• The Journal of Advanced Prosthodontics
• /
• 제2권4호
• /
• pp.117-121
• /
• 2010

PURPOSE. The present study was intended to evaluate the effect of soldering techniques with infrared ray and gas torch under different gap distances (0.3 mm and 0.5 mm) on the tensile strength and surface porosity formation in Ni-Cr base metal alloy. MATERIALS AND METHODS. Thirty five dumbbell shaped Ni-Cr alloy specimens were prepared and assigned to 5 groups according to the soldering method and the gap distance. For the soldering methods, gas torch (G group) and infrared ray (IR group) were compared and each group was subdivided by corresponding gap distance (0.3 mm: G3 and IR3, 0.5 mm: G5, IR5). Specimens of the experimental groups were sectioned in the middle with a diamond disk and embedded in solder blocks according to the predetermined distance. As a control group, 7 specimens were prepared without sectioning or soldering. After the soldering procedure, a tensile strength test was performed using universal testing machine at a crosshead speed 1 mm/min. The proportions of porosity on the fractured surface were calculated on the images acquired through the scanning electronic microscope. RESULTS. Every specimen of G3, G5, IR3 and IR5 was fractured on the solder joint area. However, there was no significant difference between the test groups (P > .05). There was a negative correlation between porosity formation and tensile strength in all the specimens in the test groups (P < .05). CONCLUSION. There was no significant difference in ultimate tensile strength of joints and porosity formations between the gas-oxygen torch soldering and infrared ray soldering technique or between the gap distance of 0.3 mm and 0.5 mm.

• 소성∙가공
• /
• 제10권2호
• /
• pp.101-110
• /
• 2001

The thermal problem of press work is classified into two cases. First, the temperature of forming die passively rises due to the heating effect of plastic deformation. The warm forming is the second case in which the external heating is applied to the die and blank holder. So, the purpose of this study is to provide database for the forming characteristics at various temperature conditions. In this study, the tensile test was carried out for the commercial steel sheets such as SCPI and SCP3C with the thickness of 0.7mm and 1.4mm respectively. The tensile strength, total elongation, Lankford value and the flow curve have been obtained at the temperature of $25^{\circ}C$, $50^{\circ}C$, $100^{\circ}C$, $150^{\circ}C$, $200^{\circ}C$, $250^{\circ}C$ and $300^{\circ}C$, respectively. From the results, we can see that both the tensile strength and total elongation decrease as the temperature increases. In the light of anisotropy, the effect of thickness is dominant than the material specs. For the temperature dependency of flow curves, there are only small differences for the work-hardening exponent, and the strength intensity decreases monotonically as temperature increases. The present results we useful as input data for the analysis of sheet metal forming processes with the various temperature conditions.

• 한국환경복원기술학회지
• /
• 제8권1호
• /
• pp.27-36
• /
• 2005

Geosynthetic reinforcements may be damaged during its installation in the filed. The installation damage mainly depends on two factors such as materials used and construction activities. This paper describes the results of a series of field tests, which are conducted to assess the installation damage of geogrid according to different maximum grain sizes of fills (40, 60, and 80 mm). These tests are done in three sites for twelve different kinds of geogrids. After field tests, the changes in tensile strength of the geogrids is determined from wide width tensile tests using both damaged and undamaged specimens. In the results of tests, tensile strength of the relatively flexible geogrids after field installation tests was decreased about from 20% to 40% according to the increment of the maximum grain size. On the other hand, for the relatively stiff geogrids, the loss of the tensile strength after site installation was examined below 5.2% independent of the maximum grain size of the soils. The results of this study show that the installation damage significantly depends on the stiffness of geogrid and is more obvious to a flexible geogrid and a fill material having higher maximum grain size.

• Journal of Welding and Joining
• /
• 제24권5호
• /
• pp.43-48
• /
• 2006

This paper is concerned with a fracture strength study of composite adhesive lap joints. The tests were carried out on specimen joints manufactured hybrid stacked composites such as the polyester and bamboo natural fiber layer. The main objective of the work was to test the fracture strength using hybrid stacked composites with a polyester and bamboo natural fiber layer. Tensile and peel strength of hybrid stacked composites are tested before appling adhesive bonding. From results, Natural fiber reinforced composites have lower tensile strength than the original polyester. and The load directional orientation and small amount and low thickness of bamboo natural fiber layer have a good effect on the tensile and peel strength of natural fiber reinforced composites. The failure strength of these materials applied adhesive bonding is also affected by fiber orientation and thickness of bamboo natural fiber layer. There for, Fiber orientation of bamboo natural fiber layer have a great effect on the tensile-shear strength of natural fiber reinforced composites including adhesive bonded joints.

• Advanced Composite Materials
• /
• 제17권2호
• /
• pp.139-156
• /
• 2008

This study aims to characterize the dynamic tensile strength of unidirectional carbon/epoxy composites. Two different carbon/epoxy composite systems, the unidirectional T700S/2500 and TR50S/modified epoxy, are tested at the static condition and the strain rate of $100\;s^{-1}$. A high-strain-rate test was performed using a tension-type split Hopkinson bar technique with a specific fixture for specimen. The experimental results demonstrated that both tensile strength increase with strain rate, while the fracture behaviors are quite different. By the use of the rosette analysis and the strain transformation equations, the strain rate effects of material principal directions on tensile strength are investigated. It is experimentally found that the shear strain rate produces the more significant contribution to strain rate effect on dynamic tensile strength. An empirical failure criterion for characterizing the dynamic tensile strength was proposed based on the Hash-in's failure criterion. Although the proposed criterion is just the empirical formula, it is in better agreement with the experimental data and quite simple.

• 한국건설순환자원학회논문집
• /
• 제7권3호
• /
• pp.279-286
• /
• 2019

본 연구에서는 기준압축강도 180MPa의 강섬유 보강 초고강도 콘크리트(UHSC)의 인장 특성에 관한 실험 연구를 수행하였다. 부피비 1%의 강섬유를 혼입하여 직접인장강도 시편과 3점 하중재하 휨 실험을 위한 프리즘 시편을 제작하였다. 제작된 시편은 균열 유도를 위하여 시편 중앙에 노치를 설정하였으며, 각 평가방법에 따라 실험을 수행하였다. 우선, 콘크리트의 균열 후 거동 특성을 파악하기 위하여 직접인장강도 실험을 수행하여 응력-변형률 곡선을 분석하였으며, 3점 하중재하 휨 실험을 통하여 하중-CMOD 곡선을 얻고, 역해석을 수행하여 응력-변형률 곡선을 분석하였다. 직접인장강도 실험과 3점 하중재하 휨 실험의 인장거동 특성은 유사하게 나타났다. 또한, SC 구조설계지침에서 제시하고 있는 인장응력-변형률 곡선 모델링을 수행하고, 측정값과 예측값의 비교분석을 수행하였다. 재료감소계수가 1.0일 때, 변형률이 0.02일 때까지 예측값은 측정값과 유사하게 나타나지만, 재료감소계수가 0.8일 때, 예측값은 측정값의 최소값에 근접한다. 또한, 변형률이 0.02를 초과하는 구간에서는 SC 구조설계지침에 의한 예측값이 측정값을 과소평가한다.

• International Journal of Concrete Structures and Materials
• /
• 제9권3호
• /
• pp.337-343
• /
• 2015

Previous studies have shown that the drying shrinkage of recycled aggregate concrete (RAC) is greater than that of natural aggregate concrete (NAC). Drying shrinkage is the fundamental reason for the cracking of concrete, and tensile creep caused by the restraint of drying shrinkage plays a significant role in the cracking because it can relieve the tensile stress and results in the delay of cracking occurrence. However, up till now, all research has been focusing on the compressive creep of RAC. Therefore, in this study, a uniaxial restrained shrinkage cracking test was executed to investigate the tensile creep properties caused by the restraint of drying shrinkage of RAC. The mechanical properties, such as compressive strength, tensile splitting strength, and Young's modulus of RAC were also investigated in this study. The results confirmed that the tensile creep of RAC caused by the restraint of shrinkage was about 20-30 % larger than that of NAC.

• 한국군사과학기술학회지
• /
• 제4권1호
• /
• pp.255-263
• /
• 2001

The main purpose of this paper is to investigate strength characteristics of Aluminum 2024-T3 in high temperature environment. Tensile test of Aluminum 2024-T3 has been carried out in high temperature environment. The stress-strain relations are investigated with temperature and Young's modulus, yield strength and ultimate strength are deduced from the test results. The modulus and strength of the test are compared with those of MIL HANDBOOK and tips on structural design in high temperature environment are suggested.

• 대한치과보철학회지
• /
• 제40권4호
• /
• pp.344-351
• /
• 2002

The purpose of this study is to compare tensile bond strength between Cr-Co alloy and three denture base resins after surface treatment. Following the manufacturer's instructions, 180 bonded specimens were made from three denture base resins (Lucitone 199. Paladent 20. POSS resin) and three surface treatment methods (sandblasting. metal primer. silicoating) 20 samples were made in each group and a half was ther-mocycled 1000 times between $5^{\circ}C$ and $55^{\circ}C$. The tensile bond strength was measured using an Instron with 5mm/min crosshead speed. Data was analyzed with one-way ANOVA, T-test and Duncan test. The results were as follows : 1. Samples with metal primer coating had significantly high tensile bond strength than the other surface treated groups (p<.05). Significantly low tensile bond strength was shown in sand blasted groups (p<.05). 2. No significant difference was observed in metal primer coating groups before and after ther-mocycling (p>.05) 3. Tensile bond strength was decreased in silicoated samples after thermocycling (p<.05). 4. Of the surface treated groups with metal primer, Lucitone 199 had the greatest bond strength and POSS resin and Paladent 20 were followed (p<.05). 5. Of the surface treated groups with silicoating, POSS resin and Lucitone 199 had greater bond strength than Paladent 20 (p<.05).

• Design & Manufacturing
• /
• 제18권2호
• /
• pp.57-63
• /
• 2024

In this study, the recyclability of commonly used PP (polypropylene) and ABS (acrylonitrile butadiene styrene) was evaluated by molding test specimens from mixture of virgin and shredded material, followed by measuring their strength properties, Experiments were conducted o two type of PP (transparent and non-transparent) and two types of ABS (white and yellow). Test specimens for each resin were prepared with shredded material ratios ranging from 10% to 50% in 10% increments. Changes in tensile strength, elastic modulus, and elastic limit were analyzed based on the mixing ratio of the shredded material. The experimental results demonstrated that the strength properties of all the resins remained consistent within a certain range, even with increasing proportions of shredded material. For transparent PP, the tensile strength ranged from 30.87± MPa, the elastic modulus from 1.23±0.04 GPa, and the elastic limit from 19.17±0.44%. Non-transparent PP exhibited a tensile strength ranging from 27.71±0.58 MPa, an elastic modulus from 1.03±0.06 GPa, and an elastic limit from 17.35±0.41%. For ABS, white ABS had a tensile strength of 39.42±0.28 MPa, an elastic modulus of 1.94±0.01 GPa, and an elastic limit of 36.76±0.25%. Yellow ABS showed a tensile strength of 39.25±0.78 MPa, an elastic modulus of 1.94±0.01 GPa, and an elastic limit of 37.14±0.23%, with values remaining consistent within this range. Based on these results, it was confirmed that the mechanical properties of the resins used in this study do not change significantly when mixed with recycled shredded material, indicating excellent mechanical recyclability.