• Journal of the Korean Ceramic Society
• /
• v.11 no.3
• /
• pp.19-26
• /
• 1974

Mechanical properties of the system PbO-B2O3-V2O5 low melting glass during crystallization by heat-treatment were investigated. Wettability of the system PbO-B2O3-V2O5 was excellent and appropriate for commercial sealing as a low melting solder glass. Crystals, during heat-treated at 30$0^{\circ}C$ of the system PbO-B2O3-V2O5 were $\beta$-4PbO.B2O3, 5PbO.4B2O3, and Pb2V2O7 mainly. The percent of crystallinity was 82$\pm$5%. Mechanical properties of the system PbO-B2O3-V2O5 were influenced not only by the differences of density and coefficient of thermal expansion and the stress induced from the difference in the density and coefficient of thermal expansion between glass phase and crystals but also crystallization conditions.

• Journal of the Korean Ceramic Society
• /
• v.50 no.1
• /
• pp.57-62
• /
• 2013

We investigated the thermal and electrical properties of the $B_2O_3-ZnO-Bi_2O_3$ glass system as a sealing material in sheath heater modules. A composition with over 90 wt% $Bi_2O_3$ in the $B_2O_3-ZnO-Bi_2O_3$ system was glassified by controlling the cooling rate. The glass transition temperature and thermal expansion coefficient in bismate glass could be controlled by the minor ingredients of ZnO, $SiO_2$, $BaO_2$, and $K_2O$. The $B_2O_3-ZnO-Bi_2O_3$ glass system bonded well to metal, and bismate glass insulating properties were comparable to those of bismate glass $B_2O_3-ZnO-PbO$ glass system in a sheath heater module.

• Journal of the Korean Society of Safety
• /
• v.20 no.4 s.72
• /
• pp.29-33
• /
• 2005

In this paper, reflectance and the dielectric characteristics for $P_2O_5-ZnO-BaO$ system and $SiO_2-ZnO-B_2O_3$ system have been investigated as a function of contents of $TiO_2$. The reflectance was decreased with increasing the contents of $TiO_2$ and the reflectance of $P_2O_5-ZnO-BaO$ system was lowered than that of $SiO_2-ZnO-B_2O_3$ system. The dielectric constant of $P_2O_5-ZnO-BaO$ system was higher than $SiO_2-ZnO-B_2O_3$ system, and the dielectric constant in the both system was increased with increasing of $TiO_2$ contents. This can be explained as the space charge effects. These results are could be applied to the under plate dielectrics of PDP required high reflective ratio and breakdown strength.

• Journal of the Korean Ceramic Society
• /
• v.20 no.3
• /
• pp.236-242
• /
• 1983

The purpose of present study is to find the structures physical properties and their inter-relations in the system of (60-x) PbO.xMO.$40B_2O_3$ glasses where MO represents for ZnO and CdO. The experiments such as differential thermal analysis infrared spectral analysis X-ray diffraction analysis density and thermal expansion measurements have been done. From infrared spectral analysis the structural units of glasses and the corresponding crystallized glasses were com-posed of $BO_3$ triangles and $BO_4$ tetrahedra. These basic units found in $PbO-B_2O_3$ binary glass system did not charge even though the divalent metallic oxides were substituted for PbO. The structures of these ternary glasses were more coalescenced than $PbO-B_2O_3$ binary glass system. This fact was supported bydecrease in thermal expansion coeffici-ent and molar volume with substitution of divalent metallic oxide for PbO. Crystalline phases obtained from the heat treatment of the $PbO-ZnO-B_2O_3$ glasses were 4PbO.2ZnO.$5B_2O_3$ PbO.2ZnO.$B_2O_3$ and unknown phases.

• 전자공학회논문지 IE
• /
• v.43 no.4
• /
• pp.8-12
• /
• 2006

In this paper, reflectance and the dielectric characteristics for $P_2O_5$-ZnO-BaO system and $SiO_2-ZnO-B_2O_3$ system have been investigated as a function of contents of $TiO_2$. The reflectance was decreased with increasing the contents of $TiO_2$ contents, and the reflectance of $P_2O_5$-ZnO-BaO system was lowered than that of $SiO_2-ZnO-B_2O_3$ system. The dielectric constant of $P_2O_5$-ZnO-BaO system was higher than $SiO_2-ZnO-B_2O_3$ system, and the dielectric constant in the both system was increased with increasing of $TiO_2$ contents. This can explained as the space charge effects. These results are could be applied to the lower dielectrics layer of PDP required high reflective ratio and breakdown strength.

• 한국정보디스플레이학회:학술대회논문집
• /
• 2004.08a
• /
• pp.1099-1102
• /
• 2004

For the development of Pb-free low temperature sintering glass frits, $BaO-B_2O_3-SiO_2$ system was examined. The content of BaO and $B_2O_3$ was changed when the content of $SiO_2$ was fixed to 10 mol%. When the content of BaO was more than 60 mol% devitrification was observed. In the sintering temperature range between 520${\sim}$620 $^{\circ}C$, the optimum sintering temperature decreased as the content of BaO increased. When BaO ${\geq}$45 mol%, the glasses were crystallized after sintering. Candidate compositions are suggested in $BaO-B_2O_3-SiO_2$ system, which can replace the PbO containing glass system.

• Journal of the Korean Ceramic Society
• /
• v.27 no.5
• /
• pp.583-588
• /
• 1990

Glass films in the binary system B2O3-SiO2 and Al2O3-SiO2 were prepared on soda-lime-silica slide glass by the dip-coating technique from TEOS and boric acid or aluminum nitrate. Thickness of the films varying with viscosity and withdrawal speed were measured and effect of composition and firing temperature on the properties such as transmittance and refractive index were investigated. nM2O3.(100-n)SiO2(M=B or Al) films containing up to 20mol% B2O3 and 40mol% Al2O3 were transparent. Maximum transmittance at visible range were obtained for the sample containing 15mol% Ba2O3 and 32.5mol% Al2O3 and heat-treated at 50$0^{\circ}C$, respectively. Refractive index of the film containing 15mol% B2O3 was mininum in the B2O3-SiO2 binary system and minimal refractive index was appeared at the film containing 32.5mol% Al2O3. In IP spectra, addition of B2O3 were increased absorption peak intensity of B-O and Si-O-B bond and addition of Al2O3 were decreased absorption peak intensity of Si-O bond, respectively.

• Journal of the Korea Institute of Information and Communication Engineering
• /
• v.5 no.5
• /
• pp.908-915
• /
• 2001

In this paper, it is analyzed theoretically that the performance degradation, caused by carrier frequency offset, in an OFDM/M-ary PSK system. Then, when Turbo coding is adopted to an OFDM/M-ary PSK system, the degree of performance enhancement is evaluated. Finally, the maximum frequency offset is calculated to satisfy the BER performance required in a Turbo coded OFDM/M-ary PSK system. As results of analysis, it is shown that the more the number of M-ary is, the worse the BER performance is. Moreover, 7dB, 9dB, and 17dB of $E_b/N_o$ are required in QPSK, 8PSK and 16PSK systems, respectively in order to satisfy the error performance, $BER=10^{-3}$ for voice communication. If $E_b/N_o$ are 10㏈ and 15㏈, the frequency offset should be below 0.05 and 0.075, respectively, for voice communication. When Turbo coding is adopted to an OFDM/M-ary PSK system, the less the number of M-ary is, the greater the performance enhancement of Turbo coding is. If the number of a M-ary system of the system is below 16, it is found that required $E_b/N_o$ is about 8dB to satisfy $BER=10^{-5}$ Moreover, in the system the Turbo coding scheme, voice communication is available with greatly low$E_b/N_o$, and 8dB of $E_b/N_o$ is enough for data communication regardless of the permission range of frequency offset.

• Journal of the Korean Ceramic Society
• /
• v.22 no.3
• /
• pp.35-40
• /
• 1985

The composition of the base glass was determined to be $Na_2O$ 15, $Fe_2O_3$ 35, $B_2O_3$ 0~20, $P_2O_5$ 30~50 by mole percent. The heating temperature for nucleation was determined by means of thermal expansion curve. Crystalline phases were investigated by X-ray diffraction method and I.R Spectra. Electrical conductivities of glass spec-imens were observed in the temperature range 25~20$0^{\circ}C$ The activation energies of these specimens were caculated. The results obtained were as follows : 1) The limit composition of the melts 15mol% $Na_2O$ 35mole% $Fe_2O_5$ 20mole% $B_2O_3$ 30mole% $P_2O_5$ was able to be formed into desired shapes during cooling, . 2) In the measurement of d. c conductivity($\delta$) on the glasses in the system $15Na_2O-35Fe_2O_3$-$B_2O_3$-(50-x) $P_2O_5$ the values decreased by replacing 5 mole% $P_2O_5$ with $B_2O_3$ 3) The d. c conducties of heat treated samples were increased by replacing $P_2O_5$ with $B_2O_3$ 4) $B_2O_3$ contributed to precipitate crystals such as${\gamma}$-$Fe_2O_3$ $Fe_3O_4$ which had the advantage of electronic conduction in heat treated samples. 5) The slope plotted Log($\delta$) versus 1/T in this glass system was linear in the measured temperature range.

• Journal of the Korean Ceramic Society
• /
• v.23 no.6
• /
• pp.25-32
• /
• 1986

Phase spearated glass is heterogeneous in microscopic point of view and the heterogeneities affect the structures of glasses. In the present work the phase separation of $BaO-B_2O_3$ glass system was investigated and the effect of $P_2O_5$ on the phase separation and crystallization was also studied in the above system. Experiments such as scanning electron microscopy X-ray diffraction and infrared spectroscopy were performed. Phase separation with $B_2O_3$ rich phase matrix and BaO rich phase droplet was observed for the glasses containing less than 6 mole% of BaO while the opposite morphology of phase separation was found for the glasses containing more than 7 mole% of BaO. Phase separation region was extended up to the glass with 22mole% of BaO when the amount of $P_2O_5$ was increased. The heat-treated glasses crystallized to BaO.$4B_2O_3$$P_2O_5$ hindered the glass from the crystalli-zation.