• Advances in concrete construction
• /
• v.10 no.4
• /
• pp.301-310
• /
• 2020

The following paper concentrates on the objective of studying the influences of extent of duration and temperature on the Pozzolanic properties as well as reactivity of locally existing natural clay of Nai Gaj, district Dadu, Sindh Pakistan. The activation of the clay only occurs through heating when temperature in a furnace chamber reaches 600, 700 and 800oC for 1, 2 and 3 hours and at 900 and 1000℃ for 1 and 2 hours. Furthermore, the strength activity index (SAI) of advanced pozzolanic material happens to be identified through 20% cement replacement for different samples of calcined clay as per ASTM C-618. The compressive strength test of samples had been operated for 7 and 28-days curing afterwards. The maximum compressive strength had been seen in mix E in which cement was replaced with clay calcined at 700℃ for 1 hour that is 27.05 MPa that is 24.31% more than that of control mix. The results gathered from the SAI verdicts the optimal activation temperature is 700℃ within a one-hour time period. The SAI at a temperature of 700℃ with a one-hour duration at 28 days is 124.31% which happens to satisfy the requirements of the new Pozzolanic material, in order to be applied in mortar/concrete (i.e., 75%). The Energy- dispersive spectrometry (EDS) along with the X-ray diffraction (XRD) have been carried out in means of verifying whether there is silica content or amorphous silica present in metakaolin that has been developed. The findings gathered from the SAI were validated, as the analysis of XRD verified that there is in fact Pozzolanic activity of developed metakaolin. Additionally, based on observation, the activated metakaolin holds a significant influence on the increase in mortar's compressive strength.

• Journal of the Korea Concrete Institute
• /
• v.18 no.5 s.95
• /
• pp.677-685
• /
• 2006

Control of the temperature difference across a section is an effective strategy to minimize the hydration-heat-induced cracks for the structures where internal restraint is dominant. The domestic code, however, overestimates probability of the crack occurrence judging from the foreign codes and construction experiences of real structures. Therefore, the background of the equation presented in the domestic code was investigated step by step to examine validity of the equation, and, as a result, it was found that the equation is established on a basis of simple elastic model where the change of elastic modulus in an early age is not considered. An advanced assessment strategy was proposed taking into account the hypoelastic model which corresponds to an incremental constitutive equation. The presented procedure resulted in an increased crack index, i.e. decreased crack risk, the value of which depends on various conditions of the mix and structures. Also, a prediction equation of the temperature difference was proposed which can readily consider the effect of the curing condition and ambient temperature in a hand calculation. For further study, the assessment equation may be more classified to strictly consider the characteristics of the mix and structures if the analytical and experimental data are accumulated.

• Korean Journal of Dental Materials
• /
• v.44 no.4
• /
• pp.311-318
• /
• 2017

The purpose of this study was to examine the effects of the curing sequence and polymerization temperature on the flexural strength and microhardness of two provisional resins (Bis-acryl resin composite and polymethyl methacrylate (PMMA)). Polymerization was carried out under various conditions, in air at $25^{\circ}C$ (control) and in hot water (40, 50, 60, 70, and $80^{\circ}C$). The flexural strength test was conducted according to ISO-4049. The Knoop hardness was measured. For the Bis-acryl resin, the temperature up to $50^{\circ}C$ did not increase the flexural strength nor the hardness of the bis-acryl resin composite (p>0.05) but higher temperatures increased the strengths. For the PMMA resin, flexural strength increased with temperatures up to $70^{\circ}C$ and then decreased slightly. Bis-acryl resin composite had higher mechanical properties than the PMMA resin. The effect of heat was more pronounced in the bis-acryl resin composite than in the PMMA resin (p<0.05).

• International Journal of Highway Engineering
• /
• v.11 no.2
• /
• pp.99-109
• /
• 2009

Fine-size exposed aggregate portland cement concrete pavements (FEACP) have surface texture of exposed aggregate by removing upper 2$\sim$3mm mortar of surface of which curing is delayed by using delay-setting agent. FEACPs have advantages of maintaining low-noise and adequate skid-resistance level during the performance period than general portland cement concrete pavements. It is necessary to ensure the durability environmental loading to prevent unexpected distress during the service life of FEACP. In the process of curing, volume change accompanied change in by moisture and temperature could be an important cause of crack in concrete to construct for successful FEACP, The use of chloride containing deicer may accelerate defects of concrete pavement, such as crack and scaling. This study aim to evaluate environmental loading resistance of FEACP, based on the estimation of shrinkage-crack-control-capability by moisture evaporation and scaling by deicer in freeze-thaw reaction.

• Journal of the Korea Concrete Institute
• /
• v.16 no.3 s.81
• /
• pp.407-414
• /
• 2004

The purpose of this study is to evaluate the ability to resist chloride ions penetration of the concrete structure under marine environment in south-east asia especially. In this study, high strength concrete(HSC) with various combination of ordinary portland cement(OPC), blast-furnace slag(SG) and silica fume(SF) are cured 23 and $35^{\circ}C$ considering the site weather, and are cured in water for 3, 7 or 56 days respectively. And to investigate the fundamental properties and the resistance of chloride penetration of various HSC, setting time, slump flow, compressive strength, void and ASTM C 1202 test were conducted. Test results show that the compressive strength of HSC is similar regardless of SG replacement ratio and total charge passed of chloride is the smallest at 40% replacement of SG. The compressive strength of G4FS HSC is, besides, outstandingly high at early age compare with other HSC, but the compressive strength of G4F HSC, which is vary according to curing temperature and condition, most high at the age after 7 days. Total passed charge of HSC get larger in the order G4FS

• Journal of the Korean Society of Propulsion Engineers
• /
• v.13 no.5
• /
• pp.1-6
• /
• 2009

A development of a composite solid propellant is carried out for an application to gas generators as an energy source of rocket system. With HTPB as a propellant binder which has 80% of particle loading ratio, a favorable rheology, and moderate curing properties at the range of $-50^{\circ}{\sim}70^{\circ}C$, AN is selected as the first kind of oxidizer having the characteristics of a low flame temperature, minimal particle residual as well as nontoxic products. AP is the second oxidant for ballistic property control. A series of experiments for the improvement of physical properties were conducted and resulted in the propellant formulation having 30% of strain rate at 8 bar of max. stress.

• Journal of the Korea Concrete Institute
• /
• v.28 no.1
• /
• pp.49-57
• /
• 2016

The aim of this study was to investigate the fundamental properties of pyroclastic flow deposit (PFD), and evaluate the fresh and strength properties of concrete mixed with PFD by indoor tests. The fresh properties, strength properties, shrinkage properties, and durability of the concrete mixed with PFD were also evaluated by outdoor plant tests. the harmful alkali-silica reaction did not occur by mixing concrete with PFD. ages. Moreover, no difficulty was found to be associated with concrete manufacture in the plant because no change in air contents and noticeable slump loss occurred by mixing concrete with PFD. The strength properties, shrinkage properties, and durability of the concrete mixed with PFD were also compared with those of normal concrete. With a suitable temperature control and curing method of concrete, the concrete mixed with PFD is considered to be useful in the construction material field.

• Proceedings of the Korean Institute of Building Construction Conference
• /
• 2006.05a
• /
• pp.35-38
• /
• 2006

This study investigated fundamental properties of lightweight foamed concrete using cement kiln dust (CKD) and both fly ash(FA) and stability agent. Test results showed that concrete incorporating more amounts of admixture decreased slump flow and it caused increase of superplasiticizer in order to secure the fluidity performance. In addition concrete adding stability agent showed stable flow state, resisting segregation of materials and decreasing bleeding capacity. Sinking depth of concrete incorporating 20% of CKD and adding 0.002% of stability agent was indicated at 0mm. For the properties of hardened concrete. compressive strength of concrete incorporating CKD declined due to a lower appearance density, compared with other specimens. The difference of that was not very significant and the value of ail specimen was higher than KS range. Moreover strength of concrete incorporating CKD was even higher at curing temperature $5^{\circ}C$. Tensile strength ratio of concrete incorporating CKD was indicated between 0.50 to 0.59, which is higher value than control concrete. Heat conductivity of concrete incorporating FA was under the KS range while concrete incorporating 20% of CKD was satisfied in KS. Concrete adding stability agent improved insulation performance due to the lower heat conductivity. In conclusion, it is possible that concrete incorporating 20% of CKD and adding 0.002% of stability agent can secure high quality of lightweight foamed concrete.

• Journal of Adhesion and Interface
• /
• v.20 no.4
• /
• pp.146-154
• /
• 2019

In this study, alkoxysilane-functionalized amphiphilic polymer (AFAP), which have hydrophilic segment and hydrophobic segment functionalized by alkoxysilane group at the same backbone, was synthesized and used as a dispersant and control agent for reaction rate in the preparation of colloidally stable organic-inorganic (O-I) hybrid sols. After reaction with fluorosilane compounds, fluorinated O-I hybrid sols were prepared and coated onto glass substrate to form hydrophobic O-I hybrid coating films through low-temperature curing process. Surface hardness and hydrophobicity of cured coating films were varied with type of solvent and composition of AFAP and fluorinated alkoxysilane compounds. At appropriate solvent and composition of fluorinated alkoxysilane compounds, O-I hybrid coating film having high transparency and surface hardness could be prepared, which could be applicable to cover window of solar cell and displays.

• Journal of the Korea Institute of Building Construction
• /
• v.15 no.4
• /
• pp.383-389
• /
• 2015

The objective of this study is to develop mixture proportioning approach of crack controlled lightweight foamed concrete without using high-pressure steam curing processes, as an alternative to autoclaved lightweight concrete blocks (class 0.6 specified in KS). To control thermal cracks owing to hydration heat of cementitious materials, 30% ground granulated blast-furnace slag (GGBS) was used as a partial replacement of ordinary portland cement (OPC). Furthermore, polyvinyl alcohol (PVA) and polyamid (PA) fibers were added to improve the crack resistance of foamed concrete. The use of 30% GGBS reduced the peak value of hydration production rate measured from isothermal tests by 28% and the peak temperature of foamed concrete measured from semi-adiabatic hydration tests by 9%. Considering the compressive strength development, internal void structure, and flexural strength of the lightweight foamed concrete, the optimum addition amount of PVA or PA fibers could be recommended to be $0.6kg/m^3$, although PA fiber slightly preferred to PVA fiber in enhancing the flexural strength of foamed concrete.