• Journal of the korean academy of Pediatric Dentistry
• /
• v.27 no.2
• /
• pp.370-378
• /
• 2000

The composite restorative resins have their insufficient resistance to wear. The subsurface degradation within the restoration is considered to be associated with wear. The aim of this study was to evaluate the resistance to degradation of six commercial composite resins in an alkaline solution. The brands studied were Clearfil APX(Kuraray), Heliomolar(Vivadent), Surefil(Dentsply), TPH(Dentsply), Tetric Ceram(Vivadent), and Z100(3M). Preweighed discs of each brand were exposed 0.1N NaOH solution at $60^{\circ}C$. After 14 days they were removed, neutralized with HCL, washed with water and dried to constant mass at $60^{\circ}C$. Resistance to degradation was evaluated on the basis of the following parameters: (a) mass loss(%) - determined from pre-and post-exposure specimen weights; (b) Si loss (ppm)-obtained from ICP-AE analysis of solution exposed to specimens; and (c) degradation depth$({\mu}m)$ - measured microscopically (SEM) from polished circular sections of exposed specimens. The results were as follows: 1. The mass loss was in descending order by Z100, TC H, S, CL, TPH and in the range of $0.45\sim3.64%$ 2. The degradation layer depth was in descending order by H, Z100, S, TC, TPH, CL and in the range of $10.85\sim73.38{\mu}m$ 3. For the Si concentration, Z100 was the highest of all 4. The highly significant correlation(r=0.81, p<0.05) was observed between mass loss and degradation depth. 5. Under scanning electronmicroscopy, the degradation of connection between resin matrix and fillers was observed 2 weeks after soaking in NaOH solution.

• Restorative Dentistry and Endodontics
• /
• v.25 no.3
• /
• pp.359-370
• /
• 2000

The purpose of this investigation was to observe the viscoelastic properties of five commercial flowable(Aeliteflo, Flow it, Revolution, Tetric flow, Compoglass flow), three conventional hybrid(Z-100, Z-250, P-60) and two condensable(Synergy compact, SureFil) resin composites. A dynamic oscillatory shear test was done to evaluate the storage shear modulus (G'), loss shear modulus(G"), loss tangent(tan ${\delta}$) and complex viscosity(${\eta}^*$) of the resin composites as a function of frequency - dynamic frequency sweep test from 0.01 to 100 rad/s at $25^{\circ}C$ - by using Advanced Rheometric Expansion System(ARES). To investigate the effect on the viscosity of resin composites of filler volume fraction, the filler weight % and volume % were measured by means of Archimedes' principle using a pyknometer. The results were as follows 1. The complex viscosity ${\eta}^*$ of flowable resins was lower than that of hybrid resins and significant differences were observed between brands. The complex viscosity ${\eta}^*$ of condensable resins was higher than that of hybrid resins. The order of complex viscosity ${\eta}^*$ at ${\omega}$=10 rad/s was as follows, Surefil, Synergy compact, P-60, Z-250, Z-100, Aeliteflo, Tetric flow, Compoglass flow, Flow it, Revolution. The relative complex viscosity of flowable resins compared to Z-100 was 0.04~0.56 but Surefil was 30.4 times higher than that of Z-100. 2. The storage shear modulus G' and the loss shear modulus G" of flowable resins were lower than those of hybrid resins but those of condensable resins were higher. The patterns of the change of loss tangent, tan ${\delta}$, of resin composites with increasing frequency were significantly different between brands. The phase angles, ${\delta}$, ranged from $30.2{\sim}78.1^{\circ}$ at ${\omega}$=10 rad/s. 3. All composite resins represent pseudoplastic nature with increasing shear rate. 4. The complex shear modulus $G^*$ and the phase angle ${\delta}$ was represented by the frequency domain phasor form, $G^*({\omega})=G^*e^{i{\delta}}=G^*{\angle}{\delta}$. The locus of frequency domain phasor plots in a complex plane was a valuable method that represent the viscoelastic properties of composite resins. 5. There was no direct linear correlationship but a weak positive relation was observed between filler volume % or weight % and the viscosity of the resin composites.

• Restorative Dentistry and Endodontics
• /
• v.27 no.3
• /
• pp.284-289
• /
• 2002

Background : The purpose of the present study was to evaluate the direct and indirect composite restorations which had been placed for 1 year Methods : The composite restorations which had been placed between 1999. Mar and 1999, Dec was evaluated after 1 year For direct restorations. Spectrum (Dentsply, USA) and Z100 (3M, USA) were used in the anterior teeth and Surefil (Dentsply, USA) were used. For class V restorations of anterior and posterior teeth. Spectrum was used. For indirect restorations, Targis/Vectris system (Vivadent/Ivoclar, Liechtenstein) was used 2 examiners evaluated marginal quality, proximal contact. discoloration, presence of 2$^{nd}$ caries, loss of filling and hypersensitivity of restorations. The restorations was clinically evaluated by modified methods based on USPHS. Results : 60 teeth were evaluated. 59 were clinically acceptable and 1 restoration which was placed in class v cavity in the posterior tooth was fallen out. In most cases, the restorations were clinically accept-able. For restorations which had been directly placed in the class II cavities, loose proximal contact was indicated as the main complaints. Conclusions : Most of Anterior and posterior restorations which bad been directly or indirectly placed for 1 year were clinically acceptable. For posterior teeth, loose proximal contact was indicated as the main problem in the directly placed Class II restorations. Long term clinical study is needed.

• Restorative Dentistry and Endodontics
• /
• v.26 no.4
• /
• pp.326-331
• /
• 2001

목적 - 최근 복합레진의 미세변연누출을 줄이기 위한 새로운 광중합 조사방법이 연구되고 있다. 또한 구치용 복합레진이 개발되면서 그 제조회사에서는 5mm 깊이까지 광중합이 가능하다고 소개하고 있다. 본 연구에서는 논리적 가설에 근거한 몇가지 광중합 조사방법이 구치부 class II 와동의 복합레진 충전시 미세변연누출에 어떠한 영향을 미치는지를 관찰하였다. 재료 및 방법 - 100개의 우식증이 없는 사람의 상하악 대구치를 사용했다. 각 치아에 교합-치은방향으로 4mm, 협설 4mm, 깊이 2mm의 class II 와동을 형성하여 인접치와 함께 베이스플레이트 왁스에 매몰하고 구치용 복합레진인 Surefil을 제조 회사의 지시대로 충전하였다. 이때 5가지의 광조사방법을 이용하여 5개의 군으로 나누어 중합하였다(Table 1). 수복된 치아들을 5$^{\circ}C$와 55$^{\circ}C$의 수조에서 번갈아 1분씩 총 500회의 온도변화를 주어 thermocycling을 실시한 후 근첨을 폐쇄하고 수복와동의 치은경계를 제외한 전 표면에 nail varnish를 2회 도포하였다. 2%의 methylene blue용액에 24시간 침적시키고 흐르는 물에 세척한 후 시편을 투명한 에폭시 레진에 매몰하였다. 매몰된 시편을 치아 장축에 평행하게 절단 연마하였다. 입체 현미경으로 미세변연누출을 관찰하고 Kruskal-Wallis One Way ANOVA 와 Dunn's Method로 통계처리 하였다. 결과 - 1. 미세누출은 1군, 4군과 5군, 2군 3군 순으로 증가였다. 이때 1군, 4군과 5군은 통계적 유의성이 없었다(P>0.05). 2. 2군의 경우 1군, 4군, 5군에 비교하여 유의성 있게 미세누출이 많았으며(P<0.05) 3군에 비하여 유의성 있게 적게 나타났다(P<0.05). 3. 3군의 경우 다른 방법들에 비교하여 통계적으로 유의성 있게 미세누출이 많았다(P<0.05).