• Journal of the Korean Society for Heat Treatment
• /
• v.6 no.4
• /
• pp.194-203
• /
• 1993

Rapid solidified splats Al-(1, 3, 5Cr) Alloys were produced by atomization-splat quenching method. Effects of mechanical alloying on the structure and mechanical properties of rapidly solidified Al-(1, 3, 5)Cr alloys were studied. Degree of mechanical alloying of Al-(1, 3, 5)Cr alloys can be determined by observing the microstructural refinement, microhardness and microstructure of Al-(l, 3, 5)Cr splats during processing. In the initial stage of mechanical alloying of the Al-(1, 3, 5)Cr splats fracturing of the grain boundaries occured first, followed after fracturing of zone A regions. Saturation hardness of Al-(1, 3, 5)Cr alloys increased proportionally with increasing concentration of the solute (Cr). Age hardening was not observed in these alloys. Decomposition temperature of Al-1Cr splats after mechanical alloying was higher than that of Al-5Cr splats. The density of $Al_7$ Cr precipitates increased proportionally with increasing chromium content, as a result, there was a transition to finely and spherically dispersed phase after mechanical alloying.

• Journal of the Korea Institute of Building Construction
• /
• v.2 no.1
• /
• pp.131-138
• /
• 2002

There is a problem to be solved for improvement of durability and safety supervision. When you do the waterproofing work of main concrete from the design stage, the material and method of construction need to be correctly applied to appropriate circumstance conditions. Epoxy have mostly been used for concrete water tank structure. Lately, lots of subjects on adaption of polyurea resin waterproofing and anticorrosive are under discussion. Then, we attempt to approach by evaluating and comparing every capabilities with another waterproofs in this study. Performance evaluation items include the adherence performance, the imprint of seal performance, temperature dependence performance, promotion weatherizing ability, Inner chemical performance. drinking water eruptive performance. Through the experiment analysis, we found that the polyurea resin waterproofing membrane is dominantly superior to other waterproofs. According to this study, we suggest the polyurea resin waterproofing membrane as a new waterproofing material for concrete structure.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2003.05a
• /
• pp.91-95
• /
• 2003

There is a problem to be solved for improvement of durability and safety supervision. When you do the waterproofing and anticorrosive work of main concrete from the design stage, the material and method of construction need to be correctly applied to appropriate circumstance conditions. Epoxy have mostly been used for concrete water tank structure. Lately, lots of subjects on adaption of polyurea resin waterproofing and anticorrosive are under discussion. Then, we attempt to approach by evaluating and comparing every capabilities with another waterproofs in this study. Performance evaluation items include the adherence performance. the imprint of seal performance, temperature dependence performance. promotion westernizing ability, inner chemical performance. drinking water eruptive performance. Through the experiment analysis, we found that the polyurea resin waterproofing membrane is dominantly superior to other waterproofs. According to this study, we suggest the polyurea resin waterproofing membrane as a new waterproofing material for concrete structure.

• Korean Journal of Materials Research
• /
• v.8 no.12
• /
• pp.1133-1137
• /
• 1998

By the mechanical alloying method Ni-W(WC) composite materials were prepared to improve the resistance for creep and sintering of Ni-anode at the operating temperature of$ 650^{\circ}C$. Amorphization was observed from the XRD analysis of mechanically alloyed powder caused by the destruction of ordered crystals. Sintering was performed at $1280^{\circ}C$ for 10 hours in $H_2$ atmosphere. From the result of dot-mapping and TEM analysis the second phase was not observed at Ni-W interface while W particles of less 0.lam were distributed finely and uniformly in Ni matrix. This finely and uniformly distributed W in Ni matrix is expected to enhance the mechanical properties of Ni-anode through the dispersion and solid solution hardening mechanisms.

• Korean Journal of Materials Research
• /
• v.27 no.4
• /
• pp.199-205
• /
• 2017

In this study, (3,4-epoxycyclohexane)methyl 3,4-epoxycyclohexylcarboxylate acrylate was synthesized by reacting (3,4-epoxycyclohexane)methyl 3,4-epoxycyclohexylcarboxylate with acrylic acid to minimize hardening shrinkage and to improve heat resistance, which are known as disadvantages of photopolymers for 3D printing application. Urethane acrylate was synthesized by reacting 1,3,5-triazine-2,4,6-triamino alcohol, 2-hexylethyl acrylate, and isophorone diisocyanate in order to improve the mechanical properties without deteriorating the heat resistance. The physical properties before and after the synthesis of the acrylate and the mechanical properties when the urethane acrylate was applied were investigated. The reaction progress of the composite was examined by FTIR and $^{13}C$ NMR. The heat deflection temperature, flexural strength, and surface hardness of the molding were measured. The curing behavior by Photo-DSC ultraviolet irradiation was also examined.

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.13 no.1
• /
• pp.75-83
• /
• 2017

This study investigated deformation behavior of major nuclear structural materials under cyclic loading conditions via cyclic stress-strain test. The cyclic stress-strain tests were conducted on SA312 TP316 stainless steel and SA508 Gr.3 Cl.1 low-alloy steel, which are used as materials for primary piping and reactor pressure vessel nozzle respectively, under cyclic load with constant strain amplitude and constant load amplitude at room temperature (RT) and $316^{\circ}C$. From the results of tests, the cyclic hardening and softening behavior, stabilized cyclic stress-strain behavior, and ratcheting behavior of both materials were investigated at both RT and $316^{\circ}C$. In addition, appropriate considerations for cyclic deformation behavior in the structural integrity evaluation of major nuclear components under excessive seismic condition were discussed.

• Elastomers and Composites
• /
• v.55 no.3
• /
• pp.222-228
• /
• 2020

Rubber materials, used in nuclear power plants, need high heat-oxidation resistance to curing or cracking under a heat aging environment. This is because they are applied to environments with high temperature, high humidity, and radiation exposure. Nuclear radiation causes additional hardening or degradation, therefore, rubber materials need radiation resistance that satisfies the general and any accidental conditions produced in the power plant. Therefore, in this study, we developed a rubber material with excellent heat and radiation resistance for the diaphragm seal of a nuclear steam generator nozzle dam. The rubber material greatly improved the reliability of the steam generator nozzle dam. In addition, 30 inch and 42 inch diaphragm seals were manufactured using the developed rubber material. A nozzle dam was installed in a nuclear power plant and tested under the same conditions as a steam generator to evaluate safety and reliability. In the future, the performance and safety of diaphragm seals developed through field tests of nuclear power plants will be evaluated and applied to currently operating and new nuclear power plants.

• Journal of Ocean Engineering and Technology
• /
• v.23 no.4
• /
• pp.85-90
• /
• 2009

Although most of existing hydration heat control methods show a certain degree of hydration heat control, generally, there are many problems as mentioned above. Therefore, our laboratory previously developed a hydration heat control method using an exposed heat pipe, which solves most of these problems and simultaneously displays excellent hydration heat control. Unfortunately, even this method had some problems such as the processing, transport, and assembly of heat pipes, and the surface treatment of a cut plane after pouring, and hardening concrete. Therefore, in this study, a hydration heat control method using an embedded pipe has been developed with the expectation that this method solves those problems in hydration heat control using an exposed heat pipe. As a result of the experiment, the peak temperature of ECHP and ICHP specimen about $4.5{\sim}6.5^{\circ}C$ than the OPC specimen and the probability of thermal cracked generated in ECHP and ICHP specimen decreased up to $13{\sim}20%$. Finally, it was confirmed in this study that the hydration heat control method using an embedded heat pipe is significantly more superior and cost effective than the existing method of an exposed one.

• Journal of the Korea Institute of Building Construction
• /
• v.6 no.4 s.22
• /
• pp.85-92
• /
• 2006

Urethane, epoxy, acrylic have common property to adhere on the concrete dried surface in the waterproofing materials at present. In the wet condition, however, the materials such as urethane, epoxy, acrylic need a long hardening time and it become a reason of water leakage as the materials breaking down. it is one of the problem to adhere to the substrate. Therefore, in this thesis, I focused to assure the structural safety and durability and quality for waterproofing and safe of construction cost by cut down the cost of labor and reduce the term of works as searching the application of field condition for high adhesive spray type of degenerated and rubberized asphalt membrane material.

• Journal of Powder Materials
• /
• v.10 no.4
• /
• pp.235-240
• /
• 2003

The $Al/Al_2O_3$ composites fabricated by powder in sheath rolling method were cold-rolled by 50% reduction and annealed for 1.8 ks at various temperatures ranging from 200 to 50$0^{\circ}C$, for improvement of the mechanical properties. The mechanical properties and texture of the composites after rolling and annealing were investigated. The tensile strength of the composites increased significantly due to work hardening after cold rolling, however it decreased due to restoration after annealing. The strength of the composites was improved by thermo mechanical treatment. On the other hand, the texture evolution with annealing temperatures wa,i different between the unreinforced material and the composites. The unreinforced material showed a deformation (rolling) texture of which main component is ｛112｝<111> at annealing temperatures up to 30$0^{\circ}C$. However, the composites have already exhibited a recrystallization texture of which main component is ｛001｝<100> after annealing at 20$0^{\circ}C$. This proves that the critical temperature for recrystailization is lower in the composites than in the unreinforced ones.