• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.859-860
• /
• 2006

TiC-$TiB_2$-SiC system was a ternary eutectic, whose eutectic composition was 34TiC-$22TiB_2$-44SiC (mol%). TiC-$TiB_2$-SiC ternary eutectic composite were synthesized by a floating zone method using TiC, $TiB_2$ and SiC powders as starting materials. The TiC-$TiB_2$-SiC eutectic composite showed a lamellar texture. TiC(022), $TiB_2(010)$ and SiC(111) of the eutectic composite were perpendicular to the growth direction. TiC-$TiB_2$-SiC ternary eutectic composite had specific relationship among the crystal planes: TiC[011]//$TiB_2[010]$//SiC[112], TiC(200)//$TiB_2$(001)//SiC(402) and $TiC(1\bar{1}1)$//$TiB_2(101)$//SiC(220).

• Journal of Korea Foundry Society
• /
• v.23 no.2
• /
• pp.77-85
• /
• 2003

Some alloying elements such as Cr, B, Ti and Si were added individually or as a mixture to Fe-30 at.%Al alloys. The alloys were melted using an arc furnace and then heat-treated for homogenization at 1000$^{\circ}C$ for 7 days and followed by rolling at 1000$^{\circ}C$. The alloying elements on rolling characteristics were investigated by the microstructures and fracture mode before and after rolling. The microstructures before rolling showed that all of the alloys had equiaxed grains. On the other hand, the microstructures of rolling plane as well as its perpendicular plane became elongated after rolling. The alloys such as Fe-30Al, Fe-30Al-3Ti, Fe-30Al-0.5B, Fe-30Al-5Cr and Fe-30Al-3Ti-0.5B revealed better rolling behaviour from the point that intergranular and cleavage fractures were not fundamentally occurred. But the addition of 5Ti or 3Si to Fe-Al alloys had detrimental effects. The Ti-added alloy system such as Fe-30Al-5Ti, Fe-30Al-5Ti-5Cr, Fe-30Al-3Ti-5Cr and Fe-30Al-5Ti-0.5B were cracked through grain and showed cleavage fracture. The Si-added alloy system such as Fe-30Al-5Si, Fe-27Al-3Si and Fe-27Al-5Cr-3Si were cracked along the grain boundary and showed intergranular fracture. $DO_3{\leftrightarrow}B_2$ transition temperature of Fe-30at.%Al alloy was 520$^{\circ}C$, whereas the addition of 3Ti and 3Ti+0.5B comparably increased the temperature to 797 and 773$^{\circ}C$, respectively.

• Journal of the Korean Society of Safety
• /
• v.20 no.4 s.72
• /
• pp.29-33
• /
• 2005

In this paper, reflectance and the dielectric characteristics for $P_2O_5-ZnO-BaO$ system and $SiO_2-ZnO-B_2O_3$ system have been investigated as a function of contents of $TiO_2$. The reflectance was decreased with increasing the contents of $TiO_2$ and the reflectance of $P_2O_5-ZnO-BaO$ system was lowered than that of $SiO_2-ZnO-B_2O_3$ system. The dielectric constant of $P_2O_5-ZnO-BaO$ system was higher than $SiO_2-ZnO-B_2O_3$ system, and the dielectric constant in the both system was increased with increasing of $TiO_2$ contents. This can be explained as the space charge effects. These results are could be applied to the under plate dielectrics of PDP required high reflective ratio and breakdown strength.

• The Korean Journal of Ceramics
• /
• v.5 no.2
• /
• pp.155-161
• /
• 1999

The tribological behaviour of monolithic SiC as well as SiC-TiC and SiC-TiC-$TiB_2$ particulate composite materials has been investigated in unlubricated oscillating sliding tests against $Al_2O_3$ at temperature in the range from room temperature up to $600^{\circ}C$. At temperatures below $600^{\circ}C$ the wear rate of the systems with the composite materials was up to 20 times lower than the wear of the $Al_2O_3$/SiC system and was dominated by the oxidation of the titanium phases. At $600^{\circ}C$ the oxidation rate of the TiC and -TEX>$TiB_2$ grains becomes predominant resulting in an enhanced wear rate of the composite rate of the TiC and TiB2 grains becomes predominant resulting in an enhanced wear rate of the composite materials. The coefficient of friction shows similar values for all materials of investigation, increasing from 0.25…0.3 at room temperature to 0.7…0.8 $600^{\circ}C$. The wear of the $Al_2O_3$/SiC system is mainly abrasive at temperatures above room temperature and is characterised by an enhanced wear of the alumina ball at $600^{\circ}C$.

• 전자공학회논문지 IE
• /
• v.43 no.4
• /
• pp.8-12
• /
• 2006

In this paper, reflectance and the dielectric characteristics for $P_2O_5$-ZnO-BaO system and $SiO_2-ZnO-B_2O_3$ system have been investigated as a function of contents of $TiO_2$. The reflectance was decreased with increasing the contents of $TiO_2$ contents, and the reflectance of $P_2O_5$-ZnO-BaO system was lowered than that of $SiO_2-ZnO-B_2O_3$ system. The dielectric constant of $P_2O_5$-ZnO-BaO system was higher than $SiO_2-ZnO-B_2O_3$ system, and the dielectric constant in the both system was increased with increasing of $TiO_2$ contents. This can explained as the space charge effects. These results are could be applied to the lower dielectrics layer of PDP required high reflective ratio and breakdown strength.

• The Korean Journal of Ceramics
• /
• v.5 no.2
• /
• pp.189-194
• /
• 1999

Crystallization of glasses in the system (Ca, Sr, Ba)$O-Al_2O_3-B_2O_3-SiO_2-TiO_2$ and dielectric properties of crystallized glasses were investigated. As increasing B2O3 content and decreasing SiO2 content in the glass, the major crystalline phase changed from $(Sr, Ba)_2TiSi_2O_8$ to (Ca, Sr, Ba)TiO3, the dielectric constant of crystallized glasses increased and the Temperature Coefficient of Capacitance (TCC) changed to negative. The dielectric constant and TCC was estimated for (Sr, Ba)2TiSi2O8 phase as 18 and -440 $ppm/^{\circ}C$, respectively and for (Ca, Sr, Ba)TiO3 phase as 307 and -1900 $ppm/^{\circ}C$, respectively. The dielectric properties of (Ca, Sr, Ba)TiO3 phase (in this study) were similar to those of (Ca, Ba) TiO_3 solid-solution^12)$, but $(Sr, Ba)_2TiSi_2O_8$ phase (in this study) and $Sr_2TiSi_2O_\;8^4$ showed the different properties.

• Journal of the Korean Ceramic Society
• /
• v.45 no.12
• /
• pp.815-820
• /
• 2008

The microstructure and mechanical properties of $TiB_2/Si$ nanocomposites based on the Ti-Si-B system, consolidated by spark plasma sintering of mechanically alloyed activated nanopowders, have been characterized. Mechanical Alloying was carried out in a planetary ball mill for 180 min with 350 rev $min^{-1}$. The powders were pressed in vacuum at a pressure of 60 MPa, generating a maximum temperature in the graphite mould of $1400^{\circ}C$. Analysis of the synthesized nanocomposites by SEM, XRD and TEM showed them to consist of $TiB_2$ second phase, sub-micron in size, with no third phase. Composites consolidated from powders mechanically alloyed from an initial elemental powder mix of 0.3 mol Si, 0.7 mol Ti, and 2.0 mol B achieved the best relative density (97%) and bending strength (774 MPa); the highest Vickers hardness of 14.7 GPa was achieved for the 0.1-0.9-2.0 mol starting composition.

• Korean Journal of Materials Research
• /
• v.8 no.3
• /
• pp.189-194
• /
• 1998

The redistribution behavior of boron during Co silicidation annealing in the Co/metal/Si system was investigated using SIMS. Ti, Nb and Hf films were used as epitaxy promoting metal layers. After annealing treatment the boron peak height was about 1 order lowered in Co/Ti/Si and Co/Nb/Si systems but the relative peak position from the surface did not change. The distribution of boron was very similar to those of Ti and Nb, because of the strong affinities of boron with them. Also, the position of the main boron peak in the Co/Hf/Si system was almost the same as that of Hf, but the distribution feature of the Co/Hf/Si system somewhat differed from those of Co/Ti/Si and Co/Nb/Si systems. This implies that the affinity between B and Hf is weaker than those of B-Ti and B-Nb. Boron tends to be depleted at the silicidelsi interface while it tends to be piled-up at the Co-metal/Co silicide interface during silicidation annealing.

• Journal of Korea Foundry Society
• /
• v.38 no.6
• /
• pp.121-131
• /
• 2018

The effect of additives on the castability of the AC2BS aluminum alloy, which contains 35% recycled scrap, was investigated. For the wide utilization of the recycled scrap AC2BS aluminum alloy, the research results were compared to those with the AC2B virgin alloy, which is typical Al-Si-Cu alloy system. It was confirmed that the addition of Al-5%Ti-1%B increased the ${\alpha}$-Al nucleation temperature during solidification and decreased the grain size through cooling curve and microstructural observations of the recycled alloy. It was also found that an addition of Al-10%Sr decreased the eutectic Si growth temperature during the solidification process and modified the shape of the eutectic Si of the recycled alloy. The characteristics of fluidity, shrinkage and solidification crack strength were evaluated. For the AC2BS aluminum alloy containing 35% recycled scrap, both ${\alpha}$-Al grain refinement due to Ti-B and eutectic Si modifications due to Sr contributed to the improvement of the fluidity. The macro- shrinkage ratio increased with additions of both Al-10%Sr and Al-5%Ti-1%B and the micro-shrinkage ratio increased with the addition of Al-10%Sr but decreased with the addition of Al-5%Ti-1%B. The casting characteristics of TiB and Sr-treated AC2BS aluminum alloy containing 35% recycled scrap are similar to those of AC2B virgin alloy. The improvement of the solidification crack strength of the AC2BS aluminum alloy was possible by the reduction of the grain boundary the stress concentration through the enhancement by both ${\bullet}{\cdot}$-Al refinement and eutectic Si modification. More extensive use of the AC2BS aluminum alloy containing 35% recycled scrap can be expected in the future.

• The Transactions of The Korean Institute of Electrical Engineers
• /
• v.56 no.9
• /
• pp.1602-1608
• /
• 2007

The composites were fabricated, respectively, using 61[vol.%] SiC-39[vol.%] $TiB_2$ and using 61[vol.%] SiC-39[vol.%] $ZrB_2$ powders with the liquid forming additives of 12[wt%] $Al_2O_3+Y_2O_3$ by hot pressing annealing at $1650[^{\circ}C]$ for 4 hours. Reactions between SiC and transition metal $TiB_2$, $ZrB_2$ were not observed in this microstructure. The result of phase analysis of composites by XRD revealed SiC(6H, 3C), $TiB_2$, $ZrB_2$ and $YAG(Al_5Y_3O_{12})$ crystal phase on the Liquid-Phase-Sintered(LPS) $SiC-TiB_2$, and $SiC-ZrB_2$ composite. $\beta\rightarrow\alpha-SiC$ phase transformation was occurred on the $SiC-TiB_2$ and $SiC-ZrB_2$ composite. The relative density, the flexural strength and Young's modulus showed the highest value of 98.57[%], 249.42[MPa] and 91.64[GPa] in $SiC-ZrB_2$ composite at room temperature respectively. The electrical resistivity showed the lowest value of $7.96{\times}10^{-4}[\Omega{\cdot}cm]$ for $SiC-ZrB_2$ composite at $25[^{\circ}C]$. The electrical resistivity of the $SiC-TiB_2$ and $SiC-ZrB_2$ composite was all positive temperature coefficient resistance (PTCR) in the temperature ranges from $25[^{\circ}C]$ to $700[^{\circ}C]$. The resistance temperature coefficient of composite showed the lowest value of $1.319\times10^{-3}/[^{\circ}C]$ for $SiC-ZrB_2$ composite in the temperature ranges from $100[^{\circ}C]$ to $300[^{\circ}C]$ Compositional design and optimization of processing parameters are key factors for controlling and improving the properties of SiC-based electroconductive ceramic composites.