• 한국건축시공학회:학술대회논문집
• /
• 한국건축시공학회 2019년도 춘계 학술논문 발표대회
• /
• pp.217-218
• /
• 2019

In this study, to overcome the limitation of material application as the surface layer of bridge decks (asphalt concrete, concrete), a newly developed waterproof sheet is proposed to be usable for both asphalt concrete and concrete. Subsequent tensile bond strength was tested, and the test results showed that the tensile bond strengths were similar to depending on the type of the surface layer material for bridge decks, confirming the applicability of the proposed material.

• Restorative Dentistry and Endodontics
• /
• 제28권6호
• /
• pp.491-497
• /
• 2003

The purpose of this study was to evaluate the correlation between hybrid layer thickness and bond strength using confocal laser scanning microscope and microtensile bond strength test of two adhesive systems. The dentin surface of human molars. sectioned to remove the enamel from the occlusal surface. Either Scotchbond Multi-Purpose(3M Dental Product, St. Paul, MN, U.S.A) or Clearfil SE Bond (Kuraray, Osaka, Japan) was bonded to the surface. and covered with resin-composite. The resin-bonded teeth were serially sliced perpendicular to the adhesive interface to measure the hybrid layer thickness by confocal laser scanning microscope. The specimen were trimmed to give a bonded cross-sectional surface area of $1\textrm{mm}^2$, then the micro-tensile bone test was performed at a cross head speed of 1.0 mm/min. All fractured surfaces were also observed by stereomicroscope. There was no significant differences in bond strengths the materials(p>0.05). However. the hybrid layers of three-step dentin adhesive system, SM, had significantly thicker than self-etching adhesive system. CS(p<0.05). Pearson's correlation coefficient showed no correlation between hybrid layer thickness and bond strengths(p>0.05). Bond strengths of dentin adhesive systems were not dependent on the thickness of hybrid layer.

• 센서학회지
• /
• 제14권6호
• /
• pp.423-429
• /
• 2005

In this paper, we proposed the fabrication process of the stable e-beam evaporation and the patterning of metals layer on the polydimethylsiloxane (PDMS) substrate. The metal layer was deposited under the various deposition rate, and its effect to the electrical and mechanical properties (e.g.: adhesion-strength of metal layer) was investigated. The influence of surface roughness to the adhesion-strength was also examined via the tape test. Here, we varied the roughness by changing the reactive ion etching (RIE) duration. The electrode patterning was performed through the conventional photolithography and chemical etching process after e-beam deposition of $200{\AA}$ Ti and $1000{\AA}$ Au. As a result, the adhesion strength of metal layer on the PDMS surface was greatly improved by the oxygen plasma treatment. The e-beam evaporation on the PDMS surface is known to create the wavy topography. Here, we found that such wavy patterns do not effect to the electrical and mechanical properties. In conclusion, the metal patterns with minimum $20{\mu}m$ line width was produced well via the our fabrication process, and its electrical conductance was almost similar to the that of metal patterns on the silicon or glass substrates.

• 한국지반공학회:학술대회논문집
• /
• 한국지반공학회 2002년도 봄 학술발표회 논문집
• /
• pp.731-738
• /
• 2002

Recently, as large constructions on the coast are performed frequently, surface layer stabilization method which Is one of the improvement methods for dredged soft clay has been applied. However, there have been few studies about the surface layer stabilization method. The purpose of this study is to clarify characteristics of ultra-soft marine clay and hardening agent. Also, optimal mixture ratio of hardening agent was verified through the laboratory tests such as statistical analysis and pilot tests. Laboratory tests were performed with proper hardening agent and test soil and standard mixing tables of hardening agent were determined according to ground conditions through statistical analysis. Also, applicability of surface layer stabilization method to field was verified by pilot tests. From the results of the tests, it was found that hardening agent materials such as cement, slag, fly-ash, inorganic salts, arwin, gypsum etc. affect on the appearing compressive strength. It was defined optimal mixture ratio which satisfies the required compressive strength from the statistical analysis. Also, It was compared the effect of ground improvement by cements and hardening agents through the pilot tests. This study will serve as data for design or construction criteria of stabilization of surface layer on ultra-soft marine clay.

• 한국표면공학회지
• /
• 제50권3호
• /
• pp.170-176
• /
• 2017

EPIG (Electroless Pd/immersion Au) process was studied to replace ENIG (electroless Ni/immersion Au) and ENEPIG (electroless Ni/electroless Pd/immersion Au) processes for bump surface treatment used in high reliable flip chip packages. The palladium and gold layers formed by EPIG process were uniform with thickness of 125 nm and 34.5 nm, respectively. EPAG (Electroless Pd/autocatalytic Au) also produced even layers of palladium and gold with the thickness of 115 nm and 100 nm. TEM results exhibited that the gold layer in EPIG surface had crystalline structure while the palladium layer was amorphous one. After annealing at 250 nm, XPS analysis indicated that the palladium layer with thickness more than 22~33 nm could act as a diffusion barrier of copper interconnects. As a result of comparing the chip shear strength obtained from ENIG and EPIG surfaces, it was confirmed that the bonding strength was similar each other as 12.337 kg and 12.330 kg, respectively.

• Restorative Dentistry and Endodontics
• /
• 제22권1호
• /
• pp.470-478
• /
• 1997

The purpose of this study was to investigate the effects of moistening mechods of dentin on the morphologic states of hybrid layers and on the interfacial bond strength between dentin and composite. Specimens were divided into 6 groups based on the surface moistening methods and materials used. After the dentin surface was conditioned with 10 % phoporic acid and irrigated: 1. The dentin surface was dried. Then bonding agent and composite were applied. 2. The dentin surface was blot-dryed. Then primer, bonding atent and composite were applied. 3. The dentin surface was dryed first. Within 20 seconds, the surface was rewetted, then primer, bonding agent and composite were applied. 4. The dentin surface was dryed. Then primer, bonding agnent and composite were applied. 5. The dentin surface was dryed first. Atter 24hrs, the surface was rewetted, and then primer, bonding agent and composite were applied. 6. The surface was conditioned with NaOCl for 5min. Then primer, bonding agent and composite were applied. To reveal the hybrid layer, scanning electron microscopy was used after the samples were ion beam etched. The shear bond strength of each group was tom pared by ANOVA. In groups 2, 3 and 4, the hybrid layer was clearly visible, but the width was more limited in group 4. In group 1 and 5, the hybrid layer was not found, and a gap was formed between dentin and composite. In group 6, the hybrid layer was not found, but the interface between the dentin and composite was intimate. The shear bond strength of each group was as follows: Group 1 : 4MPa, Group 2 : 14MPa, Group 3 : 12MPa, Group 4 : 14MPa, Group 5 : 5MPa, Group 6 : 9MPa.

• 펄프종이기술
• /
• 제30권3호
• /
• pp.63-72
• /
• 1998

This research was intended to evaluate the effect of carboxymethylcellulose(CMC) on the coating structure and surface strength of coated paper prepared with amphoteric latex based coating color. Printability and optical properties of coated papers were compared. The influence of the consolidation behavior of coating color on the coating structure and the surface strength of coated paper was investigated. Compared with the conventional anionic latex, amphoteric latex formed bulkyer, smoother and more porous coating layer, which in turn, restricted binder migration in the coating layers, and facilitated immobilization of coating colors. However, dry pick strength of coated paper was decreased. The addition of CMC to these systems had strongly influenced on. the consolidation behavior and porosity in the dry state, through forming the network structure of coating layers by the interaction with amphoteric latex particles. Thus, printability and optical properties of coated papers were improved. Results indicated that amphoteric latex could be practically applied to the paper coating to improve printability and optical properties of coated papers.

• Nuclear Engineering and Technology
• /
• 제50권2호
• /
• pp.218-222
• /
• 2018

An oxide-dispersion-strengthened (ODS) layer was formed on Zircaloy-4 tubes by a laser beam scanning process to increase mechanical strength. Laser beam was used to scan the yttrium oxide ($Y_2O_3$)-coated Zircaloy-4 tube to induce the penetration of $Y_2O_3$ particles into Zircaloy-4. Laser surface treatment resulted in the formation of an ODS layer as well as microstructural phase transformation at the surface of the tube. The mechanical strength of Zircaloy-4 increased with the formation of the ODS layer. The ring-tensile strength of Zircaloy-4 increased from 790 to 870 MPa at room temperature, from 500 to 575 MPa at $380^{\circ}C$, and from 385 to 470 MPa at $500^{\circ}C$. Strengthening became more effective as the test temperature increased. It was noted that brittle fracture occurred at room temperature, which was not observed at elevated temperatures. Resistance to dynamic high-temperature bursting improved. The burst temperature increased from 760 to $830^{\circ}C$ at a heating rate of $5^{\circ}C/s$ and internal pressure of 8.3 MPa. The burst opening was also smaller than those in fresh Zircaloy-4 tubes. This method is expected to enhance the safety of Zr fuel cladding tubes owing to the improvement of their mechanical properties.

• 한국표면공학회지
• /
• 제24권1호
• /
• pp.16-16
• /
• 1991

Generally brittle eta phase produced during TiC deposition has a effect on the TRS (transverse rupture strength ; thoughness). Therefore it is necessary to reduce eta(η), phase for the improvement of tool life. At this experiment some properties (TRS, bonding strength, tool life, eta phase)have been investigated by inserting TiN or TiCN underlayer between TiC layer and substrate. The results obtained were as follows; 1. by inserting underlayer eta phase were decreased and TRS was increased, but the bonding strength was decreased. 2. the diffusion of W, Co from the substrate was hindered by the underlayer. 3. TiC layer with TiCN underlayer had the finsest grain size. 4. by inserting underlayer (TiCN or TiN) the tool life was improved and especially notch and crater wear resistance was greatly improved.

• 한국표면공학회지
• /
• 제25권1호
• /
• pp.16-23
• /
• 1992

Generally brittle eta phase produced during TiC deposition has a bad effect on the TRS (transverse rupture strength ; thoughness). Therefore it is necessary to reduce eta(η) phase for the improvement of tool life. At this experiment some properties (TRS, bonding strength, tool life, eta phase) have been investigated by inserting TiN or TiCN underlayer between TiC layer and substrate. The results obtained were as fellows; 1. by inserting underlayer eta phase was decreased and TRS was increased, but the bonding strength was decreased. 2. the diffusion of W, Co from the substrate was hindered by the underlayer. 3. TiC layer with TiCN underlayer had the finsest gain size. 4. by inserting underlayer (TiCN or TiN) the tool life was improved and especially notch and crater wear resistance was greatly improved.