• Tribology and Lubricants
• /
• v.35 no.4
• /
• pp.237-243
• /
• 2019

Through this study, we investigate the effects of ultrasonic nanocrystal surface modification (UNSM) technology on the fatigue life of needle roller bearings. The fatigue life of untreated and UNSM-treated needle roller bearings is evaluated using a roller fatigue tester at various contact stress levels under oil-lubricated conditions. We can ascertain that the fatigue life of an UNSM-treated needle roller bearing was extended by approximately 34.3% in comparison with an untreated one, where the effectiveness of UNSM technology diminishes with increasing contact stress. The surface roughness and surface hardness of needle roller bearings before and after being treated by UNSM technology are compared and discussed to understand the role of UNSM technology in improving the fatigue life of needle roller bearings. In addition, a fractograph of the damaged bearings is observed using a scanning electron microscopy to shed light on the fracture mechanisms of bearings under different contact stress levels. We can therefore conclude that the application of UNSM technology to the needle roller bearings improves the fatigue life by reducing the friction coefficient and increasing the wear resistance; this may be attributed to a reduction in surface roughness from 0.5 to $0.149{\mu}m$ and an increase in surface hardness from 58 to 62 HRc.

• Journal of the Korean institute of surface engineering
• /
• v.38 no.4
• /
• pp.156-162
• /
• 2005

Nickel-iron nanocrystalline alloys with different compositions and grain sizes were fabricated by electro-plating for MEMS devices. The iron content of the deposits was changed by varying the nickel/iron ion ratio in the electrolyte. X-ray diffraction (XRD) analysis was applied for measuring the strength of the texture and grain size of the deposits. The nickel/iron atom ratio of the deposits was analyzed by EDS. The hardness of the alloys was evaluated by Vickers hardness indenter. The internal stress of the deposits was measured by Thin Film Stress Measurement using Stoney's formula. Surface morphology and roughness were investigated by Scanning Electron Microscopy (SEM) and Atomic Force Microscopy (AFM). The results of this study revealed that at a grain size of approximately $17\~24$nm the hardness, internal stress and roughness depend strongly on the iron content. With increasing the iron content, the hardness and internal stress of the deposits increased. An excellent correlation between the increase in the internal stress and the loss of (200) texture was found.

• Journal of Korea Foundry Society
• /
• v.22 no.5
• /
• pp.265-270
• /
• 2002

A novel jewelry master pattern manufacturing process which reduce manufacturing steps by employing a Duraform rapid prototyping mold and a low melting alloy has been suggested. The novel process follows the steps of 'jewelry 3D CAD design ${\rightarrow}$ Durafrom RP mold ${\rightarrow}$ low melting alloy master pattern' while the previous process follows more complicated steps of 'jewelry idea sketch ${\rightarrow}$ detailed drawing ${\rightarrow}$ wax carving ${\rightarrow}$ flask ${\rightarrow}$ silver master pattern.' An upper and a lower part of molds have been manufactured of Duraform powder, of which melting point is $190^{\circ}C$. A maser pattern was manufactured by pouring a low melting alloy of Pb-Sn-Bi-Cd, so called Woods Metal, of which melting point is $70^{\circ}C$, into the mold. The master pattern is a shape of a disk of 20mm diameter that contains various design factors. The variations of dimensions, surface roughness, surface pore ratio were measured by an optical microscope, a surface roughness profilometer, and a Rockwell hardness tester. The pattern made of were maeasured by an optical microscope, a surface roughness profilometer, and a Rockwell hardness tester. The pattern made of low melting alloy has sufficient surface hardness, and surface pore ratio to be used as the jewelry master pattern.

• The Journal of Korean Academy of Prosthodontics
• /
• v.39 no.1
• /
• pp.105-113
• /
• 2001

The purpose of this study is to compare effects of denture cleansers and disinfectants on the color. surface hardness, and surface roughness of reinforced acrylic resin using polyhedral oligosilsesquioxane molecules(POSS resin) to those of common resins. According to manufacturer's instructions, 45 specimens were made from three denture resins(Luciton 199, Paladent 20, POSS resin), and polished. Five denture cleansers(distilled water, glutaraldehyde, alkaline hypochlorites, chlorhexidine, alkaline peroxides) in combination with three denture resins were evaluated before and after immersion for 7 days. Color data in $L^*a^*b^*$ system were measured with a colorimeter. Surface hardness data were measured with a microhardness tester. Surface roughness data were measured with a 3-dimensional surface analyzer. Data were analyzed with two-way ANOVA, one-way ANOVA, and t-test. The results were as follows : 1. All resins(Luciton 199, Paladent 20, POSS resin) showed significant differences in color after immersion in hypochlorites(p<0.05). 2. POSS resin showed significant differences in color compared with Paladent 20 in all denture cleansers, but no statistically significant differences with Luciton 199(p<0.05). 3. Luciton 199 showed significant differences of surface hardness in chlorhexidine, Paladent 20 showed significant differences in glutaraldehyde and chlorhexidine. POSS resin showed a little change of surface in all denture cleanser, but no statistically significant differences(p<0.05). 4. Luciton 199 and Paladent 20 showed significant differences of surface roughness in hypochlorites and glutaraldehyde, and POSS resin showed no statistically significant differences in all denture cleansers(p<0.05).

• Journal of the Korean Society of Manufacturing Technology Engineers
• /
• v.7 no.2
• /
• pp.15-22
• /
• 1998

The effects of shot peening an the fatigue strength are studied in this paper. Applying the multistage shot peening on the material. the relation between the residual stress and fatigue strength compressive is investigated. Observing tensile strength elongation. reduction of area. hardness. and roughness. the results can be summarized as follows ; 1.The change of mechanical properties is small before and after the shot peening is carried out. The change of hardness is also small in high hardness material. 2.The surface roughness does not affect the fatigue strength. but the surface roughness is improved by multi-stage shot peening. 3.The fatigue strength of multi-stage shot peening material is 756MPa and is 1.78 times higher than that of un-peened material. 4.The maximum compressive residual strength of multi-stage shot peening material is -792MPa the fatigue strength seems to be improved by residual stress.

• Journal of the Korean Society for Precision Engineering
• /
• v.21 no.3
• /
• pp.100-108
• /
• 2004

Contamination of environment induces the shortage of drinkables. In this trend, the leakage of water that occurs by breakage or erosion of rubber valve seats is serious problem. Rubber is apt to cause breakage between two materials when they contact with each other. The possible way to avoid leakage of water by damage and breakdown of rubber is to replace that with metal. Because of this reason, nowadays, rubber is being substituted with metal as valve seat materials for water works. In tribology, a severe from of wear is characterized by local, macroscopic material transfer, removal, or formation of surface protrusions when two solid surfaces experience relative sliding under load. One of the major problems in sliding of metals is galling due to bad surface quality. Experimentally, there are various elements which influence on incipient galling, such as hardness, surface roughness, temperature, load, velocity and external environments. This paper is aimed at verifying the galling tendencies according to hardness, surface roughness, load and velocity and showing how much effect the factors have on the galling tendencies.

• Journal of the Korean Society of Manufacturing Process Engineers
• /
• v.19 no.8
• /
• pp.94-103
• /
• 2020

This study investigated the effects of ultrasonic nanocrystal surface modification (UNSM) on the deteriorated surface of AISI SUS316L additively manufactured (AM) using the powder bed fusion (PBF) technique. Specifically, the effects of UNSM conditions on surface topology, hardness, and anti-corrosion were examined. Before UNSM treatment, the stainless steel 316L powder was processed via the PBF machine to prepare a substrate. We observed surface changes due to UNSM treatments in PBF SUS316L substrates and examined the correlation between topology changes, roughness, hardness, and anti-corrosion. After UNSM treatment, the coarse as-built surface was refined, and a regular micro-profile was implemented. Compared to the non-treated PBF sample, the waviness and roughness of the surfaces after UNSM treatment decreased by up to 56.0% and 94.5%, respectively, and decreased further as the interval decreased. The hardness improved by up to 63.0% at a maximum depth of 500 ㎛ from top surface by the UNSM treatment. The results of the corrosion test showed that the corrosion resistance of the UNSM specimens was moderately improved compared to that of the untreated surface. This study confirmed that UNSM is an effective post-processing technique for additively manufactured parts.

• Korean Journal of Materials Research
• /
• v.17 no.12
• /
• pp.648-653
• /
• 2007

Plasma electrolytic oxidation (PEO) treatment was performed on cast Mg-6 wt%Al alloy solution-treated at 693K for 16h and aged at 498K. The surface roughness, thickness, micro-hardness, wear and corrosion properties of coatings on solution-treated and aged Mg-6 wt%Al alloy were investigated. The coatings on aged Mg-6 wt%Al alloy had thinner layer and lower micro-hardness and wear resistance than the solution-treated Mg-6 wt%Al alloy. As the aging time increased, the thickness of coatings decreased while the surface roughness was almost no changed. In addition, the micro-hardness and wear property of coatings decreased with increasing the aging time unlike the uncoated Mg-6 wt%Al alloy showing the peak micro-hardness and the best wear property after aging for 16 h. However, the coatings on Mg-6 wt%Al alloy peak-aged for 16h revealed the best corrosion resistance in 3.5% NaCl solution, which was explained based on the microstructural characteristics.

• Journal of the Korean institute of surface engineering
• /
• v.49 no.3
• /
• pp.225-230
• /
• 2016

The present work was conducted to investigate the effects of NaF concentration in phosphate and silicate-containing alkaline electrolyte on the morphology, thickness, surface roughness and hardness of anodic oxide films formed on AZ31 Mg alloy by plasma electrolytic oxidation (PEO) method. The PEO films showed flat surface morphology with pores in the absence of NaF in the electrolyte, but nodular features appeared on the PEO film surface prepared in NaF-containing electrolyte. Numerous pores ranging from 1 to $20{\mu}m$ in size were observed in the PEO films and the size of pores decreased with increasing NaF concentration in the electrolyte. Surface roughness and thickness of PEO films showed increases with increasing NaF concentration. Hardness of the PEO films also increased with increasing NaF concentration. It was noticed that hardness of inner part of the PEO films is lower than that of outer part of them, irrespective of the concentration of NaF. The low hardness of PEO films was explained by the presence of a number of small size pores less than $2{\mu}m$ near the PEO film/substrate interface.

• Journal of Technologic Dentistry
• /
• v.45 no.2
• /
• pp.39-47
• /
• 2023

Purpose: This study aimed to confirm the applicability of gloss polishing using automatic barrel finishing with respect to three-dimensional (3D)-printed resin specimens. The surface roughness and grinding angle of the 3D-printed resin specimens were observed with respect to gloss polishing time using automatic dental barrel finishing. Methods: Herein, experiments were conducted on four types of 3D-printed resin specimens. The specimens, with a thickness of 100 ㎛ each, were printed using a 3D printer. Subsequently, light polymerization was performed on these specimens for 15 min. Post this surface treatment, the specimens underwent grinding for 25 min. This process was followed by gloss polishing at 5-min intervals for up to 25 min using automatic dental barrel finishing. The specimens were photographed using a 3D optical microscope, and their surface roughness and grinding angle were measured. Results: The Ra (centerline average roughness) values of all the specimens, except for crown & bridge 10 group and those in the control group that were not polished using automatic barrel finishing, were <0.2 ㎛. However, polishing time needs to be controlled to realize the desired surface roughness and grinding amount considering the hardness of the resin used. Conclusion: Gloss polishing of 3D-printed resin can be realized using automatic dental barrel finishing. However, polishing time needs to be controlled to realize the desired surface roughness and grinding amount considering the hardness of the resin used.