Brittle microstructure created in a heat affected zone (HAZ) during the welding of low alloy steel can be eliminated by post-weld heat treatment (PWHT). If the PWHT is not possible during a repair welding, the controlled bead depositions of multi-pass welding should be applied to obtain tempering effect on the HAZ without PWHT. In order to anticipate and control the tempering effect during the temper bead welding, the definition of temperature curve obtained from the analytical solution was suggested in this research. Because the analytical solution for heat flow is expressed as a mathematical equation of weld parameters, it may be effective in anticipating the effect of each weld parameter on the tempering in HAZ during the successive bead depositions. The reheating effect by the successive bead layer on the brittle coarse grained HAZ formed by earlier bead deposition was estimated by comparing the overlapped distance between the temperature curves in the HAZ. Three layered weld specimens of SA508 base metal with A52 filler were prepared by controlling heat input ratio between layers. The tempering effect anticipated by using the overlapped distance between the temperature curves was verified by measuring the micro-hardness distribution in the HAZ of prepared specimens. The temperature curve obtained from analytical solution was expected as a good tool to find optimal temper bead welding conditions.

• Transactions of the Korean Society of Pressure Vessels and Piping
• /
• v.14 no.1
• /
• pp.58-65
• /
• 2018

The purpose of this study is to develop a Half Nozzle Repair(HNR) process to prevent the leakage from welds on small bore piping in Reactor Coolant System. The Codes & Standards of tempered bead and design requirements of J-Groove welds are reviewed. Automatic machine GTAW welding and machining equipments are developed to perform HNR process. Single pass welding and overlay welding equipments are conducted in order to obtain the optimal temper bead welding process parameters with Alloy 52M filler wire. Coarse grain heat affected zone(CGHAZ) is formed by rapid cooling rate in heat affected zone after welding. Accordingly, a proper temper bead technique is required to reduce CGHAZ in 1-Layer of welds by 2- and 3-Layers. Mock-up tests show that the developed HNR process is possible to meet ASME Code & Standard requirements without any defect.

• Journal of Welding and Joining
• /
• v.30 no.5
• /
• pp.70-75
• /
• 2012

This study is related to the laser weldability of AZ31B magnesium alloy, an all-purpose wrought alloy with good strength and ductility. In general, AZ31B is classified into AZ31B-H24 and AZ31B-O depending on temper designation. Thus, in this study, the laser weldability of AZ31B-H24 and AZ31B-O was investigated and compared. CW Nd:YAG laser was used to produce bead and butt joints. And the effects of welding conditions on the weldability of these joints were examined in detail. As a result of this study, AZ31B-H24 was found to have thinner oxide film and smaller grain size compared with AZ31B-O. Due to such difference, in bead welding, AZ31B-H24 had more wide welding range for full penetration compared with AZ31B-O. Furthermore, it was also confirmed that AZ31B-H24 and AZ31B-O have different welding conditions to obtain stable keyhole in butt welding.

• Proceedings of the KWS Conference
• /
• 2009.11a
• /
• pp.16-16
• /
• 2009

Alloy 82/182로 용접된 원자력 발전소 주기기의 이종 금속 용접부는 장기간 운전 후 응력부식균열(SCC : Stress Corrosion Cracking)에 의한 결함이 나타나게 된다. 2000년대 이후로 원자력 주기기 Alloy 82/182 용접부에서 PWSCC(Primary Water Stress Corrosion Cracking)에 의한 Degradation이 급격히 증가하는 추세를 보이고 있으며, 국내에서도 이와 관련하여 원자력 발전소의 안전성에 대한 Issue 및 대비책에 대한 관심이 고조되고 있다. 이러한 Alloy 600 용접부에 대한 결함을 예방하기 위한 대표적인 기술로써 수명연장 오버레이 기술이 있다. 원자력 주기기 노즐부는 저탄소강으로 제작되어 있으며, 저탄소강에는 제작 시 용접후열처리가 적용된다. 후열처리를 하는 주된 이유는 Tempering을 통해 열영향부의 인성 및 연성의 회복과 강도를 감소시켜 모재와 동등 또는 이 이상의 물성을 갖도록 하는 데 그 목적이 있다. 그러나 수명연장 오버레이의 경우 현장 작업 시에 후열처리가 어렵기 때문에, 이를 대체하기 위한 기술로 템퍼비드 용접을 적용할 경우 후열처리를 면제해 주고 있다. 본 연구에서는 수명연장 오버레이 기술 개발의 일환으로써 저 탄소강에 대한 템퍼비드 용접 기술을 확립하였다. 실험에 사용된 모재는 원자력 주기기의 노즐에 사용되는 SA508 Gr.3 Cl.1을 사용하였으며, 용가재는 Alloy 52 및 52M을 사용하였다. 최적 조건 도출을 위해서 실험 매트릭스를 이용하여 기본 실험을 수행하였으며, 실험에는 자동 GTAW 용접을 적용하였다. 기본 실험을 통해 얻은 최적 조건을 사용하여 PQ 시험을 수행하여 WPS를 확보하였다. 분석은 용접 후 조직 및 경도 시험, 물리시험(인장시험, 굽힘시험 및 충격시험)을 수행하였다.