• Journal of Korea Foundry Society
• /
• v.37 no.6
• /
• pp.193-198
• /
• 2017

In this study, volumes of shrinkage and porosity of A356.2 alloys during casting were analyzed as a function of melt temperature, pouring diameter, mold temperature, and Sr content. The temperature of the melt barely affected the shrinkage and porosity formation. The pouring diameter determined the pouring rate, and it was proportional to the shrinkage, yet no relationships with the density of porosity were observed. When the mold was heated at $400^{\circ}C$, shrinkage and porosity in the alloy increased above the one in the mold without heating. However, the mold without heating experienced interior shrinkage and the porosity was mainly distributed near interior shrinkage. The addition of Sr to the melt resulted in more shrinkage and less porosity.