• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2005.11a
• /
• pp.68-69
• /
• 2005

BTO ($BaTiO_3$) thin film is one of the high dielectric materials for high-density dynamic random access memories (DRAMs) due to its relatively high dielectric constant. It is generally known that BTO film is difficult to be etched by plasma etching, but high etch rate with good selectivity to pattern mask was required. The problem of sidewall angle also still remained to be solved in plasma etching of BTO thin film. In this study, we first examined the patterning possibility of BTO film by chemical mechanical polishing (CMP) process instead of plasma etching. The sputtered BTO film on TEOS film as a stopper layer was polished by CMP process with the self-developed $BaTiO_3$- and $TiO_2$-mixed abrasives slurries (MAS), respectively. The removal rate of BTO thin film using the$ BaTiO_3$-mixed abrasive slurry ($BaTiO_3$-MAS) was higher than that using the $TiO_2$-mixed abrasive slurry ($TiO_2$-MAS) in the same concentrations. The maximum removal rate of BTO thin film was 848 nm/min with an addition of $BaTiO_3$ abrasive at the concentration of 3 wt%. The sufficient within-wafer non-uniformity (WIWNU%)below 5% was obtained in each abrasive at all concentrations. The surface morphology of polished BTO thin film was investigated by atomic force microscopy (AFM).

• Bulletin of the Korean Chemical Society
• /
• v.23 no.5
• /
• pp.741-744
• /
• 2002

Single phase of multicomponent oxide ZrTiO4 film could be prepared through surface sol-gel route simply by coating the mixture of 100 mM zirconium butoxide and titanium butoxide on $Pt/Ti/SiO_2Si(100)$ substrate, following pyro lysis at $450^{\circ}C$, and annealing it at 770 $^{\circ}C.$ The dielectric constant of the film was reduced as the film thickness decreased due to of the interfacial effects caused by layer/electrode and a few voids inside the multilayer. However, the dielectric property was independent of applied dc bias sweeps voltage (-2 to +2 V).The dielectric constant of bulk film, 31.9, estimated using series-connected capacitor model was independent of film thickness and frequency in the measurement range, but theoretical interfacial thickness, ti, was dependent on the frequency. It reached a saturated ti value, $6.9{\AA}$, at high frequency by extraction of some capacitance component formed at low frequency range. The dielectric constant of bulk ZrTiO4 pellet-shaped material was 33.7 and very stable with frequency promising as good applicable devices.

• Journal of Sensor Science and Technology
• /
• v.12 no.1
• /
• pp.10-15
• /
• 2003

$PbTiO_3$/P(VDF/TrFE) thin film for pyroelectric infrared sensor's sensing materials have been fabricated by spin coating technique. 65 wt% VDF and 35 wt% TrFE were for P(VDF/TrFE) powder. $PbTiO_3$ powder was used for a ceramic - polymer composites materials. Surface of composite thin film by ceramic fraction factor was observed by SEM. The $PbTiO_3$/P(VDF/TrFE) thin film capacitancy, dielectric constant and dielectric loss measured by impedence analyzer(HP4192A) and pyroelectric coefficient was measured by semiconductor parameter analyzer(HP4145B).

• Bulletin of the Korean Chemical Society
• /
• v.28 no.12
• /
• pp.2481-2485
• /
• 2007

Spatially resolved, quantitative, non-destructive analysis using synchrotron x-ray reflectivity (XR) with subnano-scale resolution was successfully performed on the nanoporous organosilicate thin films for low dielectric applications. The structural information of porous thin films, which were prepared with polymethylsilsesquioxane and thermally labile 4-armed, star-shaped poly(ε-caprolactone) (PCL) composites, were characterized in terms of the laterally averaged electron density profile along with a film thickness as well as a total thickness. The thermal process used in this work caused to efficiently undergo sacrificial thermal degradation, generating closed nanopores in the film. The resultant nanoporous films became homogeneous, well-defined structure with a thin skin layer and low surface roughness. The average electron density of the calcined film reduced with increase of the initial porogen loading, and finally leaded to corresponding porosity ranged from 0 to 22.8% over the porogen loading range of 0-30 wt%. In addition to XR analysis, the surface and the inner structures of films are investigated and discussed with atomic force and scanning electron microscopy images.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2000.07a
• /
• pp.528-531
• /
• 2000

Deposition of PZT with UV laser ablatio was applied for realization of thin film sensors and actuators. Deposition rate of more than 20nm/min was attained by pulsed KrF excimer laser deposition, which is fairly better than those obtained by the other methods. Perovskite phase was obtained at room temperature deposition with Fast Atom Beam(FAB) treatment and annealing. Smart MEMS(Micro electro-mechanical system) is now a suject of interest in the field of micro optical devices, micro pumps, AFM cantilever devices etc. It can be fabricated by deposition of PZT thin films and micromachining. PZT films of more than 1 micron thickness is difficult to obtain by conventional methods. This is the reason why we applied excimer laser ablation for thin film deposition. The remanent polarization Pr of 700nm PZT thin film was measured, and the relative dielectric constant was determined to about 900 and the dielectric loss tangent was also measured to be about 0.04. XRD analysis shows that, after annealing at 650 degrees C in 1 hour, the perovskite structure would be formed with some amount of pyrochlore phase, as is the case of the annealing at 750 degrees C in 1 hour.

• Journal of the Korean Ceramic Society
• /
• v.37 no.3
• /
• pp.233-239
• /
• 2000

Sr0.9Bi2+xTa2O9(x=0, 0.1, 0.2, 0.3) thin films on IrO2/SiO2/Si or Pt/Ti/SiO2/Si substrate were prepared by spin coating method using SBT stock solutions synthesized by MOD process. SBT thin films on IrO2 transformed to layered perovskite phase at $700^{\circ}C$, but showed low breakdown voltage due to their porous microstructure. The smaple of Sr0.9Bi2+xTa2O9 composition showed the best dielectric and electrical properties. When the sample of the same composition was annealed at 80$0^{\circ}C$, the dielectric and electric properties were improved due to the grian growth and dense surface. the remanent polarization values(2Pr) at $\pm$3 V for IrO2 and Pt electrodes were 10.5, 7.15$\mu$C/$\textrm{cm}^2$, respectively. The SBT thin film with IrO2 electrode showed the lower coercive field. The leakage current density and breakdown voltage of SBT thin films on IrO2 were higher than those on Pt.

• Journal of Korean Vacuum Science & Technology
• /
• v.5 no.1
• /
• pp.11-18
• /
• 2001

Dielectric passivation effects on the EM(electromigration) have been a great interest with recent ULSI and multilevel structure tends in thin film interconnections of a microelectronic device. SiO$_2$, PSG(phosphosilicate glass), and Si$_3$N$_4$ passivation materials effects on the EM resistance were investigated by utilizing widely used Al-1%Si thin film interconnections. A standard photolithography process was applied for the fabrication of 0.7㎛ thick 3㎛ wide, and 200㎛ ~1600㎛ long Al-1%Si EM test patterns. SiO$_2$, PSG, and Si$_3$N$_4$ dielectric passivation with the thickness of 300 nm were singly deposited onto the Al-1%Si thin film interconnections by using an APCVD(atmospheric pressure chemical vapor deposition) and a PECVD(plasma enhanced chemical vapor deposition) in order to investigate the passivation materials effects on the EM characteristics. EM tests were performed at the direct current densities of 3.2 $\times$ 10$\^$6/∼4.5 $\times$ 10$\^$6/ A/cm$^2$ and at the temperatures of 180 $\^{C}$, 210$\^{C}$, 240$\^{C}$, and 270$\^{C}$ for measuring the activation energies(Q) and for accelerated test conditions. Activation energies were calculated from the measured MTF(mean-time-to-failure) values. The calculated activation energies for the electromigration were 0.44 eV, 0.45 eV, and 0.50 eV, and 0.66 eV for the case of nonpassivated-, Si$_3$N$_4$passivated-, PSG passivated-, and SiO$_2$ passivated Al-1%Si thin film interconnections, respectively. Thus SiO$_2$ passivation showed the best characteristics on the EM resistance followed by the order of PSG, Si$_3$N$_4$ and nonpassivation. It is believed that the passivation sequences as well as the passivation materials also influence on the EM characteristics in multilevel passivation structures.

• Journal of Sensor Science and Technology
• /
• v.27 no.1
• /
• pp.1-5
• /
• 2018

Two-dimensional (2D) niobate-based nanosheets have attracted attention as high-k dielectric materials. We synthesized strontiumsubstituted calcium niobate ($Ca_{0.8}Sr_{1.2}Nb_3O_{10}$) nanosheets by a two-step cation exchange process from $KCa_{0.8}Sr_{1.2}Nb_3O_{10}$ ceramic. The $K^+$ ions were exchanged with $H^+$ ions, and then H+ ions were exchanged with tetrabutylammonium ($TBA^+$) cations. The $Ca_{0.8}Sr_{1.2}Nb_3O_{10}$ nanosheets were then exfoliated, decreasing the electrostatic interaction between each niobate layer. Furthermore, $Ca_2Nb_3O_{10}$ nanosheets were synthesized in same process for comparison. Each exfoliated nanosheet shows a single-crystal phase and has a lateral size of over 100 nm. The nanosheets were deposited on a $Pt/Ti/SiO_2/Si$ substrate by the electrophoretic deposition (EPD) method at 40 V, followed by ultraviolet irradiation of the films in order to remove the remaining $TBA^+$ ions. The $Ca_{0.8}Sr_{1.2}Nb_3O_{10}$ thin film exhibited twice the dielectric permittivity (~60) and lower dielectric loss than $Ca_2Nb_3O_{10}$ thin films.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2000.02a
• /
• pp.77-77
• /
• 2000

Titanium oxide (TiO2) thin films have valuable properties such as a high refractive index, excellent transmittance in the visible and near-IR frequency, and high chemical stability. Therefore it is extensively used in anti-reflection coating, sensor, and photocatalysis as electrical and optical applications. Specially, TiO2 have a high dielectric constant of 180 along the c axis and 90 along the a axis, so it is highlighted in fabricating dielectric capacitors in micro electronic devices. A variety of methods have been used to produce patterned self-assembled monolayers (SAMs), including microcontact printing ($\mu$CP), UV-photolithotgraphy, e-beam lithography, scanned-probe based micro-machining, and atom-lithography. Above all, thin film fabrication on $\mu$CP modified surface is a potentially low-cost, high-throughput method, because it does not require expensive photolithographic equipment, and it produce micrometer scale patterns in thin film materials. The patterned SAMs were used as thin resists, to transfer patterns onto thin films either by chemical etching or by selective deposition. In this study, we deposited TiO2 thin films on Si (1000 substrateds using titanium (IV) isopropoxide ([Ti(O(C3H7)4)] ; TIP as a single molecular precursor at deposition temperature in the range of 300-$700^{\circ}C$ without any carrier and bubbler gas. Crack-free, highly oriented TiO2 polycrystalline thin films with anatase phase and stoichimetric ratio of Ti and O were successfully deposited on Si(100) at temperature as low as 50$0^{\circ}C$. XRD and TED data showed that below 50$0^{\circ}C$, the TiO2 thin films were dominantly grown on Si(100) surfaces in the [211] direction, whereas with increasing the deposition temperature to $700^{\circ}C$, the main films growth direction was changed to be [200]. Two distinct growth behaviors were observed from the Arhenius plots. In addition to deposition of THe TiO2 thin films on Si(100) substrates, patterning of TiO2 thin films was also performed at grown temperature in the range of 300-50$0^{\circ}C$ by MOCVD onto the Si(100) substrates of which surface was modified by organic thin film template. The organic thin film of SAm is obtained by the $\mu$CP method. Alpha-step profile and optical microscope images showed that the boundaries between SAMs areas and selectively deposited TiO2 thin film areas are very definite and sharp. Capacitance - Voltage measurements made on TiO2 films gave a dielectric constant of 29, suggesting a possibility of electronic material applications.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.06a
• /
• pp.139-142
• /
• 1998

PLZT thin films were fabricated with different Zr/Ti ratios by pulsed laser deposition. PLZT films deposited on Pt/Ti/SiO$_2$/Si substrate. This PLZT thin films of 5000${\AA}$. thickness were crystallized at 600$^{\circ}C$, 200 mTorr O$_2$ press. 2/55/45 PLZT thin film showed a maximum dielectric constant value of $\varepsilon$$\_$r/=1500, and dielectric loss was 0.O$_3$. At 2/70/30 PLZT thin film, Coercive field and remnant polarization was respectively 19[kV/cm], 8[${\mu}$C/$\textrm{cm}^2$].