• Journal of the Korean Society for Precision Engineering
• /
• v.30 no.8
• /
• pp.802-808
• /
• 2013

Thermal barrier coating (TBC) is used to protect substrates and extend the operating life of gas turbines in power plant and aeronautical applications. The major causes of failure of such coatings is spallation, which results from thermal stress due to a thermal expansion coefficient mismatch between the top coating and the bond coating layers. In this paper, the effects of the material properties and the thickness of the top coating layer on thermal stresses were evaluated using the finite element method and the equation for the thermal expansion coefficient mismatch stress. In addition, we investigated a design technique for the top coating whereby thermal resistance is exploited.

• Journal of the Korean Society for Precision Engineering
• /
• v.31 no.1
• /
• pp.15-20
• /
• 2014

Thermal barrier coating (TBC) is used to protect the substrate and extend the operating life of the gas turbine for a power plant and an aircraft. The major cause of failure of such a coating is the spallation of coating, and it results from the thermal stress between top coating and bond coating. To improve the durability of TBC system, the dense vertical cracked (DVC) coating method to insert vertical cracks is applied to a gas turbine blade. In this study, a criterion for the design of vertical crack in the DVC coating was presented using the finite element analysis.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2021.11a
• /
• pp.17-18
• /
• 2021

In the present study, Al-Zn coating was deposited by Arc thermal (AT) and plasma arc thermal (PAT) spray processes, and their corrosion characteristics were studied in 3.5% NaCl through electrochemical impedance spectroscopy (EIS), scanning electron microscope (SEM) and mechanical tests. The bond adhesion result showed that plasma arc sprayed coating had a higher value attributed to compact, dense, and less porous coating compared to arc thermal spray coating which contains defects/pores and uneven morphology as revealed by scanning electron microscope analysis. Electrochemical results revealed that the plasma arc sprayed coating had a high polarization resistance at early stage of immersion, suggesting its excellent corrosion protection performance.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.18 no.12
• /
• pp.45-51
• /
• 2019

As the separator becomes thinner, the role of thermal stability becomes more important in ensuring the high capacity of medium- and large-sized lithium-ion secondary batteries. In this study, we researched coating technology to improve the separator's thermal stability. We minimized the coating time by optimizing the design of a vertical two-stage coater that was thin, uniform, and capable of coating on both sides at the same time with a maximum 2㎛ thickness coating layer of fluorinated polymer (PVdF-HFP) on the bare polyethylene (PE) separator, which increased the thermal stability. In addition, during the coating process, a dual-jacket-roll method of drying was developed that increased the drying effectiveness without thermal damage to the separator. We also investigated the thermal stability of the separator manufactured from a coating machine, and studied the battery-applied performance by making a lithium-ion pouch battery.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.524-524
• /
• 2012

Thermal Barrier Coating (TBC)은 미사일, 로켓발사체와 같이 고온에 노출되는 장비를 열로부터 보호하기 위한 코팅이다. 일반적인 Thermal Barrier Coating (TBC)은 모재와 코팅층간의 낮은 접합력과 높은 열충격으로 인한 박리가 많이 나타난다. 그래서 접합력을 높이고, 열충격을 줄이기 위해 모재와 코팅층 사이에 본드코팅층을 만든 Duplex - Thermal Barrier Coating (Duplex-TBC)이 개발되었다. 그러나 Duplex - Thermal Barrier Coating (Duplex-TBC)은 금속재료인 본드코팅층과 세라믹재료인 탑코팅층 사이에서 박리가 많이 발생한다. 이러한 문제점을 해결하기 위해 두 가지 분말을 동시에 코팅하여 본드코팅과 탑코팅의 경계가 없는 Functional Gradient Material - Thermal Barrier Coating (FGM-TBC)의 연구가 필요하다. 본 연구에서는 Functional Gradient Material - Thermal Barrier Coating (FGM-TBC)의 열충격 특성에 미치는 진공 플라즈마 용사 조건의 영향을 조사하였다. Functional Gradient Material - Thermal Barrier Coating (FGM-TBC)는 진공 플라즈마 용사장치를 사용하여 Cu-Cr 합금위에 코팅하였다. 거리, Carrier gas flow, 그리고 챔버 내부의 압력을 달리하여 제조하였다. 사용한 분말은 본드코팅용으로 Amdry 962와 내열 세라믹코팅을 위해 204NS를 사용하였고, 각각 분말 공급조건을 조절하여 두 분말의 비율을 달리하였다. 제조한 Functional Gradient Material - Thermal Barrier Coating (FGM-TBC) 코팅은 전기로에서 50분간 가열한 후, 수조에서 10분간 냉각하는 열충격 실험을 통해 열차폐 성능을 평가 하였다. 이러한 과정에서 진공 플라즈마 용사 조건 및 FGM 조성과 비율이 내열충격 특성에 미치는 영향을 미세조직학적 관점에서 고찰하였다.

• Journal of Surface Science and Engineering
• /
• v.49 no.2
• /
• pp.172-177
• /
• 2016

In this paper, various electrochemical experiments were conducted in seawater solution to evaluate corrosion damage behavior of arc thermal sprayed Inconel 625 coating on SS400 steel in marine environment. As a result, corrosion damages of thermal sprayed Inconel 625 coating preferentially occurred at the defect area, and they were observed as a form of pitting corrosion in the galvanostatic experiments. In Tafel analysis, corrosion current density of Inconel 625 coating was relatively high due to influence of interconnected pores and Cr oxides in the thermal spray coating layer. On the other hand, the result of the potential measurement, thermal sprayed Inconel 625 coating should need the post-treatment which can compensate the defects like pores and cracks because Inconel 625 coating presented a higher potential of about 290 mV than that of the SS400 steel.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2020.06a
• /
• pp.83-84
• /
• 2020

In present study, we have deposited the Zinc coating using arc thermal spray and plasma arc spray processes onto the steel substrate and durability of the deposited coating was evaluated. The bond adhesion result shows that plasma arc sprayed Zn coating exhibited higher in its value compared to arc thermal spray. SEM shows that Zn coating deposited by plasma arc process is more compact, less porous and adherent compare to arc spray process. The corrosion resistance properties are evaluated in artificial ocean water solution with exposure periods. EIS results show that total impedance at 0.01 Hz of plasma arc sprayed coating is higher than arc thermal spray owing to the compact and less porous morphology. It is concluded that plasma arc sprayed Zn coating is better than arc thermal spray process.

• Journal of the Korea Institute of Military Science and Technology
• /
• v.23 no.5
• /
• pp.435-443
• /
• 2020

Thermal barrier coating(TBC) applied to fighter and turbine engines is a technology that improves the durability of core parts by lowering the surface temperature of base material. The thermal stress caused by mis-match of the coefficient of thermal expansion between the top coating and the TGO interface is the main cause of TBC breakage. Since the thermal stress is dependent on the microstructure of the TBC, designing microstructure of TBC can improve the durability as well as lower the thermal stress. In this study, the effect of coating thickness, volume of porosity and vertical cracking on the thermal stress was analyzed through finite element analysis. Through the analysis results, a design range of a microstructure that can improve the durability of thermal barrier coating by lowering thermal stress is proposed.

• Journal of the Korean Society of Fisheries and Ocean Technology
• /
• v.43 no.4
• /
• pp.362-369
• /
• 2007

This paper was studied on the characteristics of acid resistance and thermal shock for epoxy coatings in the strong acidic environment. The exhaust gas system, such as a air preheater, desulfurization equipment, for industrial boiler is damaged by dew point corrosion. To protect the acid corrosion, the coating using nonmetal was applied. The electrochemical polarization test, acid resistance and thermal shock test for epoxy coatings were carried out. And the acid resistance and thermal shock characteristics, aspect, and electrochemical anti-corrosion characteristics for epoxy coatings in the strong acidic environment were considered. The main results are as followings: As the epoxy glass flake coating by acidic thermal shock was damaged to the crack, blistering and elution etc., the current density of epoxy glass flake coating is high. But the damage of epoxy metal complex coating by acidic thermal shock was not occurred. Therefore the characteristics of acid resistance and thermal shock for epoxy metal complex coating is better than those for epoxy glass flake coating.

• Korean Journal of Materials Research
• /
• v.25 no.10
• /
• pp.571-576
• /
• 2015

The effects of coating thickness on the delamination and fracture behavior of thermal barrier coating (TBC) systems were investigated with cyclic flame thermal fatigue (FTF) and thermal shock (TS) tests. The top and bond coats of the TBCs were prepared by electron beam-physical vapor deposition and low pressure plasma spray methods, respectively, with a thickness ratio of 2:1 in the top and bond coats. The thicknesses of the top coat were 200 and $500{\mu}m$, and those of the bond coat were 100 and $250{\mu}m$. FTF tests were performed until 1140 cycles at a surface temperature of $1100^{\circ}C$ for a dwell time of 5 min. TS tests were also done until more than 50 % delamination or 1140 cycles with a dwell time of 60 min. After the FTF for 1140 cycles, the interface microstructures of each TBC exhibited a sound condition without cracking or delamination. In the TS, the TBCs of 200 and $500{\mu}m$ were fully delaminated (> 50 %) within 171 and 440 cycles, respectively. These results enabled us to control the thickness of TBC systems and to propose an efficient coating in protecting the substrate in cyclic thermal exposure environments.