• Journal of the Korean Ceramic Society
• /
• v.28 no.7
• /
• pp.541-548
• /
• 1991

Sinterability and stability of TZP ceramics co-stabilized by 12 mol% CeO2 and divalent or trivalent oxides less than 1 mol% were investigated. Divalent and trivalent oxides increased stability of tetragonal ZrO2. 100% tetragonal ZrO2 phase was obtained by doping 12 mol% CeO2 and 0.2 mol% CaO and MgO respectively when sintering was carried out at 1500$^{\circ}C$ for 2 hours. Divalent and trivalent oxides improved sinterability and inhibit grain growth of ZrO2. And it was found that CaO was the most effective sintering aid and grain growth inhibitor for ZrO2 in this study. Incorporation of divalent and trivalent oxides into 12Ce-TZP increased the strength of 12Ce-TZP and particulary 12Ce, 0.4Ca-TZP exhibited a flexural strength of about twofold greater than 12Ce-TZP.

• Journal of the Korean institute of surface engineering
• /
• v.40 no.4
• /
• pp.180-184
• /
• 2007

A new zirconium alloy, low-Sn Zircaloy-4 was investigated to see the effects of high pressure steam on the oxidation at high temperatures. High pressure steam turned out to enhance the oxidation at high temperatures below $1000^{\circ}C$. The oxide layer groved to deviate from the uniform layer under high steam pressures, and usually cracks were found at the thicker parts in the oxide layer. High pressure steam seems to destabilize the tetragonal oxides near the metal layer, and the monoclinic oxides transformed from the destabilized tetragonal oxides are structurally not sound, resulting in enhanced oxidation under high pressure steam.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1998.11a
• /
• pp.311-314
• /
• 1998

The effects of the additions of transition metal oxides on ZrO$_2$ - Y$_2$O$_3$ (Y$_2$O$_3$ - containing tetragonal zirconia polycrystals : Y-TZP) system has been studied by investigating fracture toughness and phase stability of the sintered specimens. In the specimens sintered at 1450$^{\circ}C$ for 2hrs in air the phase transformation from tetragonal to monoclinic was observed. The ratios of monoclinic phase to tetragonal phase were changed with the additions of CoO, Fe$_2$O$_3$ and MnO$_2$, respectively, from 0.00 to 8.00wt%. The fracture toughness was increased with increasing the monoclinic to tetragonal phase ratio and was maximum at the ratio of about 18%. However, the hardness was decreased with increasing the ratio. The additions of CoO, Fe$_2$O$_3$ and MnO$_2$ together into Y-TZP resulted in more complex behaviors of fracture toughness and hardness. The specimen with the additions of 1.5wt% Fe$_2$O$_3$, 3.0wt% Al$_2$O$_3$ and 1.5wt% CoO showed the monoclinic to tetragonal phase ratio of 18% and the highest toughness of 10.8 MPa.m$\^$$\frac{1}{2}$/ and Vickers hardness of 1201kgf/mm$^2$.

• Journal of Korea Society of Digital Industry and Information Management
• /
• v.12 no.3
• /
• pp.25-31
• /
• 2016

Mechanical properties of Y2O3-containing tetragonal ZrO2 polycrystals(Y-TZP) were investigated. Several additives were used to modify the hardness and fracture toughness of Y-TZP. The effects of these individual additives were discussed and their interactions were also analysed. Each additive, such as CoO, Fe2O3, MnO2 was found to deteriorate the mechanical properties of Y-TZP when it was used singly. But the fracture toughness of Y-TZP was significantly improved when these additives and Al2O3 were added in combination at a certain ratio. The addition of CoO, Fe2O3 and MnO2 into Y-TZP resulted in the more complex behavior of fracture toughness and hardness. The specimen with 1.5 wt%-Fe2O3, 3.0 wt% -Al2O3 and 1.5 wt%-CoO showed the monoclinic to tetragonal phase ratio of 18% and the highest toughness of $10.8MPa{\cdot}m1/2$ with Vickers hardness of 1201 kgf/mm2. However, the toughness decreased as the ratio increased and macrocracks developed beyond the ratio of 25%. Sample No. 16 is improved high Physical and Mechanical Properties.

• Journal of the Korean Ceramic Society
• /
• v.31 no.12
• /
• pp.1459-1466
• /
• 1994

A novel technique for determining the oxygen tracer diffusion coefficients in oxides was developed. After the 16O-18O solid-gas exchange reactions between 16O in the oxides and 18O in the ambient gas, Raman spectra of the cross sections of oxide samples were measured in a spatial resolution of 5 ${\mu}{\textrm}{m}$. From thus obtained Raman spectra, depth profiles of 18O concentration in the oxide samples were calculated. The oxygen tracer diffusion coefficients and the surface exchange coefficients were determined under the assumptions that samples are semi-infinite slab and that the surface exchange reactionsare not negligible. The oxygen tracer diffusion coefficient of 2.8 mol% Y2O3-containing tetragonal ZrO2 polycrystals, 8 mol% Y2O3-containing ZrO2 polycrystals, and 10 mol% Y2O3-containing cubic ZrO2 single crystals (along the a axis) are as follows.

• Journal of the Korean Ceramic Society
• /
• v.36 no.11
• /
• pp.1198-1204
• /
• 1999

The effect of sintering atmosphere on the grain sizes and phase distributions in 3Y-ZrO2 and 8Y-ZrO2 was investigated O2 and N2 were used as sintering atmospheres. In the case of 3Y-ZrO2 the sintered density was higher in N2 than in O2 while in the case of 8Y-ZrO2 contrary results were obtained. The observation can be explained by the nitrogen solubility into the zirconia lattice. That is nitrogen gas can behave as a diffusive gas contrary to the behavior in other oxides depending on the amount of Y2O3. In 3Y-ZrO2 tetragonal phase was retained at room temperature irrespective of sintering atmospheres. Grain sizes of two specimens were below 2㎛ and larger in O2 thin in N2 Under a given stress the transformability of tetragonal phase into monoclinic phase was higher in O2 than N2. The results are discussed on the basis of an effect of the grain size and non-transformable ttragonal(t') phase.

• Korean Journal of Materials Research
• /
• v.12 no.3
• /
• pp.220-224
• /
• 2002

The oxide scales formed on $Ni_3Al$-7.8%Cr-1.3%Zr-0.8%Mo-0.025%B after oxidation at 900, 1000 and 110$0^{\circ}C$ in air were studied using XRD, SEM, EPMA and TEM. The oxide scales consisted primarily of $NiO,\; NiAl_2O_4,\;{\alpha}-Al_2O_3,\; monoclinic-ZrO_2,\; and \;tetragonal-ZrO_2$. The outer layer of the oxide scale was rich in Ni-oxides, whereas the internal oxide stringers were rich in Al-oxides and $ZrO_2$. Within the above oxide scales, Cr and Mo tended to exist as dissolved ions.

• Korean Journal of Materials Research
• /
• v.20 no.7
• /
• pp.379-384
• /
• 2010

The usual ceramic process of mixing and milling in state of oxides $ZrO_2$ and $CeO_2$ was adopted in this study in a wet process to manufacture Ce-TZP. $CeO_2$-$ZrO_2$ ceramics containing 8~20 mol% $CeO_2$ were made by heat treatment at $1250\sim1500^{\circ}C$ for 5hr. The maximum dispersion point of every slurry manufactured with a mixture of $ZrO_2$ and $CeO_2$ was neat at pH10. A stable slurry with average particle size of 90 nm can be manufactured when it is dispersed with the use of ammonia water and polycarboxylic acid ammonium. The sintered Ce-TZP ceramics manufactured with the addition of $CeO_2$ in a concentration of less than 10 mol% progressed to the fracture of the specimen due to the existence of a monoclinic phase of more than 30% at room temperature. More than 99% of the tetragonal phase was created for the sintered body with the addition of $CeO_2$ beyond 18 mol%, but the degradation of the mechanical properties on the entire specimen was brought about due to the $CeO_2$ existing in a percentage above 3%. Consequently, the optimal Ce-TZP level combined in the oxide state was identified to be 16 mol% of $CeO_2$ contents.

• Journal of the Korean Chemical Society
• /
• v.61 no.1
• /
• pp.29-33
• /
• 2017

Formation of Au particles in nonstoichiometric $Cu_{2-x}{^I}Cu{_2}^{II}O_{3-{\delta}}$ ($x{\approx}0.20$; ${\delta}{\approx}0.10$) oxide from aniline + hydrochloric acid mixtures and chloroauric acid in the ratios 30 : 1; 60 : 1; 90 : 1 (S1-S3) by volume and 0.01 mol of copper acetate, $Cu(OCOCH_3)_2.H_2O$, in each case is performed by sol-gel growth. Powder x-ray diffraction (XRD) results show Au particles are dispersed in tetragonal nonstoichiometric dicopper (I) dicopper (II) oxides, $Cu_{2-x}{^I}Cu{_2}^{II}O_{3-{\delta}}$ ($x{\approx}0.20$; ${\delta}{\approx}0.10$). Average crystallite sizes of Au particles determined using Scherrer equation are found to be in the approximate ranges ${\sim}85-140{\AA}$, ${\sim}85-150{\AA}$ and ${\sim}80-150{\AA}$ in S1-S3, respectively which indicate the formation of Au nano-micro size particles in $Cu_{2-x}{^I}Cu{_2}^{II}O_{3-{\delta}}$ ($x{\approx}0.20$; ${\delta}{\approx}0.10$) oxides. Hysteresis behaviour at 300 K having low loop areas and magnetic susceptibility values ${\sim}5.835{\times}10^{-6}-9.889{\times}10^{-6}emu/gG$ in S1-S3 show weakly ferromagnetic nature of the samples. Broad and isotropic electron paramagnetic resonance (EPR) lineshapes of S1-S4 at 300, 77 and 8 K having $g_{iso}$-values ${\sim}2.053{\pm}0.008-2.304{\pm}0.008$ show rapid spin-lattice relaxation process in magnetic $Cu^{2+}$ ($3d^9$) sites as well as delocalized electrons in Au ($6s^1$) nano-micro size particles in the $Cu_{2-x}{^I}Cu{_2}^{II}O_{3-{\delta}}$ ($x{\approx}0.20$; ${\delta}{\approx}0.10$) oxides. Broad and weak UV-Vis diffuse reflectance optical absorption band ~725 nm is assigned to $^2B_{1g}{\rightarrow}^2A_{1g}$ transitions, and the weak band ~470 nm is due to $^2B_{1g}{\rightarrow}^2E_g$ transitions from the ground state $^2B_{1g}$(${\mid}d_{x^2-y^2}$>) of $Cu^{2+}$ ($3d^9$) ions in octahedral coordination having tetragonal distortion.

• Journal of Powder Materials
• /
• v.30 no.5
• /
• pp.402-408
• /
• 2023

This study focused on improving the phase stability and mechanical properties of yttria-stabilized zirconia (YSZ), commonly utilized in gas turbine engine thermal barrier coatings, by incorporating Gd₂O₃, Er₂O₃, and TiO₂. The addition of 3-valent rare earth elements to YSZ can reduce thermal conductivity and enhance phase stability while adding the 4-valent element TiO₂ can improve phase stability and mechanical properties. Sintered specimens were prepared with hot-press equipment. Phase analysis was conducted with X-ray diffraction (XRD), and mechanical properties were assessed with Vickers hardness equipment. The research results revealed that, except for Z10YGE10T, most compositions predominantly exhibited the t-phase. Increasing the content of 3-valent rare earth oxides resulted in a decrease in the monoclinic phase and an increase in the tetragonal phase. In addition, the t(400) angle decreased while the t(004) angle increased. The addition of 10 mol% of 3-valent rare-earth oxides discarded the t-phase and led to the complete development of the c-phase. Adding 10 mol% TiO₂ increased hardness than YSZ.