• 열처리공학회지
• /
• 제21권4호
• /
• pp.205-212
• /
• 2008

Characteristics of microstructures, mechanical properties and formability of two Al-20Si-5Fe-2Ni alloys produced by gas atomizing (P/M) and spray forming (S/F) respectively were compared at temperatures up to $560^{\circ}C$. Room temperature hardness values and tensile strengths of both alloys were increased in accordance with temperature after heat treatment above $300^{\circ}C$. The highest values of hardness and tensile strength of both alloys were obtained at $490^{\circ}C$. It was interpreted that increase in hardness and tensile strength according to heating temperature between $300{\sim}490^{\circ}C$ was mainly related to increase in internal stress between Al matrix and reprecipitated particles. S/F alloys showed better formability and wear property than P/M alloys due to the homogenity of microstructures above $300^{\circ}C$.

• 열처리공학회지
• /
• 제33권4호
• /
• pp.161-172
• /
• 2020

The tensile property of A5082 and A6060 aluminium wrought alloys was investigated, in terms of the strain rate sensitivity on alloy conditions by heat treatment and bake hardenability on pre-strain prior to strain ageing. The tensile test was carried out in a range of strain rate of 4.17 × 10^-5 s^-1 ~ 4.17 × 10^-5 s^-1 in room temperature and the nominal range of pre-strain was 3.0 ~ 10.5%. The tensile deformation of A5082 alloys is characterized as typical case of dynamic strain ageing with negative strain rate sensitivity for all conditions, and the tensile strength indicates a similar level regardless of alloy conditions, except only in full annealed condition. The stress-relief annealing on A6060 alloys can induce practical decrease in strength level of over approximately 100 MPa without any ductility loss, compared to as-rolled condition, while a full annealed and aged condition leads remarkable strengthening effect with the decrease of tensile elongation. Additionally, the bake hardenability of A5082 alloy by strain ageing indicates a negative dependence upon the increase of pre-strain, while A6060 alloy exhibits a positive sign even in low level relatively compared with conventional SPCC.

• 한국주조공학회지
• /
• 제38권5호
• /
• pp.95-102
• /
• 2018

The dependence of the tensile properties on variations in the porosity of A356 aluminium alloys was investigated in terms of the quality index of the tensile properties based upon the ultimate tensile strength and elongation as well as the variation of the strength coefficient and strain-hardening exponent with regard to a T6 treatment. The test specimens were prepared by low-pressure die-casting and a subsequent T6 treatment, and the experimental results of a tensile test carried out at room temperature were compared to the theoretical description using a modified constitutive model. The nominal value of the quality index of A356 alloys increases gradually with a lapse of the ageing time upon a T6 treatment, despite the fact that this value is temporarily decreased during the initial stage of ageing from a solutionised condition. Additionally, the quality index depends practically upon the porosity variation with a power law relationship without regard to whether in solutionised or artificial aged conditions. The theoretical description indicates that the strength coefficient directly determines the nominal level of the quality index. Moreover, the overall dependence of the quality index on the porosity variation is remarkably weakened with an increase in the tensile strain, whereas the quality index depends sensitively upon the porosity variation with a low value of the strain-hardening exponent.

• 한국안전학회지
• /
• 제16권3호
• /
• pp.61-67
• /
• 2001

In this study the electrical and mechanical characteristics of PET films ore analyzed after plasma surface treatment. After plasma treatment, the surface potential decay, surface potential and dielectric property were evaluated to analyze the electrical insulating property, and the tensile strength was measured as the mechanical characteristic. When plasma treatment was conducted for less than 10 minutes, it was found that the electrical insulating property was improved through evaporation of low molecular weight materials md cleaning of surface. However, for more than 10 minutes, the insulating property of plasma treated PET films was decreased due to excessive discharge energy. The tensile strength was hardly changed by Plasma treatment.

• 한국주조공학회지
• /
• 제32권1호
• /
• pp.38-43
• /
• 2012

The effects of Mg and Cu amounts on the casting characteristics and tensile property of Al-Zn-Mg-Cu alloys were investigated for the development of high strength aluminium alloys for gravity mold casting. Increase of copper amounts in Al-6%Zn-3%Mgy% Cu alloys resulted in reduction of the fluidity of these alloys and had little effects on the tensile property of these alloys. Increase of magnesium amounts from 1.0wt% to 3.3wt% in Al-6%Zn-x%Mg-0.5%Cu alloys resulted in reduction of the elongation of these alloys from 12% to 3% and increase of the tensile strength of these alloys from 340MPa to 450MPa, but had little effects on the fluidity of these alloys.

• 열처리공학회지
• /
• 제4권1호
• /
• pp.37-41
• /
• 1991

In this study, the effect of solution treatment temperature on the tensile property in intermediate thermo-mechanical treated Al-Li alloys are investigated. After the intermediate thermo-mechanical treated Al-Li, Al-Li-Mg and Al-Li-Mg-Zr alloys were solution treated at various temperatures (500, 520 and $540^{\circ}C$), these were aged at $190^{\circ}C$, $240^{\circ}C$ and tested tensile properties. The results obtained from the experiment are as follows ; 1) The optimum solution heat-treatment temperature is $540^{\circ}C$ for a Al-Li alloy, and the recrystallized grain size is about $70{\mu}m$. 2) The optimum solution heat-treatment temperature is $500^{\circ}C$ for a Al-Li-Mg alloy, and the recrystallized grain size is the most coarse in all alloys. 3) The tensile property is independent of the solution treatment temperature in a Al-Li-Mg-Zr alloy, and the recrystallized grain size is the finest owing to addition of Zr.

• 한국정밀공학회:학술대회논문집
• /
• 한국정밀공학회 2005년도 춘계학술대회 논문집
• /
• pp.220-224
• /
• 2005

The technology trend of Flat Panel Display (FPD) equipments have been demanded that there are compact and multi-function. Therefore, nano/micro scale patterned on polymeric materials of Back Light Unit (BLU) in Liquid Crystal Display (LCD) that has been investigated. This paper describes a series of Horizontal Type Micro Tensile Tester that were carried out to investigate the load strain distance performance of typical polymeric material sheets. The polymeric materials film that micro size shaped specimens for tensile test are used by Cold-Isostatic-Press (CIP). Test equipment is Horizontal type Micro Tensile Tester that is presented to measure the micro scale mechanical property of thin film for FPD. This paper presents which easy testing tools measure for micro patterned on polyethylene (PET) specimens.

• Journal of Welding and Joining
• /
• 제33권5호
• /
• pp.31-34
• /
• 2015

Microstructure and tensile property in the weld heat-affected zone (HAZ) of austenitic Fe-Mn-Al-C low density steels were investigated through transmission electron microscopy analysis and tensile tests. The HAZ samples were prepared using Gleeble simulation with high heat input welding condition of 300 kJ/cm, and the HAZ peak temperature of $1200^{\circ}C$ was determined from differential scanning calorimetry (DSC) test. The strain- stress responses of base steels showed that the addition of V improved the tensile and yield strength by grain refinement and precipitation strengthening. Tensile strength and elongation decreased in the weld HAZ as compared to the base steel, due to grain growth, while V-added steel had a higher HAZ strength as compared than V-free steel.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2001년도 춘계학술대회논문집A
• /
• pp.483-488
• /
• 2001

Until now, the tensile properties of materials can be obtained just in accordance with conventional tensile testing methods which are described in several standards such as ASTM (American Society for Testing and Materials) standard and BS (British Standard). For some cases including on-service facility materials, however, the standard testing methods cannot be applicable due to the destructive testing procedure and specimen size requirement. Therefore, simple, non-destructive and advanced indentation technique was proposed. This test measures indentation load-depth curve during indentation and analyzes the mechanical properties related to deformation and fracture. In this paper, the research trend of non-destructive evaluation of tensile properties using AIS (advanced indentation system) and its application fields are reviewed and discussed.

• Journal of Welding and Joining
• /
• 제14권4호
• /
• pp.71-78
• /
• 1996

The effect of chemical composition on mechanical properry and corrosion resistance of austenitic stainless steel was investigated. The main results obtained were as follows : 1. There was a linear relationship between the tensile strength of stainless steel and the $Cr_{eq}/Ni_{eq}$. The larger the $Cr_{eq}/Ni_{eq}$ was the higher the tensile strength of stainless steel. 2. There was a good correlationship between $Cr_{eq}/Ni_{eq}$ and intergranular, gerneral corrsion rate. 3. Intergranular corrosion rate decreased linearly with increasing Cr content. 4. General corrosion rate decreased linearly with increasing Ni content. 5. Logarithm corrosion rate of intergranular and general corrosion has a linear relationship with all of the factor of $Cr_{eq}/Ni_{eq}$, Cr and Ni content.