• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2009.10a
• /
• pp.132-136
• /
• 2009

The importance and interests for saving of energy and cost in industry has been steadily grown up. Therefore, process optimization to reduce the processing step and energy is one of the most important things. The micro-alloyed steel of which post-heat-treatment is not necessary, has attractive points for high strength materials. However, for the application of non-heat-treated steel to structural parts, it is necessary to confirm the reliability of mechanical properties. In order to estimate mechanical properties. The microstructure, hardness, tensile strength, compressive strength and tensile fatigue strength of micro-alloyed steel having 900MPa tensile strength has been investigated.

• Journal of Welding and Joining
• /
• v.29 no.1
• /
• pp.59-64
• /
• 2011

Al6082-T6 is widely used because of its corrosion resistance and excellent strength. HAZ softening occurs in MIG welding process for this aluminium alloys because this aluminium alloy is heated to higher temperature than its aging temperature during welding. Therefore, low heat input and minimum standard deviation of heat input are required for narrow HAZ width and, for higher strength of welds. In this study, Al6082-T6 was used to examine for HAZ softening with various heat input in aluminium MIG welding. For weldments, micro hardness was measured and tensile test was carried out. Minimum hardness was increased at high speed welding such as 80cm/min and 120cm/min in welding speed comparing with 40cm/min. Also, in case of high speed welding such as 80cm/min and 120cm/min, tensile strength of weldments was increased about 10% comparing with low speed welding(40cm/min).

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 1997.04a
• /
• pp.1073-1077
• /
• 1997

In this paper, we have studied internal quality including chemical compositions, microscopic structure and nonmetalic inclusion of test materials. We have analyzed machining characteristics including tensile strength value, impact value, hardness value etcs. Test materials are usd martensitic heat resisting steel, STR11 and STS420J2. The obtined results are as follows : 1. In analyzing internal quality, STR11 and STR420J2 have typical martensite structure and a minute needle-shaped structure. 2. Tensile strength and reduction of area and hardness value are large STR11 than STS420J2. But elongation impact are smaller STR11 than STS420J2. 3. Fracture surface of tensile speciman is ductile in STR11 and STS420J2.

• Proceedings of the Korean Society of Precision Engineering Conference
• /
• 2003.06a
• /
• pp.390-395
• /
• 2003

This study examined the effects of the testing temperature on the mechanical properties of the stainless steels (STS301CSP-3/4H and STS301CSP-H) for flat spring. Hardness test and fatigue test were performed at room temperature (2$0^{\circ}C$ Tensile testandcreeptestwere performed attemperature range 2$0^{\circ}C$~10$0^{\circ}C$. The micro-victors hardness values of STS301CSP-3/4H and STS301CSP-H were HV=443 and HV=488. respectively. The Elastic modulus, tensile strength, yield strength and strain of these materials were decreased with increasing testing temperature. respectively. The maximum creep strain for 100hr atcreep temperature (10$0^{\circ}C$~20$0^{\circ}C$ and creep stress (Tensile strength$\times$50%) of these materials were 0.53％~0.58%. The fatigue limit of STS301CSP-3/4H and STS301CSP-H were 64.5Kgf/mm$^2$ and 67.4Kgf/mm$^2$, respectively.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.9 no.1
• /
• pp.24-29
• /
• 2000

This paper is experimental study of machining characteristics about martensitic heat resisting steel STR11. Machining characteristics are different according to internal quality(chemical compositions, microscopic structure and nonmetallic inclusion) mechanical properties(tensile strength value impact value and hardness) and dynamic cutting force. Following are the results : 1. In analyzing internal quality test materials have typical martensite structure and a minute needle-shaped structure. 2. Tensile strength and reduction of area and hardness are larger. But values of elongation and impact values are smaller. Fracture surface of tensile specimen is ductile. 3, Cutting force is decreasing with cutting speed increasing 4. Cutting force is increasing with feed speed increasing.

• Nuclear Engineering and Technology
• /
• v.51 no.1
• /
• pp.190-197
• /
• 2019

W-K-TiC alloys with different titanium carbide concentrations (0.05, 0.1, 0.25, 0.5, 1, 2) wt.% were fabricated through Mechanical Alloying and Spark Plasma Sintering. The effects of the addition of nano-scaled TiC particles on the relative density, Vickers micro-hardness, microstructure, crystal information, thermal shock resistance, and tensile strength were investigated. It is revealed that the doped TiC nano-particles located at the grain boundaries. The relative density and Vickers micro-hardness of W-K-TiC alloys was enhanced with TiC addition and the highest Vickers micro-hardness is 731.55. As the TiC addition increased from 0.05 to 2 wt%, the room-temperature tensile strength raised from 141 to 353 MPa. The grain size of the W-K-TiC alloys decreased sharply from $2.56{\mu}m$ to 330 nm with the enhanced TiC doping. The resistance to thermal shock damage of W-K-TiC alloys was improved slightly with the increased TiC addition.

• Proceedings of the KWS Conference
• /
• 2007.11a
• /
• pp.322-324
• /
• 2007

Nd:YAG laser welding of AZ31B-H24 magnesium alloy was carried out using AZ61 filler wire(Mg-6wt%Al-1wt%Zn). Microstructure and mechanical properties of welded joint were examined by optical microscopy, scanning electronic microscopy(SEM), energy dispersive spectroscopy(EDS), electron probe micro analyzer(EPMA) and victors hardness, tensile test at the room and elevated temperature. Test results indicate that the specimens welded with AZ61 filler wire have better tensile strength, elongation and victors hardness at room temperature than those of welded without filler wire. However tensile strength are similar but elongation are quite different at elevated temperature.

• International Journal of Naval Architecture and Ocean Engineering
• /
• v.12 no.1
• /
• pp.146-156
• /
• 2020

Two High Tensile Strength Steel (EH47) plates with thickness of 70 mm were butt-welded together by multi-pass Submerged Arc Welding (SAW), also the hardness and welding residual stress were investigated experimentally. Based on Thermal-Elastic-Plastic Finite Element (TEP FE) computation, the thermal cycles during entire welding process were obtained, and the HAZ hardness of multi-pass butt welded joint was computed by the hardenability algorithm with considering microstructure evolution. Good agreement of HAZ hardness between the measurement and computational result is observed. The evolution of each phase was drawn to clarify the influence mechanism of thermal cycle on HAZ hardness. Welding residual stress was predicted with considering mechanical response, which was dominantly determined by last cap welds through analyzing its formation process.

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.7 no.2
• /
• pp.15-22
• /
• 1998

The effects of shot peening an the fatigue strength are studied in this paper. Applying the multistage shot peening on the material. the relation between the residual stress and fatigue strength compressive is investigated. Observing tensile strength elongation. reduction of area. hardness. and roughness. the results can be summarized as follows ; 1.The change of mechanical properties is small before and after the shot peening is carried out. The change of hardness is also small in high hardness material. 2.The surface roughness does not affect the fatigue strength. but the surface roughness is improved by multi-stage shot peening. 3.The fatigue strength of multi-stage shot peening material is 756MPa and is 1.78 times higher than that of un-peened material. 4.The maximum compressive residual strength of multi-stage shot peening material is -792MPa the fatigue strength seems to be improved by residual stress.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.33 no.2
• /
• pp.173-180
• /
• 2013

Compacted graphite iron(CGI), also known as vermicular graphite iron, is a metal which is gaining popularity in applications that require either greater strength, or lower weight than cast iron. Recently compacted graphite iron has been used for diesel engine blocks. Considering that using in exhaust manifold of the diesel engine, CGI340 was conducted the heat treatment during 1 hour to 96 hours from 873 to 1273 K. Mechanical characteristics were evaluated. The obtained results are as follows; The tensile strength of the heat treated specimens showed overall lower tensile strength than that of the base metal. Tensile strength decreases with increasing of heat treatment time, and the higher heat treatment temperature and the longer time, were more reduced. The fatigue limit by the ultrasonic fatigue test was approximately 130 MPa of base metal, 100 MPa of 1173 K (96 hrs) specimen, respectively. The hardness decreases with increasing heat treatment time, and the higher the heat treatment temperature was lowered hardness distribution. In CGI340, average hardness of nodular graphite was 120 Hv, average hardness of vermicular graphite was 114 Hv. This showed lower hardness than the base structure ferrite. The nodular graphite and vermicular graphite according to the heat treatment temperature and time didn't have a consistent change. However, the grain size of base structure grew with increasing of heat treatment time.