• Journal of the Microelectronics and Packaging Society
• /
• v.21 no.4
• /
• pp.57-62
• /
• 2014

Using flexible bismaleimide-triazine co-polymer as a substrate, inkjet-printed Cu films were also investigated for low-cost and process feasibility of flexible electronics. After annealing at $200^{\circ}C$ for 1 h under various reducing ambient, surface color was changed to red and electrical resistivity was decreased to the level of conductor under formic acid ambient. However, its resistivity was much higher than conventional copper films due to surface crack. In order to reduce the residual film stress after annealing, additional isothermal treatment was inserted before anneal hiring the stress relaxation applied in processes of amorphous materials. As a result, no surface crack was observed and electrical resistivity of $3.4{\mu}{\Omega}cm$ was measured after annealing at $230^{\circ}C$ with stress relaxation while electrical resistivity of $7.4{\mu}{\Omega}cm$ was observed after normal annealing without relaxation. The effect of stress relaxation was also confirmed by observing surface crack after decreasing the relaxation time to 0 min.

• Korean Chemical Engineering Research
• /
• v.44 no.2
• /
• pp.160-165
• /
• 2006

A Pd-Cu-Ni alloyed hydrogen membrane has fabricated on porous nickel support formed by nickel powder. Porous nickel support made by sintering shows a strong resistance to hydrogen embrittlement and thermal fatigue. Plasma surface modification treatment is introduced as pre-treatment process instead of conventional HCl wet activation. Nickel was electroplated to a thickness of $2{\mu}m$ in order in to fill micropores at the nickel support surface. Palladium and copper were deposited at thicknesses of $4{\mu}m$ and $0.5{\mu}m$, respectively, on the nickel coated support by DC sputtering process. Subsequently, copper reflow at $700^{\circ}C$ was performed for an hour in $H_2$ ambient. And, as a result PdCu-Ni composite membrane has a pinhole-free and extremely dense microstructure, having a good adhesion to the porous nickel support and infinite hydrogen selectivity in $H_2/N_2$ mixtures.

• Journal of Surface Science and Engineering
• /
• v.49 no.3
• /
• pp.265-273
• /
• 2016

The effects of surface modification by nitric acid on the pre-treatment of electroless copper plating were investigated. Copper was electroless-plated on the nitric acid treated graphite activated by a two-step pre-treatment process (sensitization + activation). The chemical state and relative quantities of the various surface species were determined by X-ray photoelectron spectroscopy (XPS) after nitric acid modification or pre-treatment. The acid treatment increased the surface roughness of the graphite due to deep and fine pores and introduced the oxygen-containing functional groups (-COOH and O-C=O) on the surface of graphite. In the pre-treatment step, the high roughness and many functional groups on the nitric acid treated graphite promoted the adsorption of Sn and Pd ions, leading to the uniform adsorption of catalyst ($Pd^0$) for Cu deposition. In the early stage of electroless plating, a lot of tiny copper particles were formed on the whole surface of acid treated graphite and then homogeneous copper film with low variation in thickness was formed after 30 min.

• Journal of the Korean Society for Heat Treatment
• /
• v.31 no.2
• /
• pp.41-48
• /
• 2018

In this study, microstructural changes due to extrusion, rolling and heat treatment were studied to fabricate Al-4.0wt%Zn-1.5wt%Mg-0.9wt%Cu alloys with homogeneous microstructure suitable for metal cases of smart phones and electronic products fabricated through plastic working. After extrusion microstructure and texture were developed very differently on the surface and inside. Inside, coarse grains were formed and a strong Cube component orientation was developed. On the surface, a weak texture was developed with small grains. After 72% cold rolling the intensity of the Cube component orientation was lower, and uniform texture was developed in all the layers and the R-value was uniformly predicted. After recrystallization, the grain size difference between at the surface and the inside is smaller, when 72% rolling was performed, indicating that a uniform structure is formed. Texture develops almost randomly after recrystallization and exhibits uniform R-values at all layers.

• Resources Recycling
• /
• v.10 no.2
• /
• pp.27-33
• /
• 2001

Reusing of electroless Ni-Cu-P waste solution was investigated in the plating time, plating rate, solution composion and deposit. Plating time of nickel-catalytic surface took longer than that of zincated-catalytic surface. Initial solution with 50f) waste solution additive at batch type was possible to reusing of waste solution. Plating time of initial solution at continuous type took longer 10 times over than that of batch type. Plating time of 50% waste solution additive at continuous type took longer 3.7 times over than that of batch type. Component change of nickel-copper for electroless deposition was greatly affected by depolited inferiority and larger decreased plating rate.

• Journal of Power System Engineering
• /
• v.14 no.4
• /
• pp.50-55
• /
• 2010

In order to investigate tribological effects of nano copper particles impregnated(CuN) on surface polytetrafluoroethylene(PTFE) on sealing wear and an experimental study was carried out to determine the wear behavior of copper nano-particles impregnation two kind thickness in super critical $CO_2$ liquid. Experimental results showed that the friction coefficients of CuN PTFE at the low sliding speed(0.44m/s) and the oil temperature ($60^{\circ}C$) were higher than that of virgin PTFE. And a thin nano copper particles impreganated thickness was formed on the surface in the PTFE and the specimen with this treatment has much better friction properties than the original one. Fortunately, at the high load(80 N) and the oil temperature, the friction coefficient of CuN PTFE was lower than that of virgin PTFE. This evidenced the load carrying capacity of CuN PTFE was much better than that of virgin PTFE under the high load condition(80 N) specially. Therefore, it can be concluded that the friction coefficient variation of CuN PTFE is very small but its wear rate decreases greatly with increase in sliding speed.

• Resources Recycling
• /
• v.12 no.1
• /
• pp.18-24
• /
• 2003

Reusing of electroless Ni-Cu-B waste solution was investigated in the plating time, plating rate, solution composition and deposit. Plating time of nickel-catalytic surface took longer than that of zincated-catalytic surface. Initial solution with 40% waste solution additive at batch type was possible to reusing of waste solution. Plating time of initial solution at continuous type took longer 6 times over than that of batch type. Plating time of 40% waste solution additive at continuous type took longer 2 times over than that of batch type. Component change of nickel-copper for electroless deposition was greatly affected by deposited inferiority and larger decreased plating rate.

• Proceedings of the Korean Institute of Surface Engineering Conference
• /
• 2011.05a
• /
• pp.205-206
• /
• 2011

Cu thin films for electromagnetic wave shielding were prepared on PET film and Ni-coated PET film by using Dry and Wet coating method, such as evaporation method, DC sputtering method and copper sulfate($CuSO_4$). After that, Zn thin film and Ni thin film were prepared onto the Cu thin films by using evaporation dry process and Ni electro plating wet process as a finishing treatment, respectively. The result of conductivity test and corrosion resistance test revealed Cu thin films which were formed with bigger grain size and high Cu composition rate have superior properties. Zn thin film by dry evaporation process and Ni thin film by wet electro plating process on Cu thin films were largely contributed to corrosion resistance. However, Ni thin film by wet process made conductivity of all specimen worse, the other hand, Zn thin film by dry process made it better to improve condictivity of specimens just prepared by dry process.

• Journal of Surface Science and Engineering
• /
• v.29 no.5
• /
• pp.478-481
• /
• 1996

Disproportionation reaction is very important and interesting reaction to be applied to such surface treatment as metal, alloy, compound coating, a surface etching and so on. In gaseous system, the reaction of Al chloride is applied to Al and Al alloy coating, and the similar reaction of Ti chloride is also used for Ti, Ti alloy and Ti compound coating. As for aqueous system, this reaction is utilized to such metal coat as Sn etc. and metal etching such as Cu, Fe and so on. Also in molten salts system, this reaction has many application for surface treatment like metal, alloy and compound coatings for corrosion, wear, heat resistance and so forth. For instance, carbide film, nitride film, boride film, alloy film, quite new different film from the components of substrate material are coated in single and multiple component film system by the disproportionation reaction.

• Journal of the Microelectronics and Packaging Society
• /
• v.17 no.2
• /
• pp.11-20
• /
• 2010

The effects of heat treatment on matte pure tin-plated Cu leadframes at high temperature and humidity conditions were investigated. After 1800 hrs of storage at $55^{\circ}C/85%$ RH, approximately 14.5 ${\mu}m$ long striation-shaped whiskers were observed on the surface of the without postbake treatment (WOPB) samples, while no whiskers were found in with postbake treatment (WPB) samples. The preferred orientations of Sn grains in WOPB and WPB sample did not change after the postbake treatment at $125^{\circ}C$ for 1 hr. However, both changed from (112) to (321) and (101), respectively, after 1800 hrs of storage at $55^{\circ}C/85%$ RH. The tensile stress of 8 MPa generated in as-plated sample was changed to a compression stress of 17 MPa after 2 days in room temperature storage. Due to the grain growth during postbake treatment, the WPB samples have more regular grains than the WOPB samples. In the as-plated sample, 0.32 ${\mu}m$ thickness of planar intermetallic compound (IMC) was observed. The IMCs in the WOPB and WPB samples had two distinct layers with large grains of $Cu_6Sn_5$ and with small grains of ${\eta}-Cu_{6.26}Sn_5$.