Although the basalt fiber has superior fire-resistance and chemical resistance, it has many disadvantages in its applications. Generally, the tensile and loop strengths of basalt fiber were decreased with generated frictional heat during industial appplications. To solve this problem, polytetrafluoroethylene (PTFE) coating system was introduced and a sutable coating condition was evaluated. The basalt fiber was pre-treated with triethoxytrifluoropropylsilane (TMTFPS) at various pHs and then coated with PTFE dispersions with penetrating agent sodium bis(2-ethylhexyl)sulfo succinate (DOS-Na) to increase the tensile and loop strengths as well as to reduce the fibril during working. A universial testing machine (Instron Model 3366) was used to measure tensile and loop strengths. When the PTFE dispersion with 0.25 wt% of DOS-Na was coated on the surface of basalt fiber after pre-treating with 5 wt% of PTFE, the highest tensile and loop strengths were reached to 3.5 gf/D and 2.4 gf/D, respectively.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 1992.11a
• /
• pp.136-140
• /
• 1992

The purpose of this research is to develop the lithium secondary battery. This paper describes the preparation, electrochemical properties of nontstoichiometric(NS)-$V_6O_{13}$ and characteristics of Li/$V_6O_{13}$ secondary battery. NS-$V_6O_{13}$ was prepared by thermal decomposition of $NH_4VO_3$ under Ar stream of 140ml/min~180ml/min flow rate. And then, this NS-$V_6O_{13}$ was used for cathode active material. Cathode sheet was prepared by compressing the composite of NS-$V_6O_{13}$, acetylene black(A.B) and teflon emulsion (T.E). Characteristics of the test cell are summarised as follows. Oxidation capacity of NS-$V_6O_{13}$ was about 20% less than its reduction capacity. A part of NS-$V_6O_{13}$ cathode active material showed irreversible reaction in early charge-discharge cycle. This phenomena seems to be caused by irreversible incoporation/discoporation of lithium cation to/from NS-$V_6O_{13}$ host. Discharge characteristics curve of Li/$V_6O_{13}$ cell showed 4 potential plateaus. Charge-discharge capacity was declined in the beginning of cycling and slowly increased in company with increasing of coulombic efficiency. Energy density per weight of $V_6O_{13}$ cathode material was as high as 522Wh/kg~765Wh/kg.