• 대한기계학회논문집A
• /
• 제32권11호
• /
• pp.911-917
• /
• 2008

It was found that more than 60% of the steam turbine blade damages occurred under the condition alternatively repeated wet and dry of vapor and condensed vapor at the lower pressure stage. And also, it has been well known that both the mechanical properties and environmental strength of the steam turbine blade can be changed by the crystal structure. However, in spite of these common facts, it is difficult to find out the quantitative results including the particular environmental condition as well as the actual service conditions. In this study, as a fundamental investigation to provide design information and reliability evaluation of the 12Cr alloy steel used for a steam turbine blade, stress corrosion strength of the 12Cr alloy steel of which its crystal structure is different was assessed under $2.5{\sim}3.5wt.%$ NaCl solution at 90oC. From the results, S-t curves for predicting damage life and design criterion of the 12Cr alloy steel including corrosion environment as well as S.C.C. condition were obtained.

• 한국해양공학회지
• /
• 제17권3호
• /
• pp.39-45
• /
• 2003

Shot peening is an effective method of improving the fatigue strength of components and structures. The compressive residual stress produced by surface plastic deformation with shot peening is usually regarded as the major factor in increasing fatigue strength. In this study, the influence of shot peening on corrosion was investigated. Spring steel immersed in $3.5\%$ NaCl prior was used to evaluate the effect of shot peening on fatigue properties. The immersion test was performed on the five kinds of specimens with shot peened and unpeened. The distributions of residual stresses of shot peened spring steels were measured in an X-ray diffraction apparatus, using the two-point method. Corrosion potential, polarization curve, residual stress, etc. were investigated, based on the experimental results. From test results, the effect of shot peening on the corrosion was evaluated.

• Corrosion Science and Technology
• /
• 제18권3호
• /
• pp.102-109
• /
• 2019

The hydrogen diffusion and trapping model with a numerical finite difference method (FDM) was modified and extended to accommodate $H_2S$ corrosion and scale forming processes of high-strength steel under tensile stress condition. The newly proposed diffusion model makes it possible to clearly understand combined effect of tensile stress and $H_2S$ corrosion process on hydrogen diffusion behaviors. The core concept of this theoretical approach is that overall diffusion behavior is separated into diffusion process through two respective layers: an outer sulfide scale and an inner steel matrix. Diffusion coefficient values determined by curve-fitting permeation data reported previously with the newly proposed diffusion model indicate that the application of tensile stress can contribute to continual increase in the diffusivity in the sulfide scale with a high density of defect. This suggests that the scale with a lower stability under the stress condition can be a key parameter to enhance hydrogen influx in the steel matrix. Consequently, resistance to hydrogen assisted cracking of the steel under tensile stress can be decreased significantly.

• Structural Engineering and Mechanics
• /
• 제14권2호
• /
• pp.209-221
• /
• 2002

In this paper a fracture criterion is proposed for cracked cylindrical samples of high-strength prestressing steels of different yield strength. The surface crack is assumed to be semi-elliptical, a geometry very adequate to model sharp defects produced by any subcritical mechanism of cracking: mechanical fatigue, stress-corrosion cracking, hydrogen embrittlement or corrosion fatigue. Two fracture criteria with different meanings are considered: a global (energetic) criterion based on the energy release rate G, and a local (stress) criterion based on the stress intensity factor $K_I$. The advantages and disadvantages of both criteria for engineering design are discussed in this paper on the basis of many experimental results of fracture tests on cracked wires of high-strength prestressing steels of different yield strength and with different degrees of strength anisotropy.

• Journal of Advanced Marine Engineering and Technology
• /
• 제19권3호
• /
• pp.62-69
• /
• 1995

In order to investigate the effect of TiN coating on corrosion fatigue behavior of metal, the rotary bending corrosion fatigue tests were carried out in 3% NaCl solution by using the round bar specimens of high-speed steel, SKH-9, coated with TiN by PVD method. From the experimental results, fatigue strength of TiN coating steel in air was obvious improvement as compared with that of the substrate because of the restriction of dislocation movement in near surface of the substrate by hard thin film. In 3% NaCl solution, corrosion fatigue life of TiN coating specimen in high stress level was improvement same as in air. But in low stress level, corrosion fatigue life of TiN coating one was equivalent to that without coating, due to much crack initiated from corrosion pits formed at the substrate by failure of coating layer.

• Corrosion Science and Technology
• /
• 제4권1호
• /
• pp.33-38
• /
• 2005

Some feasibility studies are conducted to produce an advanced ceramic coating, which reveals superior chemical and mechanical strength, on metal base structure used in chemical plant. This advanced coating on metallic frame can replace ceramic delivery pipe and reaction chamber used in chemical plant, which are operated in hi-temperature and corrosive/erosive environment. An dual spraying is adopted to reduce the residual stress in order to increase the coating thickness and the residual stress is estimated by in-situ manner. Then new methodology is tried to form special coating of yttrium aluminum garnet(YAG), which reveals hi-strength and low-creep rates at hi-temperature, superior anti-corrosion property, hi-stability against Alkali-Vapor corrosion, and so on, on iron base structure. To verify the formation of YAG during thermal spraying, XRD(X ray diffraction) technique was used.

• 대한기계학회:학술대회논문집
• /
• 대한기계학회 2004년도 춘계학술대회
• /
• pp.102-107
• /
• 2004

Suspension part should have enough endurance during its lifetime to protect passenger. Therefore, the coil spring is one of the major suspension part of an automobile. Corrosion fatigue strength of the coil spring depends on many factors including mechanical and environmental properties. In this paper, residual stresses by shot peening was analyzed using finite element analysis and evaluated its effect on corrosion fatigue strength.

• Journal of Welding and Joining
• /
• 제11권2호
• /
• pp.42-52
• /
• 1993

The corrosion fatigue fracture behaviour of dual phase steel was investigated in 3% NaCl solution at 302MPa and 137MPa. Fatigue test was conducted by cantilever type of self-made rotary bending fatigue testing machine. The fatigue strength increased with increasing the hardness of 2nd phase. Corrosion pit originated at the boundary of the 2nd phase. The size and number of corrosion pits were influenced by the 2nd phase hardness, and pits remained constant in size just after they were transited into cracks. The life of crack initiation was effected by stress level. The shape of relation of .DELTA. K and da/dN has smaller scattering in it in 3% NaCl solution than that in air. The higher the 2nd phase hardness is, the greater the corrosion fatigue life becomes. Corrosion fatigue fracture behaviour was primarily effected by mechanical factor in case of high stress(302MPa), but by electro-chemical reaction in a lower stress(137MPa). As stress level got lower and hardness of the 2nd phase got higher, the roughness of fracture surface increased.

• 대한기계학회논문집A
• /
• 제29권7호
• /
• pp.930-937
• /
• 2005

One of the useful technology for light-weightening of components required in the automobile and machine industry is to use of high strength materials. To improve material properties, carbonizing treatment, nitrifying treatment, and shot-peening method are representatively applied, However, the shot-peening method is generally used to remove the surface defect of steel and to improve the fatigue strength on surface. Benefits by shot peening are to make increase resistance against fatigue, stress corrosion cracking, fretting, galling, erosion and closing of pores. In this paper, investigated the effect of shot peening on the corrosion of SUP-9 steel immersed in $3.5\%$ NaCl solution and corrosion characteristics by the heat treatment during shot peening process. The immersion test was performed on the four kinds of specimens. Corrosion potential, polarization curve, residual stress and etc. were investigated from the experimental results.

• 한국해양공학회지
• /
• 제2권2호
• /
• pp.122-129
• /
• 1988

Recently with the rapid development in marine and shipbuliding industries such as marine structures, ship and chemical plants, there occurs much interest in the study of corrosion fatigue characteristics which was closed up an important role in mechanical design. In this study, the 5086 Al-alloy was tested by use of rotary bending fatigue tester. The retardation effect of overload on the corrosion fatigue crack propagation in sea environment was quantitatively studied. 1) Retardation effect of corrosion fatigue crack propagation is most eminent when overload ratio is 1.52, overload magnitude corresponds to about 77% and 55% of yield strength and tensile strength respectively. 2) After overload ratio 1.52 was used, retardation of corrosion fatigue crack growth rate is largely retarded and quasi-threshold stress intensity factor range($\Delta\textrm{K}_{th}$) appears. 3) According to m of experimental constant, retardation effect of corrosion fatigue crack propagation corresponds to about 25% of constant stress amplitude when overload ratio is 1.52. 4) When overload ratio 1.52 was used, retardation parameter (RP) decreases to about 0.43 and corrosion sensitivity (S)decreses to about 2.1.