• Journal of the Korean Institute of Electrical and Electronic Material Engineers
• /
• v.19 no.2
• /
• pp.145-152
• /
• 2006

The densification behavior and electrical conductivity of $Ce_{0.8}Gd_{0.2}O_{1.9}$ ceramics were investigated with the strontium gallate concentration ranging from 0 to $5\;mol\%$. Both the sintered density and grain size were found to increase rapidly up to $0.5\;mol\%$ $Sr_2Ga_2O_5$, and then to decrease with further addition. Dense $Ce_{0.8}Gd_{0.2}O_{1.9}$ ceramics with $97\%$ of the theoretical density could be obtained for $0.5\;mol\%$ $Sr_2Ga_2O_5$-added specimen sintered at $1250^{\circ}C$ for 5 h, whereas pure $Ce_{0.8}Gd_{0.2}O_{1.9}$ ceramics needed to be sintered at $1550^{\circ}C$ in order to obtain an equivalent theoretical density, Electrical conductivity was measured as a function of dopant content, over the temperature range of $350\;-\;600^{\circ}C$ in air. Total conductivity of $0.5\;mol\%$ $Sr_2Ga_2O_5$-added specimen showed the maximum conductivity of $2.37{\times}10^{-2}{{\Omega}-1}{\cdot}cm^{-1}$ at $500^{\circ}C$, The addition of strontium gallate was found to promote the sintering properties and electrical conductivities of $Gd_2O_3$-doped $CeO_2$.