• Nuclear Engineering and Technology
• /
• v.54 no.12
• /
• pp.4481-4490
• /
• 2022

In this study, a new rupture disk corrosion test (RDCT) method was developed for real-time detection of stress corrosion cracking (SCC) initiation of Alloy 600 in a primary water environment of pressurized water reactors. In the RDCT method, one side of a disk specimen was exposed to a simulated primary water at high temperature and pressure while the other side was maintained at ambient pressure, inducing a dome-shaped deformation and tensile stress on the specimen. When SCC occurs in the primary water environment, it leads to the specimen rupture or water leakage through the specimen, which can be detected in real-time using a pressure gauge. The tensile stress applied to the disk specimen was calculated using a finite element analysis. The tensile stress was calculated to increase as the specimen thickness decreased. The SCC initiation time of the specimen was evaluated by the RDCT method, from which result it was found that the crack initiation time decreased with the decrease of specimen thickness owing to the increase of applied stress. After the SCC initiation test, many cracks were observed on the specimen surface in an intergranular fracture mode, which is a typical characteristic of SCC in the primary water environment.

• Journal of the Korea Safety Management & Science
• /
• v.9 no.1
• /
• pp.65-76
• /
• 2007

The likelihood of failure for the stress corrosion cracking (SCC) of caustic cracking, which affect to a risk of facilities, was analyzed through the risk based-inspection using API-581 BRD. We found that SCC of the caustic cracking was occurred above 5 % NaOH concentration, and the technical module subfactor (TMSF) was maximized for above 50 % concentration. The heat traced and monitoring were not sensitive to the TMSF with NaOH concentration and temperature. But the steam out was more of less affect minimum value of the TMSF. Also, the inspection number, the inspection effectiveness, and the year since inspection were very sensitive to the TMSF with NaOH concentration and temperature. Therefore, the plan of next inspection will be established with compositively considering those at once.

• Corrosion Science and Technology
• /
• v.17 no.1
• /
• pp.6-11
• /
• 2018

Outdoor exposure tests using of 7B04 aluminium alloy samples including plate, tensile and various SCC samples were carried out in Tuandao station, Shandong province (East of China) and Wanning station, Hainan province (South of China). Corrosion characteristics including weight loss, microstructure, tensile strength and SCC susceptibility were investigated. The corrosion rates in Tuandao and Wanning showed high to low and the corrosion rates changed to the following equation of $w=at^b$ (b<1). The corrosion of 7B04 aluminium alloy in Wanning was more serious than that in Tuandao. Pitting appeared at early stage of expose test, and it can be changed to general corrosion with test time extension. The 7B04 aluminium alloy of which specimen shapes are forging and thick plate also showed SCC (Stress corrosion cracking) in the marine atmosphere. The higher SCC sensitivity was observed in Wanning station than in Tuandao station. The 7B04 aluminium alloy with a high stress level was more sensitive to SCC. Intergranular and transgranular or a mixed mode of cracking can be observed in different marine exposure.

• Corrosion Science and Technology
• /
• v.3 no.1
• /
• pp.14-19
• /
• 2004

Crack growth rate and threshold stress intensity factor for stress corrosion cracking(SCC), $K_{ISCC}$ were measured for type 403 stainless steel in 3,5% NaCl solution at room temperature and SCC was monitored by electrochemical noise technique during $K_{ISCC}$ testing. In rising load test, pits were formed at the tip of pre-crack for the pre-cracked compact tension specimen unlike in smooth round specimen in which only unstable pits were observed and hence immune to SCC. Micro-cracks were found to initiate from the pits in the former specimen, and initiation of micro-crack as well as macro-crack was detected by electrochemical noise technique in rising load $K_{ISCC}$ tests. Crack growth rate increased with increasing either displacement rate or stress intensity factor at crack initiation and was higher in rising load $K_{ISCC}$ test compared to constant load $K_{ISCC}$ test at given stress intensities.

• Transactions of the Korean Society of Mechanical Engineers
• /
• v.8 no.6
• /
• pp.569-575
• /
• 1984

The characteristics of the stress corrosion cracking of SUS 304 stainless steel weldments were studied with the speciments of the constant displacement type under the environment of 42% MgC $l_{2}$ boiled solution (143.+.-.2.deg.C). The susceptibility of initiation and propagation of the stress corrosion crack was quantitatively inspected in the weld metal, heat affected zone and heat affected zone with including the reinforcement shape, respectively. Also, those susceptibility were discussed in connection with the change of mechanical and microstructural characteristics caused by heating cycle of welding. Main results obtained are as follows: (1)Stress corrosion cracking is easiest to initiate and propagate in the heat affected zone of weldment. (2)The susceptibility of stress corrosion cracking of the weldment is largely improved by eliminating the reinforcement part of the weld bead. (3)The dominant factor of the cracking susceptibility of the heat affected zone appeared to be the phenomenon of softening and sensitizing caused by welding heat cycle. (4)Under the low loading conditions, the behavior of stress corrosion cracking of the SUS 304 steel weldment is largely influenced by the pitting phenomenon in the front region of the main crack.

• 한국태양에너지학회:학술대회논문집
• /
• 2008.11a
• /
• pp.280-287
• /
• 2008

In case of low pressure steam turbine used in power plant, it was operated in wet steam and high stress condition. Therefore, it is possible that the corrosion damage of low pressure was induced by this condition. According to previous study, about 30% of total blade failure correspond to corrosion fatigue or SCC(stress corrosion cracking) in low pressure turbine. Especially, LSB(last stage bucket) of low pressure turbine has a higher hardness to prevent erosion damage due to water droplet however, generally this is more dangerous for SCC damage. Therefore, to improve reliability of turbine blade. various methods for SCC evaluation has been developed. In this study, the crack found in LSB during in-service inspection was evaluated using microstructure analysis and stress analysis. From the stress analysis, the optimum size of fillet to remove the crack was proposed. And also, the reliability was evaluated for modified LSB using GOODMAN diagram.

• Journal of the Korean institute of surface engineering
• /
• v.53 no.5
• /
• pp.219-226
• /
• 2020

This paper investigated the characteristics of anodized aluminum 6061-T6 alloy for corrosion and stress corrosion cracking(SCC) under natural seawater. The hard anodizing oxide film formed on the 6061-T6 was a uniform thickness of about 25 ㎛. The corrosion characteristics were performed with a potentiodynamic polarization test. SCC was characterized by a slow strain rate tensile test under 0.005mm/min rate. As a result, the anodizing film showed no significant effect on SCC in the slow strain rate test. However, the corrosion current density of base metal was measured to be approximately 13 times higher than that of the anodized specimen. Therefore, the anodizing film significantly improved the corrosion resistance of 6061-T6 alloy in natural seawater.

• Journal of Welding and Joining
• /
• v.12 no.4
• /
• pp.63-75
• /
• 1994

The conventional SCC(stress corrosion cracking) test methods have much difficulty in evaluating the SCC behaviors of the localized zone like HAZ, bond line and weld metal because of the specimen size. Accordingly, the purpose of this paper is to develop the new SCC test method of the welded zone by evaluating the SCC susceptibility on parent metal and various microstructures of the welded zone by SP(small punch) test method using miniaturized small specimen and SSRT(slow strain rate test) method(SP-SSRT). Besides, this study is to verify the efficiency of the SP-SSRT results through AE(acoustic emission) test which is a useful technique to monitor the microfracture processes of the material. From the results of SCC susceptibility, SEM observation and AE test, it can be concluded that the SP-SSRT test using miniaturized small specimen(10mm*10mm*0.5mm) will be a good test method to evaluate the SCC susceptibility on the local zone such as the welded zone.

• Journal of Welding and Joining
• /
• v.18 no.3
• /
• pp.97-105
• /
• 2000

The stress corrosion cracking(SCC) and hydrogen embrittlement cracking(HEC) characteristics of a weathering steel weldment were investigated in aerated acid-chloride solution. The electrochemical properties of weldment were investigated by polarization test and galvanic corrosion test. Weathering steel did not show passive behavior in the acid-chloride solution. Galvanic corrosion between the weld metal and the base metal was not observed because the base metal was anodic to the weld metal. The slow-strain-rate tests(SSRT0 were conducted at a constant strain rate o 7.87×{TEX}$10^{-7}${/TEX}/s at corrosion potential, and at potentiostatically controlled anodic and cathodic potentials. The weldment of weathering steel was susceptible to both anodic dissolution SCC and hydrogen evolution HEC.

• Corrosion Science and Technology
• /
• v.5 no.3
• /
• pp.85-89
• /
• 2006

KAERI(Korea Atomic Energy Research Institute) has developed a repassivation rate test system which can be operated at $300^{\circ}C$. It consists of an autoclave, three electrodes for an electrochemical test and a diamond scratch tip. All the electrodes are electrically insulated from the autoclave by using high temperature fittings. Reproducible repassivation curves of alloy 600 at 300 C were obtained. Repassivation rate of alloy 600 at pH 13 was slower than that of pH 10. Stress corrosion cracking test was carried as a function of the pH at a high temperature. At pH 10, alloy 600 showed a severe stress corrosion cracking(SCC), whereas it did not show a SCC at pH 7. From the viewpoint of a relationship between the current density and the charge density, a big difference was observed in the two solutions; the slope of pH 13 was steeper than that of pH 10. So the stress corrosion susceptibility at pH 13 seems to be higher than that of pH 10. The system would be a good tool to evaluate the SCC susceptibility of alloy 600 at a high temperature.