• Journal of Korea Foresty Energy
• /
• v.17 no.1
• /
• pp.36-46
• /
• 1998

The aim of this study was to develop the noise and vibration damping wood-based composites by using viscoelastic polymer materials. Polyvinylchloride(PVC) was plasticized with 20-140 phr bis(2-ethylhexyl) phthalate(DOP) and the dynamic tensile mechanical properties were measured at 110Hz and approximate temperature range -100 to 150$^{\circ}$ using a Rheovibron Instrument. The PVC/DOP blends were shown to be compatible in all proportions, and both T(E”$_{max}$) and T(tan${\delta}_{max}$) shifted to the lower temperature side as the DOP content increased. The vibration damping properties of wood/polymer composites were measured using the Rheovibron instrument in a bending mode. The composite damping factor(tan ${\delta}_{c}$) of wood /PVC-DOP/wood sandwich structure correlated with the loss factor and that of the coated structure correlated with the loss modulus(E”) of the polymer layer. In addition, the sandwich structure was found to be more effective in damping than the coated structure. The logarithmic decrement (${\Delta}$c) curve of a sandwich structure, which was determined by the free-free flexural vibration method was similar in shape to the tan ${\delta}_{c}$ curve.

• Elastomers and Composites
• /
• v.56 no.4
• /
• pp.209-216
• /
• 2021

In this study, we observed the mechanical properties, thermal stability, and low temperature sealing performance of fluorosilicone elastic composites. When the blend ratio of Phenyl vinyl methyl silicone (PVMQ) was increased, the tensile strength, modulus at 100%, and compression set were decreased. The thermal stability of fluorosilicone elastic composites showed a similar tendency. These were caused by poorer green strength of PVMQ than Fluorosilicone rubber (FVMQ). The change in the tensile strength and elongation at -40℃ showed a decreasing tendency with increasing PVMQ blend ratio. By increasing the PVMQ blend ratio, low-temperature performance was improved. The Dynamic mechanical analysis (DMA) results showed that T_g was decreased and low-temperature performance was improved with increasing PVMQ blend ratio. However tanδ was decreased becaused of the poor green strength and elasticity of PVMQ. From a hysteresis loss at -40℃, the hysteresis loss value was increased and fluorosilicone elastic composites showed the decreasing tendency of elasticity with increasing PVMQ blend ratio. From the TR test, TR10 was decreased with increasing PVMQ blend ratio. FS-4 (45% PVMQ blended composites) showed a TR10 of -68.0℃ that was 5℃ lower than that of FS-1 (100% FVMQ). The gas leakage temperature was decreased with increasing PVMQ blend ratio. The gas leakage temperature of FS-4 was -69.2℃ that was 5℃ lower than that of FS-1. Caused by the polymer chain started to transfer from a glassy state to a rubbery state and had a mobility of chain under T_g, the gas leakage temperature showed a lower value than T_g. The sealing performance at low temperature was dominated by T_g that directly affected the mobility of the polymer chain.