• 한국세라믹학회지
• /
• 제32권10호
• /
• pp.1147-1161
• /
• 1995

When ceramic membrance was made from metal salt solution in place of metal akoxide solution, crack free and good adhesion to supporter was optimized for sol stability and good adhesion force. A starting sol was prepared from aluminum oxychloride aqueous solutjion in order to inhibit the grain growthof Al2O3 during heat treatment. The crack free dip coating can't be achieved in 1mol/ι zirconium oxychloride solution because of the high viscosity which interferes with the hydration copolymerization between Al3+ ion and Zr4+ ion. Thus Al2O3-ZrO2 sol stability and viscosity for dip coating was effective when 0.01 mol/ι zirconium oxychloride was added. The minimizing of crack and achieving better adhesion to the supporter wa obtained by microwave drying, surfactant addition and ultrasonic dip coating in wet atmosphere. The result seems to minimize the capillary force and improve the adhesive ability to supporter during the process. Where the average pore size of Al2O3-ZrO2 ultrafilter ceramic membrane measured 17 Å by the BET method and observed γ-Al2O3 phase with tetragonal zirconia after firing at 700℃.

• 한국세라믹학회지
• /
• 제38권10호
• /
• pp.936-941
• /
• 2001

5.31 mol% ${Y_2}{O_3}$-4.45 mo1% ${Nb_2}{O_5}$-90.31 mo1% $ZrO_2$에 ${Al_2}{O_3}$를 첨가한 복합체를 제조하여 알루미나 입도가 복합체의 균열 전파 저항성에 미치는 영향을 조사하였다. $ZrO_2/{Al_2}{O_3}$ 복합체에서는 R-cuve 거동이 관찰되었으며 0.2, $2.8{\mu}m$ ${Al_2}{O_3}$가 20 vol%가 첨가된 복합체의 인성값은 각각 7.9, $8.8MPam^{1/2}$이었다. 파괴인성값의 차이는 ${Al_2}{O_3}$ 입도 크기에 의존하는 $ZrO_2/{Al_2}{O_3}$ 복합체 내의 정방정 $ZrO_2$의 결정립 크기 차이에 의한 것으로 추정된다.

• 한국세라믹학회지
• /
• 제25권3호
• /
• pp.225-230
• /
• 1988

$Y_2O_3$가 $thickapprox$1mol.% 고용된 정방정 지르코니아를 알루미나에 20vol.% 섞어 체조립에 의해 과립으로 만든 다음 여기에 알루미나에 단사정 지르코니아를 10 ~30 vol.%섞어 만든 과립을 15~30vol.%가 되도록 과립형태로 분산시켜 성형 및 소결함으로써 단사정 및 정방정 지르코니아의 분산영역이 서로 다른 불균질 조직의 $Al_2O_3-ZrO_2$복합체를 제조하여 강도 및 열충격 거동을 관찰하였다. 이러한 불균질 조직의 $Al_2O_3-ZrO_2$ 복합체는 분산 agglomerate 내의 낮은 소결밀도에 의한 기공의 존재, 단사정상에 의한 미세균열, 또 이에 따른 주위에의 압축응력 등이 복합적으로 작용하여 향상된 열충격 거동을 보여 주었다.

• 한국세라믹학회지
• /
• 제33권4호
• /
• pp.432-440
• /
• 1996

본 연구는 졸-겔법을 이용하여 알칼리 조건인 pH 10에서 제조한 ZrO2의 하소온도에 따른 분말특성과 코발트 흡착량에 미치는 하소온도의 영향에 대하여 검토하였다. 졸-겔법을 이용하여 ZrO2 분말을 제조하고, 600, 800, 1000, 1200, 140$0^{\circ}C$로 하소한 후, X-선 회절법, SEM, BET 방법, Fourier transform 적외선(FT-IR), 열중량 및 열시차분석법(TG-DTA)등을 이용하여 특성을 분석하였다. 알칼리조건인 pH 10에서 제조한 ZrO2는 하소온도가 $600^{\circ}C$일때 고온수에서 코발트 흡착량이 가장 우수하였으며, 이때 $600^{\circ}C$로 하소한 ZrO2의 비표면적은 24.03m2/g이였으며 25$0^{\circ}C$의 고온수에서 코발트 흡착량은 0.16m-eq/g이였다.

• Bulletin of the Korean Chemical Society
• /
• 제27권6호
• /
• pp.821-829
• /
• 2006

A series of catalysts, $NiO/La_2O_3-ZrO_2/WO_3$, for acid catalysis was prepared by the precipitation and impregnation methods. For the $NiO/La_2O_3-ZrO_2/WO_3$ samples, no diffraction lines of nickel oxide were observed, indicating good dispersion of nickel oxide on the catalyst surface. The catalyst was amorphous to X-ray diffraction up to 300 ${^{\circ}C}$ of calcination temperature, but the tetragonal phase of $ZrO_2$ and monoclinic phase of $WO_3$ by the calcination temperatures from 400 ${^{\circ}C}$ to 700 ${^{\circ}C}$ were observed. The role of $La_2O_3$ in the catalyst was to form a thermally stable solid solution with zirconia and consequently to give high surface area and acidity. The high acid strength and high acidity were responsible for the W=O bond nature of complex formed by the modification of $ZrO_2$ with $WO_3$. For 2-propanol dehydration the catalyst calcined at 400 ${^{\circ}C}$ exhibited the highest catalytic activity, while for cumene dealkylation the catalyst calcined at 600 ${^{\circ}C}$ showed the highest catalytic activity. 25-$NiO/5-La_2O_3-ZrO_2/15-WO_3$ exhibited maximum catalytic activities for two reactions due to the effects of $WO_3$ modifying and $La_2O_3$ doping.

• 한국세라믹학회지
• /
• 제45권2호
• /
• pp.126-131
• /
• 2008

In this study, we prepared zirconia gel by the sol-gel method and investigated its photoluminescence properties by varying pyrolysis temperature. The addition of acetic acid into a Zr-alkoxide solution resulted in forming the bidentate ligands with Zr ions and producing a stable gel. At the pyrolysis temperature of $350^{\circ}C$, the zirconia nanocrystals with tetragonal structure gradually appeared in the gel. The PL intensity of the zirconia gel increased with increasing the pyrolysis temperature up to $350^{\circ}C$, but decreased above the temperature. Concurrently, its PL peak wavelength continuously shifted from ${\sim}440\;nm$ to ${\sim}550\;nm$ with the temperature. The PL characteristics of the zirconia gels were closely associated with decomposition of residual organic groups, the formation of the zirconia nanocrystals, and the tetragonal to monoclinic phase transformation.

• 디지털산업정보학회논문지
• /
• 제12권3호
• /
• pp.25-31
• /
• 2016

Mechanical properties of Y2O3-containing tetragonal ZrO2 polycrystals(Y-TZP) were investigated. Several additives were used to modify the hardness and fracture toughness of Y-TZP. The effects of these individual additives were discussed and their interactions were also analysed. Each additive, such as CoO, Fe2O3, MnO2 was found to deteriorate the mechanical properties of Y-TZP when it was used singly. But the fracture toughness of Y-TZP was significantly improved when these additives and Al2O3 were added in combination at a certain ratio. The addition of CoO, Fe2O3 and MnO2 into Y-TZP resulted in the more complex behavior of fracture toughness and hardness. The specimen with 1.5 wt%-Fe2O3, 3.0 wt% -Al2O3 and 1.5 wt%-CoO showed the monoclinic to tetragonal phase ratio of 18% and the highest toughness of $10.8MPa{\cdot}m1/2$ with Vickers hardness of 1201 kgf/mm2. However, the toughness decreased as the ratio increased and macrocracks developed beyond the ratio of 25%. Sample No. 16 is improved high Physical and Mechanical Properties.

• 한국세라믹학회지
• /
• 제27권2호
• /
• pp.201-210
• /
• 1990

The mullite-15v/o ZrO2 composites were prepared by dispersing ZrO2-3m/o Y2O3 powders into the mullite matrix in order to improve the mechanical properties of the mullite. The densification and retention of t-ZrO2 in the matrix of synthetic mullite were also investigated. From IR spectroscopic analysis, the obtained amorphous SiO2-Al2O3 powder was observed to have Si-O-Al chemical bond in its structure which might result in the homogeneous mullite composition. The lattice parameter of the mullite powder calcined above 130$0^{\circ}C$ (a0=7.5468$\AA$) is nearly close to the value of stoichiometric mullite (71.8wt% Al2O3, a0=7.5456$\AA$). The sintering behavior, microstructure, flexural strength and fracture toughness of the mullite and mullite-15v/o ZrO2 composites have been studied. The mullite-15v/o ZrO2(+3m/o Y2O3) ceramics with relative densities of 96% were obtained when sintered at 1$600^{\circ}C$. The flexural strength and fractrue toughness of the composites sintered at 1$600^{\circ}C$(calcination temperature of mullite powders ; 125$0^{\circ}C$) had maximum values of 307MPa and 2.50MPa.m1/2, respectively. The fracture toughness improvement in the mullite-ZrO2 cmoposite is assumed to be resulted from the combined effect of the stress-induced phase transformation of tetragonal ZrO2 and the crack deflection due to microcracking by the monoclinic ZrO2 formation.

• 한국세라믹학회지
• /
• 제30권1호
• /
• pp.1-6
• /
• 1993

Dielectric and piezoelectric porperties of pseudoternary xPb(Al2/3W1/3)O3-(1-x)Pb(Zr0.52Ti0.48)O3 (x=1~10mol%) ceramic system have been investigated as a function of the amount of PAW[Pb(Al2/3W1/3)O3] and sintered from 110$0^{\circ}C$ to 120$0^{\circ}C$ for 1hr. As the amount of PAW increases, the c/a of tetragonal structure decreases. The grain size was reduced with increasing the amount of PAW addition. However, the density, dielectric constant and electromechanical coupling factor(kp) exhibited a maximum value at the amount of 5mol% PAW addition.

• 한국세라믹학회지
• /
• 제26권5호
• /
• pp.719-727
• /
• 1989

By using commercial zirconia powder CeO2-ZrO2 ceramics containing 8~16mol% CeO2 was made by heat treatment at 1350~155$0^{\circ}C$ for 1~10hr. The minimum amount of CeO2 for obtaining complete tetragonal phase was 12mol%, and in the tetragonal phase region fracture toughness of Ce-TZP was decreased with increasing CeO2 content and the maximum value was obtained when 12mol% CeO2 was added. The bending strength goes through maximum at 14mol% CeO2. Fracture mode of Ce-TZP transformed from intergranular to transgranular fracture with increasing CeO2 content, so the morphology of fracture surface of 16mol% Ce-TZP was wholly transgranular and this tendency was independent on grain size. The crystal structure of the 12mol% Ce-TZP was monoclinic with fringes along the grain boundaries which are lying in the particular plane from the TEM observation. The chemical composition of the sintered body was homogeneous as a whole and some amorphism or air pocket was observed at the triple junction.