The effect of grain size on corrosion resistance and high temperature oxidation behavior was studied in 22Cr-15Ni-5W super austenitic stainless steels for desulfurization equipment as a heat power station. In the high temperature oxidation test, oxidation rate was increased as the temperature increased from $600^{\circ}C\;to\;800^{\circ}C$. In vapor, oxidation rate was faster than that in air. Because the vapor was inhibited nucleation of $Cr_2O_3$ film. And the high temperature oxidation resistance at $600^{\circ}C{\sim}800^{\circ}C$ was excellent from all specimens and specimen of the smallest grain size was the most excellent. Because increasing of diffusion course through the grain-boundary was promoted nucleation and growth of $Cr_2O_3$ film. In the test temperature at $600^{\circ}C{\sim}800^{\circ}C$, Cr rich round particle oxide was formed in air, whereas Fe rich needle type oxide was developed in vapor.

• Korean Journal of Materials Research
• /
• v.20 no.4
• /
• pp.194-198
• /
• 2010

Cubic boron nitride (c-BN) is a promising material for use in many potential applications because of its outstanding physical properties such as high thermal stability, high abrasive wear resistance, and super hardness. Even though 316L austenitic stainless steel (STS) has poor wear resistance causing it to be toxic in the body due to wear and material chips, 316L STS has been used for implant biomaterials in orthopedics due to its good corrosion resistance and mechanical properties. Therefore, in the present study, c-BN films with a $B_4C$ layer were applied to a 316L STS specimen in order to improve its wear resistance. The deposition of the c-BN films was performed using an r.f. (13.56 MHz) magnetron sputtering system with a $B_4C$ target. The coating layers were characterized using XPS and SEM, and the mechanical properties were investigated using a nanoindenter. The friction coefficient of the c-BN coated 316L STS steel was obtained using a pin-on-disk according to the ASTM G163-99. The thickness of the obtained c-BN and $B_4C$ were about 220 nm and 630 nm, respectively. The high resolution XPS spectra analysis of B1s and N1s revealed that the c-BN film was mainly composed of $sp^3$ BN bonds. The hardness and elastic modulus of the c-BN measured by the nanoindenter were 46.8 GPa and 345.7 GPa, respectively. The friction coefficient of the c-BN coated 316L STS was decreased from 3.5 to 1.6. The wear property of the c-BN coated 316L STS was enhanced by a factor of two.