• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 2003.05a
• /
• pp.295-298
• /
• 2003

High temperature deformation behavior of a Ti-Al intermetallic compound has been investigated. Specimens with a near gamma and a lamella structures were obtained by performing heat treatment at 1200 and 1330$^{\circ}C$, respectively, for 24 hr and stabilized at 900$^{\circ}C$ for 4 hr followed by air cooling. A series of load relaxation tests has been conducted on these samples at temperatures ranging from 850 to 950$^{\circ}C$ to construct flow curves in the strain rate range from 10$\^$-6//s to 10$\^$-3//s. Strain hardening was observed even at the temperature of 950$^{\circ}C$ in both the near gamma and the lamella structures. Further aging treatment for 12 hr at test temperatures has found to cause no softening in both microstructures.

• Proceedings of the Korean Society for Technology of Plasticity Conference
• /
• 1999.03b
• /
• pp.135-139
• /
• 1999

The static softening behavior of AISI 4140 could be characterized by the hot torsion test in the temperature ranges of 10$0^{\circ}C$~120$0^{\circ}C$ and strain rate ranges of 0.05/sec~5/sec. Deformation efficiency which was based on dynamic materials model was calculated from flow stress curves obtained continuous deformation. Interrupted deformation was performed with 2 pass deformation in the pass strain ranges of 0.25{{{{ epsilon _p}}}} ~3{{{{ epsilon _p}}}} and interrupted time ranges of 0.5~100sec. The dependences of process variables pass strain ({{{{ epsilon _i}}}}) stain rate ({{{{ {. } atop {$\varepsilon$ } }}}}) temperature (T) and interpass time ({{{{ {t }_{i } }}}}) on static recrystallization (SRX) and metadynamic recrystallization .(MDRX) could be indicidually predicted from the modified Avrami's equations. Comparison of the softening kinetics between MDRX and SRX showed that the rate of MDRX was more rapid than that of SRX for the same deformation variables. Controlled multipass deformations were performed using deformation efficiency static and metadynamic recrystallization of AISI 4140.

• Proceedings of the Computational Structural Engineering Institute Conference
• /
• 2000.10a
• /
• pp.182-189
• /
• 2000

This paper presents a simple and reliable constitutive model for predicting the nonlinear response of reinforced concrete subjected to general membrane loadings. Based on the concept of equivalent uniaxial strain, constitutive relations of concrete are presented in the axes of orthotropy. The behavior of cracked concrete is described by a system of orthogonal cracks, which follows the principal strain directions and rotates according to the loading history. Simple hysteretic rules defining the cyclic stress-strain curves of concrete and steel are used. In addition, the stiffness and strength degradation of cracked concrete is included in the formulation. Correlation studies between analytical results and experimental values from idealized shear panel tests are conducted with the objective to establish the validity of the proposed model.

• Metals and materials international
• /
• v.24 no.6
• /
• pp.1249-1255
• /
• 2018

High temperature compression tests for newly developed Al-Zn-Mg alloy were carried out to investigate its hot deformation behavior and obtain deformation processing maps. In the compression tests, cylindrical specimens were deformed at high temperatures ($300-500^{\circ}C$) and strain rates of 0.001-1/s. Using the true stress-true strain curves obtained from the compression tests, processing maps were constructed by evaluating the power dissipation efficiency map and flow instability map. The processing map can be divided into three areas according to the microstructures of the deformed specimens: instability area with flow localization, instability area with mixed grains, and stable area with homogeneous grains resulting from continuous dynamic recrystallization (CDRX). The results suggest that the optimal processing conditions for the Al-Zn-Mg alloy are $450^{\circ}C$ and a strain rate of 0.001/s, having a stable area with homogeneous grains resulting from CDRX.

• Korean Journal of Metals and Materials
• /
• v.48 no.4
• /
• pp.305-314
• /
• 2010

The development of textures and microstructures during plastic deformation in a hot-extruded AZ 31 Mg alloy was investigated using a compression test with such parameters as deformation temperature, strain rate. It was observed from true stress-strain curves that twinning involves changes of the flow stresses. In the early stages of deformation at temperatures lower than $200^{\circ}C$, the occurrence of twins resulted in a decrease of the work-hardening rate, which increased drastically at a true strain of -0.05. The evolution of the deformation textures were assessed with the aid of EBSD analyses in terms of the competition between twinning and slip activity.

• Journal of the Korea Concrete Institute
• /
• v.15 no.5
• /
• pp.726-736
• /
• 2003

Concrete columns confined with high-strength fiber composites can enhance its strength as well as maximum strain. In recent years, several equations have been developed to predict the behavior of the concrete columns confined with fiber composites. While the developed equations can predict the compressive strength of the confined columns with reasonable agreement, these equations are not successful in predicting the observed maximum strain of the columns. In this paper, a total of 61 test results is analysed to propose an equation to predict both compressive strength and maximum strain of concrete cylinders. The proposed equation takes into account the effects of confining pressure and cylinder size. Furthermore, in order to verify the proposed stress-strain curve for concrete cylinders, six cylindrical specimens were tested. Comparisons between the observed and calculated stress-strain curves of the tested cylinders showed reasonable agreement.

• Journal of the Korean Recycled Construction Resources Institute
• /
• v.6 no.4
• /
• pp.349-356
• /
• 2018

In this study, material properties of steel fiber reinforced high strength concrete (FRHSC) with the compressive strength of about 120MPa were modeled. Steel fiber content of 1.0%, 1.5%, and 2.0% was considered as experimental variable. First of all, compressive strength tests were carried out to determine compressive characteristics of concrete, and compressive stress-strain curves were modeled. For conventional concrete with moderate compressive strength, the stress-strain curves are in the form of parabolic curves, but in the case of high strength concrete reinforced with steel fiber, the curves increase linearly in the form of the straight line. In addition, to understand the tensile properties of FRHSC, the crack mouth opening displacement (CMOD) test was performed, and the tensile stress-CMOD curve was calculated through inverse analysis. When the steel fiber content increased from 1.0% to 1.5%, there was a significant difference of tensile strength. However, when the amount of steel fiber was increased from 1.5% to 2.0%, there was no significant difference of tensile strength, which might result from the poor dispersion and arrangement of steel fiber in concrete.

• Proceedings of the KSME Conference
• /
• 2004.11a
• /
• pp.190-195
• /
• 2004

The compression-compression fatigue properties of the closed cell Al-Si-Ca alloy foams have been studied. The monotonic and cyclic compressive properties were compared with each other and the fatigue stress-life (S-N) curves were presented. In compression-compression fatigue, the crushing was found to initiate in a single band which broadens gradually with additional fatigue cycles. Progressive shortening of the specimen took place due to a combination of low cycle fatigue failure and cyclic ratcheting which is in accordance with the findings of previous researchers [1-3]. Young's modulus of the foam was found to decrease with the increasing strain in case of fatigue test however in case of monotonic compression test the value of Young's modulus increased with the strain (number of cycles). The endurance limit on the basis of $10^{7}$ cycles obtained by extrapolating the experimental results were 0.98 MPa and 1.70 MPa for load ratios 0.1 and 0.5 respectively which are 34 % and 59 % of the plateau stress.

• Journal of Mechanical Science and Technology
• /
• v.14 no.2
• /
• pp.152-158
• /
• 2000

The contents of this paper include the evaluation of corrosion characteristics and the behaviour of stress corrosion cracking (SCC) for the weldment and post weld heat treatment (PWHT) specimen and parent of HT -60 steel using a slow strain rate test (SSRT) in synthetic seawater. Corrosion characteristics were obtained from the polarization curves by potentiostat, and SCC phenomena were evaluated through the parameters such as reduction of area and time to failure by comparing the experimental results in corrosive environment with those obtained in air. Corrosion rate of the weldment was the fastest, followed by parent and PWHT specimen. SCC phenomena between the weldment of HT-60 steel and synthetic seawater were shown. Besides, SCC was dependent upon the pulling speed greatly. Maximum severity of SCC was obtained at a speed of $10^{-6}mm/min$, whereas SCC could not be seen almost at $10^{-4}mm/min$. The resistance to SCC for PWHT specimen was improved considerably compared that of the weldment at $10^{-6}mm/min$. In case of SCC failure, it was verified from SEM examination that brittle mode and lots of pits could be seen at the fractured region near the surface of the specimen.

• Journal of the Korean Ceramic Society
• /
• v.41 no.1
• /
• pp.19-23
• /
• 2004

The Hertzian indentation contact damage behavior of porous alumina with controlled pore shape was investigated by experiments. Porous alumina ceramics containing well-defined pore shape, size and distribution were prepared by incorporation of fugitive spherical starch. Porous alumina with isolated pore structure was prepared with porosity range up to 30%. The indentation stress-strain curves of porous alumina were constructed. Elastic modulus and yield stress can be obtained from the stress-strain relationship. Impulse excitation method for the measurement of elastic modulus was also conducted as well as Hertzian indentation and was confirmed as a useful tool to evaluate the elasticity of highly porous ceramics. Elastic modulus of the inter-connected pore structure is more sensitive to porosity than that of the isolated pore structure. When the specimen had isolated pore structure, higher yield point was obtained than it had inter-connected pore structure. This study proposed that the elastic modiulus of porous ceramics is strongly related to not only porosity, but also the structure of pore.