• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2002.10b
• /
• pp.199-200
• /
• 2002

Three-body abrasive wear resistance of mild steel, low alloy steel (Bisalloy) and 27%Cr white cast iron was investigated using a ball-cratering test. Glass beads, silica sand, quartz and alumina abrasive particles with sizes larger than $100{\mu}m$ were used to make slurries. It was found that the wear rates of all three materials tested increased with time when angular abrasive particles were used and were rather constant when round particles were used. This increase in wear rates was mainly due to the gradual increase in ball surface roughness with testing time. Abrasive particles with higher angularity caused higher ball surface roughness. Mild steel and Bisalloy were more affected by this ball surface roughness changes than the hard white cast iron. Generally, three-body rolling wear dominated. The contribution of two-body grooving wear increased when the ball roughness was significant. More grooves were found when round particles were used or the size of the particles was decreased.

• Journal of Welding and Joining
• /
• v.19 no.5
• /
• pp.540-547
• /
• 2001

This study has evaluated the wear behavior of PTA (Plasma Transferred Arc) Inconel 625 and Stellite 6 overlays on Nimonic 80A substrate. Nimonic 80A alloy was also included for comparison. In order to evaluate the wear performance, three-body abrasive wear test and pin-on-disk dry sliding wear test were performed. Microstructural development during the solidification of deposits is also discussed. Wear test results show that the wear rate of Stellite 6 deposit is lower than that of Inconel 625 deposit and Nimonic 80A. The sliding wear resistance of overlay deposits follows a similar trend to the abrasive wear resistance, but for Nimonic 80A. The main wear mechanisms were abrasive wear for Inconel 625 deposit, adhesive wear and delamination for Stellite 6 deposit in pin-on-disk dry sliding wear test and ploughing in three-body abrasive wear test. Cross sectional examinations of the worn surface of pin specimens after pin-on-disk dry sliding wear test implies that the plastic deformation near worn surface has occurred during the wear testing.

• Proceedings of the Korean Society of Tribologists and Lubrication Engineers Conference
• /
• 2000.11a
• /
• pp.332-340
• /
• 2000

Friction properties of automotive brake pads containing different types of abrasivess were investigated. Five different abrasives, including o-quartz, magnesia, magnetite, alumina, zircon, were employed in this investigation and size effects of the abrasives on friction characteristics were also studied using 1, 50, 140$\mu\textrm{m}$ size zircon. Experimental results showed that the hardness and size of these abrasive particles were strongly related to friction behaviors and wear mechanisms. Harder and smaller abrasives showed higher friction coefficient and more wear. The surfaces of friction materials with different sizes of abrasives showed that two different modes of abrasion (two-body and three-body abrasion) appeared during sliding. Considering the above results, abrasive materials were thought to destroy transfer film and the extent of the destruction depends on the types and sizes of abrasive particles. A mechanism of the wear mode transition (two-body to three body abrasive motion) was suggested considering the binding energy and friction energy in terms of abrasive particle size.

• Proceedings of the KSME Conference
• /
• 2007.05a
• /
• pp.148-153
• /
• 2007

The effect of silicon carbide (SiC) and graphite fillers incorporation on the abrasive wear behaviour of glass-vinyl ester (G-V) composites have been investigated. The three-body abrasive wear behaviour was assessed by rubber wheel abrasion tests (RWAT). The worn surfaces were examined using scanning electron microscopy (SEM). The addition of SiC and graphite fillers in G-V composite improves the abrasion resistance under different loads/abrading distances. The SEM studies indicate the reasons for failure of composites and influencing parameters.

• Proceedings of the KWS Conference
• /
• 2001.05a
• /
• pp.245-247
• /
• 2001

In this study, the effects of dilution on the wear behavior of PTAW (Plasma Transferred Arc Welding) Inconel 625, Inconel 718 and Stellite 6 overlays on Nimonic 80A were investigated. Inorder to evaluate the wear performance, two-body and three-body abrasive wear test, and dry sliding wear test were performed. According to wear tests, the wear rate of deposit with dilution 30% was higher than that of dilution 10% by 10%, and it was also found the plastic deformation near worn surface.

• Tribology and Lubricants
• /
• v.28 no.1
• /
• pp.1-6
• /
• 2012

In this paper, a three elastic body sliding contact problem is modeled to investigate more precise wear mechanisms related with the sealing surface. A 3-D finite element contact model, a small spherical elastic particle, PTFE seal and steel surface, is solved using a nonlinear finite element code MARC. The deformed seal and steel surface shapes, von-Mises and principal stress distributions are obtained for different seal sliding distances. The entrapped small particle within PTFE seal results in very high stresses on the steel surface which exceeded its yield strength and produce plastic deformation such as groove and torus. The sealing surface could also be worn down by sub-surface fatigue due to intervening small particles together with the well-known abrasive wear. Therefore the proposed contact model adopted in this paper can be applied in design of various sealing systems, and further studies are required.

• Tribology and Lubricants
• /
• v.24 no.4
• /
• pp.186-189
• /
• 2008

The flow induced vibration in the nuclear fuel assembly causes the fretting wear between the fuel cladding tubes and the supporting grids. The reduction in tube thickness due to the fretting wear could be related to the serious damage on nuclear fuel assembly. In this paper, the effect of the water flow on fretting wear of nuclear fuel cladding tube against supporting grid was investigated through the fretting wear tester with water spout equipment. The test results were compared with the data conducted in the stationary water. At stationary water environment the wear debris was trapped between fretting surfaces, and then the fretting wear occurred by three-body abrasion. However, in the case of water flow, the two-body abrasive wear was the dominant wear mechanism, because the wear debris was easily removed by water flow.

• Tribology and Lubricants
• /
• v.34 no.6
• /
• pp.209-216
• /
• 2018

Sapphire is a substrate material that is widely used in optical and electronic devices. However, the processing of sapphire into a substrate takes a long time owing to its high hardness and chemical inertness. In order to process the sapphire ingot into a substrate, ingot growth, multiwire sawing, lapping, and polishing are required. The lap grinding process using pellets is known as one of the ways to improve the efficiency of sapphire substrate processing. The lap grinding process ensures high processing efficiency while utilizing two-body abrasion, unlike the lapping process which utilizes three-body abrasion by particles. However, the lap grinding process has a high material removal rate (MRR), while its weakness is in obtaining the required surface roughness for the final polishing process. In this study, we examine the effects of free abrasives in lap grinding on the material removal characteristics of sapphire substrate. Before conducting the lap grinding experiments, it was confirmed that the addition of free abrasives changed the friction force through the pin-on-disk wear test. The MRR and roughness reduction rate are experimentally studied to verify the effects of free abrasive concentration on deionized water. The addition of free abrasives (colloidal silica) in the lap grinding process can improve surface roughness by three-body abrasion along with two-body abrasion by diamond grits.

• Tribology and Lubricants
• /
• v.25 no.1
• /
• pp.49-55
• /
• 2009

The frictional properties of automotive brake pads with four different ceramic materials such as magnesia, hematite, alumina, and zircon were investigated. A Krauss type friction tester using gray iron disks was used to examine the friction coefficient, intensity of friction force oscillation, and the tribe-surfaces. Results showed that the friction coefficient increased as the hardness of abrasives increases. Friction oscillation was also increased with hardness of the abrasives. However, the friction materials containing less abrasive particles produced stable friction films on the sliding surface. The transition between two-body and three body abrasion during sliding also played a crucial role in destructing the friction film on the pad surface and in determining various frictional properties.

• Journal of Welding and Joining
• /
• v.18 no.5
• /
• pp.105-111
• /
• 2000

The wear behavior of thermal sprayed AlSiMg-40TiC composite coatings were studied as a function of load and sliding velocity under unlubricated conditions. Experiments were performed using a block-on-ring(WC-6wt%/Co, Hv 1500) type. The tests were carried out a various load(30∼ 125.5N) and sliding velocity(0.5∼2.0m/s). Three wear rate regions were observed in the AlSiMg-40TiC composite coatings. The wear rate in region I at low load (less then 8N( were less than 1×{TEX}$10^{-5}${/TEX}㎣/m. Low wear rates in region I resulted from the load-bearing capacity of TiC particles. The transition from region I to II occurred when the applied load exceeded the fracture and pull-out strength of the particles. The TiC fractured particles trapped between the specimen and the counterface acted as third-body abrasive wear. The subsurface layer worn surface in region II was composed of the mechanically mixed layer (MML). The wear rate increase abruptly above a critical load (region III). The high wear rate in region III was induced by frictional temperature and involves massive surface damage.