• Journal of the Microelectronics and Packaging Society
• /
• v.12 no.4 s.37
• /
• pp.307-313
• /
• 2005

Electromigration behavior in the Sn96.5Ag3.0Cu0.5 solder lines was investigated and compared Sn96.5Ag3.0Cu0.5 with eutectic SnPb. Measurements were made for relevant parameters for electromigration of the solder, such as drift velocity, threshold current density, activation energy, as well as the product of diffusivity and effective charge number (DZ$\ast$). The threshold current density were measured to be $2.38{\times}10^4A/cm^2$ at $140^{\circ}C$ and the value represented the maximum current density which the SnAgCu solder can carry without electromigration damage at the stressing temperatures. The electromigration energy was measured to 0.56 eV in the temperature range of $110-160^{\circ}C$. The measured products of diffusivity and the effective charge number, DZ$\ast$ were $3.12{\times}10^{-10} cm^2/s$ at $110^{\circ}C$, $4.66{\times}10^{-10} cm^2/s$ at $125^{\circ}C$, $8.76{\times}10^{-10} cm^2/s$ at $140^{\circ}C$, $2.14{\times}10^{-9}cm^2/s$ at $160^{\circ}C$ SnPb solder existed incubation stage, while SnAgCu did not have incubation stage. It was thought that the diffusion mechanism of SnAgCu was different from that of SnPb.

• Korean Journal of Weed Science
• /
• v.31 no.3
• /
• pp.294-307
• /
• 2011

This experiment carried out to confirm characteristics of macrogranule (GG) for herbicidal efficacy by using remote-controlled aerial application (RCAA) to control annual and perennial weeds in rice paddy field, application methods, and application times of formulation types. Particle of 500 g GG having average diameter of 2.5~3 mm was over 85 percent, the bulk density of the particle was $0.2\sim0.4g\;mL^{-1}$ and the particle was water floating granule. Active ingredients and external form of halosulfuronmethyl+mefenacet GG remained stable under condition of storage stability test. The disintegration time of the GG was faster as the water temperature was increased. But disintegration time was not affected by pH on the water conditions. By using hand, spoon and power applicator, drift distances of GG were 4~5m, 7 m and 10~12 m, respectively. GG showed good herbicidal efficacy and plant safety in all of the application methods such as, using hand, spoon, power applicator and RCAA. Application times of GG, GR, SC and TB by hand in $4,000m^2$ were 38 min. 4 sec, 42 min. 20 sec, 38 min. 10 sec and 21 min. 4 sec, respectively, but application time of GG by using RCAA was 1 min 32 sec. According to appearance and characteristics of formulation types, suspension concentrate (SC) and GG were possible formulation types for RCAA.