• Journal of Korea Foundry Society
• /
• v.30 no.2
• /
• pp.76-82
• /
• 2010

Effect of reaction time and sludge formation on the thickness of die soldering reaction layer has been studied in Al-9Si-0.3Mg casting alloy. Ternary ${\alpha}_{bcc}-Al_8Fe_2Si$ and ${\alpha}_{hcp}-Al_8Fe_2Si$ intermetallic compounds formed at the interface of SKD61 tool steel by interaction diffusion of Al, Fe and Si atoms after 0.5hr and 6hr immersion time, respectively. Binary ${\eta}-Fe_2Al_5$ additionally formed at the interface of SKD61 tool steel after 10hr immersion time. Thickness of soldering reaction layer in die surface increased as immersion time increased from 0.5hr to 24hr. Sludge formation was ascertained in the samples which were immersed in the melts more than 10hr. Reaction of die soldering after sludge formation was more accelerated than that of before sludge formation due to a decrease in Fe content, followed by higher diffusion rate of Al in the melt by sludge formation.

• Journal of Korea Foundry Society
• /
• v.29 no.4
• /
• pp.169-175
• /
• 2009

Effect of iron and manganese contents on die soldering reaction has been studied in Al-9wt.%Si-0.3wt.%Mg alloy. Ternary ${\alpha}_{hcp}-Al_8Fe_2Si$ and ${\alpha}_{bcc}-Al_8Fe_2Si$ intermetallic compounds formed by interaction diffusion between Al-Si-Mg system alloy melt and SKD61 die steel surface. Thickness of soldering reaction layer in die steel surface decreased as Fe and Mn contents of the melts increased : When Fe content of Al-9wt.%Si-0.3wt.%Mg melts at constant 0.5wt%Mn content was 0.15wt.%, 0.45wt.% and 0.6wt.%, thickness of soldered layer of each alloy was $64.5{\mu}m,\;57.3{\mu}m$ and $46.9{\mu}m$ respectively. For Mn content of the alloy melts at constant 0.45wt.%Fe content was 0.30wt.%, 0.50wt.% and 0.70wt.%, thickness of soldered layer of each alloy was $66.1{\mu}m,\;57.3{\mu}m$ and $48.3{\mu}m$ respectively.

• Journal of the Microelectronics and Packaging Society
• /
• v.17 no.1
• /
• pp.1-7
• /
• 2010

Interfacial reaction characteristics of a Bi-10Cu-20Sb-0.3Ni Pb-free alloy on Cu pad was investigated by reflow soldering at $430^{\circ}C$. The thickness of interfacial reaction layers with respect to the soldering time was also measured. After the reflow soldering, it was observed that a $(Cu,Ni)_2Sb$, a $Cu_4Sb$ intermetallic layer, and a haze layer, which is consisted of Bi and $Cu_4Sb$ phases, were successively formed at the Bi-10Cu-20Sb-0.3Ni/Cu interface. The total thickness of the reaction layers was found to be linearly increased with increasing of the reflow soldering time up to 120 s. As the added Ni element did not participate in the formation of the thickest $Cu_4Sb$ interfacial layer, suppression of the interfacial growth was not observed.

• Journal of the Korean institute of surface engineering
• /
• v.36 no.5
• /
• pp.373-378
• /
• 2003

With increasing environmental concerns, application of lead-free solder and fluxless soldering process have been taken attention from the electronic packaging industry. Plasma treatment is one of the soldering methods for the fluxless soldering, and it can prevent environmental pollution cased by flux. On this study fluxless soldering process under $Ar-H_2$plasma using lead free solders such as Sn-3.5 wt%Ag, Sn-3.5 wt%Ag-0.7 wt%Cu and Sn-37%Pb for a reference was investigated. As the plasma reflow has higher soldering temperature than normal air reflow, the effects of UBM(Under Bump Metallization) thickness on the interfacial reaction and bonding strength can be critical. Experimental results showed in case of the thin UBM, Au(20 nm)/Cu(0.3 $\mu\textrm{m}$)/Ni(0.4 $\mu\textrm{m}$)/Al(0.4 $\mu\textrm{m}$), shear strength of the soldered joint was relatively low as 19-27㎫, and it's caused by the crack observed along the bonded interface. The crack was believed to be produced by the exhaustion of the thin UBM-layer due to the excessive reaction with solder under plasma. However, in case of thick UBM, Au(20 nm)/Cu(4 $\mu\textrm{m}$)/Ni(4 $\mu\textrm{m}$)/Al(0.4 $\mu\textrm{m}$), the bonded interface was sound without any crack and shear strength gives 32∼42㎫. Thus, by increasing UBM thickness in this study the shear strength can be improved to 50∼70%. Fluxed reflow soldering under hot air was also carried out for a reference, and the shear strength was 48∼52㎫. Consequently the fluxless soldering with plasma showed around 65∼80% as those of fluxed air reflow, and the possibility of the $Ar-H_2$ plasma reflow was evaluated.

• Proceedings of the International Microelectronics And Packaging Society Conference
• /
• 2000.04a
• /
• pp.73-73
• /
• 2000

Shear strength of BGA solder joints on Cu pad was studied for Cu-contained Sn n.5 a and 2.5wt.% Cu) and Sn-Pb (o.5wt.% Cu) solders, with emphasis on the roles of the C Cu-Sn intermetallic layer thickness and the roughness of the interface between the i intermetallic layer and solder. The shear strength test was performed both for a as-soldered s이der joints with soldering reaction times of 1, 2, 4 min and for aged s이der j joints at 170 C up to 16 days. The Cu addition to both pure Sn and eutectic Sn-Pb s solders increased the intermetallic layer thickness at both soldering and aging t temperatures. The Cu addition also resulted in changes in the roughness of the interface b between the intermetallic layer and solder at as-soldered states. With increasing Cu c content. the interface roughened for Sn-Cu solders whereas it flattened for Sn-Pb-Cu s solders. The shear fractures in all solder joints investigated were confined in the bulk s solder rather than through the intermetallic layer. Therefore, the effect of Cu content in s solders on the shear strength of the solder joints was primarily attributed to its i influence on the micros$\sigma$ucture of bulk solder, such as the size and spatial distributions of CU6Sn5 precipitates. In addition, the critical intermetallic layer thickness for a m maximum shear strength seemed to depend on the Cu content in bulk solder.older.

• Progress in Superconductivity
• /
• v.7 no.2
• /
• pp.179-183
• /
• 2006

As a material for SFCL(Superconducting Fault Current Limiter), BSCCO tube with metal stabilizer is a promising candidate, assuring the stability and large power capacity, For the application, the proper soldering technique, which overcome the difficulties of the joining between BSCCO and metal stabilizer, is required. In this study, after soldering In-Bi solder and In-Sn solder with BSCCO superconductor, welding properties between BSCCO and solders were investigated. Because ceramic materials is difficult to weld, Ag electro-plating on BSCCO 2212 is used for intermetallic layer. To find out the best welding condition for superconductor, soldering is tested in the maximum temperature from $155^{\circ}C\;to\;165^{\circ}C$ in the reflow oven. By investigating the composition and thickness of IMC (lntermetallic Compound) created in the reaction of Ag with solder, we analyzed the welding properties of High-Tc superconductor from a micro point of view.

• Journal of the Microelectronics and Packaging Society
• /
• v.7 no.2
• /
• pp.13-19
• /
• 2000

Shear strengths of BGA solder joints on Cu pads were studied for Cu-containing Sn (0, 1.5, and 2.5 wt.% Cu) and Sn-40Pb (0 and 0.5wt.% Cu) solders, with emphasis on the roles of the Cu-Sn intermetallic layer thickness and the roughness of the interface between the intermetalic layer and solder. The shear strength test was performed for as-soldered solder joints with various soldering reaction times up to 4 min. The addition of Cu to the pure Sn solder results in an enhanced growth of the intermetallic layer whereas the effect of Cu addition to the Sn-40Pb solder is primarily on the reduction of the roughness of the intermetallic/solder interface. The critical thickness of the intermetallic layer for a maximum shear strength depends on the solder materials, which was measured to be ~ 2.3 $\mu\textrm{m}$ for Sn-Cu solders and ~ 1.2 $\mu\textrm{m}$ for Sn-Pb-Cu solders. The shear strength at the critical intermetallic layer thickness seems to increase as the intermetallic/solder interface becomes rougher. This is in accordance with the observation that the sheared fracture occurred initially within the solder tends to shift towards the intermetallic/solder interface as the intermetallic layer grows above the critical thickness.