• Proceedings of the KIEE Conference
• /
• 1993.07b
• /
• pp.1103-1105
• /
• 1993

Microwave characteristics of the system (1-X) ${Na}_{1/2}{Sm}_{1/2}TiO_3$[NST]-X ${Li}_{1/2}{Nd}_{1/2}TiO_3$[LNT] were investigated. The dielectric constant and unloaded Q were 86,1950 respectively for NST at 3GHz and 80,500 for LNT. 0.4 NST - 0.6 LNT system has the dielectric constant ${\varepsilon}r$=86.2, Q=930(3GHz), temperature coefficient of the resonant frequency ${\tau}f$ = 8 ppm/$^{\circ}C$ when sintered at $1450^{\circ}C$ for 2h.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.21 no.6
• /
• pp.517-523
• /
• 2008

The microwave dielectric properties of $LiNb_3O_8-TiO_2$ based ceramics with low firing agents, CuO, $Bi_2O_3$, $B_2O_3$, $SiO_2$, $TiO_2$, were investigated to improve the sintering condition for the LTCC system. According to the X-ray diffraction and SEM, the ceramics of $LiNb_3O_8-TiO_2$ with low firing agents showed no significant second phases within a range of experiments, and fine microstructures. By adding the low firing agents, the sintering temperature decreased from $1200^{\circ}C$ to $925^{\circ}C$. Based on the results of electrical measurements, the $LiNb_3O_8-TiO_2$ ceramics showed a promising microwave dielectric properties for LTCC applications, those are ${\varepsilon}_r$ (dielectric constant) = 44, Q f (quality factor) = 18000, and ${\tau}_f$ (the temperature coefficient of resonant frequency) = $-1.5\;ppm/^{\circ}C$.

• Journal of the Korean Ceramic Society
• /
• v.39 no.1
• /
• pp.26-32
• /
• 2002

The effects of $Nd_2O_3$ addition to $Q{\cdot}f_{0}(GHz)$ ceramics with ${\varepsilon}_r$ of 126, $Q{\cdot}f_{0}(GHz)$ of 2240 and of $68\;ppm/^{\circ}C$ on their microwave properties were investigated. For the addition of 5 wt% $Nd_2O_3$, the dielectric constant (${\varepsilon}_r$) showed maximum value of 131, then decreased with the further addition of $Nd_2O_3$. $Q{\cdot}f_{0}(GHz)$ value was still increased to 3533 with 9 wt% $Nd_2O_3$ addition, it is influenced by densification of grain boundary. With more addition of $Nd_2O_3$ up to 18 wt%, the abnormal grain growth have influence on the decreasing of $Q{\cdot}f_{0}(GHz)$ value. But with the further addition of $Nd_2O_3$ over 25 wt%, the $Q{\cdot}f_{0}(GHz)$ value was again increased by the effect of the second phase ($Nd_2Ti_2O_7$) forming. The temperature coefficient of resonant frequency (${\tau}_f$) was decreased from $+\;68\;ppm/^{\circ}C$ with the addition of $Nd_2O_3$, reached $0\;ppm/^{\circ}C$ at 12 wt% addition, and became negative with the further addition of $Nd_2O_3$. The optimum microwave dielectric properties were obtained for $0.3CaTiO_3-0.7(Li_{1/2}Nd_{1/2})TiO_3$ with 9 wt% $Nd_2O_3$ sintered at $1425^{\circ}C$ for 3 hrs. The dielectric constant (${\varepsilon}_r$), the $Q{\cdot}f_{0}(GHz)$ value, and the temperature coefficient of resonant frequency (${\tau}_f$) were 108, 3533, and $+\;6\;ppm/^{\circ}C$, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.07b
• /
• pp.682-685
• /
• 2002

The $0.96MgTiO_3-0.04SrTiO_3$ ceramics with $B_2O_3$(10wt%) were prepared by the conventional mixed oxide method. The structural properties were investigated with sintering temperature by XRD. According to the X-ray diffraction pattern of the $0.96MgTiO_3-0.04SrTiO_3$ ceramics with $B_2O_3$(10wt%), the ilmenite $MgTiO_3$ and perovskite $SrTiO_3$ structures were coexisted and secondary phase of the $MgTi_2O_5$ were appeared. In the case of $0.96MgTiO_3-0.04SrTiO_3+B_2O_3$(10wt%) ceramics sintered $1225^{\circ}C$, dielectric constant, quality factor and temperature coefficient of resonant frequency were 19.82, 62,735GHz, $-2.983ppm/^{\circ}C$, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2006.06a
• /
• pp.292-293
• /
• 2006

$ZnNb_2O_6$ ceramics were sintered under the presence of zinc-borosilicate(ZBS) glass and resultant microwave dielectric properties were investigated with a view to applying the composition to LTCC technology. The addition of 10~30 wt% ZBS glass ensured successful sintering below $900^{\circ}C$. In general, increased addition of ZBS glass increased sinterability but it decreased the dielectric properties significantly due to the formation of an excessive liquid and second phases. The sintered $ZnNb_2O_6$ ceramics at $900^{\circ}C$ with 25 wt% ZBS glass demonstrated 15.8 in dielectric constant(${\varepsilon}_r$), 5,400 in quality factor($Q{\times}f_0$), and $-98\;ppm/^{\circ}C$ in temperature coefficient of resonant frequency(${\tau}_f$).

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2002.11a
• /
• pp.350-353
• /
• 2002

The microwave dielectric properties and the microstructures on $Bi_{0.97}Nb_{0.03}O_{4}$doped with $V_{2}O_{5}$ were systematically investigated. $Bi_{0.97}Tm_{0.03}Nb_{0.03}O_{4}$ ceramics sintered at $920-960^{\circ}C$were mainly consisted of orthorhombic and triclinic phases after addition of $V_{2}O_{5}$. The apparent density increased slightly with increasing the $V_{2}O_{5}$ addition. The dielectric $constants(\varepsilon_r)$ also increased with $V_{2}O_{5}$ addition(30-45). The $Q{\times}f_0$ values measured on $Bi_{0.97}Tm_{0.03}NbO_4$ ceramics doped with $V_{2}O_{5}$ were between 2,000 and 12,000[GHz] when the sintering temperatures are in the range of $920-960[^{\circ}C]$. It was confirmed the temperature coefficient of the resonant $frequency(\tau_f)$ can be adjusted from a positive value of $+10[ppm/^{\circ}C]$ to a negative value of $-15ppm/^{\circ}C$ by increasing the amount of $V_{2}O_{5}$. Based on our experimental results, the Bi0.97Tm0.03NbO4(added V2O5) ceramics can be applied to multilayer microwave devices at low sintering temperatures.

• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.16 no.11
• /
• pp.975-978
• /
• 2003

The microwave dielectric properties and the microstructures on B $i_{0.97}$T $m_{0.03}$Nb $O_4$ doped with $V_2$ $O_{5}$ were systematically investigated. B $i_{0.97}$T $m_{0.03}$Nb $O_4$ ceramics sintered at 920-96$0^{\circ}C$ were mainly consisted of orthorhombic and triclinic phases after addition of $V_2$ $O_{5}$. The apparent density increased slightly with increasing the $V_2$ $O_{5}$ addition. The dielectric constants($\varepsilon$$_{r}$) also increased with $V_2$ $O_{5}$ addition(30-45). The Q${\times}$ $f_{0}$ values measured on B $i_{0.97}$T $m_{0.03}$Nb $O_4$ ceramics doped with $V_2$ $O_{5}$ were between 2,000 and 12,000[GHz] when the sintering temperatures were in the range of 920-960[$^{\circ}C$]. It was confirmed that the temperature coefficient of the resonant frequency($\tau$$_{f}$) can be adjusted from a positive value of +10ppm/$^{\circ}C$ to a negative value of -15ppm/$^{\circ}C$ by increasing the amount of $V_2$ $O_{5}$ Based on our experimental results, the B $i_{0.97}$T $m_{0.03}$Nb $O_4$(added $V_2$ $O_{5}$) ceramics can be applied to multilayer microwave devices at low sintering temperatures.ng temperatures.emperatures.ratures.

• Journal of the Microelectronics and Packaging Society
• /
• v.10 no.2
• /
• pp.13-17
• /
• 2003

In this study, new LTCC materials of $ZnWO_4$-LiF system were developed for the application to RF Module fabrication. Pure $ZnWO_4$ must be sintered above $1050^{\circ}C$ in order to obtain up to 98% of full density. The measured dielectric constant ($\epsilon_r$)quality factor ($Q{\times}f0$), and temperature coefficient of resonant frequency ($\tau_f$ were 15.5, 74000 GHz, and $-70ppm^{\circ}C$, respectively. LiF addition resulted in a liquid phase formation at 81$0^{\circ}C$ due to interaction between ZnWO$_4$ and LiF. Therefore, ZnWO$_4$ with 0.5∼1.5 wt% LiF could be densified at $850^{\circ}C$. In the given LiF addition range, the sintering shrinkage increased with increasing LiF content. Addition of LiF slightly lowered the dielectric constant from 15.5 to 14.2∼15 due to lower dielectric constant of LiF. Qxfo value decreased with increasing LiF content. This can be explained in terms of the interaction between LiF and $ZnWO_4$, and inhomogeneity of grain structure.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2007.06a
• /
• pp.298-298
• /
• 2007

Influence of $TiO_2$ on the dielectric properties of the $Bi(Nb_{0.7}Ta_{0.3})O_4$ ceramic with 7 wt% zinc borosilicate(ZBS) glass was investigated as a function of the $TiO_2$ contents with a view to applying this system to LTCC technology. The $Bi(Nb_{0.7}Ta_{0.3})O_4$ ceramic addition of 7 wt% ZBS glass ensured successful sintering below $900^{\circ}C$. But, TCF of $Bi(Nb_{0.7}Ta_{0.3})O_4$ ceramic is large negative values, respectively, it is necessary to adjust to zero TCF for practical applications Therefore, the addition of materials having positive TCF, such as $TiO_2$, might be an effective method for the improvement. In general, increasing addition of $TiO_2$ increased dielectric constant and TCF but it decreased the sinterability and $Q{\tiems}f$ value significantly due to the dielectric property and high sintering temperature of $TiO_2$. $Bi(Nb_{0.7}Ta_{0.3})O_4$ ceramic with 7 wt% ZBS glass and then addition 0.5 wt% $TiO_2$ sintered at $900^{\circ}C$ demonstrated 42 in the dielectric constant(${\varepsilon}_r$), 1,000 GHz in the $Q{\times}f$ value, and $10{\pm}5\;ppm/^{\circ}C$ in the temperature coefficient of resonant frequency(${\tau}_f$).

• Korean Journal of Materials Research
• /
• v.8 no.7
• /
• pp.659-663
• /
• 1998

The effect of Bi-substitution in $BaO.(Nd_{1-x}Bi_x)_2O_3.4TiO_2$ ceramic was studied on the formation of crystal phases, microstructure, and microwave dielectric properties. $BaO.(Nd_{1-x}Bi_x)_2O_3.4TiO_2$, solid solution (0$\leq$x$\leq$0.2) were formed by Bi-substitution into the Nd site of $BaO.(Nd_{1-x}Bi_x)_2O_3.4TiO_2$ ceramics. Average grain size increased with Bi-substitution. Dielectric constant(${\varepsilon}_r$) increased from 84 to U8, and the temperature coefficient of resonant frequency(${\tau}_f$) decreased from 44 ppm/$^{\circ}C$ to -30 ppm/$^{\circ}C$ when Bi contents increased up to x=0.2 in $BaO.(Nd_{1-x}Bi_x)_2O_3.4TiO_2$ solid solutions. $BaO.(Nd_{1-x}Bi_x)_2O_3.4TiO_2$ solid solutions with x=0.04~0.08 showed the most superior microwave dielectric properties, those are ${\varepsilon}_r$= 89-92, Q . f = 5855~6091 GHz, and (${\tau}_f$)= -7.5-7.5 ppm/$^{\circ}C$.