• Journal of the Korean Crystal Growth and Crystal Technology
• /
• v.17 no.6
• /
• pp.238-244
• /
• 2007

Nano-sized ZnO crystals were successfully incorporated using ion exchange method in TMA-A zeolite synthesized by the hydrothermal method. The optimal composition for the synthesis of TMA-A zeolite was resulted in a solution of $Al(i-pro)_3$:2.2 TEOS:2.4 TMAOH:0.3 NaOH:200 $H_2O$. 0.3g of TMA-A zeolite and 5mol of $ZnCl_2$ solution were employed for the preparation of ZnO incorporated TMA-A zeolite. The ZnO incorporated TMA-A zeolite precursors, prepared from the process of mixing, stirring, centrifugal separation and drying, were calcined at temperatures from 400 to $600^{\circ}C$ for 3 h. The crystallization process of ZnO incorporated TMA-A zeolite was analyzed by X-ray diffraction (XRD). The Brunaur-Emett-Teller (BET) surface area of the ZnO incorporated TMA-A zeolite was measured. Subsequently, the morphology and the particle size depending on the temperature and time were observed using scanning electron microscopy(SEM), transmission electron microscopy(TEM) and particle size analyzer.

• Resources Recycling
• /
• v.28 no.6
• /
• pp.36-45
• /
• 2019

The spent petroleum catalysts contain rare metals such as vanadium, nickel, molybdenum, and cobalt. Therefore, the leaching of these rare metals from spent petroleum catalysts by organic acid was investigated in the present study. The leaching efficiency of metals by organic acid was in the following order: oxalic acid > tartaric acid > citric acid > maleic acid > ascorbic acid. Among the organic acids employed in this work, oxalic acid can be considered to be superior to the other acids in terms of metals leaching efficiency. The effect of several leaching conditions such as temperature, acid concentration, pulp density, stirring speed, and reaction time on the leaching of metals was investigated. Vanadium and molybdenum were selectively dissolved by oxalic acid from the spent catalysts. The leaching kinetics of vanadium by oxalic acid was also investigated. An activation energy of 8.76 kJ/mol indicated that the leaching kinetics of vanadium by oxalic acid solution was controlled by mass transfer.

• Analytical Science and Technology
• /
• v.10 no.3
• /
• pp.203-208
• /
• 1997

Barium titanyl oxalate(BTO) was precipatated by utilizing the thermal decomposition of dimethyl oxalate in acidic aqueous solution having $BaCl_2$ and $TiCl_4$. Particle morphology of BTO was influeneced by the various experimental factors. i.e.. the faster rate to nucleation with higher temperature and the higher ratio of [DMO]/[$Ba^{2+}+Ti^{4+}$] was found to correspond to the faster rate of transformation of particle size distribution from unimodal to broad unimodal through bimodal. The BT powder obtained by calcination at $900^{\circ}C$ in air consists of larger particles than BT generated by general coprecipitation method and shows tetragonal symmetry. The stirring during reaction was also found to have much effect upon characteristics of BTO and BT.

• Transactions of the Korean Society of Mechanical Engineers B
• /
• v.36 no.10
• /
• pp.1033-1041
• /
• 2012

Performance evaluation of a direct carbon fuel cell (DCFC) was conducted according to coals and a graphite particle. Several fuel properties such as thermal reactivity, textural structure, gas adsorption characteristic, and functional groups on the surface of fuels were investigated and their effects on electrochemistry were discussed. The strong carbon structure inside of fuels led the rapid potential decreasing in high current density region, because it caused small surface area and low pore volume. The functional groups on the surface were related to the low current density region. The maximum current density and power density of fuels were affected by the total carbon content in fuels. The effect of operating conditions such as stirring rate and operating temperature was investigated in this study.

• Korean Journal of Food Science and Technology
• /
• v.29 no.2
• /
• pp.255-260
• /
• 1997

Glucomannan was isolated from konjac (Amorphophallus konjac) flour by precipitating in aqueous alcohol solution. Konjac glucomannan films were prepared at various concentrations up to 1.0% (w/v) in aqueous glycerol solutions. Tensile strength (TS), percent elongation (E), water vapor permeability (WVP) as the barrier property and the solubility of the films were varied with glucomannan concentrations, glycerol contents and storage humidities. TS was decreased as the glucomannan concentration in the film and relative humidity for storage increased, and E was vice versa. WVP showed better barrier properties compared with other polysaccharides films. Glycerol contents in the film significantly affccted TS and E, but did not affect WVP. The glucomannan films were completely dissolved in the water by 150 min stirring at room temperature.

• Journal of Korea Technical Association of The Pulp and Paper Industry
• /
• v.48 no.1
• /
• pp.75-81
• /
• 2016

This study was conducted to investigate the effects of deep eutectic solvent (DES) treatment on BCTMP fibers and handsheets properties. DES was prepared using lactic acid and betaine (LB), and the molar ratio of these two components mixtures was controlled to 2:1 (LB 2:1) and 5:1 (LB 5:1). As results, 2% of BCTMP pulp (o.d. weight) was extracted when it was treated by LB 5:1 at $50^{\circ}C$ for 12 hours, stirring constantly at 120 rpm. In contrast, lignin was not extracted when BCTMP was mildly treated by the LB DES mixed with 50% of distilled water at the reacting condition of temperature $60^{\circ}C$ for 2 hours using water bath. These results indicate that conditioned water content and adequate reaction time are needed to achieve effective extraction of lignin. It was also found that stiffening of cellulose fiber due to the mild treatment of LB DES to BCTMP fiber leads to the increase of paper bulk without the loss of strength.

• Korean Journal of Materials Research
• /
• v.20 no.9
• /
• pp.451-456
• /
• 2010

A promising candidate material for a $H_2$ permeable membrane is SiC due to its many unique properties. A hydrogen-selective SiC membrane was successfully fabricated on the outer surface of an intermediate multilayer $\gamma-Al_2O_3$ with a graded structure. The $\gamma-Al_2O_3$ multilayer was formed on top of a macroporous $\alpha-Al_2O_3$ support by consecutively dipping into a set of successive solutions containing boehmite sols of different particle sizes and then calcining. The boehmite sols were prepared from an aluminum isopropoxide precursor and heated to $80^{\circ}C$ with high speed stirring for 24 hrs to hydrolyze the precursor. Then the solutions were refluxed at $92^{\circ}C$ for 20 hrs to form a boehmite precipitate. The particle size of the boehmite sols was controlled according to various experimental parameters, such as acid types and acid concentrations. The topmost SiC layer was formed on top of the intermediate $\gamma-Al_2O_3$ by pyrolysis of a SiC precursor, polycarbosilane, in an Ar atmosphere. The resulting amorphous SiC-on-$Al_2O_3$ composite membrane pyrolyzed at $900^{\circ}C$ possessed a high $H_2$ permeability of $3.61\times10^{-7}$ $mol{\cdot}m^{-2}{\cdot}s^{-1}{\cdot}Pa^{-1}$ and the $H_2/CO_2$ selectivity was much higher than the theoretical value of 4.69 in all permeation temperature ranges. Gas permeabilities through a SiC membrane are affected by Knudsen diffusion and a surface diffusion mechanism, which are based on the molecular weight of gas species and movement of adsorbed gas molecules on the surface of the pores.

• Journal of the Korean Ceramic Society
• /
• v.44 no.10
• /
• pp.562-567
• /
• 2007

To precipitate the complex gels of the pH 6, 7, 8, 9 included in a flux and an aluminum hydroxides gel, an aqueous solution of a mixture of $Na_2CO_3\;and\;Na_2PO_4{\cdot}12H_2O$ was added with stirring in an aqueous solution of a mixture of $Al_2(SO_4){_3}{\cdot}18H_2O,\;Na_2SO_4\;and\;K_2SO_4$, and then the complex gels were aged in 20 h at $90^{\circ}C$. As the hydrolysis pH changed, it had an effect on the physical properties such as the crystal structure, crystal morphology and a phase transition temperature of the AlO(OH) gel, and also on the crystal structure, crystal morphology, particle size and particle size distribution of the ${\alpha}-Al_2O_3$ platelets prepared by molten-salt precipitation. Also, in this study, the complex gels were crystallized at $1,200^{\circ}C$ and thereafter dried at $110^{\circ}C$, and then it was investigated to effect of the hydrolysis pH on the crystal structure, morphology and particle size distribution of the ${\alpha}-Al_2O_3$ platelets crystals using XRD, DTA, SEM and particle size analyzer.

• Proceedings of the Korean Institute of Electrical and Electronic Material Engineers Conference
• /
• 2008.11a
• /
• pp.429-429
• /
• 2008

Li$[Ni_{1/2}Co_{1/2}]O_2$ powder were synthesized from co-precipitation spherical metal oxide, $[Ni_{1/2}Co_{1/2}](OH)_2$. The preparation of metal hydroxide was significantly dependent on synthetic conditions, such as pH, amount of chelating agent, stirring speed, etc. The optimized condition resulted in $[Ni_{1/2}Co_{1/2}](OH)_2$, of which the particle size distribution was uniform and the particle shape was spherical, as observed by scanning electron microscopy. Calcination of the uniform metal hydroxide with LiOH at higher temperature led to a well-ordered layer-structured Li$[Ni_{1/2}Co_{1/2}]O_2$, as confirmed by X-ray diffraction pattern. Also these materials have ${\alpha}-NaFeO_2$ ($R\bar{3}m$) structure. Due to the homogeneity of the metal hydroxide, $[Ni_{1/2}Co_{1/2}](OH)_2$, the final product, Li$[Ni_{1/2}Co_{1/2}]O_2$, was also significantly uniform, i.e., the average particle size was of about 10 to 15 ${\mu}m$ in diameter and the distribution was relatively narrow. As a result, the corresponding tap-density was also high approximately 2.41 $gcm^{-3}$, of which the value is comparable to that of commercialized $LiCoO_2$.

• Journal of Korea Foundry Society
• /
• v.17 no.2
• /
• pp.170-179
• /
• 1997

A noble technique has been developed for fabricating in situ formed $TiC_p/Al$ composites. In this process, fairly stable TiC particles were in situ synthesized in liquid aluminum by the interfacial reaction between an Al-Ti melt and SiC, which is a comparatively unstable carbide from the view-point of thermodynamics. It is possible in the present process to generate TiC particles of nearly 1 ${\mu}m$ in diameter, even utilizing SiC of 14 ${\mu}m$ as raw material. However, the dispersion behavior of TiC particles in the matrix depends on the size of the raw material SiC. Decomposing finer SiC makes the dispersion of TiC particles more uniform and the mechanical properties of composites are improved accordingly. The structure of in situ composites and their mechanical properties are affected by the fabrication temperature and the stirring time. It has been found that the most suitable condition for fabrication should be applied depending on the size of the raw material, even if the same kinds of carbide are used. Furthermore, although Al-Ti-Si system intermetallic compounds are detected in a $TiC_p/Al-Si$ composite which is fabricated by conventional melt-stirrng method, these compounds can not be observed in a $TiC_p/Al-Si$ composite made by this in situ production method. Hence the mechanical properties of the in situ $TiC_p/Al-Si$ composite are superior to those of the conventional $TiC_p/Al-Si$ composites.