• 한국환경과학회지
• /
• 제16권6호
• /
• pp.683-688
• /
• 2007

In this study, N doped $TiO_2$ (TiO-N) thin film was prepared by DC magnetron sputtering method to show the photocatalytic activity in a visible range. Various gases (Ar, $O_2\;and\;N_2$) were used and Ti target was impressed by 1.2 kW -5.8 kW power range. The hysteresis of TiO-N thin film as a function of discharge voltage wasn't observed in 1.2 and 2.9kW of applied power. Cross sections and surfaces of thin films by FE-SEM were tiny and dense particle sizes of both films with normal cylindrical structures. XRD pattern of $TiO_2$ and TiO-N thin films was appeared by only anatase peak. Red shift in UV-Vis adsorption spectra was investigated TiO-N thin film. Photoactivity was evaluated by removal rate measurement of suncion yellow among reactive dyes. The photodegradation rate of $TiO_2$ thin film on visible radiation was shown little efficiency but TiO-N was about 18%.

• 대한환경공학회지
• /
• 제27권1호
• /
• pp.59-66
• /
• 2005

[ $TiO_2$ ]박막은 DC 마그네트론 스퍼터링법을 이용하여 다양한 스퍼터링 파라미터(전력 $0.6{\sim}5.2\;kw$, 기판온도 실온${\sim}350^{\circ}C$, 산소량 $0{\sim}50\;sccm$($O_2+Ar$ 90 sccm, 압력은 약 1 mtorr))를 통하여 증착되었다. TiO-N박막도 가스의 유량비를 제외하고는 $TiO_2$박막과 같은 스퍼터링 조건하에서 증착되었다. 이러한 스퍼터링 파라미터에서 증착된 박막의 전기적 특성을 분석하기 위하여 시트저항을 측정하였고, 박막의 두께(${\alpha}$-step), 표면 거칠기(AFM), 형성 조직(FE-SEM, XRD)을 분석하여 최적 스퍼터링 파라미터를 도출하였다. 최적 스퍼터링 파라미터에서 제조된($TiO_2$, TiO-N)박막을 이용하여 광활성도를 평가하기 위하여 VOCs물질 중 toluene, 반응성 염료인 Suncion Yellow를 대상 물질로 선정하여 적용성 연구를 수행하였다. 실험에서 광촉매 박막은 적용물질에 대해서 광활성을 양호하게 보였으며, 특히 TiO-N광촉매 박막은 가시광 영역에서도 최대 33%의 톨루엔(5 ppm) 제거 효율을 나타내었다.