• Proceedings of the Korean Society Of Semiconductor Equipment Technology
• /
• 2005.05a
• /
• pp.139-145
• /
• 2005

In the study, in order to deposit TaN thin film using diffusion barrier and bottom electrode we made the Plasma Assisted ALD equipment and confirmed the electrical characteristic of TaN thin films deposited PAALD method, PAALD equipment depositing TaN thin film using PEMAT(pentakis(ethylmethlyamlno) tantalum) Precursor and $NH_3$ reaction gas is aware that TaN thin film deposited of high density and amorphous phase with XRD measurement The degree of diffusion and react ion taking place in Cu/TaN(deposited using 150 W PAALD)/$SiO_2$/Si systems with increasing annealing temperature was estimated from MOS capacitor property and the $SiO_2(600\;\AA)$/Si system surface analysis by C-V measurement and secondary ion material spectrometer(SIMS) after Cu/TaN/$SiO_2(400\;\AA)$ system etching. TaN thin film deposited PAALD method diffusion barrier have a good diffusion barrier property up to $500^{\circ}C$.

• Journal of the Semiconductor & Display Technology
• /
• v.4 no.2 s.11
• /
• pp.39-43
• /
• 2005

In the study, in order to deposit TaN thin film for diffusion barrier and bottom electrode we made the Plasma Assisted ALD equipment and confirmed the electrical characteristics of TaN thin films grown PAALD method. Plasma Assisted ALD equipment depositing TaN thin film using PEMAT(pentakis(ethylmethlyamino) tantalum) precursor and NH3 reaction gas is shown that TaN thin film deposited high density and amorphous phase with XRD measurement. The degree of diffusion and reaction taking place in Cu/TaN (deposited using 150W PAALD)/$SiO_{2}$/Si systems with increasing annealing temperature was estimated for MOS capacitor property and the $SiO_{2}$, (600${\AA}$)/Si system surface analysis by C-V measurement and secondary ion material spectrometer (SIMS) after Cu/TaN/$SiO_{2}$ (400 ${\AA}$) layer etching. TaN thin film deposited PAALD method diffusion barrier have a good diffusion barrier property up to 500$^{\circ}C$.

• Proceedings of the Korean Vacuum Society Conference
• /
• 2012.02a
• /
• pp.377-377
• /
• 2012

Microprocessor technology now relies on copper for most of its electrical interconnections. Because of the high diffusivity of copper, Atomic layer deposition (ALD) $TaN_x$ is used as a diffusion barrier to prevent copper diffusion into the Si or $SiO_2$. Another problem with copper is that it has weak adhesion to most materials. Strong adhesion to copper is an essential characteristic for the new barrier layer because copper films prepared by electroplating peel off easily in the damascene process. Thus adhesion-enhancing layer of cobalt is placed between the $TaN_x$ and the copper. Because, cobalt has strong adhesion to the copper layer and possible seedless electro-plating of copper. Until now, metal film has generally been deposited by physical vapor deposition. However, one draw-back of this method is poor step coverage in applications of ultralarge-scale integration metallization technology. Metal organic chemical vapor deposition (MOCVD) is a good approach to address this problem. In addition, the MOCVD method has several advantages, such as conformal coverage, uniform deposition over large substrate areas and less substrate damage. For this reasons, cobalt films have been studied using MOCVD and various metal-organic precursors. In this study, we used $C_{12}H_{10}O_6(Co)_2$ (dicobalt hexacarbonyl tert-butylacetylene, CCTBA) as a cobalt precursor because of its high vapor pressure and volatility, a liquid state and its excellent thermal stability under normal conditions. Furthermore, the cobalt film was also deposited at various $H_2/NH_3$ gas ratio(1, 1:1,2,6,8) producing pure cobalt thin films with excellent conformality. Compared to MOCVD cobalt using $H_2$ gas as a reactant, the cobalt thin film deposited by MOCVD using $H_2$ with $NH_3$ showed a low roughness, a low resistivity, and a low carbon impurity. It was found that Co/$TaN_x$ film can achieve a low resistivity of $90{\mu}{\Omega}-cm$, a low root-mean-square roughness of 0.97 nm at a growth temperature of $150^{\circ}C$ and a low carbon impurity of 4~6% carbon concentration.