• Elastomers and Composites
• /
• v.43 no.2
• /
• pp.113-123
• /
• 2008

Epoxy resins are thermoset polymers that exhibit good adhesion, creep resistance, heat resistance, and chemical resistance. These polymers, however, give poor resistance to crack propagation and low impact strength. In this study, epoxy/carboxyl-terminated butadiene acrylonitrile (CTBN) and epoxy/amine-terminated butadiene acrylonitrile (ATBN) composites were prepared with different ratio of CTBN and ATBN to improve low impact strength of epoxy resin. The impact strength of epoxy/elastomeric composites shows high values with increasting nonpolar surface free energy while the tensile strength and the glass transition are decreased. The highest surface free energy, impact strength observed when 15 phr CTBN and 15 phr ATBN added, respectively. It can be concluded that as liquid rubber to improve impact strength of epoxy resin, ATBN is more preferable to CTBN.

• Journal of Technologic Dentistry
• /
• v.39 no.1
• /
• pp.43-52
• /
• 2017

Purpose: Physical and chemical properties of gold is most suitable to be restored of teeth to its original state. Recently zirconia was used instead of gold because of esthetical and intimacy of human body. Because of high strength and high abrasion resistance of zirconia, all zirconia artificial tooth lead to wear the original tooth of opposite site. To preserve this original tooth, zirconia artificial tooth covered with dental ceramic glass was used. When joining the zirconia core and dental ceramic glass, difference of their thermal expansion coefficient and wetting ability is generated the residual stress at interface lead to crack. In order to solve this problem, intermediate layer what is called zir-liner was imported to decrease the residual stress and increase the bonding strength. Methods: In this study, to identify the optimum conditions for manufacturing process, various methods to rough the surface of zirconia core were adopted, and vary the thickness of interlayer, and analyzed bond strength. Results: Bond strength of sanding specimens group showed higher than that of non-sanding specimens group, and once applied intermediate layer with sanding specimens showed highest bond strength with 28 MPa. SEM photomicrographs of zirconia cores fired at $1500^{\circ}C$ showed parallel straight lines in sanding and pockmarked surface in blasting surfaces as abrasion traces. Observation of the destruction section after shear test by SEM were carried out. Liner applied non-sanding group and non-liner applied sanding group all showed interfacial crack. Sandblasting group with non-liner showed remained dental ceramic glass on the surface of zirconia. Sandblasting group with once applied liner showed partially remained liner and dental ceramic glass on the surface of zirconia. XRD analysis revealed that sandblasting group showed higher monoclinic peaks than other specimens group and this result was due to the high collision energy for stress induced phase transformation. Conclusions: A study on the improvement of bonding strength between zirconia and dental ceramic glass steadily carried out for the future to practical use.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.27 no.1
• /
• pp.54-63
• /
• 2023

In this paper, the effect of corrosion level and crack width on the cohesive strength-slip behavior of corroded steel rebar and concrete interface is conducted. The existing studies mainly focus on the decrease in bond strength with respect to the level of corrosion; there are, however, few studies on the decrease in cohesive strength according to the crack width of the concrete surface due to corrosion. Therefore, in this study, a series of tests for the cohesive strength, slip behavior and mass loss of the reinforcing bar is evaluated at the surface of corroded rebar and concrete. It is found that the tendency to decrease the bond strength is closely related to the crack width rather than the corrosion level. Hence, to determine the degradation performance for the bond strength-slip behavior relation, the occurrence of cracks on the concrete surface can be a suitable index.

• Steel and Composite Structures
• /
• v.3 no.4
• /
• pp.231-242
• /
• 2003

This paper deals with the formulation and development of fracture criteria for high-strength structural members containing surface damage in the form of notches (i.e., blunt defects). The important role of the yield strength of the material and its strain hardening capacity (evaluated by means of the constitutive law or stress-strain curve) is analysed in depth by considering the fracture performance of notched samples taken from high-strength steels with different levels of cold drawing (the most heavily drawn steel being commercial prestressing steel used in prestressed concrete). The final aim of the paper is to establish fracture-based design criteria for structural members made of steels with distinct yield strength and containing very different kinds of notch-shape surface damage.

• Journal of Surface Science and Engineering
• /
• v.29 no.4
• /
• pp.238-252
• /
• 1996

In order to study the effect of interface oxides on the adhesion strength of the copper/epoxy system, copper foils were immersed in black oxide or brown oxide forming solutions before lamination with epoxy prepregs, and variation of peel strength with the treatment time were investigated. Results showed that peel strength decreased rapidly up to 1 minute of treatment lime and remained constant in the case of the black oxide treated specimens, which was accompanied by the thickening of $Cu_2O$ at the Copper/Epoxy interface during the period. In contrast, peel strength increased rapidly up to 1 minute of treatment time and remained constant in the case of the brown oxide treated specimens, which could be ascribed to the thickening of CuO. Subsequent heat treatments of the Copper/Epoxy laminations at $120^{\circ}C$ in air showed that peel strength remained constant in the case of the black oxide treated specimens but decreased gradually in the case of the brown oxide treated specimens. Following XPS analyses revealed that the latter was possibly caused by the coalescence of CuO at the Copper/Epoxy interface into $Cu_2O$.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2004.05a
• /
• pp.240-243
• /
• 2004

A new shear connection for the application of precast decks to PSC girders was proposed and push-off tests were conducted to evaluate the horizontal shear strength of the shear connection. Major parameters of the tests were connector type, shank area, vertical load, surface condition and bedding height. Judging from the test results, shear strength of the suggested shear connection was proportional to the shank area and yield strength of the connectors and was in inverse proportion to the bedding height. Shear connection with shear key at the surface showed better performance. An empirical equation for the evaluation of the shear strength of the shear connection without considering bond strength was proposed and it showed good correlation with the test results.

• Proceedings of the Korea Concrete Institute Conference
• /
• 2009.05a
• /
• pp.249-250
• /
• 2009

Recently, the interest on self-compacting concrete (SCC) without any mechanical vibration is increasing as the demand for high-strength and high surface quality of precast element increased. In this work, precast beam element with 7m length was manufactured using high-strength SCC with design strength of 60MPa, resulting in high-strength and high surface quality was obtained from the precast beam cast by high-strength SCC.

• Journal of the Korean Ceramic Society
• /
• v.45 no.10
• /
• pp.600-604
• /
• 2008

Although titanium-ceramic systems have gained substantial interests in dental prosthetic field, bonding problem between porcelain and titanium has not been solved. Main obstacle in titanium-porcelain bonding is excessive oxidation of titanium during porcelain firing. The effects of several coating materials on the bonding strength of titanium-porcelain system were investigated in this study. RF sputtering and electroplating of platinum significantly increased the bonding strength of porcelain-titanium specimen. However, coatings of Ni-Au, Ir, and ceramics(zirconia and hydroxyapatite) did not showed a significant effect on bonding strength. Platinum might be a promising material for the protective layer of excessive oxidation of titanium during porcelain firing, resulting in increase in the bonding strength.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.44 no.1
• /
• pp.58-64
• /
• 2012

As a first step to apply PVAm (polyvinylamine) on packaging paper by surface treatment, three types of linerboards were impregnated with PVAm solution. The effect of PVAm pick-up on strength properties of linerboard was investigated. The pick-up of PVAm was controlled by varying concentration of PVAm solution. It was found that dry tensile strength, tensile energy absorption, burst strength and compressive strength of linerboard were increased by applying PVAm. In addition, wet tensile strength was significantly improved with increasing PVAm pick-up. However, folding endurance was found to be decreased with increasing PVAm pick-up.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.8 no.5
• /
• pp.181-187
• /
• 2000

Fatigue tests under acid fog environment were carried out to investigate the effect of acid fog on the corrosion fatigue strength of SM55C in comparison with distilled water. Main results obtained are as follows. The fatigue strength of SM55C under acid fog environment are remarkably decreased as compared with that of distilled water specimen. The corrosive effect of acid fog on fatigue strength are more serious under low stress amplitude level than under high stress amplitude level, and this leads to continuous reduction of fatigue strength. Under acid fog environment in early stage of crack growth. because the corrosive components dissolve the crack face offensively. the unstable fracture surface appears. But, the stable corrosion precipitation and products layer are formed on the fracture surface in accordance with the time pass.