• 한국분말야금학회:학술대회논문집
• /
• 한국분말야금학회 2006년도 Extended Abstracts of 2006 POWDER METALLURGY World Congress Part 1
• /
• pp.165-166
• /
• 2006

Nb-Ti alloys were hydrogenated to prepare fine and contamination-free powders. Cracks were introduced in the alloys when they were annealed at 1473 K and cooled in a hydrogen atmosphere. The fragments produced by hydrogen-induced cracking are brittle and the friability enhanced with the Ti content of the alloy, which is beneficial for further refinement of particle size. We also demonstrate that Nb-Ti powders with the average particle size less than 1 m can be produced by ball milling at a temperature lower than 203 K. Furthermore, hydrogen-free powders can then be obtained by annealing above the temperature corresponding to hydrogen desorption from Nb solid solution.

• 한국주조공학회지
• /
• 제22권6호
• /
• pp.288-292
• /
• 2002

Ni-base amorphous alloys were manufactured using melt-spinning and Cu-mold die casting methods. Amorphous formability, the supercooled liquid region before crystallization and mechanical properties were examined. The reduced glass transition temperature and the supercooled liquid region of $Ni_{51} Nb_{20} Zr_9 Ti_9 Co_8 Cu_3$alloy were 0.621 and 46 K respectively. $Ni_{51} Nb_{20} Zr_9 Ti_9 Co_8 Cu_3$ alloy was produced in the rod shape 3mm diameter using the Cu-mold die casting. Hardness, compression strength, elongation and elastic modulus of the alloy were 850 DPN, 2.75 GPa, 1.8% and 150 GPa respectively. Moreover, compression strength of 2.75 GPa was the highest value in the amorphous bulk alloy produced up to now.

• Journal of Periodontal and Implant Science
• /
• 제36권4호
• /
• pp.849-861
• /
• 2006

타이타늄은 기계적 특성이 우수하고 생체적합성이 뛰어나 의료용 장비의 주 재료로 사용되고 있으며 타이타늄 보다 기계적 특성이 더 우수한 타이타늄 합금들(주로 Ti-6Al-4V와 Ti-6Al-7Nb 합금)도 개발되어 치과와 의료용 임플란트로 사용되고 있다. 그러나 타이타늄 합금 성분들 중 알루미늄 (aluminum)과 바나디움(vanadium)은 인체에 노출되면 세포손상과 신경계에 문제를 일으킬 수 있다. 따라서 인체에 독성이 없으면서 기계적 성질과 생체적합성이 우수한 타이타늄 합금의 개발이 필요하다. 최근 인체에 독성이 없는 성분들이 함유된 새로운 ${\beta}$ - 형태의 타이타늄 합금들이 개발되고 있는데, ${\beta}$ - 타이타늄 합금은 그 기계적 성질이 기존의 ${\alpha}+{\beta}$ 타이타늄 합금에 비해 우수하다고 알려져 있다. 최근 새로운 ${\beta}$ - 타이타늄 합금이 전남대학교 부설 타이타늄 연구소에서 개발되었다. 이 연구는 새로 개발된 ${\beta}$ - 타이타늄 합금의 생채 적합성을 세포 증식도, 알카리 인산 분해 효소 활성과 유전자 증폭을 통해 알아보고자 하였다. 그 결과는 다음과 같다; 1. Titanium-6aluminum-4vanadium (Ti-6Al-4V) 합금 표면애서의 세포 증식율은 Titanium-Titanium8Tantalum-3Niobium (Ti-8Ta-3Nb) 합금과 순수 타이타늄 표면에 비해 유의하게 낮았다(p<0.00l). Ti-8Ta-3Nb 합금 표면에서의 증식도는 순수 타이타늄 표면과 유사하였다. 2. Ti-8Ta-3Nb 합금과 순수 타이타늄에서 배양된 세포이 알카리 인산 분해 효소의 활성도는 Ti-6Al-4V 합금에서의 것보다 유의하게 높았다 (p<0.001). 3. 유전자 증폭 분석 결과, Ti-8Ta-3Nb 합금과 순수 타이타늄에서 collagen type I과 bone sialoprotein mRNA 가 유사한 수준으로 발현되었다. 이상의 결과는 생체 적합성 측면에서 Ti-8Ta-3Nb 합금과 순수 타이타늄의 차이가 없음을 보여주며 따라서 Ti-8Ta-3Nb 합금이 의학 및 치의학 영역에서 새로운 임프란트 재료로 사용될 수 있음을 의미한다.

• 한국재료학회:학술대회논문집
• /
• 한국재료학회 2009년도 춘계학술발표대회
• /
• pp.48.2-48.2
• /
• 2009

Ti와 Ti-6%Al-4%V합금은 내 부식성 및 생체 적합성이 매우 우수하기 때문에 현재 생체재료로써 널리 사용되고 있다. 하지만 Ti-6%Al-4V합금에 포함된 Al과 V이 신체에 좋지 않은 영향을 줄 수 있다는 연구 결과가 보고되면서 새로운 생체재료의 연구가 활발히 진행되고 있다. 본 연구에서는 생체에 무해한 Ti-Nb와 hydroxyapatite(HAp)를 복합 첨가하여 고에너지볼밀링(high-energy mechanical milling, HEMM)으로 나노 합금분말을 제조 후 급속소결에 의하여 Ti-Nb/HAp 생체재료를 제조 하였다. 제조한 Ti-Nb/HAp 생체용 복합재료에서 HAp 첨가량과 분말의 밀링, 믹싱에 따른 조직 변화와 소결체의 생체적합성의 변화 및 기계적 특성의 변화를 분석하였다. 이때 Ti-42%Nb에 HAp의 첨가량을 0%, 5%, 10%, 15%로 변화를 주었고, 밀링은 고에너지볼밀링기를 이용하여 0~8시간 동안 실시하였다. 그 결과 밀링 시간이 증가할수록 합금 분말의 크기가 미세해졌으며, 특히 8시간 밀링시 분말의 크기가 나노 크기로 감소하여 기계적 특성(경도 및 강도)이 우수해지는 것을 알 수 있었다.

• 한국방사성폐기물학회:학술대회논문집
• /
• 한국방사성폐기물학회 2003년도 가을 학술논문집
• /
• pp.395-400
• /
• 2003

사용후핵연료 금속전환체의 장기저장 안정성 확보를 위해 금속전환체의 주성분인 금속우라늄과 산화 안정화 후보물질인 Nb, Ti, Ni, Zr, Hf 등을 첨가한 모의금속전환체 합금을 제작하여 $200^{\circ}C~300^{\circ}C$ 온도구간에서 순수 산소분위기로 산화시험을 수행하였다. U-Nb, U-Zr, U-Ti 합금은 순수 금속우라늄보다 무게증가 측면에서의 산화저항성이 높았으나, U-Hf, U-Ni 합금의 경우에는 오히려 순수 금속우라늄보다 산화 저항성이 낮게 나타났다. 시편에 대한 미세성분 및 조직을 광학현미경, SEM, EPMA 등을 통해 분석하였다. 각 합금의 산화율 및 활성화에너지를 구한 결과 U-Nb 합금의 활성화에너지가 높고 산화 저항성이 가장 양호한 것으로 나타나 산화 저항성 후보물질로 선정하였다.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2006년도 추계학술발표회 초록집
• /
• pp.67-68
• /
• 2006

• 소성∙가공
• /
• 제8권3호
• /
• pp.319-319
• /
• 1999

From isothermal and cyclic oxidation tests on thermomechanically treated Ti-5%Al, Ti47%Al-4%Cr, and Ti-48%Al-2%Cr-2%Nb alloys at 800, 900, 1000℃ in air, it was found that Ti-48%Al-2%Cr-2%Nb and Ti-47%Al-4%Cr had the best and the worst oxidation resistance, respectively. The oxide scales consisted primarily of TiO₂and Al₂O₃, with and without a small amount of dissolved Cr and 7b ions, depending on the alloy composition. These ions were slightly enriched inside the inner oxide layer, and strongly enriched around the scale-matrix interface. The outer TiO₂-rich layer was formed by the outward diffusion of Ti ions, while the inner (TiO₂+A1₂O₃,) mixed layer was formed by the inward transport of oxygen. The outward movement of Al ions farmed the intermediate Al₂O₃-rich Iayer, above talc prepared alloys.

• Corrosion Science and Technology
• /
• 제8권4호
• /
• pp.143-147
• /
• 2009

In biomedical implants and dental fields, titanium has been widely utilized for excellent corrosion resistance and biocompatibility. However, Ti and its alloys are nonbioactive after being implanted in bone. In this study, for the purpose of improvement in biocompatibility the anodic $TiO_2$ layer on Ti-xNb alloys were fabricated by electrochemical method in phosphate solution, and the effect of Nb content on the pore size, the morphology and crystallinity of Ti oxide layer formed by the anodic oxidation method was investigated. The Ti containing Nb up to 3 wt%, 20 wt% and 40 wt% were melted by using a vacuum furnace. The sample were cut, polished, and homogenized for 24 hr at $1050^{\circ}C$ for surface roughness test and anodizing. Titanium anodic layer was formed on the specimen surface in an electrolytic solution of 1 M phosphoric acid at constant current densities ($30mA/cm^2$) by anodizing method. Microstructural morphology, crystallinity, composition, and surface roughness of oxide layer were observed by FE-SEM, XRD, EDS, and roughness tester, respectively. The structure of alloy was changed from $\alpha$-phase to $\beta$-phase with increase of Nb content. From XRD results, the structure of $TiO_2$ formed on the Ti-xNb surface was anatase, and no peaks of $Nb_2O_5$ or other Nb oxide were detected suggesting that Nb atoms are dispersed in $TiO_2$-based solid solution. Surface roughness test and SEM results, pore size formed on surface and surface roughness decreased as Nb content increased. From the line analysis results, intensity of Ti peak was high in the center of pore, whereas, intensity of O peak was high in the outside of pore center.

• Journal of Korean Dental Science
• /
• 제10권1호
• /
• pp.10-21
• /
• 2017

Purpose: The purpose of this study was to investigate the electrochemical characteristics of nanotubular Ti-25Nb-xZr ternary alloys for dental implant materials. Materials and Methods: Ti-25Nb-xZr alloys with different Zr contents (0, 3, 7, and 15 wt.%) were manufactured using commercially pure titanium (CP-Ti), niobium (Nb), and zirconium (Zr) (99.95 wt.% purity). The alloys were prepared by arc melting in argon (Ar) atmosphere. The Ti-25Nb-xZr alloys were homogenized in Ar atmosphere at $1,000^{\circ}C$ for 12 hours followed by quenching into ice water. The microstructure of the Ti-25Nb-xZr alloys was examined by a field emission scanning electron microscope. The phases in the alloys were identified by an X-ray diffractometer. The chemical composition of the nanotube-formed surfaces was determined by energy-dispersive X-ray spectroscopy. Self-organized $TiO_2$ was prepared by electrochemical oxidation of the samples in a $1.0M\;H_3PO_4+0.8wt.%$ NaF electrolyte. The anodization potential was 30 V and time was 1 hour by DC supplier. Surface wettability was evaluated for both the metallographically polished and nanotube-formed surfaces using a contact-angle goniometer. The corrosion properties of the specimens were investigated using a 0.9 wt.% aqueous solution of NaCl at $36^{\circ}C{\pm}5^{\circ}C$ using a potentiodynamic polarization test. Result: Needle-like structure of Ti-25Nb-xZr alloys was transform to equiaxed structure as Zr content increased. Nanotube formed on Ti-25Nb-xZr alloys show two sizes of nanotube structure. The diameters of the large tubes decreased and small tubes increased as Zr content increased. The lower contact angles for nanotube formed Ti-25NbxZr alloys surfaces showed compare to non-nanotube formed surface. The corrosion resistance of alloy increased as Zr content increased, and nanotube formed surface showed longer the passive regions compared to non-treatment surface. Conclusion: It is confirmed that corrosion resistance of alloy increased as Zr content increased, and nanotube formed surface has longer passive region compared to without treatment surface.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2016년도 추계학술대회 논문집
• /
• pp.119-119
• /
• 2016

Over the last years the anodic formation of ordered $TiO_2$ nanotube layers has created significant scientific interest. Titanium oxide nanotube formation on the titanium or titanium alloy surface is expected to be important to improve cell adhesion and proliferation under clinical conditions. It should be possible to control the nanotube size and morphology for biomedical implant use by controlling the applied voltage, alloying element, current density, anodization time, and electrolyte. $TiO_2$ nanotubes show excellent biocompatibility, and the open volume in the tubes may be exploited as a drug release platform and so on. Therefore, in this study, Nanotube shape on the Ti-29Nb-xHf alloys with applied potentials was reserched. $TiO_2$ nanotube formation on Ti-29Nb-xHf alloys was carried out using anodization technique as a function of applied DC potential (10 V to 30 V and 30 V to 10 V) and anodization time for 60~120 min in $1MH_3PO_4$ with small additions of (0.8 wt. %, to 1.2 wt. %) NaF. The morphology change of anodized Ti-29Nb-xHf alloys was determined by FE-SEM, XRD, and EDS.