• 전력전자학회:학술대회논문집
• /
• 전력전자학회 2008년도 하계학술대회 논문집
• /
• pp.643-645
• /
• 2008

Stainless steel 304 and 316 plates were deposited with the multi-layered coatings of titanium film (0.1um) and gold film (1-2um) by an electron beam evaporation method. The XRD patterns of the stainless steel plates modified with the multi-layered coatings showed the crystalline phases of the external gold film and the stainless steel substrate. Surface microstructural morphologies of the stainless steel bipolar plates modified with multi-layered coatings were observed by AFM and FE-SEM images. The external gold films formed on the stainless steel plates showed microstructure of grains of about 100nm diameter. The grain size of the external surface of the stainless steel plates increased with the gold film thickness. The electrical resistance and water contact angle of the stainless steel bipolar plates covered with multi-layered coatings were examined with the thickness of the external gold film.

• 한국표면공학회지
• /
• 제39권1호
• /
• pp.1-8
• /
• 2006

In this study, effect of sputtering after plasma nitriding and before PVD coating on the microstucture, microhardness, surface roughness and the adhesion strength of CrN thin films were investigated. Experimental results showed that this sputtering process not only removed surface compound layer which formed during a plasma nitriding process but also induced an alteration of the surface of plasma nitrided substrate in terms of microhardness distribution and surface roughness, which in turn affected the adhesion strength of PVD coatings. After sputtering, microhardness distribution showed general decrease and the surface roughness became increased slightly. The critical shear stress measured from the scratch test on the CrN coatings showed an approximately twice increase in the binding strength through the sputtering prior to the coating and this could be attributed to a complete removal of compound layer from the plasma nitrided surface and to an increase in the surface roughness after sputtering.

• 한국표면공학회지
• /
• 제39권6호
• /
• pp.268-275
• /
• 2006

In this study, effect of sputtering on the plasma-nitriding substrate and before PVD coating on the microstucture, microhardness, surface roughness and the adhesion strength of CrZrN thin films were investigated. Experimental results showed that this sputtering process not only removed surface compound layer which formed during a plasma nitriding process but also induced an alteration of the surface of plasma nitrided substrate in terms of microhardness distribution, surface roughness. This in turn affected the adhesion strength of PVD coatings. After sputtering, microhardness distribution showed general decrease and the surface roughness became increased slightly. The critical shear stress measured from the scratch test on the CrZrN coatings showed an approximately 1.4 times increase in the adhesion strength through the sputtering prior to the coating and this could be attributed to a complete removal of compound layer from the plasma nitrided surface and to an increase in the surface roughness after sputtering.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2016년도 추계학술대회 논문집
• /
• pp.105-105
• /
• 2016

Recently, high power impulse magnetron sputtering (HIPIMS) has attracted considerable attentions due to its high potential for industrial applications. By pulsing the sputtering target with high power density and short duration pulses, a high plasma density and high ionization of the sputtered species can be obtained. HIPIMS has exhibited several merits such as increased coating density, good adhesion, microparticle-free and smooth surface, which make the HIPIMS technique desirable for synthesizing hard coatings. However, hard coatings present intrinsic defects (columnar structures, pinholes, pores, discontinuities) which can affect the corrosion behavior, especially when substrates are active alloys like steel or in a wear-corrosion process. Atomic layer deposition (ALD), a CVD derived method with a broad spectrum of applications, has shown great potential for corrosion protection of high-precision metallic parts or systems. In ALD deposition, the growth proceeds through cyclic repetition of self-limiting surface reactions, which leads to the thin films possess high quality, low defect density, uniformity, low-temperature processing and exquisite thickness control. These merits make ALD an ideal candidate for the fabrication of excellent oxide barrier layer which can block the pinhole and other defects left in the coating structure to improve the corrosion protection of hard coatings. In this work, CrN/Al2O3/CrN multilayered coatings were synthesized by a hybrid process of HIPIMS and ALD techniques, aiming to improve the CrN hard coating properties. The influence of the Al2O3 interlayer addition, the thickness and intercalation position of the Al2O3 layer in the coatings on the microstructure, surface roughness, mechanical properties and corrosion behaviors were investigated. The results indicated that the dense Al2O3 interlayer addition by ALD lead to a significant decrease of the average grain size and surface roughness and greatly improved the mechanical properties and corrosion resistance of the CrN coatings. The thickness increase of the Al2O3 layer and intercalation position change to near the coating surface resulted in improved mechanical properties and corrosion resistance. The mechanism can be explained by that the dense Al2O3 interlayer acted as an excellent barrier for dislocation motion and diffusion of the corrosive substance.

• 한국표면공학회지
• /
• 제52권4호
• /
• pp.227-232
• /
• 2019

Mo-N based coatings have been studied for enhancing mechanical characteristics of thin films. In the case of Mo-X-N coatings, the microstructure and mechanical properties can be affected by the addition of the third element. In this work, Mo-Cu-N coatings were successfully fabricated with varying the Cu content from 4.5 at% to 31 at% by the co-sputtering method. Thus, properties of the coatings were analyzed by EDS, SEM, XRD, AFM, nano indentation and scratch test techniques. From observed results, MoxN bonds were made in a nitrogen atmosphere and Cu elements were present at grain boundaries. In addition, coatings with the Cu content above 14 at% had a Cu3N peak in the XRD results. Thus, it is suggested that the formation of Cu3N phase affected the microstructure and mechanical properties of Mo-Cu-N coatings. Mechanical properties of Mo-Cu-N coatings were found to be relatively better at Cu content of about 12 at%.

• 한국표면공학회지
• /
• 제49권6호
• /
• pp.580-586
• /
• 2016

Cr-Si-Al-N coating with different Si content were deposited by hybrid physical vapor deposition (PVD) method consisting of unbalanced magnetron (UBM) sputtering and arc ion plating (AIP). The deposition temperature was $300^{\circ}C$, and the gas ratio of $Ar/N_2$ were 9:1. The CrSi alloy and aluminum targets used for arc ion plating and sputtering process, respectively. Si content of the CrSi alloy targets were varied with 1 at%, 5 at%, and 10 at%. The phase analysis, composition and microstructural analysis performed using x-ray diffraction (XRD) and field emission scanning electron microscopy (FESEM) including energy dispersive spectroscopy (EDS), respectively. All of the coatings grown with textured CrN phase (200) plane. The thickness of the Cr-Si-Al-N films were measured about $2{\mu}m$. The friction coefficient and removal rate of films were measured by a ball-on-disk test under 20N load. The friction coefficient of all samples were 0.6 ~ 0.8. Among all of the samples, the removal rate of CrSiAlN (10 at% Si) film shows the lowest values, $4.827{\times}10^{-12}mm^3/Nm$. As increasing of Si contents of the CrSiAlN coatings, the hardness and elastic modulus of CrSiAlN coatings were increased. The morphology and composition of wear track of the films was examined by scanning electron microscopy (SEM) and energy dispersive spectroscopy, respectively. The surface energy of the films were obtained by measuring of contact angle of water drop. Among all of the samples, the CrSiAlN (10 at% Si) films shows the highest value of the surface energy, 41 N/m.

• 한국표면공학회:학술대회논문집
• /
• 한국표면공학회 2008년도 추계학술대회 초록집
• /
• pp.45-46
• /
• 2008

Hard coatings of TiN which exhibit a large variation in their electrical resistivities, have been prepared in magnetron sputtering system using bipolar pulsed DC generator. TiN coatings have also been prepared using a DC generator in the same sputtering system under identical deposition conditions. Microstructural, Mechanical, Crystallographic properties of TiN films using continuous and bipolar pulsed DC generators were examined. Field emission scanning microscope and Nanoindenter have been used to characterize the coatings.

• Tribology and Lubricants
• /
• 제34권6호
• /
• pp.313-317
• /
• 2018

Carbon-based coatings, including carbon nanotubes (CNTs), graphene, and buckyball ($C_{60}$), receive much interest because of their outstanding mechanical and electrical properties for a wide range of electromechanical component-based applications. Previous experimental results demonstrate that these carbon-based coatings are promising solid lubricants because of their superior tribological properties, and thus help prolong the lifetime of silicon-based applications. In this study, CNT coatings are deposited on a bare silicon (100) substrate by electrodynamic spraying under different deposition conditions. During the coating deposition, the applied voltage, CNT concentration of the solution, distance between the injecting nozzle and the substrate and diameter of the injecting nozzle are optimized to control the thickness and surface roughness of the CNT coatings. The surface morphology and thickness of the coatings are characterized by scanning electron microscopy (SEM) and atomic force microscopy (AFM), respectively. The friction and wear properties of the coatings are investigated by using a pin-on-reciprocating-type tribotester under various experimental conditions. The friction coefficient of the CNT coating is as low as 0.15 under high normal loads. The overall results reveal that CNT coatings deposited by electrodynamic spraying provide relatively uniform with superior lubrication performance.

• 한국표면공학회지
• /
• 제41권6호
• /
• pp.287-291
• /
• 2008

Reactively magnetron sputtered TiN films were deposited on Si wafers under varying bias voltage and characterized by X-ray diffraction, field-emission scanning electron microscopy and Nanoindentation. The films deposited under an Ar + $N_2$ atmosphere exhibited a mixed (200)-(111) orientation with a strong (200) texture, which subsequently changed to a strong (111) texture with increasing bias voltage. The changes in texture and grain size of the TiN thin films are due to one or a combination of factors such as strain energy, surface free energy, surface diffusivity and adatom mobility. The influence of each factor depends on the processing conditions. The average deposition rate and grain size were calculated from FE-SEM images of the films indicating that the deposition rate was lower at the films deposited under bias voltage.

• 한국표면공학회지
• /
• 제34권5호
• /
• pp.435-444
• /
• 2001

WC-( $Ti_{1-x}$ A $l_{x}$) N coatings of constant changing Al concentration were deposited on S45C substrates by high-ionization sputtered PVD method. The Al concentration could be controlled by using evaporation source for Al and fixing the evaporation rate of the metals (i.e, WC- $Ti_{0.86}$A $l_{0.14}$N, WC- $Ti_{0.72}$A $l_{0.28}$N, and WC- $Ti_{0.58}$A $l_{0.42}$N). The corrosion behavior of WC-( $Ti_{1-x}$ A $l_{x}$)N coatings in a deaerated 3.5% NaCl solution was investigated by electrochemical corrosion tests and surface analyses. The measured galvanic corrosion currents between coating and substrate indicated that WC- $Ti_{0.72}$A $l_{0.28}$N coating showed the best resistance of the coating tested. The results of potentiodynamic polarization tests showed that the WC- $Ti_{0.72}$A $l_{0.28}$N coating deposited with 32W/c $m^2$ of Al target revealed higher corrosion resistance. This indicated that the WC- $Ti_{0.72}$A $l_{0.28}$N coating is effective in improving corrosion resistance. In EIS, the WC- $Ti_{0.72}$A $l_{0.28}$N coating showed one time constant loop and increased a polarization resistance of coating ( $R_{coat}$) relative to other samples. Compositional variations of WC-( $Ti_{1-x}$ A $l_{x}$)N coatings were analyzed by EDS and XRD analysis was performed to evaluate the crystal structure and compounds formation behavior. Surface morphologies of the films were observed using SEM and AFM. Scratch test was performed to measure film adhesion strength.strength. adhesion strength.strength.