• Journal of Power System Engineering
• /
• v.20 no.3
• /
• pp.11-16
• /
• 2016

The effect of carbides on the tensile properties in 0.5C-17Cr-0.5Ni martensitic stainless steel was studied. With the increase of austenitizing temperature, the volume fraction of residual carbide was decreased rapidly. In tempered specimens after quenching, the volume fraction of total carbide was decreased with the increase of austenitizing temperature. In tempered specimens after quenching, strength was decrease and elongation was increased with the increase of austenitizing temperature. Tensile strength was increase and elongation was decreased with the increase of volume fraction of residual and total carbides. With the increase of austenitizing temperature, the tensile properties of mod. 0.5C-17Cr-0.5Ni martensitic stainless was affected greatly by residual carbide than tempered carbide.

• Journal of Korea Foundry Society
• /
• v.19 no.1
• /
• pp.33-37
• /
• 1999

White cast iron of 3%C-10%Cr-5%Mo-5%W was casted, and then heat treated with three different methods such as homogenizing, austenitizing and tempering to observe its effects on the microstructure, hardness and abrasive wear resistance. In uni-directional soldification, bamboo tree-like $M_7C_3$ carbide grew along with the heat flow direction, and fishbone-like $M_6C$ carbide was dispersed randomly among $M_7C_3$ carbides. While almost pearlitic structures were observed in the as-cast specimen, those of the heat treated specimens consisted of secondary carbide, retained austenite and tempered martensite. In austenitized specimen, the amounts of retained austenite were 60.88% due to the higher cooling rate encountered in forced air cooling. On the other hand, the amounts of retained austenite were reduced from 60.88% to 23.85% in tempered specimen due to the transformation of austenite into tempered martensite. The hardness of tempered specimen showed the highest value, and then decreased in the order of austenitized, as-cast and homogenized specimens. But, the abrasive wear resistance of austenitized specimen was the highest, and then decreased in the order of tempered, as-cast and homogenized specimens.

• Nuclear Engineering and Technology
• /
• v.46 no.3
• /
• pp.413-422
• /
• 2014

Presented in this study are the variations of microstructures and mechanical properties with tempering and Post-Weld Heat Treatment (PWHT) conditions for SA508 Gr.4N steel used as Reactor Pressure Vessel (RPV) material. The blocks of model alloy were austenitized at the conventional temperature of $880^{\circ}C$ then tempered and post-weld heat treated at four different conditions. The hardness and yield strength decrease with increased tempering and PWHT temperatures, but impact toughness is significantly improved, especially in the specimens tempered at $630^{\circ}C$. The sample tempered at $630^{\circ}C$ with PWHT at $610^{\circ}C$ shows optimum mechanical properties in hardness, strength, and toughness, excluding only the transition property in the low temperature region. The microstructural observation and quantitative analysis of carbide size distribution show that the variations of mechanical properties are caused by the under-tempering and carbide coarsening which occurred during the heat treatment process. The introduction of PWHT results in the deterioration of the ductile-brittle transition property by an increase of coarse carbides controlling cleavage initiation, especially in the tempered state at $630^{\circ}C$.

• Korean Journal of Metals and Materials
• /
• v.47 no.7
• /
• pp.406-415
• /
• 2009

A study was conducted on the effects of carbon, tungsten, and vanadium on the wear properties and surface roughness of four High Speed Steel (HSS) rolls manufactured by the centrifugal casting method. Hot-rolling simulation tests were carried out using a high-temperature wear tester capable of controlling speed, load, and temperature. HSS rolls contained a large amount (up to 25 vol.%) of carbides such as MC, $M_{2}C$, $M_{7}C_{3}$, and $M_{6}C$ carbides formed in the tempered martensite matrix. The matrix consisted mainly of lath tempered martensite when the carbon content in the matrix was small, and contained a considerable amount of plate tempered martensite when the carbon content increased. The high-temperature wear test results indicated that the wear properties and surface roughness of the rolls improved when the amount of hard MC carbides formed inside solidification cells increased. The rolls distribution was also homogeneous. The best wear properties and surface roughness were obtained from a roll where a large amount of MC carbides was homogeneously distributed in the lath tempered martensite matrix. The proper contents of carbon equivalent, tungsten equivalent, and vanadium were 2.0~2.3%, 9~10%, and 5~6%, respectively.

• Korean Journal of Materials Research
• /
• v.25 no.12
• /
• pp.666-671
• /
• 2015

In this study, we investigated the effect of the residual carbides and tempered carbides precipitated by tempering treatment after quenching on the pitting corrosion of mod. 440A martensitic stainless steel. In quenched specimens and tempered specimens after quenching of mod. 440A martensitic stainless steel, the volume fraction of the residual carbides and total carbides decreased with the increase of the austenitizing temperature. Pitting resistance increased with the increase of austenitizing temperature. With the increase of the volume fraction of the residual and total carbides, the pitting resistance of mod. 440A martensitic stainless steel was decreased. The pitting resistance of mod. 0.5C-17Cr-0.5Ni 440A martensitic stainless steel had stronger affected by residual carbides than precipitated carbides produced by tempering.

• Journal of the Korean Society for Heat Treatment
• /
• v.7 no.1
• /
• pp.35-43
• /
• 1994

For the purpose of studying the change of mechanical properties of weld parts, shielded metal are welding, one-pole and two-pole submerged arc welding were accomplished weldability on $60kg/mm^2$ quenched and tempered high strength steel. Charpy impact values of the weld metal in welded parts by SMAW and SAW were lower than those of the heat affected zone and increased in order of bond, coarsened, refined and carbon spheroidized regions in the heat affected zone. Grain size of prior austenite or M-A constituent did not significantly affect toughness of welded parts, but precipitated carbide films which forms at the grain boundaries or within matrix and volume fraction of pearilte were most important factor for toughness.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.18 no.4
• /
• pp.292-303
• /
• 1998

Recent study has demonstrated that some magnetic properties are sensitive to the microstructural state of material. The ASTM A 508 Gr. 3 reactor pressure vessel steel has various microstructural changes including martensitic and bainitic phases, and various sizes of grain and precipitates in the weld heat-affected zone (HAZ). To correlate the microstructural state with Barkhausen noise (BN), specimens were prepared through simulating various weld thermal cycles using a thermal simulator. The conventional magnetic properties, i.e. coercive force, remanence and maximum induction, did not change significantly, whereas the BN amplitude and energy during a magnetization cycle changed markedly with microstructural state. The BN increased with increasing grain and carbide sizes, and the tempered bainite structure showed higher BN parameter than tempered martensite.

• Advances in materials Research
• /
• v.13 no.3
• /
• pp.183-194
• /
• 2024

D3 tools steel and 440C stainless steel (SS) are normally being employed for application such as knife blade and cutting tools. These steels are iron alloys which have high carbon and high chromium content. In this study, lab work focused on the microstructural and corrosion behavior of D3 tools steel and 440C SS after went through heat treatment processes. Heat treatments for both steels were started with normalizing at 1020 ℃, continue with hardening at 1000 ℃followed by oil quenching. Cryogenic treatment was carried out in liquid nitrogen for 24 hours. The addition of cryogenic heat treatment is believed to increase the hardness and corrosion resistance for steels. Both samples were then tempered at two different tempering temperatures, 160 ℃ and 426 ℃. For corrosion test, the samples were immersed in NaCl solution for 30 days to study the corrosion behavior of D3 tool steel and 440C SS after heat treatment. The mechanical properties of these steels have been investigated using Rockwell hardness machine before heat treatment, after heat treatment (before corrosion) and after corrosion test. Microstructure observation of samples was carried out by scanning electron microscopy. The corrosion rate of these steels was calculated after the corrosion test completed. From the results, the highest hardness is observed for D3 tool steel which tempered at 160 ℃(54.1 HRC). In terms of microstructural analysis, primary carbide and pearlite in the as-received samples transform to tempered martensite and cementite after heat treatment process. From this research, for corrosion test, heat treated 440C SS sample tempered with 426 ℃possessed the excellent corrosion resistance with corrosion rate 0.2808 mm/year.

• Journal of the Korean Society for Heat Treatment
• /
• v.7 no.1
• /
• pp.25-34
• /
• 1994

To investigate the effect of austenitizing tempratures on the mechanical properties and corrosion resistance of 0.19%C-13.6%Cr martensitic stainless steel, the changes in martensitic trasformation temperatures, mechanical properties and anodic polarization curve were examined after changing the austenitizing temperatures and tempering temperatures. On increasing heating rate at the same austenitizing temperatures, $A_s$, $A_r$ and $M_s$ increased. And the $M_s$ temperature showed to be decreased with increasing austenitizing temperature. With increasing tempering temperature up to $500^{\circ}C$, strength, hardness and impact value were not changed remarkably, on the other hand the tensile strength and hardness decreased and impact value increased after tempering above $550^{\circ}C$ owing to the $M_{23}C_6$ carbide precipitation. The abrupt decrease in elongation at the tempering temperture of $500^{\circ}C$ proved to the precipitation of $M_7C_3$ carbide. The effect of austenitizing temperature on the mechanical properties of the tempered specimen showed to be decreased in impact value and elongation at the austenitizing temperature of $1150^{\circ}C$. At low tempering temperatures the corrosion resistance of the tempered specimen was not changed obviously with increasing tempering temperature. On the other hand, the resistance decreased above the tempering temperature of $600^{\circ}C$ due to the precipitation of $M_{23}C_6$ carbides. The corrosion resistance showed to be improved with increasing the austenitizing temperature owing to the dissolution of carbides.

• Journal of the Korean Society for Heat Treatment
• /
• v.13 no.1
• /
• pp.27-34
• /
• 2000

This present study were investigated effect of Ni contents on the microstructure and strength characteristic in 9Cr ferritic heat-resistant steel added 1.7%W in place of Mo in order to restrain laves phase formation. The result obtained from this study are as follow. Volume fraction, number of particles per unite area and particle size of carbide decreased with increase of Ni contents. Other side, carbides of $M_{23}C_6$ type was mainly precipitated in this steel, but laves phases could not precipitated in spite of increasing of aging time. With increase of tempering temperature, hardness was increased, and maximum value was showed around 873k by secondary hardening due to precipitation of $W_2C$ type carbide and then, was decreased. Tensile and yield strength due to decrease precipitation amount of carbide and number of particles per unite area was decreased, but elongation and impact value was increased. In case of aged specimen after tempering than tempered specimen, strength was higher and elongation was lower due to increasing of precipitated amount of carbide and number of particles per unite area.