• Journal of Welding and Joining
• /
• v.24 no.3
• /
• pp.22-26
• /
• 2006

It is necessary to investigate the welding performance and fracture resistance of welding part in structure. This study presented a most suitable condition of welding process for butt and lap joints by $CO_2$ arc welding which is widely used in the vehicle structure. Also it was conducted to tensile and fatigue test under various welding conditions. For butt and lap joints, the best conditions of welding voltage and current were 30V and 320A, respectively, in 3.2 and 4.5 mm thick steel plate. Under this condition it could be taken the highest tensile strength and fatigue strength, and a good bead appearance.

• Korean Journal of Materials Research
• /
• v.31 no.3
• /
• pp.172-180
• /
• 2021

In this study, using the plasma spray method, tensile and compression fatigue tests are performed in saline solution to examine the effect of Ti undercoat on corrosion fatigue behavior of alumina-coated specimens. The alumina-coated material using Ti in the undercoat shows better corrosion fatigue strength than the base material in the entire stress amplitude range. Fatigue cracking of UT specimens occurs in the recess formed by grit-blasting treatment and progresses toward the base metal. Subsequently, the undercoat is destroyed at a stage where the deformation of the undercoat cannot follow the crack opening displacement. The residual stress of the UT specimen has a tensile residual stress up to about 100 ㎛ below the surface of the base material; however, when the depth exceeds 100 ㎛, the residual stress becomes a compressive residual stress. In addition, the inside of the spray coating film is compressive residual stress, which contributes to improving the fatigue strength characteristics. A hardened layer due to grit-blasting treatment is formed near the surface of the UT specimen, contributing to the improvement of the fatigue strength characteristics. Since the natural potential of Ti spray coating film is slightly higher than that of the base material, it exhibits excellent corrosion resistance; however, when physiological saline intrudes, a galvanic battery is formed and the base material corrodes preferentially.

• Journal of Korea Foundry Society
• /
• v.1 no.2
• /
• pp.10-18
• /
• 1981

In this paper tensile strength and fatigue propagation rate were investigated by aging treatment $(T_6)$ and thermomechanical treatment (TMT) of 7075-Al Alloy specimen. The results of teat showed that TMT improved tensile strength and fatigue crack propagation due to bomogenization of microstructure. In TMT, the results of comparison between T-H' AHA and T-AHA and $T-AH{\cdot}{\cdot}{\cdot}$and $T-HA{\cdot}{\cdot}{\cdot}$were showed that T-AHA and $T-AH{\cdot}{\cdot}{\cdot}$treatments, after solution treatment, which are aging treated before rolling have higher tensile strength. Our investigation on high temperature stability at the Specimen for $T_6$, T-AHA, $T-AH{\cdot}{\cdot}{\cdot}$treatments resulted in rapid reduction of tensile strength over $150^{\circ}C$, but the reduction of tensile strength for specimen of TMT was smoothed than $T_6$.

• Advanced Composite Materials
• /
• v.18 no.1
• /
• pp.43-59
• /
• 2009

The current study assessed the effect of a bolt hole on tensile fatigue properties of CFRP laminates. Two specimens, i.e. $[(0/90)_3]S$, $[(0/45/90/-45)_2]_S$, were analyzed using a finite element method and were experimentally tested for cases, both with and without a hole, whose diameter corresponded to 0.12 times the specimen width. Delamination positions predicted by a 3-dimensional static finite element analysis were matched well to those observed by an ultrasonic imaging system in the middle of fatigue test. A hole whose diameter corresponds to 0.12 times the specimen width caused the fatigue strength to decrease by 9% and 11% under 5 Hz loading frequency, and by 22% and 25% under 10 Hz loading frequency for $[(0/90)_3]_S$ and $[(0/45/90/-45)_2]_S$, respectively. Because the decrease in sectional area due to the hole was normalized in calculation of the tensile strength, a stress concentration around the hole is believed to induce the strength degradation of fatigue specimens. From the finite element analyses, the stress concentration factor around a hole was expected as 8.8 and 9.5 for $[(0/90)_3]_S$ and $[(0/45/90/-45)_2]_S$, respectively.

• Journal of Welding and Joining
• /
• v.19 no.1
• /
• pp.112-117
• /
• 2001

The factor affecting on the fatigue strength of spot welded specimen have been studied. To analyze and predict crack initiation position and propagation directions on the spot welded area are very important for strength design of the automobile body structure. In fact, there are a various of loads in running automobile but, it is impossible to replay like an actual conditions in the laboratory. So, in this study tensile-shear type and in-plane bending type specimens were used in fatigue test and includes an analysis of fatigue crack initiation position and propagation directions about earth specimens. The results obtained in the present study are summarized as follows: 1. In tensile-shear type fatigue test, the region of fatigue crack initiation position was affected by out-of-plane bending deformation due to bending angle. 2 In in-plane bending type fatigue test, the behavior of fatigue crack initiation position and propagation derections due to angle between upper plate and lower plate was dominated by magnitude of in-plane bending moment.

• Transactions of Materials Processing
• /
• v.7 no.6
• /
• pp.530-538
• /
• 1998

Elimination of the heat treatment process is very important in automation of metal forming since controlling heat treatment by computer has many difficulties and it has bottle neck problem. non-heat-treated steels materials which are not in need of heat treatment have been developed for cold forging. However to apply non-heat-treated steel to structural parts. it is necessary to prove reliability of mechanical properties. In order to define the reliability of mechanical properties we have investigated microstructure, hardness, the tensile strength compressive strength and tensile fatigue strength for both steels. Considering the results of high cycle fatigue test for both specimen the characteristics of non-heat-treated steel are decided on the yield strength, It has same tendency for heat-treated steel. Therefore non-heat-treated steel which has the appropriate yield strength may be applied in cold forging.

• Journal of Welding and Joining
• /
• v.18 no.1
• /
• pp.52-58
• /
• 2000

Spot welding, namely a kind of electric resisting welding has been used widely in field of automobile and aircraft industries because of easiness to apply. Specimens used in this study was a mild steel of 1.2mm thickness and the electrode was a Cu-Cr alloy of 6mm diameter. The surface sheared of specimens after testing of tensile shear was observed by SEM(scanning electron microscope) after ultrasonic cleaning for 10min., and microstructures and grain size of all specimens were measured with using of O.M.(Optical microscope). By the means of measurement and observations of tensile shear load, fatigue strength and share surface, the weldability of spot welding was evaluated. When tensile shearing testing, fracture starting point in all specimens was took place at the bond between HAZ(Heat affected zone) and nugget. With increasing in number of layers, fatigue strength was decreased. With increasing in electric current, grain size in the HAZ became more fine.

• Journal of Welding and Joining
• /
• v.17 no.3
• /
• pp.50-54
• /
• 1999

Feasibility study of the application of a developed annealed austenitic stainless steel at cryogenic temperature has been performed for membrane tank of LNG ship. Chemical properties of developed stainless steel are compared with a domestic commercial stainless steel and a foreign stainless steel which are used for LNG ships. Tensile properties at cryogenic temperature and fatigue strength at room temperature are measured for but and lap joints which are TIG welded specimens. Developed stainless steel having a small amount of titanium component shows the finest grain size in the HAZ, compared with the other stainless steel studied. Tensile strength, elongation and fatigue strength of the developed stainless steel are equal to those of the foreign stainless steel studied and are higher than the domestic commercial stainless steel studied.

• Proceedings of the KSME Conference
• /
• 2000.11a
• /
• pp.129-134
• /
• 2000

Recently, HIPS(High Impact Polystyrene) materials are spot-lighted as office equipment, home electronics, electronics appliances housing, packing containers, etc. But its using are occur to problem caused by fatigue fracture. However, its strength is larged affected by environmental conditions. So, in this paper it tried to analyze the effect of temperature by tensile test and fatigue test. It was observed that yield strength and ultimate strength, fatigue life of same stress decreased relatively with increase temperature. Further, this paper predict S-N curve using the result of tensile test and micro vickers hardness test. For this purpose, the management in the engineering department is able to design the fatigue life of HIPS(HR-1360) materials.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2007.10a
• /
• pp.334-337
• /
• 2007

Austenitic stainless steel is used as high temperature components such as gas turbine blade and disk because of its good thermal resistance. In the present investigation, tensile and low cycle fatigue(LCF) behavior of stainless steel for turbine disks was studied at wide temperature range $20^{\circ}C\;{\sim}\;750^{\circ}C$. In the tensile tests, it was shown that elastic modulus, yield strength, ultimate tensile strength decreased when temperature increased. The effect on fatigue failure of the parameters such as plastic strain amplitude, stress amplitude and plastic strain energy density was also investigated. Coffin-Manson and Morrow models were used to adjust experimental data and predict the fatigue life behavior at different mean strain values during cyclic loading of high temperature components.