• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.9 no.6
• /
• pp.1745-1753
• /
• 2008

We analyzed the physical and chemical properties such as proximate analysis, ultimate analysis, heating values, thermogravimetric analysis, and combustion test for the organic sludge discharged from chemical and petrochemical product manufacturing industries in the industrial complex. The average combustible and ash content of organic sludges from chemical and petrochemical product manufacturing industries were 17.42%, 7.45%, and 18.25%, 4.22%, respectively. The C, H, O, N, and S compositions for chemical and petrochemical product manufacturing industries were 33.06, 4.34, 24.81, 5.18, and 0.72%. And those compositions for petrochemical product manufacturing industries were 36.58, 4.74, 26.79, 5.09, and 0.49%, respectively. From the TGA test, the minimum temperature for combustion of the sludge discharged from B company was $700^{\circ}C$ for direct use for energy and 2 sludges(F and N companies) were about $600^{\circ}C$. According to the basic combustion test, high concentration of CO was formed because oxidation and pyrolysis reaction take place in the batch type reactor at the same time. From this phenomena we could obtain the significant data for the overheating and breakage of furnace.

• Elastomers and Composites
• /
• v.49 no.2
• /
• pp.144-148
• /
• 2014

Compression set (CS) and weight loss by thermal degradation of the ACM rubber composite sample prepared for an automotive part were measured simultaneously at several given temperatures of $150^{\circ}C$, $160^{\circ}C$, $170^{\circ}C$, and $180^{\circ}C$. Using the relationship between them, thermal life of the sample could be predicted at a given operating temperature by applying Toops method which is based on the analysis of non-isothermal TGA thermograms. Conversion by weight loss showed a linear relationship with CS changes, exhibiting 4.2% at CS 40%. Activation energy of thermal degradation was calculated as 120.2 kJ/mol at 4.2% of weight loss from Flynn-Wall-Ozawa analysis. When the expected life was set as time to reach CS 40% at $120^{\circ}C$, the life time of the sample was calculated as 9,700 hrs when Toops method was applied.

• Journal of Nuclear Fuel Cycle and Waste Technology(JNFCWT)
• /
• v.7 no.3
• /
• pp.175-182
• /
• 2009

The spent cationic exchange resins and anionic exchange resins were separated from mixed spent exchange resins by a fluidized bed gravimetric separator. The separated resins were identified by an elemental analysis and thermogravimetric analysis. The each test sample was prepared by diluting the slurry made by wet ball milling the cationic exchange resins and the anionic exchange resins separated as a spherical granular form for 24 hours. The resulting test samples showed a slurry form of less than $75{\mu}m$ of particle size and 25,000ppm of $COD_{cr}$. The decomposition conditions of each test samples from a thermal power plant were obtained with a lab-scale(reactor volume : 220mL) supercritical water oxidation(SCWO) facility. Then pilot plant(reactor volume : 24 L) tests were performed with the test samples from a thermal power plant and a nuclear power plant successively. Based on the optimal decomposition conditions and the operation experiences by lab-scale facility and the pilot plant, a commercial plant(capacity : 150kg/h) can be installed in a nuclear power plant was designed.

• Journal of the Korean Wood Science and Technology
• /
• v.43 no.1
• /
• pp.96-103
• /
• 2015

The aim of this paper is to analyze combustion characteristics of treated woods by fire retardants which are prepared by several borate and phosphate compound solutions. The combustion characteristics for flame retardant treated wood were carried out using thermogravimetric analysis (TGA) to measure their combustion heat and flame retardant test using cone-calorimeter. The result of TGA and flame retardant test showed that single chemical solution affected the char forming and flame delay. The mixed retardants solutions was believed to be related to the efficacy and property of single chemical. The retention value and concentration of the retardants also affected the performance of fire retardant treated woods. The fire retardants FR1 and FR2 satisfied the requirement of The 3 Grade of Korean building codes.

• Journal of Hydrogen and New Energy
• /
• v.30 no.6
• /
• pp.531-539
• /
• 2019

The development of cost-effective electrocatalysts with high durability is one of the most important challenges for the commercialization of polymer electrolyte fuel cells (PEFCs). The durability of the electrocatalyst has been studied in terms of structural change in the active metal and the support. In particular, in fuel cell vehicles, degradation of the carbon-based support is known to have a significant effect on the electrocatalyst deterioration since the start-up/shut-down cycle is frequently repeated. The requirements for the support of the electrocatalyst include high surface area, electrical conductivity, chemical stability, and so on. In this study, we propose the evaluation methods for choosing better support materials and present the physicochemical properties that promising carbon supports should have. Three kinds of carbon materials with different crystallinity are compared. From in-depth study using X-ray diffraction, Raman spectroscopy, thermogravimetric analysis, and accelerated stress test, it is clearly confirmed that the durability of carbon-supported electrocatalysts is closely related to the physicochemical properties of the carbon supports.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.12 no.1
• /
• pp.53-62
• /
• 2024

In this paper, an experimental study on the strengths and material properties of concrete manufactured by using coal gangue, as a fine aggregate was conducted. Experimental parameters included coal gangue aggregate contents as a replacement of fine aggregate by 50 % and 100 % (by volume) and fly ash contents. The water-binder ratio was fixed at 0.38. In addition, 30 % of the OPC binder was replaced with fly ash in some mixtures. Test of the unit weight, compressive, split tensile, and flexural tensile strength of concrete were performed and test results were analyzed. Unit weight, compressive strength, split tensile strength, and flexural tensile strength decreased as the coal recycled aggregates increased. In addition, TGA and SEM experiments, which are microstructure experiments, were conducted to analyze thermogravimetric analysis and ITZ by section.

• Clean Technology
• /
• v.23 no.4
• /
• pp.378-387
• /
• 2017

To obtain epoxy resin with permanently attached flame-retardant groups, phosphorus compound containing di-hydroxyl group [10-(2,5-dihydroxyphenyl)-9,10-dihydro-9-oxa-10-phospha phenanthrene-10-oxide, DOPO-HQ] and silicone compound containing di-hydroxyl group (polydimethylsiloxane, hydroxyl terminated, PDMS) were reacted with uncured epoxy prepolymer (diglycidyl ether of bisphenol A, DGEBA) and then cured using 4,4-diaminodiphenylmethane (DDM) as a crosslinking agent. The properties of the resulting epoxy materials were characterized using Fourier transform infrared (FTIR) spectrometer, differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), limiting oxygen index (LOI) test/vertical burning test (UL 94-V test), tensile properties test and impact test. This study examined the effect of phosphorus/silicone compound contents on the thermal/mechanical properties and flame retardancy of cured epoxy resins containing phosphorus and silicone compounds. It was found that the thermal/mechanical properties of epoxy resins containing phosphorus and silicone components were higher than those of simple epoxy resin. The flame-retardancy (LOI: 29.9 ~ 31.8% and UL 94-V: V-0) of all samples containing phosphorus compound and phosphrous compound/silicone compound was found to be passed the flame-retardant requirements (LOI: > 30%, UL 94-V: V-0) of LOI and vertical burning tests. However, the flame-retardancy (LOI: 21.4% and UL 94-V: no rating) of simple epoxy resin was found to be failed the flame-retardant requirements.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.12 no.1
• /
• pp.8-16
• /
• 2024

Limestone (CaCO₃, calcium carbonate), which is used as a raw material in the portland cement and steel industry, emits CO₂ through decarbonation by high temperatures in the manufacturing process. To reduce CO₂ emissions by the use of raw materials like limestone, it has been proposed to replace limestone with various industrial by-products that contain CaO but less or none of the carbonated minerals, that cause CO₂ emissions. Loss of Ignition (LOI), Thermogravimetric analysis (TG), and Infrared Spectroscopy (IR) are used to quantitative the amount of CO₂ emission by using these industrial by-products, but CO₂ emissions can be either over or underestimated depending on the characteristics of by-product materials. In this study, we estimated CO₂ contents by LOI, TG, IR and DTG(Differential Thermogravimetric analysis) of calcite(CaCO₃) and samples that contain CO₂ in the form of carbonate and whose weight increases by oxidation at high temperatures. The test results showed for CaCO₃ samples, all test methods have a sufficient level of reliability. On the other hand, for the CO₂ content of the sample whose weight increases at high temperature, LOI and TG did not properly estimate the CO₂ content of the sample, and IR tended to overestimate compared to the predicted value, but the estimated result by DTG was close to the predicted valu e. From these resu lts, in the case of samples that contain less than a few percent of CO₂ and whose weight increases during the temperature that carbonate minerals decompose, estimating the CO₂ content using DTG is a more reasonable way than LOI, TG, and IR.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.9 no.5
• /
• pp.1359-1367
• /
• 2008

We analyzed the physical and chemical properties such as proximate analysis, ultimate analysis, heating values, thermogravimetric analysis, and combustion test for the organic sludges generated from paper and beverage manufacturing industries in the industrial complex. The average water and combustible content of the organic sludges from paper and beverage manufacturing industries were 66.07% and 14.67%, 54.98% and 26.77%, respectively. From the ultimate analysis of the organic sludges, C, H, O, N, and S compositions were 21.75%, 3.42%, 32.70%, 0.63%, and 0.30%, respectively. For beverage manufacturing industries, C, H, O, N, and S compositions were 39.88%, 4.28%, 23.20%. 2.65%, and 0.35%, respectively. According to the results of investigating the lower heating values by Dulong's equation, 1 sludge(T company) was on the range of over 2,000 kcal/kg. This sludge could be directly applied to industries which try to use the energy by direct incineration. From the TGA test, the minimum combustion temperature of A company's sludge was about $700^{\circ}C$ for direct use for energy and that of 3 sludges(C, I, and T company) were at least over $800^{\circ}C$.

• Polymer(Korea)
• /
• v.31 no.1
• /
• pp.31-36
• /
• 2007

It has been reported that the surface properties of the plasma treated material were changed while maintaining its bulk properties. In this study, surface modification of nylon fiber by plasma treatment was tried to attain high water-repellency Nylon fiber was treated with RF plasma under a vacuum system using various parameters such as gas specious, processing time and processing power. Morphological changes by low pressure plasma treatment were observed using scanning electron microscopy (SEM) and atomic force microscopy (AFM). Moreover, the mechanical and inherent properties were analyzed by tensile strength, differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). The high water-repellency property of nylon fiber was evaluated by a water-drop standard test under various conditions in terms of aging effect. The results showed that the water-repellency of plasma-surface-treated nylon fiber was greatly improved compared to untreated nylon fiber.