• Proceedings of the Korea Committee for Ocean Resources and Engineering Conference
• /
• 2002.05a
• /
• pp.68-74
• /
• 2002

The tensile tests to identify the statistical tensile properties and the acoustic emission characteristics were conducted for STS304 stainless steel at $600^{\circ}C,\;700^{\circ}C$. From tensile tests performed by constant cross head speed controls with 1mm/min, rates at each elevated temperature, the scatters were observed in tensile strength, reduction of area, elongation and the acoustic emission parameters. The effect of temperature on the scatter of tensile behavior was larger at $700^{\circ}C$. The distributions of tensile properties was well followed in 3-parameter Weibull. The AE counts and energy of the $700^{\circ}C$ specimens were smaller than the $600^{\circ}C$.

• Journal of the Korea Academia-Industrial cooperation Society
• /
• v.21 no.1
• /
• pp.129-137
• /
• 2020

In designing a high strength bolted beam splice using steel for building structures, it is necessary to present the appropriate steel grade selection criteria for how to determine the cover plate steel grade. This study examined the difference in tensile behavior according to the steel grades through static tensile tests simulating the beam member high strength bolt joints flange. For this purpose, the specimens were designed and fabricated with the main variables, such as the thickness, steel grade and the strength of flange and cover plate, which are expected to affect the splice strength and behavior. The tensile test results for a total of 48 specimens showed that the tensile-load capacity exceeded the design tensile strength applied with a nominal strength of steel in all specimens. When the design strength of the cover plate exceeded 1.25 times that of the flange plate, the flange plate governed the behavior of splice. The change in maximum tensile load due to the change in flange steel grade is not very large, but there is a difference in deformation. The test results confirmed that the steel grade and thickness of the cover plate were the main factors affecting the beam splice behavior.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2005.05a
• /
• pp.151-154
• /
• 2005

One of the most important characteristics of Engineered Cementitious Composite (ECC) is its strain hardening behavior up to $5\∼6\%$of stain under a tensile loading. So, the ductile behavior of ECC should be utilized in applications to maximize the performance of structures. Thus, in this study, the ductile behavior of ECC as a repair material applied to the tensile region under flexural loads is numerically examined using a developed numerical model. Several strain capacities of ECC are examined to predict the behavior of ECC strengthened flexural structures. The results show that a certain optimal level of ductility in ECCs for repair applications exists and it is an important factor to consider when using ECC as a repairing material.

• Journal of Mechanical Science and Technology
• /
• v.16 no.9
• /
• pp.1093-1101
• /
• 2002

Continuous fiber ceramic composites (CFCCs) have advantages over monolithic ceramics : Silicon Nitride composites are not well used for application because of their low fracture toughness and fracture strength, but CFCCs exhibit increased toughness for damage tolerance, and relatively high stiffness in spite of low specific weight. Thus it is important to characterize the fracture resistance and properties of new CFCCs materials. Tensile and flexural tests were carried out for mechanical properties and the fracture resistance behavior of a SCS6 fiber reinforced Si$_3$N$_4$ matrix CFCC was evaluated. The results indicated that CFCC composite exhibit a rising R curve behavior in flexural test. The fracture toughness was about 4.8 MPa$.$m$\^$1/2 , which resulted in a higher value of the fracture toughness because of fiber bridging. Mechanical properties as like the elastic modulus, proportional limit and the ultimate strength in a flexural test are greater than those in a tensile test. Also a numerical modeling of failure process was accomplished for a flexural test. This numerical results provided a good simulation of the cumulative fracture process of the fiber and matrix in CFCCs.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2000.04a
• /
• pp.373-378
• /
• 2000

The heat resistant material, in service, may experience static loading, cyclic loading, or a combination of two. An experimental study of crack growth behavior of STS 316L austenitic stainless steel under fatigue, and creep-fatigue loading conditions were carried out on compact tension specimens at various tensile hold times. In the crack growth experiments under hold times. In the crack growth experiments under hold time loading conditions, tensile hold times were ranged from 5 seconds to 100 seconds and its behavior was characterized using the $\Delta$K parameter. The crack growth rates generally increase with increasing hold times. However in this material, the trend of crack growth rates decreases with increasing hold times for short hold time range relatively. It is attributed to a decline in the cyclic crack growth rate as a result of blunting at the crack tip by creep deformation. The effect of grain size on the creep behavior of STS 316L was investigated. Specimens with grain size of 30, 65 and 125${\mu}{\textrm}{m}$ were prepared through various heat treatments and they were tested under various test conditions. The fracture mode of 316L changed from transgranular to intergranular with increasing grain size.

• Geomechanics and Engineering
• /
• v.29 no.6
• /
• pp.627-643
• /
• 2022

Water-rock interactions have a significant influence on the mechanical behavior of rocks. In this study, uniaxial compression and tension tests on different water-treated sandstone samples were conducted. Acoustic emission (AE) monitoring and micro-pore structure detection were carried out. Water-rock interactions and their effects on rock mechanical behavior were discussed. The results indicate that water content significantly weakens rock mechanical strength. The sensitivity of the mechanical parameters to water treatment, from high to low, are Poisson ratio (𝜇), uniaxial tensile strength (UTS), uniaxial compressive strength (UCS), elastic modulus (E), and peak strain (𝜀). After water treatment, AE activities and the shear crack percentage are reduced, the angles between macro fractures and loading direction are minimized, the dynamic phenomenon during loading is weakened, and the failure mode changes from a mixed tensile-shear type to a tensile one. Due to the softening, lubrication, and water wedge effects in water-rock interactions, water content increases pore size, promotes crack development, and weakens micro-pore structures. Further damage of rocks in fractured and caved zones due to the water-rock interactions leads to an extra load on the adjoining coal and rock masses, which will increase the risk of dynamic disasters.

• Journal of the Korean Society of Industry Convergence
• /
• v.23 no.3
• /
• pp.375-380
• /
• 2020

In this study, we tried to evaluate the mechanical properties of Polycarbonate(PC) and acrylonitrile-butadiene-styrene(ABS) plastic materials, which are frequently used as parts of home appliances and machinery, when repeated impacts were applied. A repeating impact tester for this research was designed and manufactured to apply repetitive impacts. Two types of plastic were repeatedly impacted under a constant load, and a tensile test was performed on the plastic material that was impacted. The tensile strength of PC plastic materials that received impact more than 2000 times was reduced by about 45 % and elongation was reduced by about 10 % when compared to impact free specimens. On the other hand, in ABS plastic, a reduction of tensile strength of about 20 % was observed at about 2,000 impacted specimen, but at about 20,000 repetitive impacted specimen, a tensile strength decrease of about 65 % was observed. And the elongation was reduced by 10 % due to the cyclic harding behavior of the material.

• Geomechanics and Engineering
• /
• v.14 no.2
• /
• pp.203-209
• /
• 2018

Reliable estimation of compressive as well as tensile in-situ stresses is critical in the design and analysis of underground structures and openings in rocks. Kaiser effect technique, which uses acoustic emission from rock specimens under cyclic load, is well established for the estimation of in-situ compressive stresses. This paper investigates the Kaiser effect on marble specimens under cyclic uniaxial compressive as well as cyclic uniaxial tensile conditions. The tensile behavior was studied by means of Brazilian tests. Each specimen was tested by applying the load in four loading cycles having magnitudes of 40%, 60%, 80% and 100% of the peak stress. The experimental results confirm the presence of Kaiser effect in marble specimens under both compressive and tensile loading conditions. Kaiser effect was found to be more dominant in the first two loading cycles and started disappearing as the applied stress approached the peak stress, where felicity effect became dominant instead. This behavior was observed to be consistent under both compressive and tensile loading conditions and can be applied for the estimation of in-situ rock stresses as a function of peak rock stress. At a micromechanical level, Kaiser effect is evident when the pre-existing stress is smaller than the crack damage stress and ambiguous when pre-existing stress exceeds the crack damage stress. Upon reaching the crack damage stress, the cracks begin to propagate and coalesce in an unstable manner. Hence acoustic emission observations through Kaiser effect analysis can help to estimate the crack damage stresses reliably thereby improving the efficiency of design parameters.

• Korean Journal of Metals and Materials
• /
• v.50 no.10
• /
• pp.703-710
• /
• 2012

The effects of the ordering reaction on high temperature mechanical behavior is investigated by tensile tests at $2{\times}10^{-2}/s-3.3{\times}10^{-5}/s$ up to $745^{\circ}C$. The tensile deformed region is examined by differential scanning calorimeter (DSC), TEM, and high resolution neutron diffraction (HRPD). The results showed that a plateau of tensile strength appeared at $150-500^{\circ}C$ whereas the elongation minimum occurred at about $600^{\circ}C$. This suggests that the occurrence of a plateau does not cause the elongation minimum. The temperature of the elongation minimum decreases with the strain rate. HRPD results show a lattice contraction in the tensile deformed specimen at the temperature of the plateau occurring region. The plateau of tensile strength, the lattice contraction, and the occurrence of serration appeared in the same temperature region.

• Proceedings of the Korean Geotechical Society Conference
• /
• 1999.03a
• /
• pp.105-112
• /
• 1999

In recent the superior economic benefits and the convenience of installation increased the use of geosynthetics, especially geogrids with the effects of high tensile strength. In this study, various tests were conducted to determine the physical and chemical properties of geogrids which contains durability under various critical conditions, creep behavior and the stability for installation damage in fields. With analysis of test results, the partial and total safety factors were determined and presented the long term design strength of flexible geogrids.