• Carbon letters
• /
• 제15권4호
• /
• pp.255-261
• /
• 2014

Multi-walled carbon nanotube reinforced epoxy composites were fabricated using shear mixing and sonication. The mechanical, viscoelastic, thermal, and electrical properties of the fabricated specimens were measured and evaluated. From the images and the results of the measurements of tensile strengths, the specimens having 0.6 wt% nanotube content showed better dispersion and higher strength than those of the other specimens. The Young's moduli of the specimens increased as the nanotube filler content was increased in the matrix. As the concentrations of nanotubes filler were increased in the composite specimens, their storage and loss moduli also tended to increase. The specimen having a nanotube filler content of 0.6 wt% showed higher thermal conductivity than that of the other specimens. On the other hand, in the measurement of thermal expansion, specimens having 0.4 and 0.6 wt% filler contents showed a lower value than that of the other specimens. The electrical conductivities also increased with increasing content of nanotube filler. Based on the measured and evaluated properties of the composites, it is believed that the simple and efficient fabrication process used in this study was sufficient to obtain improved properties in the specimens.

• 항공우주시스템공학회지
• /
• 제16권1호
• /
• pp.12-16
• /
• 2022

유도 용접은 비접촉식으로 깨끗하고 빠른 공정으로 현재 주목받고 있다. 하지만 열가소성 수지는 전자기장에 영향을 받지 않기 때문에 유도 용접은 서셉터(Susceptor)라는 발열체가 필요하다. 고품질 접합을 목표로 연구가 진행되고 있지만, 결국 발열체라는 이물질이 들어가기 때문에 기준이 필요하다. 시편의 제작과 시험은 ASTM D5868에 근거하여 진행된다. 본 논문에서 평가 기준은 용접된 접합면의 상태와 기공률, 전단강도로 총 3가지를 근거로 판단할 것을 제안한다. 용접되는 접착면은 용융되고 냉각되면서 고형화가 되기 때문에 급격한 온도 변화는 기공을 발생시킬 수 있다. 또한 가열이 균일하지 않다면 원하는 성능을 기대하기 힘들다. PA6 (CF 30%) 엔지니어링 플라스틱을 이용하여 서셉터 제작과 유도 용접 그리고 성능 검증으로 진행하였다.

• 한국지반공학회논문집
• /
• 제32권8호
• /
• pp.27-33
• /
• 2016

본 연구에서는 미생물 고결토의 압축강도 및 인장강도 개선을 위하여 PVA(Polyvinyl alcohol) 섬유를 혼합하는 연구를 수행하였다. 미생물 고결토의 인장강도 특성을 개선하기 위해 모래에 섬유를 혼합한 다음 미생물 배양액을 7일 동안 1일 2회 총14회 반복주입하여 고결을 유도하였다. 모래는 Ottawa모래를 사용하였으며, 섬유는 PVA섬유를 세 종류의 함유량(0, 0.4, 0.8%)으로 혼합하였다. 미생물은 Bacillus sp. 미생물을 사용하였으며, 공시체의 크기는 직경 5cm, 높이 10cm로 제작하였다. 고결이 완료된 다음 일축압축강도, 인장강도시험을 실시하였으며, 시험 후에는 탄산칼슘 석출량과 SEM 분석을 실시하였다. 섬유의 함유량이 증가함에 따라 평균 일축압축강도는 증가하다가 약간 감소하는 경향을 보이지만, 인장강도는 점진적으로 증가하는 경향을 보였다. 탄산칼슘 석출량이 유사하다고 볼 경우, 압축강도는 약 30%의 강도 증가를 발생하였지만, 인장강도는 약 160%의 강도 증가를 보였다. 공시체의 취성도를 나타내는 압축강도와 인장강도의 비는 섬유 함유량이 0%인 경우 약 8 정도에서 섬유 함유량이 0.8%로 증가할 경우 4까지 감소하였으며, 동일한 조건에서 섬유의 함유량이 증가할수록 인장강도의 증가 폭은 커짐을 확인하였다. 이러한 섬유를 혼합한 미생물 고결토는 전단파괴 방지 및 인장강도 증진을 요하는 사면 등의 분야에 적용 가능 할 것으로 판단된다.

• 대한토목학회논문집
• /
• 제28권3A호
• /
• pp.331-340
• /
• 2008

본 연구는 상부 플랜지가 없는 I형 강재 거더, 즉 역T형의 강재 거더의 일부를 콘크리트에 매립한 역T형강-콘크리트 합성바닥판의 구조거동을 실험적 연구를 통해 분석하여 이를 토대로 새로운 개념의 교량 바닥판 상세를 제안하고자 실시하였다. 이를 위해 기존의 철근콘크리트 바닥판과 강합성 바닥판 시험체를 제작하여 정적 휨파괴 시험을 실시하였다. 이로부터 극한 및 최대하중을 평가하였으며, 전단홀 관통 철근의 적용 유무에 따른 구조거동의 변화를 분석하였다. 실험 결과 전단홀 관통 철근을 적용할 경우에는 충분한 전단강도가 확보되어 전형적인 인장파괴 형태를 나타내고, 극한 및 최대하중 모두 철근콘크리트 바닥판보다 높아지는 것을 알 수 있었다. 또한 철근콘크리트 바닥판보다 강합성 바닥판의 처짐이 크게 발생하는 것으로 나타났다.

• 대한기계학회논문집A
• /
• 제39권7호
• /
• pp.693-700
• /
• 2015

혼합모드 피로하중을 받는 균열을 갖은 CTS 시편에 대하여 균열경로 예측이론과 Tanaka 의 등가 응력확대계수식을 적용하여 피로균열진전거동을 평가하였다. 새롭게 생성되는 균열선단의 응력확대계수 산정은 ANSYS 를 이용한 유한요소법을 통해 이루어졌고, 균열경로와 균열증분은 마이크로소프트 엑셀에 프로그래밍한 균열경로예측식과 Paris 식으로 계산되었다. 균열증분으로 새롭게 생성된 균열선단의 기하학적인 정보는 엑셀의 기능을 이용해 ANSYS 의 KSCON 명령어가 인식할 수 있게 변화시켜 균열모델링을 용이하게 하였다. 반복적인 균열해석을 위해 유한요소법과 엑셀을 결합한 FECTUM(Finite Element Crack Tip Updating Method)을 개발하였다. 개발된 FECTUM 을 편측 3 점 굽힘을 통해 혼합모드의 구현이 가능한 SENB 시편(Single Edge Notched Bend Specimen)에 적용해본 결과, 균열경로는 물론 파단될 때까지의 피로하중 반복수의 차이가 3% 미만으로 잘 일치하는 모습을 보여, 개발된 기법의 타당성을 검증하였다.

• Journal of the Korean Wood Science and Technology
• /
• 제41권1호
• /
• pp.51-57
• /
• 2013

직물형 유리섬유 조합에 따른 보강 집성재의 볼트 접합부 전단 성능을 알아보기 위하여 인장형 전단시험을 실시하였다. 보강재는 직물형 유리섬유로서 유리섬유 배열 형태는 평직형과 능직형을 사용하였다. 보강 집성재는 5층으로 직물형 유리섬유의 삽입 위치와 조합 형태를 달리하여 층재 사이에 삽입 적층시켜 제작하였다. 인장형 전단 시험편은 강판 삽입형로서 끝면거리 7D에 직경 12, 16 mm의 볼트로 접합하였다. 체적비 1% 직물형 유리섬유 보강 집성재의 경우 12 mm 볼트 접합부의 항복 전단내력은 집성재 외층부보다 내층부를 보강한 시험편에서 10% 큰 값을 나타내었다. 체적비 2% 직물형 유리섬유 보강 집성재의 항복 전단내력은 12 mm 볼트 접합부의 경우 각층재 사이에 삽입 적층시킨 시험편이 보강하지 않은 접합부보다 약 22% 향상되었으며, 16 mm 볼트 접합부의 항복 전단내력은 약 20% 향상되었다.

• Structural Engineering and Mechanics
• /
• 제86권5호
• /
• pp.607-619
• /
• 2023

This study, it was tried to evaluate the asphalt behavior under tensile loading conditions through indirect Brazilian and direct tensile tests, experimentally and numerically. This paper is important from two points of view. The first one, a new test method was developed for the determination of the direct tensile strength of asphalt and its difference was obtained from the indirect test method. The second one, the effects of particle size and loading rate have been cleared on the tensile fracture mechanism. The experimental direct tensile strength of the asphalt specimens was measured in the laboratory using the compression-to-tensile load converting (CTLC) device. Some special types of asphalt specimens were prepared in the form of slabs with a central hole. The CTLC device is then equipped with this specimen and placed in the universal testing machine. Then, the direct tensile strength of asphalt specimens with different sizes of ingredients can be measured at different loading rates in the laboratory. The particle flow code (PFC) was used to numerically simulate the direct tensile strength test of asphalt samples. This numerical modeling technique is based on the versatile discrete element method (DEM). Three different particle diameters were chosen and were tested under three different loading rates. The results show that when the loading rate was 0.016 mm/sec, two tensile cracks were initiated from the left and right of the hole and propagated perpendicular to the loading axis till coalescence to the model boundary. When the loading rate was 0.032 mm/sec, two tensile cracks were initiated from the left and right of the hole and propagated perpendicular to the loading axis. The branching occurs in these cracks. This shows that the crack propagation is under quasi-static conditions. When the loading rate was 0.064 mm/sec, mixed tensile and shear cracks were initiated below the loading walls and branching occurred in these cracks. This shows that the crack propagation is under dynamic conditions. The loading rate increases and the tensile strength increases. Because all defects mobilized under a low loading rate and this led to decreasing the tensile strength. The experimental results for the direct tensile strengths of asphalt specimens of different ingredients were in good accordance with their corresponding results approximated by DEM software.

• 한국구조물진단유지관리공학회 논문집
• /
• 제8권2호
• /
• pp.205-211
• /
• 2004

본 연구의 목적은 CFM으로 전단 보강된 보의 실험으로 CFM의 전단 보강 효과를 평가하는 것으로서, 실험 변수는 메쉬의 배치 방향, 정착 클립의 개수, 전단 스팬비이다. 실험에서, 전체적으로 모르터와 RC보에서의 부착 파괴는 가력 초기부터 발생하여 최대 내력의 약 60% 정도에서 완전히 파괴되었으며, 전단 내력에 대한 CFM의 기여도는 CFM 최대 인장 강도의 약 19.6%인 것으로 나타났다. 또한 전단 스팬비가 1.0인 경우 대각선 방향으로 메쉬를 배치할 때 전단 보강 효과가 높은 것으로 나타났으나, 1.5인 시험체의 경우, 정착 클립의 개수가 많을 경우 보강 효과가 높은 것으로 나타났다.

• 대한토목학회논문집
• /
• 제33권2호
• /
• pp.643-653
• /
• 2013

기존의 연약지반 개량공법의 대체공법으로 유럽과 국내에서는 소정의 인장강도를 갖는 토목섬유로 골재말뚝의 외벽을 감싸는 공법에 대한 연구가 많이 증가하였다. 이 연구에서는 이와 같은 공법에서 골재말뚝의 외벽을 감싸는 원주형 섬유의 인장강도에 따른 지반보강 효과 및 보강 메커니즘 등을 파악하기 위하여 모래-팩, 점토-팩 복합토에 대한 삼축압축시험을 실시하였다. 또한 모래다짐말뚝공법을 모사하는 모래-점토 복합토와 모래다짐말뚝을 원주형 섬유로 보강한 모래-점토-팩 복합토에 대한 삼축압축시험을 실시하여 치환율(${\alpha}_s$)과 인장강도($T_{\alpha}$)에 따른 보강효과와 거동의 차이를 비교하였다. 시험결과 섬유의 보강효과로 인한 강도증가는 섬유의 수평방향 인장강도와 밀접한 관계가 있고, 섬유에 의한 구속응력 증가효과(${\Delta}{\sigma}_3$)에 의해서 점착절편(c, c')의 증가효과가 매우 크게 발생하는 것으로 나타났다. 또한, 모래다짐말뚝이 토목섬유로 보강된 경우(모래-팩-점토)와 그렇지 않은 경우(모래-점토)를 비교해 볼 때 삼축압축시 전단거동(전단강도, 파괴시 간극수압계수, 응력비 등)에 있어서 큰 차이를 보이는 것으로 나타났다.

• 콘크리트학회논문집
• /
• 제14권5호
• /
• pp.638-644
• /
• 2002

본 연구에서는 압축강도 1400 kgf/$\textrm{cm}^2$ 를 갖는 불포화 폴리에스터 폴리머 콘크리트를 이용하여 제작한 C형 시험체에 대한 편심압축 시험을 통하여 폴리머 콘크리트 휨부재의 응력-변형률 관계를 구명하고 등가직사각형 응력블럭의 파라미터 $\alpha$, $\beta$1, ${\gamma}$를 산출하였다. 아울러 인장철근비를 달리하는 5종의 전단스팬비 4.0인 철근 보강 폴리머 콘크리트 보에 대한 휨시험에서 얻어진 극한모멘트 시험값과 C형 시험체 응력-변형률 곡선에서 산출되는 파라미터 $\alpha$=0.61, $\beta$1=0.73 를 이용하여 계산된 이론적인 극한모멘트 값을 비교하여 보았던 바, 인장철근비가 0.50 $\rho$b 이상일때 시험값과 이론값이 비교적 잘 부합됨을 확인 할 수 있었다. 그러나 폴리머 콘크리트 휨 부재에 대한 보다 정확한 설계기준의 마련을 위해서는 압축강도와 크기를 변수로 하는 C형 시험체에 대한 보다 많은 시험을 통한 파라미터의 체계적인 연구가 필요하다.