• Proceedings of the KWS Conference
• /
• 2002.10a
• /
• pp.384-389
• /
• 2002

This study was aimed to evaluate the weldability and optimize the welding conditions for flash butt welding of 780MPa grade steel applied to the automotive bumper reinforcement. And then the relationship between the welding conditions and the joint performance relating specifically to coil-joining steel would be established. The effect of welding conditions between flashing and upsetting process was elucidated. Microstructure observation of the joint indicated that the decarburized band was mainly changed with upsetting process. Width of HAZ was also related to the upsetting conditions rather than the flashing conditions. Generally maximum hardness at HAZ was correlated with $C_{eq}$ of steel and the empirical relationship was obtained to estimate the HAZ properties. Tensile elongation at the joint was usually decreased with increasing the initial clamping distance. Investigation of fracture surface after tensile and bending tests reveal that the origin of cracking at the joint was oxide inclusions composed of $SiO_2$, MnO, $Al_2$ $O_3$, and/or FeO. The amount of inclusions was dependent on the composition ratio of Mn/Si in steel. If this ratio was above 4, the amount of inclusions was low and then the resistance to cracking at the joint was enough to maintain the joint performance. It was obtained that the flashing process influenced the conditions for the energy input to establish uniform or non-uniform molten layer, while the upsetting conditions influenced the joint strength. Heat input variable during flashing process was also discussed with the joint properties.

• Journal of Welding and Joining
• /
• v.9 no.4
• /
• pp.17-27
• /
• 1991

The direct brazing technology which could be used for the simplification of brazing process and the improvement of brazed joint quality was studied with $Al_2O_3$ and stainless steels. The brazing of $Al_2O_3$ to STS304 or STS430 was performed under different brazing conditions such as brazing filler metal, temperature, heating rate and brazing time. Microstructural observation and chemical analysis be SEM/EPAM were carried out to verify the quality of brazed joints. 4-point bending strength of brazed joints was also measured to find the optimal brazing conditions. The results showed that, in brazing of $Al_2O_3$, the mixed oxide layer resulted from the reaction between Ti in filler metal and oxide layer on the material surface to be brazed was found to be bery important for the joint quality. The width of oxide layer varied with the brazing conditions such as brazing time, heating rate and chemical composition of filler metals. The strength of brazed joints was more affected by the type of materials and their thermal properties than by brazing heat cycle.

• Journal of the Korean Society for Heat Treatment
• /
• v.20 no.2
• /
• pp.65-71
• /
• 2007

Microstructural changes and hardness variations in STS 304 steel have been investigated during the processes of carbide dispersion (CD) carburization; carburization, austenitization, subzero treatment and tempering. The carbon content of the surface layer increased up to maximum 4.0% after carburization, and the content was homogenized with the value of 2.3% to the $95{\mu}m$ from the surface after austenitization. The carbide appeared during CD carburization process was $Cr_7C_3$ type, which was composed network carbides along the austenite grain boundaries, square type carbides in the interior of the grain and fine nano-sized carbides. The fine nano-sized carbides precipitated at the austenitization stage and possibly subzero treatment stage were coarsened after tempering at $200^{\circ}C$, resulting the hardness decrease. The tempered steel without subzero treatment increased hardness with increasing time due to the continuous precipitation of fine carbides during tempering. The nano-sized carbide appeared square type morphology.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.21 no.4
• /
• pp.406-414
• /
• 2001

Ultrasonic guided waves were explored to apply them to the long range inspection of polyethylene coated steel gas pipes. The steel pipes have such dimensions as 190.7mm inside diameter and 5.3mm thickness. The outside surface of the pipe is coated by a polyethylene layer of $1.9{\pm}0.5mm$ thickness. Non-axisymmetric guided waves were excited on the outside surface of the polyethylene coated pipe by using a 0.5MHz transducer with a variable angle shoe. Frequency and phase velocity tuning was used to find optimum guided wave modes for the inspection. The dispersive characteristics of the modes were analyzed in time-frequency representation obtained by short time Fourier transforms. Sample results were presented for artificial defects such as wall thinning and hole.

• Transactions of the Korean Society of Mechanical Engineers A
• /
• v.26 no.8
• /
• pp.1690-1697
• /
• 2002

The effects of re-peening on the fatigue damaged material are studied in this paper. The effects of re-peening process on surface hardness, surface roughness, surface compressive residual stress, and fatigue life are investigated. The results can be summarized in brief as follows: The depth of hardening layer was increased by re-peening process. There is no large variation of the surface roughness by re-peening process. The compressive residual stress of shot-peened specimen decreases under the fatigue loading and then increases again by re-peening process. Re-peening process increases the fatigue lifo of shot-peened and fatigue damaged specimen. The increase of fatigue lift under high stress level is much higher than under low stress level.

• Applied Microscopy
• /
• v.43 no.2
• /
• pp.88-97
• /
• 2013

Technical investigation to figure out the problems arising during in-situ heating electron backscatter diffraction (EBSD) analysis inside scanning electron microscopy (SEM) was carried out. EBSD patterns were successfully acquired up to $830^{\circ}C$ without degradation of EBSD pattern quality in steels. Several technical problems such as image drift and surface microstructure pinning were taking place during in-situ experiments. Image drift problem was successfully prevented in constant current supplying mode. It was revealed that the surface pinning problem was resulted from the $TiO_2$ oxide particle formation during heating inside SEM chamber. Surface pinning phenomenon was fairly reduced by additional platinum and carbon multi-layer coating before in-situ heating experiment, furthermore was perfectly prevented by improvement of vacuum level of SEM chamber via leakage control. Plane view in-situ observation provides better understanding on the overall feature of recrystallization phenomena and cross sectional in-situ observation provides clearer understanding on the recrystallization mechanism.

• Steel and Composite Structures
• /
• v.45 no.3
• /
• pp.349-367
• /
• 2022

In this research, an approach combining a semi-analytical method and an analytical method is presented to investigate the static and dynamic post-buckling behavior of the sandwich functionally graded (FG) porous cylindrical shells exposed to external pressure. The sandwich cylindrical shell considered is composed of a viscoelastic core and two FG porous (FGP) face layers. The viscoelastic core is made of Kelvin-Voigt-type material. The material properties of the FG porous face layer are considered continuous through each face thickness according to a porosity coefficient and a volume fraction index. Two types of sandwich FG porous viscoelastic cylindrical shells named Type A and Type B are considered in the research. Type A shell has the porosity evenly distributed across the thickness direction, and Type B has the porosity unevenly distributes across the thickness direction. The FG face layers are considered in two cases: outside metal surface, inside ceramic surface (OMS-ICS), and inside metal surface, outside ceramic surface (IMS-OCS). According to Donnell shell theory, von-Karman equation, and Galerkin's method, a discretized nonlinear governing equation is derived for analyzing the behavior of the shells. The explicit expressions for static and dynamic critical buckling loading are thus developed. To study the dynamic buckling of the shells, the governing equation is examined via a numerical approach implementing the fourth-order Runge-Kutta method. With a procedure presented by Budiansky-Roth, the critical load for dynamic post-buckling is obtained. The effects of various parameters, such as material and geometrical parameters, on the post-buckling behaviors are investigated.

• Tribology and Lubricants
• /
• v.20 no.6
• /
• pp.306-313
• /
• 2004

Many of the current development in surface modification engineering are focused on multilayered coatings, which have the potential to improve the tribological properties. Four different multilayered coatings were deposited on AISI D2 steel in this study. The prepared samples are designed as $WC-Ti_{0.6}Al_{0.4}N,\;WC-Ti_{0.53}Al_{0.47}N,\;WC-Ti_{0.5}Al_{0.5}N\;and\;WC-Ti_{0.43}Al_{0.57}N$. The multilayered coatings were investigated with respect to coating surface and cross-sectional morphology, roughness, adhesion, hardness, porosity and tribological behaviors. Especially, wear tests of four multilayered coatings were performed by using a ball-on-disc configuration with a linear sliding speed of 0.017 m/sec and a normal load of 5.38 N load. The tests were carried out at room temperature in air by employing AISI 52100 steel ball $(H_R\;=\;66) $ having a diameter of 10 mm. The surface morphology, and topography of the wear scars of samples and balls have been determined by using scanning electron spectroscopy (SEM). Also, wear mechanism was determined by using SEM coupled with energy-dispersive spectroscopy (EDS). Results have showed an improved wear resistance of the $WC-Ti_{1-x}Al_xN$coatings with increasing of Al (aluminum) concentration.

• Journal of the Korean Society for Nondestructive Testing
• /
• v.20 no.5
• /
• pp.397-401
• /
• 2000

The corrosion-fatigue characteristics of the 12Cr steel, which is widely used in fossil power plants as a turbine blade material, are evaluated nondestructively by use of the Rayleigh surface wave. In this study, the frequency dependency of the Rayleigh surface wave is investigated indirectly by measuring the angular dependency of the backward radiation of the incident ultrasonic wave in the aged specimens, and then compared to the corrosion-fatigue characteristics. The width of the backward radiation profile decreases as the increase of the aging temperature, which seems to result from the increase of the effective degrading layer thickness. This parameter also shows an inversely proportionality to the exponent, m, in the Paris law which predicts the crack size increasement due to fatigue. The result observed in this study demonstrates high potential of the backward radiated ultrasound as a tool for the nondestructive evaluation of the corrosion-fatigue characteristics of the aged materials.

• Journal of the Korea institute for structural maintenance and inspection
• /
• v.19 no.5
• /
• pp.83-91
• /
• 2015

With varying conditions of concrete surface, induced chloride contents are changed and this is a key parameter for steel corrosion and service life in RC (Reinforced Concrete) structures. Many surface enhancement techniques using impregnation have been developed, however the evaluation techniques for chloride behavior through doubly layered media and time-dependent diffusion are rarely proposed. This paper presents an analysis technique considering double-layer concrete and time-dependent diffusion behavior, and the results are compared with those from the previous test results through reverse analysis. The chloride profiles from the surface-impregnated concrete exposed to atmospheric, tidal, submerged zone for 2 years are adopted. Furthermore surface chloride contents and diffusion coefficients are obtained, and are compared with those from Life365. Through consideration of time effect, the relative error decreases from 0.28 to 0.20 in atmospheric, 0.29 to 0.11 in tidal, and 0.54 to 0.40 in submerged zone, respectively, which shows more reasonable results. Utilizing the diffusion coefficients from Life365, relative errors increases and it needs deeper penetration depth (e) and lower diffusion coefficient ratio ($D_1/D_2$) due to higher diffusion coefficient.