• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part2
• /
• pp.990-991
• /
• 2006

• 한국철도학회:학술대회논문집
• /
• 한국철도학회 2006년도 추계학술대회 논문집
• /
• pp.225-230
• /
• 2006

We have investigated mechanical behaviors of composite materials containing Ni-Ti shape memory alloy(SMA) wires by performing several experimental methods. In this study, several sample specimens were fabricated in order to perform photo-elasticity tests and impact tests under various test conditions for investigating the mechanical behaviors of the SMA composite materials. From the test results, the shape memory effect of SMA in composite materials can be considered as one of possible ways in controlling crack growth in the materials.

• Smart Structures and Systems
• /
• 제30권3호
• /
• pp.255-261
• /
• 2022

When no extensometer is available in a generic tensile-compression test carried out by a universal testing machine (for instance the model BIONIX from Material Testing Systems (MTS)), the test results only provide the relative displacement between the machine grips. The test does not provide any information on the local behaviour of the material. This contribution presents the potential of an application of Digital Image Correlation (DIC) toward the reconstruction of the behaviour along the specimen. In particular, the authors test a Ni-Ti shape memory alloys (SMA) specimen with emphasis on the coupling of the two measurement techniques.

• 한국소성가공학회:학술대회논문집
• /
• 한국소성가공학회 2007년도 춘계학술대회 논문집
• /
• pp.118-121
• /
• 2007

Bulk metallic glass (BMG)/crystalline composites comprising a copper based BMG alloy and crystalline nickel were produced by means of eloctroless plating of nickel on $Cu_{54}Zr_{22}Ti_{18}Ni_6$ BMG powder and subsequent consolidation using spark plasma sintering. The plastic deformation behavior of BMG/crystalline composites was examined by uniaxial compression test at various temperatures in the supercooled liquid region (SLR) of the BMG alloy. The evolution of strain states during uniaxial compression was tackled by microstructure observations. Deformation temperature played an important role in the deformation behavior of BMG/crystalline composites, which was attributed to a strong temperature dependence of the flow stress of the BMG alloy in the SLR. BMG/crystalline composites deformed homogenously in the temperature range where the flow stress of the BMG alloy was close to that of crystalline nickel. In contrast, inhomogeneous deformation was observed in the temperature range where the flow stress of the BMG alloy largely differs from that of crystalline nickel.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2003년도 춘계학술대회 논문집
• /
• pp.426-429
• /
• 2003

In this study, phase transformation characteristics of Nitinol shape memory alloy with 54.5wt%Ni-45.5wt%Ti were investigated by varying with annealing treatment and cutting conditions through DSC(differential scanning calorimetry). Annealing treatment conditions were considered as heat treated time of 5 min, 15 min, 30 min, and 45 min, heat treated temperature of 40$0^{\circ}C$, 50$0^{\circ}C$, 5$25^{\circ}C$, 55$0^{\circ}C$, 575$^{\circ}C$, $600^{\circ}C$, $700^{\circ}C$, 80$0^{\circ}C$, and 90$0^{\circ}C$, and environmental condition of heat treatment under vacuum or air. Cutting conditions were considered as no cutting, one side cutting, and two side cutting. Tensile test was also conducted on Nitinol shape memory alloy to investigate thermomechanical characteristics by varying with annealing heat treatment histories. According to the results, annealing treatment and cutting conditions were found to significantly affect on phase transformation and thermomechanical characteristics of Nitinol shape memory alloy.

• 한국결정성장학회지
• /
• 제22권5호
• /
• pp.227-232
• /
• 2012

차세대 원자력발전용 고온 열교환기 소재로 이용될 가능성이 높은 Ni-Cr계 고온합금인 Inconel 617과 Hastelloy X의 표면처리에 따른 FLiNaK(LiF-NaF-KF) 용융염 하에서의 고온물성에 대한 연구를 수행하였다. Inconel 617과 Hastelloy X기판 상에 각각 PVD인 arc discharge 및 sputtering법에 의해 TiAlN 및 $Al_2O_3$ 박막을 코팅 하였다. 이러한 표면처리가 이들 합금의 FLiNaK 용융염 하 고온 안정성에 미치는 영향에 대해 연구하였다. 용융염 하 Ni-Cr계 고온합금의 부식 원리를 이해하기 위해, 용융염 수송 loop에 사용 중 파단된 Inconel 파이프에 대한 미세구조 분석을 수행하였다. 표면처리 된 합금들을 $600^{\circ}C$ 용융염 내에서 열처리 하였으며, 열처리 전후 시편들에 대해 상형성, 미세구조 등 고온 물성 변화를 측정하였다. 연구결과 코팅되지 않은 경우 보다 TiAlN 및 $Al_2O_3$ 박막이 코팅된 소재에서 보다 우수한 고온 안정성을 보여주었다.

• International Journal of Precision Engineering and Manufacturing
• /
• 제9권2호
• /
• pp.63-68
• /
• 2008

Hard and brittle materials, such as Ni- and Ti-based alloys, glass, and ceramics, are very useful in aerospace, marine, electronics, and high-temperature applications because of their extremely versatile mechanical and chemical properties. One Ni-based alloy, Inconel 718, is a precipitation-hardenable material designed with exceptionally high yield strength, ultimate tensile strength, elastic modulus, and corrosion resistance with outstanding weldability and excellent creep-rupture properties at moderately high temperatures. However, conventional machining of this alloy presents a challenge to industry. Ultrasonic vibration cutting (UVC) has recently been used to cut this difficult-to-machine material and obtain a high quality surface finish. This paper describes an experimental study of the UVC parameters for Inconel 718, including the cutting force components, tool wear, chip formation, and surface roughness over a range of cutting conditions. A comparison was also made between conventional turning (CT) and UVC using scanning electron microscopy observations of tool wear. The tool wear measured during UVC at low cutting speeds was lower than CT. UVC resulted in better surface finishes compared to CT under the same cutting conditions. Therefore, UVC performed better than CT at low cutting speeds for all measures compared.

• 한국주조공학회지
• /
• 제42권6호
• /
• pp.392-397
• /
• 2022

In order to compliant the stringent exhaust emission regulations, higher fuel efficiency and cleaner exhaust gas in combustion engines have been required. To improve combustion efficiency, an exhaust gas temperature is increasing, therefore higher temperature resistance is required for components in exhaust system, especially turbine wheel in turbocharger. IN100 looks quite attractive candidate as it has high temperature properties with low density, however it has low castability due to poor ductility at high temperature. In this study, the balance of Al and Ti composition was optimized from the base alloy IN100 to improve the high temperature ductility by expanding the γ single phase region below the solidification temperature, while obtaining the high temperature strength by maintaining the volume fraction of γ' phase equivalent to IN100 around 1000℃. Furthermore, the high temperature creep rupture life increased by adding a small amount of Ta. The alloy developed in this study has high castability, low density and high specific strength at high temperature.

• International Journal of Korean Welding Society
• /
• 제3권1호
• /
• pp.39-44
• /
• 2003

The welded specimens were made by butt welding of the 2 wires of 50mm length using the pulsed YAG laser. The laser welded wires were tested for investigating the shape memory effect and the ability of super elasticity. The fatigue properties of the welded wires were investigated using the rotary bending fatigue tester specially designed for wires. Moreover, the effect of defocusing distance during laser welding on the static and fatigue properties was Investigated. The shape memory effect and super elasticity of the laser welded wires were approximately identical with that of base metal at the test temperature below 353K. However, the welded wires were broken within elastic limit at the test temperature above 353k. Under the cyclic bending loading conditions, the welded wires could be useful only below the elastic limit, while the base metal had sufficient fatigue life even the stress induced M-phase region. The fatigue strength of the welded wires was about half of that of the base metal. The deterioration of the static and fatigue properties in the welded wires was proven to be from the large difference of the transformation behavior between the base metal and welded part that is caused by vaporization of Ni-content at the welded part during the welding process. The defocusing distance below 3mm acted more largely on lowering the strength of the welded wires than that of 6mm or 8mm.

• 한국분말재료학회지
• /
• 제16권1호
• /
• pp.9-15
• /
• 2009

Amorphization and crystallization behaviors of $Ti_{50}Cu_{50}Ni_{20}Al_{10}$ powders during high-energy ball milling and subsequent heat treatment were studied. Full amorphization obtained after milling for 30 h was confirmed by X-ray diffraction and transmission electron microscope. The morphology of powders prepared using different milling times was observed by field-emission scanning electron microscope. The powders developed a fine, layered, homogeneous structure with prolonged milling. The crystallization behavior showed that the glass transition, $T_g$, onset crystallization, $T_x$, and super cooled liquid range ${\Delta}T=T_x-T_g$ were 691,771 and 80 K, respectively. The isothermal transformation kinetics was analyzed by the John-Mehn-Avrami equation. The Avrami exponent was close to 2.5, which corresponds to the transformation process with a diffusion-controlled type at nearly constant nucleation rate. The activation energy of crystallization for the alloy in the isothermal annealing process calculated using an Arrhenius plot was 345 kJ/mol.