• Structural Engineering and Mechanics
• /
• v.44 no.4
• /
• pp.417-429
• /
• 2012

Taking the superficial temperature increment as the major fatigue damage indicator, the infrared thermography was used to predict fatigue parameters (fatigue strength and S-N curve) of welded joints subjected to fatigue loading with a high mean stress, showing good predictions. The fatigue damage status, related to safety evaluation, was tightly correlated with the temperature field evolution of the hot-spot zone on the specimen surface. An energetic damage model, based on the energy accumulation, was developed to evaluate the residual fatigue life of the welded specimens undergoing cyclic loading, and a good agreement was presented. It is concluded that the infrared thermography can not only well predict the fatigue behavior of welded joints, but also can play an important role in health detection of structures subjected to mechanical loading.

• Proceedings of the Korean Society of Machine Tool Engineers Conference
• /
• 2005.05a
• /
• pp.191-196
• /
• 2005

The effects of shot peening on the fatigue strength of SK-5M steel is investigated by experiment. The shot peening process is investigated optimum peening condition by changing impeller speed and exposure time. Bending fatigue test is accomplished to investigate the effect of optimum peening condition on the fatigue characteristics. As exposure time is increased, fatigue life in high stress is increased in early stage, become the maximum from 60 to 100 seconds, and then is decreased. Observing fracture surface through SEM after fatigue test, we can see clear configuration of cracks and peening layer.

• The KSFM Journal of Fluid Machinery
• /
• v.16 no.4
• /
• pp.15-21
• /
• 2013

This study aims to estimate the fatigue resistance of small wind composite blade using the fatigue life estimation formula in the GL guideline. For this, firstly, we estimated a turbine blade's bending moment spectrum by using wind profile wind profile and BEMT. And fatigue tests were performed to obtain the S-N curve of composite materials used in blade. In addition, a finite element analysis was used to identify fatigue critical locations and fatigue stress spectrum. And the fatigue resistance of composite blade were evaluated using the rainflow cycle counting, and Goodman diagram and the fatigue life estimation formula in the GL guideline.

• Journal of the Korean Society of Marine Environment & Safety
• /
• v.27 no.2
• /
• pp.387-393
• /
• 2021

In this study, finite element analysis was performed to evaluate a method of increasing the fatigue life of the pipe connection structure commonly used in the topside structure of offshore platforms. MSC Patran/Nastran, a commercial analysis program, was used, and the critical structural model was selected from the global analysis. To realize the stress concentration phenomenon according to the load, modeling using 8-node solid elements was implemented. The main loads were considered to be two lateral loads and a tensile load on a diagonal pipe. To check the hotspot stress at the main location, a 0.01 mm dummy shell element was applied. After calculating the main stress at the 0.5-t and 1.5-t locations, the stress generated in the weld was estimated through extrapolation. In some sections, this stress was observed to be below the fatigue life that should be satisfied, and reinforcement was required. For reinforcement, a bracket was added to reduce the stress concentration factor where the fatigue life was insufficient without changing the thickness or diameter of the previously designed pipe. Regarding the tensile load, the stress in the bracket toe increased by 23 %, whereas the stress inside and outside of the pipe, which was a problem, decreased by approximately 8 %. Regarding the flexural load, the stress at the bracket toe increased by 3 %, whereas the stress inside and outside of the pipe, which was also a problem, decreased by approximately 48 %. Owing to the new bracket reinforcement, the stress in the bracket toe increased, but the S-N curve itself was better than that of the pipe joint, so it was not a significant problem. The improvement method of fatigue life is expected to be useful; it can efficiently increase the fatigue life while minimizing changes to the initial design.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.19 no.6
• /
• pp.1422-1430
• /
• 1995

Al6061 alloy reinforced with 15 volume% of Saffil fibers was fabricated by squeeze infiltration method. Uniform distribution of reinforcements and good bondings between reinforcements and matrix alloy were found in the microstructure of composites. Comparing with A16061 matrix alloy, tensile strength and elastic modulus of $Al_{2}$O$_{3}$/Al composites were increased up to 26% and 31%, respectively. Cyclic deformation and fatigue behavior of $Al_{2}$O$_{3}$/Al metal matrix composites were studied. The specimens were cycled using tension-tension(R=0.1) loading and under load controlled fatigue test. Cyclic stress-displacement curve through fatigue test was obtained. Fatigue strength of $Al_{2}$O$_{3}$/Al composites was about 200 MPa, i.e.0.55 of applied stress level(q). During fatigue test, $Al_{2}$O$_{3}$/Al composites displayed cyclic hardening at all applied stress levels. The most of resultant displacement due to permanent plastic deformation occurred in less than the first 5% of fatigue life. Displacement-to-failure of the fatigue test was smaller than that of the tensile test because of accumulative damage by cumulative plastic deformation.

• Steel and Composite Structures
• /
• v.22 no.2
• /
• pp.353-368
• /
• 2016

This paper extends our recent work on the fatigue behavior of stud shear connectors in steel and recycled tyre rubber-filled concrete (RRFC) composite beams. A series of 16 fatigue push-out tests were conducted using a hydraulic servo testing machine. Three different recycled tyre rubber contents of concrete, 0%, 5% and 10%, were adopted as main variable parameters. Stress amplitudes and the diameters of studs were also taken into consideration in the tests. The results show that the fatigue lives of studs in 5% and 10% RRFC were 1.6 and 2.0 times greater of those in normal concrete, respectively. At the same time, the ultimate residual slips' values of stud increased in RRFC to highlight its better ductility. The average ultimate residual slip value of the studs was found to be equal to a quarter of studs' diameter. It had also been proved that stress amplitude was inversely proportional to the fatigue life of studs. Moreover, the fatigue lives of studs with large diameter were slightly shorter than those of smaller ones and using larger ones had the risk of tearing off the base metal. Finally, the comparison between test results and three national codes was discussed.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.2 no.6
• /
• pp.1-8
• /
• 1994

To enhance the strength of gears for transmission, Generally caburizing heat treatment is applied. But there are some problems in this technology the distortion of gears during heat treatment process, and the discontinuity of manufacturing process. For these reasons, the high frequency induction hardening process is widely used. This method is one of the surface hardening process to improve the wear resistance and fatigue life of the machine components. In this study, to compare the bending fatigue strength of caburized gear with that of induction hardened gear, bending fatigue testing of gears with two different cases was performed by using an electrohydraulic servo-controlled fatigue testing machine and double tooth bending fatigue test fixture. Fatigue life distributions at constant stress levels were established directly from fatigue data. For gear design, the fatigue strength distribution at specified life is more important. This distribution is obtained by statical transformation from fatigue life distribution. Reliability of bending fatigue strength was estimated by P-S-N curves and Weibull distribution.

• Transactions of the Korean Society of Automotive Engineers
• /
• v.13 no.2
• /
• pp.1-9
• /
• 2005

An end beam is one of the most important structural members supporting uncovered freight under in-service loading. In general, it needs to endure over 25 years. However fatigue fracture has occurred at dynamic stress concentration location of the end beam because user's specifications demanded high speed and vehicle manufacturer made the uncovered freight car with comparatively low strength and stiffness. For durability analysis, finite element analysis is performed to evaluate the problem of uncovered freight structure and local strain. The uncovered freight car was operated on actual problematic railroad line to measure dynamic stress versus time history on the critical part from which a crack is initiated often. Rainflow cycle counting method was used to estimate fatigue damage at dangerous area under operating condition. Therefore, this study shows that analytical fatigue life at the end beam can be predicted on the basis of S-N curve and structure analysis and has a fairly good correlation with experimental fatigue life.

• Journal of Ocean Engineering and Technology
• /
• v.4 no.2
• /
• pp.250-250
• /
• 1990

In this paper, fatigue tests were carried out at stress test levels of 461 MPa, 441 MPa, and 431 MPa by using smooth specimen of$2_{1/4}$ Cr-1 Mo steel with the stress ratio(R) of 0.05. The initiation, growth and coalescense process of the major cracks and sub-cracks among the fatigue cracks on the smooth specimen are investigated and measured under each stress level at a constant cycle ratio by the replica technique with optical microscope. Some of the important results are as follows: In spite of the difference of stress levels, the major crack data gather into a small band in the curve of surface crack length and crack depth against cycle ratio N/Nf. The sub-crack data, however, deviate from the band of the major crack. The growth rates, da/dN, of major and sub-crack plotted against the stress intensity factor range, ${\Delta}K$, have the tendency to be compressed on a relatively small band. But it is more effective to predict fatigue life through major cracks. The propagation behavior of surface microcracks on the smooth specimens coincides with that of the specimen having an artificial small surface defect or through crack.

• Journal of the Korean Society for Railway
• /
• v.20 no.5
• /
• pp.658-667
• /
• 2017

Rail is the main track component, playing the most important role in safe railways. For the sake of safety, it is strictly required to secure reliability against fatigue and destruction of rail. In this paper, by field measurement on concrete track, it is confirmed that the rail surface roughness and rail bending stress are linearly correlated with each other; the bending stress of rail can be presented as a function of train speed, track support stiffness, and rail surface roughness. The fatigue life of rail can be estimated by deriving the S-N curve through the fatigue test.