\;wt.\%,\;Al_2O-3\;12.91\~21.95\;wt.\%,\;Fe_2O_3\;3.22\~9.89\;wt.\%,\;K_2O\;1.85\~4.49\;wt.\%,\;MgO\;0.68\~2.90\;wt.\%,\;Na_2O\;0.48\~2.34\;wt.\%,\;CaO\;0.42\~6.72\;wt.\%,\;TiO_2\;0.53\~l.32\;wt.\%,\;P_2O_5\;0.06\~0.51\;wt.\%\;and\;MnO\;0.05\~0.69\;wt.\%.$ According to the AMF diagram for stream sediments and rocks, the stream sediments are plotted on boundary of tholeiitic series and calk alkaline series, which shows that contents of $Fe_2O_3$ are higher in stream sediments than rocks. According to variation diagram of $SiO_2$ versus $(K_2O+Na_2O),$ stream sediments are plotted on subalkaline series. Contents range of trace and rare earth elements for stream sediments in the Gwangiu area are Ba$590\~2170$ppm, Be1\~2.4$ppm, Cu$13\~79$ppm, Nb$20\~34$ppm, Ni$10\~50$ppm, Pb$17\~30$ppm, Sr$70\~1025$ ppm, V$42\~135$ppm, Zr$45\~171$ppm, Li$19\~77$ppm, Co$4.3\~19.3$ppm, Cr$28\~131$ppm, Cs$3.1\~17.6$ppm, Hf$5\~27.6$ppm, Rb$388\~202$ppm, Sb$0.2\~l.2$ ppm, Sc$6.4\~17$ppm, Zn$47\~389$ppm, Pa$8.8\~68.8$ppm, Ce$62\~272$ppm, Eu$1\~2.7$ppm and Yb$0.9\~6$ppm.

• Economic and Environmental Geology
• /
• v.31 no.4
• /
• pp.297-310
• /
• 1998

Geochemical characteristics of environmental toxic elements at the Narim mine area were investigated on the basis of major, minor, rare earth element geochemistry and mineralogy. Ratios of $Al_2O_3/Na_2O$ and $K_2O/Na_2O$ in soils and sediments range from 11.57 to 22.21 and from 1.86 to 3.93, and are partly negative and positive correlation against $SiO_2/Al_2O_3$ (3.41 to 4.78), respectively. These suggested that sediment source of host granitic gneiss could be due to rocks of high grade metamorphism originated by sedimentary rocks. Characteristics of some trace and rare earth elements of V/Ni (0.33 to 1.95), Ni/Co (2.00 to 6.50), Zr/Hf (11.27 to 53.10), La/Ce (0.44 to 0.55), Th/Yb (4.07 to 7.14), La/Th (2.35 to 3.93), $La_N/Yb_N$ (6.58 to 13.67), Co/Th (0.63 to 2.68), La/Sc (3.29 to 5.94) and Sc/Th (0.49 to 1.00) are revealed a narrow range and homogeneous compositions may be explained by simple source lithology. Major elements in all samples are enriched $Al_2O_3$, MgO, $TiO_2$ and LOI, especially $Fe_2O_3$ (mean=7.36 wt.%) in sediments than the composition of host granitic gneiss. The average enrichment indices of major and rare earth elements from the mining drainage are 2.05 and 2.91 of the sediments and are 2.02 and 2.60 of the soils, normalizing by composition of host granitic gneiss, respectively. Average composition (ppm) of minor and/or environmental toxic elements in sediments and soils are Ag=14 and 1, As=199 and 14, Cd=22 and 1, Cu=215 and 42, Pb=1770 and 65, Sb=18 and 3, Zn=3333 and 170, respectively, and extremely high concentrations are found in the subsurface sediments near the ore dump. Environmental toxic elements were strongly enriched in all samples, especially As, Cd, Cu, Pb, Sb and Zn. The level of enrichment was very severe in mining drainage sediments, while it was not so great in the soils. Based on the EPA value, enrichment index of toxic elements is 8.63 of mining drainage sediments and 0.54 of soils on the mining drainage. Mineral composition of soils and sediments near the mining area were partly variable being composed of quartz, mica, feldspar, amphibole, chlorite and clay minerals. From the gravity separated mineralogy, soils and sediments are composed of some pyrite, arsenopyrite, chalcopyrite, sphalerite, galena, goethite and various hydroxide minerals.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2002.07a
• /
• pp.25-37
• /
• 2002

The most important industrial application of gamma radiation in characterizing green compacts is the determination of the density. Examples are given where this method is applied in manufacturing technical components in powder metallurgy. The requirements imposed by modern quality management systems and operation by the workforce in industrial production are described. The accuracy of measurement achieved with this method is demonstrated and a comparison is given with other test methods to measure the density. The advantages and limitations of gamma ray densitometry are outlined. The gamma ray densitometer measures the attenuation of gamma radiation penetrating the test parts (Fig. 1). As the capability of compacts to absorb this type of radiation depends on their density, the attenuation of gamma radiation can serve as a measure of the density. The volume of the part being tested is defined by the size of the aperture screeniing out the radiation. It is a channel with the cross section of the aperture whose length is the height of the test part. The intensity of the radiation identified by the detector is the quantity used to determine the material density. Gamma ray densitometry can equally be performed on green compacts as well as on sintered components. Neither special preparation of test parts nor skilled personnel is required to perform the measurement; neither liquids nor other harmful substances are involved. When parts are exhibiting local density variations, which is normally the case in powder compaction, sectional densities can be determined in different parts of the sample without cutting it into pieces. The test is non-destructive, i.e. the parts can still be used after the measurement and do not have to be scrapped. The measurement is controlled by a special PC based software. All results are available for further processing by in-house quality documentation and supervision of measurements. Tool setting for multi-level components can be much improved by using this test method. When a densitometer is installed on the press shop floor, it can be operated by the tool setter himself. Then he can return to the press and immediately implement the corrections. Transfer of sample parts to the lab for density testing can be eliminated and results for the correction of tool settings are more readily available. This helps to reduce the time required for tool setting and clearly improves the productivity of powder presses. The range of materials where this method can be successfully applied covers almost the entire periodic system of the elements. It reaches from the light elements such as graphite via light metals (AI, Mg, Li, Ti) and their alloys, ceramics ($AI_20_3$, SiC, Si_3N_4, $Zr0_2$, ...), magnetic materials (hard and soft ferrites, AlNiCo, Nd-Fe-B, ...), metals including iron and alloy steels, Cu, Ni and Co based alloys to refractory and heavy metals (W, Mo, ...) as well as hardmetals. The gamma radiation required for the measurement is generated by radioactive sources which are produced by nuclear technology. These nuclear materials are safely encapsulated in stainless steel capsules so that no radioactive material can escape from the protective shielding container. The gamma ray densitometer is subject to the strict regulations for the use of radioactive materials. The radiation shield is so effective that there is no elevation of the natural radiation level outside the instrument. Personal dosimetry by the operating personnel is not required. Even in case of malfunction, loss of power and incorrect operation, the escape of gamma radiation from the instrument is positively prevented.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2014.02a
• /
• pp.476-476
• /
• 2014

서론: 저 전력 소모를 필요로 하는 무선 센서 네트워크 관련 기술의 급격한 발달과 함께 자체 전력 수급을 위한 진동 에너지 수확 기술에 대한 연구가 활발히 이루어지고 있다. 다양한 구조와 소재를 압전 외팔보에 적용하여 제안하고 있다. 그 중에서도 진동 기반의 에너지 수확 소자는 주변 환경에서 쉽게 진동을 얻을 수 있고, 높은 에너지 밀도와 제작 방법이 간단하다는 장점을 가지고 있어 많은 분야에 응용 및 적용 가능하다. 기존 연구에서는 2차원적으로 진동 에너지 수확을 위한 휜 구조의 압전 외팔보를 제안 하였다. 휜 구조를 갖는 압전 외팔보는 각각의 짧은 두 개의 평평한 외팔보가 일렬로 연결된 것으로 볼 수 있다. 하나의 짧고 평평한 외팔보는 진동이 가해지면 접선 방향으로 응력이 생겨 최대 휨 모멘텀을 갖게 된다. 그러므로 휜 구조를 갖는 외팔보는 진동이 인가됨에 따라 길이 방향과 수직 방향으로 진동한다. 하지만, 이 구조는 수평 방향으로 가해지는 진동에 대한 에너지를 수확하기에는 한계점을 가진다. 즉, 3축 방향에서 임의의 방향에서 진동 에너지를 수확하기는 어렵다. 본 연구에서는 3축 방향에서 에너지를 효율적으로 수확할 수 있도록 헤어-셀 구조의 압전 외팔보 에너지 수확소자를 제안한다. 제안된 소자는 길이 방향과 수직 방향뿐만 아니라 수평 방향으로도 진동하여 임의의 방향에서 진동 에너지를 수확할 수 있다. 구성 및 공정: 제안하는 소자는 3축 방향에서 임의의 진동을 수확하기 위해서 길이를 길게 늘이고 길이 방향을 따라 휘어지는 구조의 헤어-셀 구조로 제작하였다. 외팔보의 구조는 외팔보의 폭 대비 길이의 비가 충분히 클 때, 추가적인 자유도를 얻을 수 있다. 그러므로 헤어-셀 구조의 에너지 수확 소자는 기본적인 길이 방향, 수직방향 그리고 수평방향에 더불어 추가적으로 뒤틀리는 방향을 통해서 3차원적으로 임의의 주변 진동 에너지를 수확하여 전기적인 에너지로 생성시킬 수 있다. 제작된 소자는 높은 종횡비를 갖는 무게 추($500{\times}15{\times}22{\mu}m3$)와 길이 방향으로 길게 휜 압전 외팔보($1000{\times}15{\times}1.7{\mu}m3$)로 구성되어있다. 공정 과정은 다음과 같다. 먼저, 실리콘 웨이퍼 위에 탄성층을 형성하기 위해 LPCVD SiNx를 $0.8{\mu}m$와 LTO $0.2{\mu}m$를 증착 후, 각각 $0.03{\mu}m$과 $0.12{\mu}m$의 두께를 갖는 Ti와 Pt을 하부 전극으로 스퍼터링한다. 그리고 Pb(Zr0.52Ti0.48)O3 박막을 $0.35{\mu}m$ 두께로 졸겔법을 이용하여 증착하고 상부 Pt층을 두께 $0.1{\mu}m$로 순차적으로 스퍼터링하여 형성한다. 상/하부 전극은 ICP(Inductively Coupled Plasma)를 이용해 건식 식각으로 패턴을 형성한다. PZT 층과 무게 추 사이의 보호막을 씌우기 위해 $0.2{\mu}m$의 Si3N4 박막이 PECVD 공정법으로 증착되고, RIE로 패턴을 형성된다. Ti/Au ($0.03/0.35{\mu}m$)이 E-beam으로 증착되고 lift-off를 통해서 패턴을 형성함으로써 전극 본딩을 위한 패드를 만든다. 초반에 형성한 실리콘 웨이퍼 위의 SiNx/LTO 층은 RIE로 외팔보 구조를 형성한다. 이후에 진행될 도금 공정을 위해서 희생층으로는 감광액이 사용되고, 씨드층으로는 Ti/Cu ($0.03/0.15{\mu}m$) 박막이 스퍼터링 된다. 도금 형성층을 위해 감광액을 패턴화하고, Ni0.8Fe0.2 ($22{\mu}m$)층으로 도금함으로써 외팔보 끝에 무게 추를 만든다. 마지막으로, 압전 외팔보 소자는 XeF2 식각법을 통해 제작된다. 제작된 소자는 소자의 여러 층 사이의 고유한 응력 차에 의해 휨 변형이 생긴다. 실험 방법 및 측정 결과: 제작된 소자의 성능을 확인하기 위하여 일정한 가속도 50 m/s2로 3축 방향에 따라 입력 주파수를 변화시키면서 출력 전압을 측정하였다. 먼저, 소자의 기본적인 공진 주파수를 얻기 위하여 수직 방향으로 진동을 인가하여 주파수를 변화시켰다. 그 때에 공진 주파수는 116 Hz를 가지며, 최대 출력 전압은 15 mV로 측정되었다. 3축 방향에서 진동 에너지 수확이 가능하다는 것을 확인하기 위하여 제작된 소자를 길이 방향과 수평 방향으로 가진기에 장착한 후, 기본 공진 주파수에서의 출력 전압을 측정하였다. 진동이 길이방향으로 가해졌을 때에는 33 mV, 수평방향으로 진동이 인가되는 경우에는 10 mV의 최대 출력 전압을 갖는다. 제안하는 소자가 수 mV의 적은 전압은 출력해내더라도 소자는 진동이 인가되는 각도에 영향 받지 않고, 3축 방향에서 진동 에너지를 수확하여 전기에너지로 얻을 수 있다. 결론: 제안된 소자는 3축 방향에서 진동 에너지를 수확할 수 있는 에너지 수확 소자를 제안하였다. 외팔보의 구조를 헤어-셀 구조로 길고 휘어지게 제작함으로써 기본적인 길이 방향, 수직방향 그리고 수평방향에 더불어 추가적으로 뒤틀리는 방향에서 출력 전압을 얻을 수 있다. 미소 전력원으로 실용적인 사용을 위해서 무게추가 더 무거워지고, PZT 박막이 더 두꺼워진다면 소자의 성능이 향상되어 높은 출력 전압을 얻을 수 있을 것이라 기대한다.

• Composites Research
• /
• v.27 no.4
• /
• pp.146-151
• /
• 2014

In this study, the experimental study has been performed by varying the polarization of the electric field and impact force to check the piezoelectric characteristics of piezoelectric paint sensor. Piezoelectric paint sensor used in this study is composed of epoxy resin with a hardener and PNN-PZT powder in 1:1 weight ratio. The dimensions of the paint sensor specimen are $40{\times}40{\times}1mm^3$ and regular specimens were made using a mold. The voids are removed from the specimen in the vacuum desiccator. Both upper side and bottom side of the paint sensor were coated with silver paste for making an electrode and then dried at room temperature for a day. The poling treatment has been carried out under controlled conditions of the electric field in order to check the effect of piezoelectric sensitivities, while the poling temperature was fixed at room temperature and the poling time was set to 30 min. The piezoelectric sensitivities have been measured by comparing output voltage from paint sensor with output force from impact hammer when the impact hammer hits the paint sensor. In result, the effect of the electric field has been evaluated for the sensitivity and describe the result.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.174-174
• /
• 2008

초음파를 이용하여 액체 연료를 분사하면 균일한 입경과 미립화가 우수하며 에너지 절약과 공해방지등을 할 수 있다. 또한 유속과 유량에 관계없이 이용할 수 있어 반도체 분야의 웨이퍼와 평판 표시기상에 사진 석판용 화학물질의 균일도포 컴퓨터 하드 디스크의 광택제 도포등에 사용할 수 있다. 이처럼 초저의 유출 용량을 요구하는 모든 공정 및 액체연료의 분사가 요구되는 모든 산업에 적용할 수 있는 장점을 가지고 있다. 하지만 현제까지 주로 사용되고 있는 초음파노즐의 액츄에이터는 단판액츄에이터형로 높은 교류전압을 인가해주어야 하는 단점을 가지고 있다. 이 단점을 해결하기 위해 적층액츄에이터형을 사용하여 초음파 노즐 구동하면 낮은 교류 입력전압에서도 단판액츄에이터형 초음파 노즐과 같은 특성을 가질 수 있다. 또한 초음파 노즐의 구동시 기계적인 진동을 이용하므로 많은 열을 발생시켜 노즐의 온도가 상승하여 세라믹 액츄에이터에도 그 영향을 미치게 되어 열적 열화 현상이 일어날 수 있기에 높은 큐리온도를 가지는 액츄에이터가 필요하다. 본 실험에서는 $Pb(Mn_{1/3}Nb_{2/3})_{0.02}(Ni_{1/3}Nb_{2/3})_{0.12}(Zr_{0.50}Ti_{0.50})_{0.86}O_3$ 조성을 사용하여 $900^{\circ}C$의 저온에서 액상 소결하여 적층혈액츄에이터를 제작하였으며 압전 및 유전 특성을 조사하였다. 제작된 초음파노즐을 구동하기 위해서는 약 36kHz의 30V이상의 교류입력전압 할 수 있는 구동회로가 필요로 한다. 압전액츄에이터의 구동을 위해서는 정확한 정현파 입력이 필요 없다. 압전액츄에이터의 특성상 유사 정현파 입력 만으로도 임피던스 매칭이 이루어지기 때문에 설계가 쉽고 간편한 Push-Pull 방식을 이용한 PWM인버터를 사용하였고 인버터의 출력 주파수를 34~38kHz까지 가변 할 수 있게 설계하였다. 제작된 적층액츄에이터형 초음파 노즐을 PWM인버터로 실제 액체 연료인 경유를 분사하였을 때의 액츄에이터의 온도 변화에 따른 공진주파수와 온도 의존성, 전기적 특성을 조사하고 미립화 분사되는 경유의 미립자 크기 및 최대 분사량을 조사 하였다.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.190-190
• /
• 2008

자연적으로 발생되는 파도, 비, 우박 등과 철도, 차량 및 엘리베이터 등과 같은 인위적인 설치, 이동에 의해 발생되는 진동에너지는 우리 일상생활에서 가장 흔하게 발생할 수 있는 에너지원인데, 이러한 진동에너지는 압전 소재를 이용하여 재생 가능하여 최근에는 이에 대한 연구가 활발히 진행되어 왔다. 예를 들면, 미국의 MIT에서는 인간이 걸을 때 신발에 가해지는 압력을 이용하여 전력을 발생시키는 연구를 진행하여 2.9 mW의 전력을 얻었다. 특히 이러한 기술은 인간의 걷기 운동 등과 같은 일상적인 동작으로 필요한 전력을 얻을 수 있고, 세라믹 소자를 이용하기 때문에 전자노이즈가 발생되지 않을 뿐 아니라 반영구적으로 사용할 수가 있어서, 소형 전자기기 등에 서 기존 이차전지를 대체 또는 보완 할 수 있는 기술로 검토되고 있다. PZT계 세라믹스는 높은 유전상수와 우수한 압전특성으로 이러한 압전발전 분야에서 가장 널리 사용되어지고 있다. 하지만 에너지 효율을 높이기 위하여 적층 구조의 제작 시 구조적 특성상 내부전극이 도포된 상태에서 동시 소결이 필요한데, $1000^{\circ}C$ 이상의 높은 소결온도 때문에 소재 원가가 낮은 Ag전극 대신 값비싼 Pd나 pt가 다량 함유된 Ag/Pd, Ag/Pt 전극이 사용되고 있어 경제성이 떨어지는 단점을 갖게 된다. 순수 Ag 전극을 사용하거나 Ag의 비율이 높은 내부전극을 사용하기 위해서는 $900^{\circ}C$ 이하에서 소결되고 우수한 전기적 특성을 보이는 압전 세라믹스 소재를 개발 하는 것이 필요하다. 따라서 본 연구에서는 압전특성이 우수한 $(Pb_{1-x}Cd_x)(Ni_{1/3}Nb_{2/3})_{0.25}(Zr_{0.35}/Ti_{0.4})O_3$ 계의 조성을 설계하고, 소결온도를 낮추기 위해서 2 단계 하소법을 이용하였다. 또한 $MnCO_3$, $SiO_2$, $Pb_3O_4$ 등을 소랑 첨가하여 액상 소걸 특성을 부여하여 소결 온도를 감소시키려는 시도도 하였다. 소결체의 전체적인 제조 공정은 일반적인 벌크 세라믹의 소걸 공정을 따랐다. 최종 소결된 시편을 XRD분석을 통하여 상을 확인하였고 SEM을 이용하여 미세조직을 관찰 하였다. 전기적 특성을 평가하기 위하여 두께를 1mm로 연마한 시편에 Ag 전극을 도포하여 $650^{\circ}C$ 에서 열처리한 후, 분극처리 하였다. Impedance analyzer를 이용하여 압전 특성 (전기기계결합계수 및 기계적품질계수)을 측정 하였고, 압전전하상수는 $d_{33}$-meter로 측정하였다. 본 연구에서는 압전체에 가해지는 하중의 크기, 시편의 크기, 하중을 가하는 방법, 에너지 저장회로의 최적화 등을 다양하게 시도하면서 에너지 변환 및 저장 효율을 평가하였다.