• Journal of Welding and Joining
• /
• 제2권1호
• /
• pp.49-57
• /
• 1984

The influence of weld defect, residual stress and microstructure on the Low Cycle Fatigue(L. C. F.) behaviour of AISI 304L austenitic stainless steel weldment has been studied. The specimens were welded by shielded metal are welding process, post weld heat treated(PWHT) at 900.deg.C for 1.5hrs, and tested under total strain controlled condition at room temperature. The results of the experiment showed that weld defect affected the L.C.F. behaviour of weldment deleteriously compared to the residual stress or microstructure, and it reduced the L.C.F. life about 70-80%. The PWHT exhibited beneficial effect on the L.C.F. behaviour and increased the L.C.F. life about 120%. This enhancement by PWHT was attributed to the removal of residual stress and recovery of weld metal ductility. The cyclic stress flow of as welded specimens showed intermediate cyclic softening, whereas those of heat treated specimens showed continuous cyclic hardening, and this difference was explained in terms of the residual stress removal and dislocation behaviour. Scanning electron microscopy studies of fatigue fracture surface showed that weld defects of large size and near weld surface were detrimental to the L.C.F. behaviour of weldment.

• Corrosion Science and Technology
• /
• 제3권2호
• /
• pp.81-86
• /
• 2004

The sulfide stress corrosion cracking (SSCC) resistance of API X70 grade steel weldment has been studied using SSCC test in NACE TM-O177 method A. Also, microstructures and hardness distribution of weldment was investigated. The microstructure of SAW joint composed ferrite, pearlite and some MA constituent. Instead of hardening in CGHAZ, softening on the HAZ near base metal occurred. The low carbon TMCP type steel used for SAW showed softening behaviour in the HAZ adjacent to base metal, which was known to be closely related with the SOHIC (stress oriented hydrogen induced cracking). The SSC testing revealed that the API X70 SAW weld was suitable for sour service, satisfying the NACE requirements. By suppressing softening in the ICHAZ region, the SSCC resistance of low carbon TMCP steel welded joints could be more improved.

• Journal of Welding and Joining
• /
• 제17권3호
• /
• pp.96-101
• /
• 1999

Microstructures and mechanical properties of weldments were studied for EH36 TMCP higher-strength hull steel with electrogas welding jprocess. In case of a newly designed EH36 TMCP steel for large heat input welding process, the Microstructures of HAZ shows more narrow width of grain coarsed region than that of conventional EH36 TMCP weldments, the amount of acicular ferrite, which is beneficial to impact toughness, increased while the amount of grain-boundary ferrite decreased. Charpy V-notched impact tests show that a newly designed EH36 TMCP steel weldment satisfies all the requirement of specifications, especially at the fusion line +2mm where the conventional EH36 TMCP steel fails to exceed the requirement.

• Journal of Welding and Joining
• /
• 제27권5호
• /
• pp.34-41
• /
• 2009

Thermal and mechanical characteristics in dissimilar SS400-STS304 steel weldment have been investigated by 3D thermal elastic-plastic analysis. Moreover, the influence of welding residual stresses on the mechanical behaviour of this welded joint, by applying superimposed external load (tension load) was determined. The residual stresses obtained by numerical simulation were compared with the experimentally measured results. The FE results were in good agreement with the measured values. The mechanical test (hardness, tensile test) and metallurgical analysis was carried out to ensure the weld integrity. Hence, possibility of applying SS400-STS304 dissimilar steels in industries has been established.

• 동력기계공학회지
• /
• 제13권4호
• /
• pp.43-48
• /
• 2009

The purpose of this study is to show how to eliminate the noises and to obtain the data related with the relationship between AE signal characteristics and mechanical behaviors for the pressure vessel steel. Various kinds of noises are introduced into the AE data in the course of experiments. Accordingly, real AE data have to be obtained after tests. AE test was carried out under four point bending load. Among AE signals, counts and signal strength are used to find out the differences of AE characteristics between the basemetal and weldment. After tests, this paper shows the procedures of filtering the noises against basemetal of the pressure vessel steel to obtain the real data around crack tip. Relationships between plastic zone size and cumulative AE counts are shown also. AE signals were absent within an elastic region, regardless of the specimens. Most of AE signals are produced in the process of plastic deformation. The deformation and fracture modes of basemetal and weldment are quiet different.

• 대한용접접합학회:학술대회논문집
• /
• 대한용접접합학회 2002년도 Proceedings of the International Welding/Joining Conference-Korea
• /
• pp.408-411
• /
• 2002

Effect of in-situ vibration on the properties of A-grade steel SMA weldment has been investigated. Welding was performed on the steel fixed at the experimental jig under the mechanical vibration of a given frequency. The applied frequency varied from 39 to 43.5 Hz (harmonic frequency). For weldments formed under the vibration with a sub-harmonic frequency, both the columnar width of the weld metal and the prior austenite grain size of the HAZ near the fusion line clearly decreased. This indicates that the vibration increase the cooling rate after welding. Vibration effect was also found at the weld metal formed at the center region of the weldment. The weld metal showed liner microstructure both in columnar zone and in equiaxed zone with thinner grain boundary ferrite. However mechanical properties of the weld metal did not exactly follow the microstructural changes developed under the vibration. The weld metal formed under the vibration revealed higher yield and tensile strength but lower ductility and impact toughness, compared with the conventional weld metal.

• 한국해양공학회지
• /
• 제22권6호
• /
• pp.27-34
• /
• 2008

The temperature distribution in the weldment is not uniform because a weldment is locally heated. Thermal plastic deformation results from the local expansion and shrinkage by the heating and cooling of metal. Therefore, residual stresses and distortion occur in the weldment. In this study, we had conducted on the weld thermal cycle simulation that is supposed as the HAZ on SS400 steel and STS304 steel. The residual stresses that were obtained from the drawing and the weld thermal cycle simulation were estimated by X-ray diffraction. We also carried out ultrasonic test for the weld thermal cycle simulated specimens, and then conducted on nondestructive evaluation by the ultrasonic parameters obtained ultrasonic test. From the results, residual stresses of weld thermal cycle simulated specimens after the residual stress removal heat treatment are lower than that of the drawing.

• 대한기계학회논문집A
• /
• 제27권9호
• /
• pp.1444-1450
• /
• 2003

The fatigue life and tensile strength of JLF-1 steel (Fe-9Cr-2W-V-Ta) and its TIG weldment were investigated at the room temperature and $400^{\circ}C$. Four kinds of test specimens, which associated with the rolling direction and the TIG welding direction were machined. The base metal of JLF-1 steel represented almost anisotropy in the tensile properties for the rolling direction. And the base metal of JLF-1 steel showed lower strength than that of TIG weldment. Also, the strength of all materials entirely decreased in accordance with elevating test temperature. Moreover, the fatigue limit of weld metal was largely increase than that of base metal at both temperatures. The fatigue limit of JLF-1 steel decreased in accordance with elevating test temperature. The fatigue limit of JLF-1 steel decreased in accordance with elevating test temperature. The SEM fractography of tensile test specimen showed conspicuous cleavage fracture of a radial shape. In case of fatigue life test specimen, there were so many striations at crack initiation region, and dimple was observed at final fracture region as a ductile fracture mode.

• 한국재료학회지
• /
• 제14권1호
• /
• pp.78-82
• /
• 2004

In this study, the degree of creep damages on the weldment accelerated creep degradation was nondestructively evaluated by replica method. The frequency of creep cavities occurrence has been observed highly at the intercritical HAZ. The life fraction of weldment damaged by creep has shown from 0.25(damage grade: 2) to 0.75(damage grade: 4) when it reptured. The degree of creep damages is considered to be evaluated by the metallographic replica method which is one of nondestructive evaluation methods.

• Journal of Welding and Joining
• /
• 제21권1호
• /
• pp.99-106
• /
• 2003

This research was aimed to evaluate the material degradation with various microstructures of X20CrMoV121 steel weldment by Advanced Small Punch(ASP) test. Due to the regional limitation on constitutive structures, the minimized loading ball(${\varphi}1.5mm$) and bore diameter of lower die(${\varphi}3mm$) were designed for the ASP test. The micro-hardness test was also performed to assess the mechanical properties with artificial aging heat treatment. Material degradation was estimated by ductile-brittle transition temperature(DBTT). The results obtained from the ASP test were compared with those from conventional small punch(CSP) test and CVN impact test for several weldment microstructures. It was found that the ASP test clearly showed the microstructural dependance on the material degradation in the weldment.