• Journal of the Korean institute of surface engineering
• /
• v.36 no.2
• /
• pp.116-121
• /
• 2003

Ti-Si-N coating layers were deposited onto WC-Co substrates by a hybrid system of arc ion plating (AIP) and sputtering techniques. The tribological behaviors of Ti-Si-N coating layers with various Si contents were investigated by the dry sliding wear experiments, which were conducted at three different sliding speeds, 0.1, 0.3, 0.5 m/s, against the steel and alumina balls. In the case of steel ball, the average friction coefficient slightly decreased with increasing the sliding speed regardless of Si content due to adhesive wear behavior between coating layer and steel ball. At constant sliding speed, the average friction coefficient decreased with increase of Si content. On the contrary, in the case of alumina ball, the average friction coefficient increased with increasing the sliding speed regardless of Si content, indicating that the abrasive wear behavior was more dominant when the coating layers slide against alumina ball. Through these experimental results, it was found that the tribological behaviors of Ti-Si-N coating layers were effected by factors such as Si content, sliding speed, and kinds of counterpart materials rather than the hardness of coating layer.

• Journal of the Korean Society for Heat Treatment
• /
• v.37 no.4
• /
• pp.163-171
• /
• 2024

SCR420H steel is a low-carbon chromium alloy steel designed for carburizing heat treatment. Recently, research is being conducted on high-temperature carburization heat treatment to reduce costs and CO₂ emissions by shortening the carburization time to meet the international carbon neutral policy. However, this high-temperature carburization heat treatment coarsens the steel grains and causes a decrease in mechanical properties. In this study, a large amount of Ti was added to increase the grain refinement effect in the high-temperature carburizing process. We investigated the microstructure and precipitates of SCR420H steel without Ti (Al steel) and with Ti (AlTi steel). Thermodynamic calculations showed that the AlN and (Ti,Nb)(C,N) precipitated in Al steel, while (Ti,Nb)(C,N) and Ti₄C₂S₂ precipitated in AlTi steel. Addition of Ti increases the fraction of bainite after reheating process. Transmission electron microscopy analysis shows that small amounts of AlN and (Ti,Nb)(C,N) precipitates are formed in the Al steel. The addition of Ti increases the density of (Ti,Nb)(C,N) precipitates and induces the formation of Ti₄C₂S₂ precipitates, increasing the grain coarsening temperature (GCT) under all heat treatment conditions. Higher reheating temperatures also resulted in higher GCT values due to increased precipitation.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2001.06a
• /
• pp.3-3
• /
• 2001

Recently TiN, TiAlN, CrN hardcoatings have adapted many industrial application such as die, mold and cutting tools because of good wear resistant and thermal stability. However, in terms of high speed process, general hard coatings have been limited by oxidation and thermal hardness drop. Especially in the case of PCB drill, high speed cutting and without lubricant process condition have not adapted these coatings until now. Therefore more recently, superhard nanocomposite coating which have superhard and good thermal stability have developed. In previous works, WC-TiAlN new nanocomposite film was investigated by cathodic arc ion plating system. Control of AI concentration, WC-TiAlN multi layer composite coating with controlled microstructure was carried out and provides additional enhancement of mechanical properties as well as oxidation resistance at elevated temperature. It is noted that microhardness ofWC-TiA1N multi layer composite coating increased up to 50 Gpa and got thermal stability about $900^{\circ}C$. In this study WC-TiAlN nanocomposite coating was deposited on PCB drill for enhancement of life time. The parameter was A1 concentration and plasma cleaning time for edge sharpness maintaining. The characteristic of WC-TiAlN film formation and wear behaviors are discussed with data from AlES, XRD, EDS and SEM analysis. Through field test, enhancement of life time for PCB drill was measured.

• Transactions of Materials Processing
• /
• v.15 no.5 s.86
• /
• pp.366-372
• /
• 2006

The effect of coating time in arc ion plating on surface properties of the TiN-coated high speed steel(SKH51) is presented in this paper. Surface roughness, micro-hardness, coated thickness, atomic distribution of TiN and adhesion strength are measured for various coating times. It has been shown that the coating time has a deep influence on the micro-hardness, the coated thickness, the atomic distribution of Ti and the adhesion strength of the SKH51 steels but that it has little influence on the surface roughness.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.11a
• /
• pp.259-262
• /
• 1998

PbTi $O_3$ family ceramics can be used for the piezoelectric transformer using thickness extensional vibration mode because it is a material with the large anisotropy between electromechanical coupling factors $k_{t}$ and $k_{p}$. However, PbTi $O_3$ family ceramics have a difficult poling condition on account of its large anisotrophy. In this study, the structural and piezoelectric properties of (P $b_{0.76}$ $Ca_{0.24}$)[ $Ti_{0.96}$(M $n_{1}$3/S $b_{2/3}$)$_{0.04}$] $O_3$ system ceramics were investigated as a function of poling voltage in order to find the best poling condition.ion.n.n.ion.n.

• Journal of the Korean Vacuum Society
• /
• v.4 no.S2
• /
• pp.40-48
• /
• 1995

$TiB_2$-TiN double-layer coating have been prepared by ion beam enhanced deposition. AES, XRD, TEM and HRTEM were employed to characterize the $TiB_2$ layer. The microhardness of the coatings was evaluated by an ultra low-load microhardness indenter system, and the tribological behavior was examined by a ball-on-disc tribology wear tester. It was found that in a single titanium diboride layer, the composition is uniform along the depth of the film, and it is mainly composed of nanocrystalline $TiB_2$ with hexagonal structure, which resulted from the ion bombardment during the film growth. The hardness of the $TiB_2$ films increases with increasing ion energy, and approaches a maximum value of the $TiB_2$ films increases with increasing ion energy, and approaches a maximum value of 39 Gpa at ion energy of 85 keV. The tribological property of the TiB2 films is also improved by higher energy of 85keV. The tribological property of the $TiB_2$ films is also improved by higher energy ion beam bombardment. There is no major disparity in the mechanical properties of double-layer $TiB_2$/TiN coatings and TiN/$TiB_2$ coatings. Both show an improved wear resistance compared with single-layer $TiB_2$ films. The adhesion of double-layer coatings is also superior to that of single-layer films.

• Journal of the Korean institute of surface engineering
• /
• v.34 no.2
• /
• pp.105-114
• /
• 2001

$Al_2$$O_3$ coatings were deposited on M2 high speed steels by the plasma enhanced chemical vapor deposition (PECVD) process, using a gas mixture of AlC1$_3$, $H_2$, $CO_2$ and Ar $Al_2$$O_3$ coatings had interference color and showed amorphous phase. $A1_2$X$A1_3$/($Ti_{0.5}$ /$Al_{0.5}$ )N double layer coatings were produced in the sequence of substrate $NH_3$ plasma pretreatment, ($Ti_{0.5}$$Al_{0.5}$)N depoition process, $Al_2$$O_3$ deposition process. $Al_2$ $O_3$/( $Ti_{0.5}$A $l_{0.5}$)N double layer coatings showed NaCl structure in ( $Ti_{0.5}$A $l_{0.5}$)N layer and amorphous phase in A1$_2$ $O_3$ layer. It was shown that $Al_2$ $O_3$ columns continuously grew onto ( $Ti_{0.5}$A $l_{0.5}$)N columns. ( $Ti_{0.5}$A $l_{0.5}$)N single coating and $Al_2$ $O_3$/( $Ti_{0.5}$A $l_{0.5}$)N double layer coating were oxidized at $700^{\circ}C$, 80$0^{\circ}C$, 90$0^{\circ}C$ for 1hr, 3hr in atmosphere. At 80$0^{\circ}C$, single layer coatings were oxidized, which were examined substrate oxide particle. But $Al_2$ $O_3$/ ( $Ti_{0.5}$A $l_{0.5}$)N double layer coatings maintained the asdeposited state. Therefore, $Al_2$ $O_3$/ ( $Ti_{0.5}$A $l_{0.5}$)N double layer coatings have moreexcellent oxidation resistance than ( $Ti_{0.5}$A $l_{0.5}$)N single layer coatings.X> 0.5/)N single layer coatings.s.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.7 no.3
• /
• pp.468-473
• /
• 2003

In this paper, for enhancement of property on a-Si:H TFTs We measure interface characteristics of ferroelectrics thin film and a-Si:H thin film. First, SrTiO$_3$ thin film is deposited bye-beam evaporation. Deposited films are annealed for 1 hour in N2 ambient at $150^{\circ}C∼600^{\circ}C$. Dielectric characteristics of deposited SrTiO$_3$ films are very good because dielectric constant shows 50∼100 and breakdown electric field are 1 ∼ 1.5 MV/cm. a-SiN:H,a-Si:H(n-type a-Si:H) are deposited onto SrTiO$_3$ film to make MFNS(Meta1/ferroelectric/a-SiN:H/a-Si:H) by PECVD. After the C-V measurement for interface characteristics, MFNS structure shows no difference with MNS(Metal/a-SiN:H/a-Si:H) structure in C-V characteristics but the insulator capacitance value of MFNS structure is much higher than the MNS because of high dielectric constant of ferroelectric.

• Proceedings of the KIEE Conference
• /
• 1995.07c
• /
• pp.1069-1071
• /
• 1995

The electrical properties of Al/TiN/Ti contact are investigated at submicron contacts. The contact resistance and contact leakage current are dependent on metallization, surface dopant concentration, semiconductor surface treatment and contact plug ion implantation. In this paper, the contact resistance and contact leakage current are studied according to surface dopant concentration, semiconductor surface treatment and contact plug ion implantation at 0.8 micron contact. The contact resistance and contact leakage current increases with increasing substrate ion concentration. HF cleaning represents high contact resistance but low contact leakage current while CDE cleaning represents low contact resistance but high contact leakage current. Contact plug ion implantation decreases contact resistance but increases contact leakage current. Specially, RTA represents good electrical properties.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09b
• /
• pp.1026-1029
• /
• 2006

Particulate reinforced titanium composites were produced by PM rout. Differents volumetric percentages of TiN reinforcements were used, 5,10,15 vol%. Samples were uniaxial pressed and vacuum sintered at differents temperatures between $1200-1300^{\circ}C$. Density, porosity, shrinkage, mechanical properties and microstructure were studied. Elastic properties and strength resistance were analysed by flexural strength and tension tests, and after the test, fractured samples were analysed too, obtaining a correlation between the fracture, interparticulated or intraparticulated, and the reinforcement addition.. Hardness and microhardness test were applied too, in order to complete the study about mechanical properties. In order to study wear resistance pin-on-disc test were used. In addition, the temperature influence, the reactivity between matrix and reinforcement, and the microstructures developed were observed by optical and electron microscopy.