The present research work is on the effect of sawdust ash (SDA) on the mechanical strengths of self compacting concrete (SCC) using naphthalene sulfonate (NS) as a plasticizer. Experiments on compressive, flexural and splitting tensile strengths are conducted and the data analyzed using the Minitab 15 software. The results showed that SDA can defer the reaction of cement hydration and prolong the setting times of cement paste. This was very much pronounced on the flexural and splitting tensile strengths at 90 days of curing which are 36 % and 33 % higher than the control strengths, respectively. The study has proposed strength relations of mortar compressive strength with the flexural and splitting tensile strengths and these are, 5 and 7 times respectively. The flexural strength is 1.5 times that of the splitting tensile. Finally, linear models were developed on these relationships.

• Proceedings of the KSME Conference
• /
• 2001.06a
• /
• pp.231-236
• /
• 2001

A newly developed Advanced Indentation System (AIS), which is a portable and nondestructive system for evaluating tensile properties, was used to measure mechanical behavior of materials used under high temperature and pressure conditions. This test measures indentation load-depth curve during indentation and analyzes the mechanical properties related to deformation and fracture. Aging effects of Cr-Mo and Cr-Mo-V steel at high temperature were simulated. Tensile properties including yield strength and tensile strength at various temperature are obtained from the test. For all test materials and conditions, the AIS-derived results were in good agreement with those from conventional standard test method. Examples of the test results ate given and potential applications of the AIS to assess the integrity of aging structures are briefly discussed.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.05a
• /
• pp.374-377
• /
• 2009

Glass fiber reinforced nylon has been used in many plastic industries. Mechanical properties of reinforced plastics depend upon types of glass fiber as well as loading of glass fiber. Tensile properties of glass fiber reinforced nylon66 have been studied for different glass fiber types and sizes. Types of glass fibers were circular and flat, and diameters were 7, 10, and 13 micrometers. Orientations of glass fibers in the matrix of nylon66 have been analyzed through X-ray CT. Tensile specimens were prepared by cutting out of square plates of $100{\times}100{\times}3mm$ with different angles such as 0, 45, and $90^{\circ}$ to the flow direction. As the loading of glass fiber increases to 45 wt% tensile strength increases up 2.5 times compare with neat nylon66. Anisotropic tensile strength has been observed and minimum tensile strength was measured in the specimen cut from perpendicular to the flow direction.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.25 no.11
• /
• pp.886-894
• /
• 2012

In order to develop electrical insulation materials, epoxy-nanosilica-microsilica mixture composites (ENMC) was synthesized, and mechanical properties such as their tensile and flexural strength, and AC insulation breakdown strength were investigated. Properties of mechanical strength and AC insulation breakdown strength are analyzed as scale and shape parameter with respect to weibull plot. Their tensile and flexural strength, AC insulation breakdown strength were compared original epoxy or EMC to ENMC. The 4 phr nano-silica addition and the 65 wt% micron-silica mixture composite (ENMC) was found to have the highest tensile and flexural strength. In the tensile strength was improved 29%, and flexural strength was improved 60.9% higher than those of the original epoxy. In the insulation breakdown strength, ENMC_4 phr was improved 17% and ENMC_5 phr was improved 15.8% higher than those of the EMC.

• Journal of Welding and Joining
• /
• v.26 no.5
• /
• pp.60-65
• /
• 2008

Ferritic stainless steels of the 400 series have been available for automotive exhaust system, heat exchanger, radiater etc. in various industrial because heat resistance, corrosion resistance and strength are excellent. Especially, automotive exhaust system is required good heat resistance because typical temperature of exhaust system exposed during operation of engine is reach up to $800^{\circ}C$. However, research for effect of high temperature in ferritic stainless steels is not enough. In this study, high temperature tensile properties of lap weld of ferritic stainless steels(STS 429) were investigated. In accordance with heat input, lap welds had been produced and were evaluated at high temperature($800^{\circ}C$) to compare high temperature tensile properties. In addition, room temperature tensile tests were carried out for non-aging and aging specimens. As a result of R.T tensile test, non-aging specimens were fractured in base metal except for low heat input specimen and aging specimens were fractured in weld metal. Also high temperature tensile test were carried out by aging specimen. After high temperature tensile test, fracture of aged specimen was occurred in base metal except for low heat input specimen. Fracture surface of low heat input specimen in weld metal was confirmed as brittle fracture with observation using scanning electron microscope(SEM). Significant decrease in ultimate tensile strength (between 82 and 85%) was observed for aged ferritic stainless steels(STS 429) when tested at high temperature.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2004.10a
• /
• pp.508-511
• /
• 2004

This study focused on the effect of autonomic microcapsules on the mechanical properties of structural material. Several types of microcapsules with healing agents were manufactured by varying agitation speed of high speed stirrer. The size distribution of microcapsules was measured by a particle size analzer. The epoxy specimens embedded with microcapsules were manufactured and the degree of cure of such epoxy specimen was measured by a differential scanning calorimetry. The tensile modulus and tensile strength in epoxy specimens embedded with microcapsules were evaluated in order to investigate the effects of microcapsules on mechanical properties of structural materials. The configuration of microcapsules and morphology of fracture surfaces for the epoxy specimen were examined by an optical microcope and a scanning electron microscope. According to the results, tensile strength of the epoxy specimen embedded with microcapsules was indicated a little reduction, but tensile modulus was not much affected on microcapsules.

• Transactions of Materials Processing
• /
• v.16 no.1 s.91
• /
• pp.36-41
• /
• 2007

Thermoplastic elastomer(TPE) can be recycled and molded such as commercial thermoplastic. Therefore TPE has being widely applied on automobile, household and etc. in these days. This study shows the variation of mechanical properties and shrinkage on TPE moldings for variation of injection molding conditions such as injection pressure, holding pressure, melt temperature, mold temperature and etc. Mechanical properties in relation to tensile strength, hardness and shrinkage in connection with precision dimension of part are investigated. The tensile strength and shrinkage of the experimental TPEs are mainly influenced by injection pressure and melt temperature. All injection molding conditions scarcely affect on hardness. To verify the variation of tensile strength and shrinkage, morphology of TPE molding was scanned by the SEM. The morphology showed that as the melt temperature increased, the rubber particles on the TPE became smaller and widely were dispersed. This behavior of rubber particles influenced on the increase of tensile strength.

• Journal of Powder Materials
• /
• v.9 no.4
• /
• pp.211-217
• /
• 2002

It is well known that the powder injection molding(PIM) process can overcome the shape limitations of traditional powder compaction, the costs of machining, the productivity limits of isostatic pressing and slip casting, and the defect and tolerance limitations of conventional casting. Increasing demands from industry for not only the dimensional accuracy nut mechanical strength in PIMed parts have had much effort focused on the investigation of mechanical properties of mechanical strength in PIMed parts have had much effort focused on the investigation of mechanical properties of sintered parts formed with high-strength metallic powders. The 17_4 PH $10\mu{m}$ were injection-molded into flat tensile specimens. Sintering of the compacts was carried out at the various temperatures ranging from 900 to $1350^{\circ}C$. Sintering behavior of the compacts and tensile properties of sintered specimens were investigated.

• Proceedings of the KSME Conference
• /
• 2004.04a
• /
• pp.258-263
• /
• 2004

Mechanical property evaluation of micrometer-sized structures is necessary to help design reliable microelectromechanical systems(MEMS) devices. Most material properties are known to exhibit dependence on specimen size and such properties of microscale structures are not well characterized. This paper describes techniques developed for tensile testing of materials used in MEMS. Epi-polycrystalline silicon is currently the most widely used material, and its tensile strength has been measured as 1.52GPa. We have developed an uniaxial testing machine for testing microscale specimen using electro-magnetic actuator. The field magnet and the moving coil taken from an audio-speaker were utilized as the components of the actuator. Structure of specimen was designed and manufactured for easy handling and alignment. In addition to the static tensile tests, new techniques and procedures for measuring strength are described.

• Proceedings of the Korean Powder Metallurgy Institute Conference
• /
• 2006.09a
• /
• pp.114-115
• /
• 2006

[ $FerroTitanit^{(R)}$ ] is an extremely high alloyed PM material containing about 20 to 35 wt.% titanium based carbides. Such materials are designed to achieve a high wear resistance, but the high volume fraction of hard phases causes a comparable low ductility in case of tensile loading. In the present study the mechanical properties of different Ferro-Titanit grades (variations in chemical composition and in heat treatment) were investigated by means of tensile tests. The mechanical properties and the fracture behaviour will be related to the chemical composition, the heat treatment and the microstructure.