• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.66-66
• /
• 2009

Various alloy system, such as Cu-Sn-Ti, Cu-Ag-Ti, and Ni-B-Cr-based alloy are used for the brazing of diamond grits. However, the problem of the adhesion strength between the diamond grits and the brazed alloy is presented. The adhesion strength between the diamond grits and the melting filler alloy is predicted by the contact angle, thereby, instead of diamond grit, the study on the wettability between the graphite and the brazing alloy has been indirectly executed. In this study, Cu-13Sn-12Ti filler alloy was manufactured, and the contact angles, the shear strengths and the interfacial area between the graphites(diamond grits) and braze matrix were investigated. The contact angle was decreased on increasing holding time and temperature. The results of shear strength of the graphite joints brazed filler alloys were observed that the joints applied Cu-13Sn-12Ti alloy at brazing temperature 940 $^{\circ}C$ was very sound condition indicating the shear tensile value of 23.8 MPa because of existing the widest carbide(TiC) reaction layers. The micrograph of wettability of the diamond grit brazed filler alloys were observed that the brazement applied Cu-13Sn-12Ti alloy at brazing temperature $990^{\circ}C$ was very sound condition because of existing a few TiC grains in the vicinity of the TiC layers.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.47-47
• /
• 2009

용착금속의 미세조직은 크게 Acicular ferrite(AF), Ferrite with aligned second phase(FS), Primary ferrite(=Grain boundary Ferrite) 등으로 나눌 수 있다. 이 중 침상형 페라이트(AF)는 인성과 강도를 동시에 증가시킬 수 있으므로 이를 다량 확보하는 것이 용접산업의 관건이다. 본 연구에서는 침상형 페라이트 발생에 기여한다고 알려진 Ti 함량을 용착금속에서 단계적으로 조절하여 나타나는 미세조직과 특성변화를 관찰하였다. 모재는 HSB-600을 사용하였으며 용접재료는 ER100S-G급의 Ti가 함유되어 있는 것(A)과 미함유된 것(B)을 사용하였다. 모재 성분의 희석을 방지하기 위해 V-Groove 가공 후 Buttering 용접을 실시하였다. 중앙에 가공된 V-그루브에 이들 재료를 적절히 조합하고 용접(입열량 20kJ/cm)하여 Ti함유량을 총 4가지(0.002~0.025% Ti)로 제어하였다. 용접 후 각각의 시편에 대해 미세조직, 충격시험, O/N분석, 성분분석 등의 시험을 진행하였다. 미세조직 관찰결과 Ti함량이 증가할수록 AF는 증가하고 FS는 감소함을 확인할 수 있었으며 충격시험결과 Ti가 많이 함유된 시편일수록 더 낮은 연성취성 천이온도(DBTT)를 나타내었다. EDS와 SEM으로 관찰한 결과 Ti함량 증가에 따라 비금속개재물의 크기는 작아지고 밀도는 높아지는 것을 확인할 수 있었으며 개재물 내에서의 Ti함량도 더 많아지는 것을 확인 할 수 있었다.

• Tribology and Lubricants
• /
• v.6 no.1
• /
• pp.116-125
• /
• 1990

An experimental programme was established to determine the wear behaviour of TiN coatings of thickness 1 $\mu$m and 3 $\mu$m. by PECVD with the variation of applied load, sliding velocity and sliding distance. It was shown that oxidation of transferred metal as sliding speed increased formed oxide film so that it contributed in decreasing the wear rate. With the roller-on-disc tribometer employed, the wear rate of the roller specimen was decreased with the increase in sliding distance due to the reduction in effective contact pressure. Finally, the severe cracks concentrated at the trailing edge of contact surface were explained in terms of high tensile stress prevailing at the trailing edge of the contact and were identified as a dominant wear mechanism as well as the strong local welding between coating layer and the counter surface, leading to the debonding of the coating layer.

• Proceedings of the KWS Conference
• /
• v.43
• /
• pp.130-132
• /
• 2004

석출물의 용해 온도보다 낮은 온도에서의 석출물의 야금학적인 거동을 예측하였다. 평균 사이즈 석출물의 지속적인 성장만을 고려하는 기존의 모델과 달리, 본 연구에서 제안된 모델의 경우에는, Gibbs-Thomson equation으로부터 유도되는 critical particle size를 고려하였다. 제안된 모델을 이용해서 TiN석출물의 거동을 예측하였으며, 이를 실험 결과 및 기존의 모델에 의한 예측 값과 비교하였다. 석출물들의 분포는 전형적인 log-normal 분포를 따르는 것으로 관찰되었으며, 본 연구에서 제안된 모델이 기존의 모델에 비해서 실험결과와 잘 일치함을 확인할 수 있었다.

• Proceedings of the KWS Conference
• /
• 2007.11a
• /
• pp.248-250
• /
• 2007

이 연구는 cBN과 활성 Ag계 금속필러메탈을 이용하여 접합계면에서의 금속성분과 화합물, 탄화물의 거동을 분석하는데 있다. 진공 브레이징은 $900{\sim}1000^{\circ}C$에서 $25^{\circ}C$ 간격으로, 유지 시간은 각각 5, 10, 15, 20분으로 실시하였다. Ag-Cu-Ti을 사용하여 브레이징된 cBN은 $950{\sim}1000$도, 유지시간 10분 사이에서 각각 건전한 계면과 표면을 얻을 수 있었으며, 계면에서 Ti-rich상과 화합물이 확인되었다. 이상의 결과로 부터 화합물의 생성과 건전한 접합공정은 브레이징 온도와 시간이 좌우하며, N과 B, Ti의 함유량이 cBN의 브레이징 접합 특성의 중요변수로 생각되어진다. cBN과 Ag계 브레이징 필러의 계면에서의 미세조직 및 화학반응의 메커니즘은 DTA, SEM, EPMA, XRD를 이용하여 분석하였다.

• Journal of Welding and Joining
• /
• v.28 no.3
• /
• pp.92-98
• /
• 2010

Ferritic stainless steels, which have relatively small thermal expansion coefficient and excellent corrosion resistance, are increasingly being used in vehicle manufacturing, in order to increase the lifetime of exhaust manifold parts. But, there are limits on use because of the problem related to cosmetic resistance, corrosions of condensation and high temperature salt etc. So, Aluminum-coated stainless steel instead of ferritic stainless steel are utilized in these parts due to the improved properties. In this investigation, Al-8wt% Si alloy coated 409L ferritic stainless steel was used as the base metal during Gas Tungsten Arc(GTA) welding. The effects of coated layer on the microstructure and hardness were investigated. Full penetration was obtained, when the welding current was higher than 90A and the welding speed was lower than 0.52m/min. Grain size was the largest in fusion zone and decreased from near HAZ to base metal. As welding speed increased, grain size of fusion zone decreased, and there was no big change in HAZ. Hardness had a peak value in the fusion zone and decreased from the bond line to the base metal. The highest hardness in the fusion zone resulted from the fine re-precipitation of the coarse TiN and Ti(C, N) existed in the base metal during melting and solidification process and the presence of fine $Al_2O_3$ and $SiO_2$ formed by the migration of the elements, Al and Si, from the melted coating layer into the fusion zone.

• Journal of Welding and Joining
• /
• v.16 no.2
• /
• pp.93-99
• /
• 1998

The effects of welding conditions of gas metal arc welding on the elements loss of solid wire, oxygen content and impact toughness of weld metals were studied. Deoxidizing elements loss was increased with increase of arc voltage in both short-circuit transfer mode and globular transfer mode. It is believed that increase of arc voltage results in increase of reaction time between elements in the droplet and surrounding gas at the end of wire and in the arc column. Based on the thermodynamic equilibrium model, the oxygen content of weld metal can be predicted with the content of silicon and manganese as following : [%O] = $K([%Si][%Mn])^{-0.25}$, K = -15518/T+6.01. The equilibrium temperature was dependent on shielding gas, and it was 187$0^{\circ}C$ for $CO_2$ gas and 180$0^{\circ}C$ for 20%$CO_2$-80%Ar gas. The oxygen content of weld metal which shows maximum impact toughness was varied with deoxidizing alloy system of wires, 0.041 wt% for Si-Mn type wire and 0.026 wt% for Si-Mn-Ti type wire.

• Journal of Korean Society of Occupational and Environmental Hygiene
• /
• v.24 no.4
• /
• pp.547-555
• /
• 2014

Objective: This study was conducted to investigate the association between subjective distress symptoms and argon welding among workers in Gyeongnam Province shipyard. Method: 31 argon and 29 non-argon welding workers were selected as study subjects in order to measure concentrations of personal dust, welding fumes and other hazardous materials such as ZnO, Pb, Cr, FeO, MnO, Cu, Ni, $TiO_2$, MgO, NO, $NO_2$, $O_3$, $O_2$, $CO_2$, CO and Ar. An interviewer-administered questionnaire survey was also performed on the same subjects. The items queried were as follows: age, height, weight, working duration, welding time, welding rod amounts used, drinking, smoking, and rate of subjective distress symptoms including headache and other symptoms such as fever, vomiting and nausea, metal fume fever, dizziness, tingling sensations, difficulty in breathing, memory loss, sleep disorders, emotional disturbance, hearing loss, hand tremors, visual impairment, neural abnormality, allergic reaction, runny nose and stuffiness, rhinitis, and suffocation. Statistical analysis was performed using SPSS software, version 18. Data are expressed as the mean ${\pm}SD$. An ${\chi}^2$-test and a normality test using a Shapiro wilk test were performed for the above variables. Logistic regression analysis was also conducted to identify the factors that affect the total score for subjective distress symptoms. Result: An association was shown between welding type (argon or non-argon welding) and the total score for subjective distress symptoms. Among the rate of complaining of subjective distress symptoms, vomiting and nausea, difficulty breathing, and allergic reactions were all significantly higher in the argon welding group. Only the concentration of dust and welding fumes was shown to be distributed normally after natural log transformation. According to logistic regression analysis, the correlations of working duration and welding type (argon or non-argon) between the total score of subjective distress symptoms were found to be statistically significant (p=0.041, p=0.049, respectively). Conclusion: Our results suggest that argon welding could cause subjective distress symptoms in shipyard workers.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.46-46
• /
• 2009

과거 고강도강 용접부에서 발생하는 저온균열은 주로 용접열영향부에서 발생하였는데, 이러한 문제점을 해결하기 위하여 강재 메이커들은 고강도강의 용접성을 향상시키고자 노력하였다. 이러한 노력의 결과로 TMCP, HSLA 강 등이 개발되었고 이들 강재는 예열온도를 저하시킬 수 있다는 장점 때문에 보편화되어 사용되었다. 이러한 강재는 모재 예열온도를 기준으로 적용하게 되면 용착금속에서 저온균열이 발생하는 경우가 있다. 따라서 이제는 용접재료의 용접성, 즉 용접재료의 저온균열 저항성을 평가 할 수 있는 기법이 요구된다. 본 연구의 목적은 용착금속의 저온균열 저항성을 평가하는 것인데, 저온균열 저항성은 용착금속의 미세조직에 따라 다르게 나타날 수 있다. 용착금속의 합금조성은 기본적으로 용착금속에 요구되는 최저 강도와 충격인성을 만족할 수 있도록 설계한다. 하지만 유사한 강도의 유사한 합금조성이더라도 일부 합금 성분에 의해 용착금속의 미세조직들은 상이하게 나타날 수 있는데, 미세조직 특성에 의하여 용착금속의 강도와 저온인성이 결정된다. 용착금속의 저온균열 저항성을 평가하기위하여 Gapped Bead-on-Groove(G-BOG) 시험에 사용된 모재는 50mm 두께의 mild steel을 사용하였으며, 모재의 희석을 방지하기위해 15mm 깊이로 V-groove 가공 후 buttering 용접 하였다. 용접된 시편은 다시 5mm 깊이로 V-groove로 2차 가공 후 Ar + 20% $Co_2$ gas를 사용하여 용접하였다. 용접재료는 ER-100S-G grade로 비슷한 합금조성을 갖는 2 종류를 사용하였다. A용접재료는 Ti 이 0.1% 함유 되었으며, B용접재료는 Ti 함유되지 않은 것을 사용하였다. 또한 예열 온도에 따라 저온균열 감수성을 평가하기위하여 모재의 예열온도를 각각 상온, $50^{\circ}C,\;75^{\circ}C,\;100^{\circ}C$로 하여 실험을 진행하였다. 용착금속의 미세조직을 확인해본 결과 Ti 함유된 A 용착금속 미세조직은 대부분 침상형페라이트로 나타났으며, Ti 함유되지 않은 B 용착금속 미세조직은 대부분 베이나이트로 나타났다. G-BOG 시험 결과 Ti 함유된 A 시편이 Ti 함유되지 않은 B 시편보다 저온균열 발생량이 적었다. 이는 용착금속의 미세조직분포 및 특성에 따라 저온균열감수성이 다르다는 것을 나타낸다.

• Composites Research
• /
• v.19 no.2
• /
• pp.28-34
• /
• 2006

[ $Cu-TiB_2$ ] metal matrix composites with various weight fractions of $TiB_2$ were fabricated by combination of manufacturing process, SPS (self-propagating high-temperature synthesis) and SPS (spark plasma sintering). The feasibility of $Cu-TiB_2$ composites for welding electrodes and sliding contact material was investigated through experiments on the tensile properties, hardness and wear resistance. To obtain desired properties of composites, composites are designed according to reinforcement's shape, size and volume fraction. Thus proper modeling is essential to predict the effective material properties. The elastic moduli of composites obtained by FEM and tensile test were compared with effective properties from the original Eshelby model, Eshelby model with Mori-Tanaka theory and rule-of-mixture. FEM result showed almost the same value as the experimental modulus and it was found that Eshelby model with Mori-Tanaka theory predicted effective modulus the best among the models.