• Korean Journal of Mineralogy and Petrology
• /
• v.35 no.2
• /
• pp.111-123
• /
• 2022

Carbonate green rust (CGR) and sulfate green rust (SGR) commonly occur in nature. In this study, CGR and SGR were synthesized through co-precipitation, and their formation mechanisms and physicochemical properties were investigated. X-ray diffraction (XRD) and Rietveld refinement showed both CGR and SGR with layered double hydroxide structure were successfully synthesized without any secondary phases under each synthetic condition. Refined structural parameters (unit cell) for two green rusts were a (=b) = 3.17 Å and c = 22.52 Å for CGR and a (=b) = 5.50 Å and c = 10.97 Å for SGR with the crystallite size 57.8 nm in diameter from (003) reflection and 40.1 nm from (001) reflections, respectively. Scanning electron microscopy/energy dispersive X-ray spectroscopy (SEM/EDS) results showed that both CGR and SGR had typical hexagonal plate-like crystal morphologies but their chemical composition is different in the content of C and S. In addition, Fourier transform infrared (FT-IR) spectroscopy analysis revealed that carbonate (CO₃^2-) and sulfate (SO₄^2-) molecules were occupied as interlayer anions of CGR and SGR, respectively. These SEM/EDS and FT-IR results were in good agreement with XRD results. Changes in the solution chemistry (i.e., pH, Eh and residual iron concentrations (Fe(II):Fe(III)) of the mixed solution) were observed as a function of the injection time of hydroxyl ion (OH^-) into the iron solution. Three different stages were observed in the formation of both CGR and SGR; precursor, intermediator, and green rust in the formation of both CGR and SGR. This study provides co-precipitation methods for CGR and SGR in a way of the stable synthesis. In addition, our findings for the formation mechanisms of the two green rusts and their physicochemical properties will provide crucial information with researches and industrials in utilizing green rust.

• Journal of Korean Society of Environmental Engineers
• /
• v.29 no.7
• /
• pp.778-782
• /
• 2007

This study investigated the dechlorination mechanisms of TCE by Fe(II) associated with cement. Batch slurry experiments were peformed to investigate the behaviors of selected ions; Fe(II), Fe(III), $Ca^{2+}$, $SO_4^{2-}$ in cement/Fe(II) system. The kinetic experiments of TCE in cement/Fe(II) systems showed that injected Fe(II) was mostly sorbed on cement within 0.5 day and 90% of injected 200 mM sulfate was sorbed on cement within 0.5 day when $[TCE]_0$ = 0.25 mM and $[Fe(II)]_0$ = 200 mM. The kinetic experiments of TCE in hematite/CaO/Fe((II) systems were conducted for simulation of cement/Fe(II) system. Calcium oxide that is one of the major components in cement hydration reactions or has a reactivity in limited conditions. Hematite assumed the ferric iron oxide component of cement. The reactivities observed in hematite/CaO/Fe(II) system were comparable to those reported for cement/Fe(II) systems containing similar molar amounts of Fe(II). The behavior of Fe(II) and $SO_4^{2-}$ sorbed on solid phase at an early stage of reaction in hematite/CaO/Fe(II) system was similar to that of cement/Fe(II) system. Ferric ion was released from hematite at an early period of reaction at low pH. The experimental evidence of kinetic test using hematite/CaO/Fe(II) system implies that the reactive reductant is a mixed-valent Fe(II)-Fe(III) mineral, which may be similar to green rust. Fe(II) sorbed on cement can be converted to new mineral phase having a reactivity such as Fe(II)-Fe(III) (hydr)oxides in cement/Fe(II) systems.