• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.32 no.3
• /
• pp.89-95
• /
• 2022

In this study, glassy carbon coating was performed on the graphite using a phenolic resin and a curing agent was mixed with ethylene glycol as an additive to form the uniform surface. The phenolic resin was dried and cured under the environments of hot air, then converted into a glassy carbon layer by pyrolysis at 500~1,500℃. FTIR, XRD, SEM analysis, and density/porosity/contact angle measurement were performed for characterization of glassy carbon. The pyrolysis temperature for high-quality glassy carbon was optimized to be about 1,000℃. As the content of the additive increased, the effect of reducing surface defects on the coated surface, reduction of porosity, increase of contact angle, and increase of density were investigated in this study. The method of forming a glassy carbon coating layer through an additive is expected to be applicable to graphite coating and other fields.

• The korean journal of orthodontics
• /
• v.29 no.5 s.76
• /
• pp.613-625
• /
• 1999

The purpose of this study was to compare the bracket shear bond strengths of the crystal growth solutions with those of the $37\%$ phosphric acid etch technique. The 4 crystal growth solutions were made experimentally in the lab, that is, (1) $30\%$ polyacrylic acid solution containing 0.3 M sulfuric acid (ES 1), (2) $30\%$ polyacrylic acid solution containing 0.6M sulfuric acid (ES 2), (3) $30\%$ polyacrylic acid solution containing 0.3 M sulfuric acid and 0.6 M lithium sulfate(ES 3), and (4) $30\%$ polyacrlic acid solution containing 0.3 M sulfuric acid and $5\%$ phosphoric acid(ES4). The $37\%$ phosphoric acid solution used as a control. Bovine lower incisor tooth enamel was treated by the above solutions for 60 sec, washed out for 20 sec with slow water stream, and bonded lower anterior edgewise bracket with the light curing orthodontic composite resin adhesives. The teeth bonded brackets were stored in the distilled water at room temperature for 24 h, and followed to test the bracket shear bond strength. The acid etch technque showed 177.6 kg/$cm^2$ of mean shear bond strength which was the highest among the enamel treatment solutions. ES 1 shown 58.4 kg/$cm^2$ of mean shear bond strength and that of ES 4 showed 66.5 kg/$cm^2$. There was no significant difference between the two(p>0.05). ES2 showed 110.6kg/$cm^2$ of mean shear bond strength which was $62.3\%$ of that of acid etch technique. ES 3 showed 131.1 kg/$cm^2$ of mean shear bond strength which was the highest among experimental crystal growth solutions and which was $74\%$ of that of acid etch technique. The shear bond strengths of the crystal growth solutions were significantly lower that that of acid etch technique(p<0.05). The results sugest that although bracket shear bond strength of $30\%$ polyacrylic acid solution containing 0.3M sulfuric acid and 0.6 M lithium sulfate were showed the highest, it is low for the clinical application of this solution.